目前,关于焊接方法对X90管线钢焊接接头组织性能的影响相关报道较少。采用手工电弧焊(SMAW)、熔化极气体保护焊(GMAW)、埋弧焊(SAW)3种焊接方法对X90管线钢进行对接焊。利用金相显微镜(OM)、扫描电镜(SEM)及能谱仪(EDS)对焊接接头及冲击断口进行显微组织及成分分析,分析了焊接方法对X90管线钢焊接接头组织性能的影响规律。结果表明:焊缝区组织主要为粒状贝氏体和针状铁素体;SMAW粗晶区组织主要为多边形铁素体、粒状贝氏体及M/A组织,GMAW和SAW粗晶区组织主要为粗大的铁素体、粒状贝氏体及板条贝氏体;3种焊接接头硬度分布趋势一致,盖面层硬度最高;SMAW、GMAW和SAW焊接接头抗拉强度依次为714,771,790 MPa,断后伸长率依次为23.3%,22.9%,20.0%;SAW与GMAW熔合线处20℃冲击吸收功比SMAW高约40 J,断裂机制为微孔聚集型,在韧窝底部有金属碳化物粒子析出。     

焊前热处理对J55钢自动TIG焊接头组织性能的影响

目的 针对J55钢焊接性较差、接头热影响区（HAZ）易出现脆硬马氏体组织等问题,在焊前对J55钢母材进行热处理,研究其焊接接头。方法 在焊前对J55钢母材进行了760℃与880℃的热处理,采用TIG焊方法进行了焊接,研究了热处理前后TIG焊对接头显微组织和力学性能的影响。结果 经焊前760℃热处理后,母材中的珠光体（P）含量显著减少并且发生细化,焊后接头HAZ组织转变为晶界铁素体（GBF）、针状铁素体（AF）和P;经焊前880℃热处理后,母材的显微组织主要为多边形铁素体（PF）和AF,在焊后接头的HAZ中形成了PF、贝氏体（B）和M-A组元。2种热处理接头焊缝区（WZ）的盖面层组织为GBF和AF,靠近和远离盖面层的打底层组织主要为PF和P;未热处理接头HAZ组织为PF、B和马氏体（M）。与2种热处理接头相比,未热处理接头的显微硬度居中,抗拉强度最高,延伸率最低,拉伸断裂位于熔合线与HAZ之间,断口呈脆性断裂特征。与760℃热处理相比,经880℃热处理的焊接接头HAZ显微硬度最高值达523 HV,为760℃热处理的2.2倍,接头抗拉强度提高了2.2%,但延伸率降低了7.6%。2种热处理接...     

X70管线钢焊接接头热影响区的冲击性能

对X70管线钢焊接接头热影响区进行了冲击试验,对结果进行了分析。结果表明：X70管线钢焊接接头热影响区冲击试样的冲击功与断口剪切面积基本成线性比例关系,冲击功越高,剪切面积越大。焊接接头热影响区冲击试样的断口由韧性区、脆性区和韧脆混合区组成。脆性区为解理断裂,韧脆混合区为准解理断裂。     

低碳贝氏体钢双面埋弧焊接头的组织和低温韧性

对低碳贝氏体钢进行双面埋弧焊焊接,并用光学显微镜和PSW750型示波冲击试验机对焊接接头进行表征,研究了钢的显微组织和低温韧性。结果表明:低碳贝氏体钢双面埋弧焊后,焊缝区的组织为针状铁素体和粒状贝氏体;HAZ的组织为贝氏体铁素体和粒状贝氏体;HAZ熔合线附近的硬度最高,远离熔合线硬度降低并逐渐接近母材金属的硬度;随着温度的降低焊接过程中的凝固偏析、高度集中的位错源来不及松弛应力集中以及分布在晶界上的Ti、Mo等微合金元素形成的碳氮化物,导致焊接接头焊缝区和HAZ韧性降低并在-20℃和-60℃发生韧脆转变。     

不同热输入下X90管线钢CGHAZ组织及脆化研究

通过模拟X90管线钢不同焊接热输入下的单道次焊接热循环过程,对热模拟后的CGHAZ试样进行显微组织观察、冲击以及硬度试验,并对冲击断口进行微观形貌观察,重点研究不同热输入下X90管线钢CGHAZ的微观组织和脆化现象。结果表明:X90管线钢焊接热循环后CGHAZ组织主要为板条贝氏体(LB)、粒状贝氏体(GB)和M/A组元;随着焊接热输入的增加,组织中LB减少,GB和M/A数量增多且尺寸增大;CGHAZ表现为粗晶脆化,冲击吸收功在E=20kJ/cm时出现最大值,冲击断口在E≥30kJ/cm时表现为明显脆断;CGHAZ未出现软化现象。因此,推荐X90管线钢焊接热输入大小低于30kJ/cm。     

退火处理对异种钢激光焊接头组织及性能的影响

目的 通过研究相同时间不同退火温度下304/Q345激光焊接头的组织和性能,得到优化后的退火处理制度,为制定异种钢激光焊退火工艺提供一定的理论指导和技术支撑。方法 基于前期大量试验,在激光功率和离焦量不变的情况下,调节焊接速度由15 mm/s到35 mm/s,通过改变焊接速度获得性能优异的焊接接头。由于异种钢物理化学性能差异较大,接头组织不均匀,因此还需对激光焊接头进行退火处理。结果 焊缝区显微组织由板条马氏体与残余奥氏体组成,Q345低碳钢热影响区显微组织为多面体状铁素体与黑色珠光体,其中铁素体含量更多,304奥氏体不锈钢热影响区在奥氏体晶界上析出了铁素体。不同退火温度下碳元素均由Q345低碳钢侧向焊缝迁移,在Q345低碳钢侧形成脱碳层,在焊缝中形成黑色条带状增碳层。随着退火处理温度的升高,峰值温度升高,高温停留时间变长,碳迁移强度随之增加,黑色条带状区域增碳层宽度增大。拉伸性能测试结果表明,试样均断裂于Q345母材一侧,且断口存在韧窝,属于典型韧性断裂。此外,焊缝区硬度(390HV左右)最高,热影响区硬度(300HV)次之,母材的硬度(130HV左右)最低。结论 在给定试验参数范围内,优化后的最佳退火工艺参数为550 ℃-1.5 h。     

NM360钢与Q345钢异种钢焊接接头组织与性能研究

为了解NM360钢与异种钢焊接应用过程中焊接接头的力学性能,本文对NM360调质钢和Q345热轧钢采用气体保护焊进行异种钢焊接,对焊接接头进行了力学性能试验及微观组织观察,并分析了NM360钢ICHAZ的软化机理.研究表明:Q345热轧钢焊接接头CGHAZ组织为贝氏体+魏氏组织,为HAZ硬度值最高的区域,FGHAZ和ICHAZ组织为P+F;NM360调质钢焊接接头CGHAZ组织为低碳马氏体,FGHAZ组织为低碳马氏体+少量的粒状贝氏体,晶粒细小,为HAZ硬度值最高的区域,ICHAZ组织为回火马氏体+铁素体+粒状贝氏体,铁素体组织是造成ICHAZ硬度值大幅度降低的原因.     

590 MPa级高强钢双面双弧立焊焊缝组织性能

为研究590 MPa级高强钢双面双弧工艺得到的焊接接头组织与性能的关系,采用钨极氩弧焊(TIG)与熔化极气体保护焊(MAG)方法获得成型良好的焊接接头,经过拉伸、冲击、弯曲试验及光学显微镜、扫描电镜、EBSD分析,对590 MPa级高强钢双面双弧立焊打底焊与盖面焊焊接接头的组织及性能进行了研究.结果表明:打底焊缝组织主要为贝氏体,盖面焊缝组织以贝氏体与针状铁素体为主;打底焊缝经历过一次热循环后组织得到一定程度的细化;打底焊缝硬度值与盖面焊缝相近,盖面焊缝热影响区最高硬度值高于打底焊缝热影响区最高硬度;2 mm坡口间隙性能较5 mm坡口间隙有较大提高,2 mm坡口间隙断口以韧窝断裂为主,5 mm坡口间隙断口以解理断裂为主.     

预变形对X90管线钢显微组织和力学性能的影响

采用拉伸试验、冲击试验、光学显微镜(OM)、扫描电镜(SEM)、显微硬度测试仪等研究了0.5%~6%预拉伸变形对X90管线钢显微组织及力学性能的影响。结果表明:随着预拉伸变形量的增加,X90管线钢晶粒增大,位错塞积导致强度增加,均匀延伸率下降,呈现典型的加工硬化特点,抗拉强度的增幅要小于屈服强度,屈强比增大;随着变形量的增加冲击吸收功逐渐由291J减小至235J,冲击试样断口的韧窝减小,伴随第二相粒子析出;显微硬度中间层较边缘区增加少,预拉伸在6%时边缘显微硬度为325HV。X90管线钢的预拉伸在4%以内能保证管线钢的正常服役。     

1.4003铁素体不锈钢与Q235-C钢焊接接头的组织和力学性能

采用室温拉伸、不同温度冲击、硬度及金相检验等分析方法对用熔化极混合气体保护焊焊接的1.4003铁素体不锈钢与Q235-C钢焊接接头的显微组织和性能进行了研究.试验结果表明:该焊接接头的抗拉强度与母材相当,焊缝的冲击性能略低于母材,1.4003铁素体不锈钢的热影响区(HAZ)冲击性能较差,焊缝为奥氏体+铁素体双相组织;Q235-C钢的熔合区出现明显界限,1.4003铁素体不锈钢焊接热影响区为晶粒粗大的单一铁素体组织.     

Local mechanical properties of radial friction welded supermartensitic stainless steel pipes

In this work, supermartensitic stainless steel pipes were radial friction (RF) welded and their microstructures and local mechanical properties (hardness, fracture toughness and micro-tensile strength) were characterized in the as-welded condition. Defect-free RF welds were produced with a matching consumable ring (CR) under optimized welding conditions. The formation of a fine structure consisting of a mixture of virgin martensite and some stable austenite retained in the CR region was observed. On the other hand, the presence of virgin martensite plus δ-ferrite was found in the microstructures of the heat affected zone (HAZ) and thermo-mechanically affected zone (TMAZ). A ductile fracture was detected in the CR and weld interface regions at −40 °C. Moreover, both the CR and weld interface regions showed higher hardness and strength values than those of the base material (overmatching), without presenting significant losses in ductility and fracture toughness, which was attributed directly to the fine transformed microstructure of the weld region.     

Microstructures and mechanical properties of welded joints of novel 3Cr pipeline steel using an inhouse and two commercial welding wires

The welded joints of the novel 3Cr pipeline steel were fabricated via the gas tungsten arc welding (GTAW) technique using an inhouse welding wire labeled as R01 and two kinds of commercial wires (H08Cr3MoMnA and TGS-2CML). Microhardness, impact toughness and tensile properties of the joints were measured, and microstructure characteristics were observed by scanning electron microscopy (SEM). The results show that under selected welding procedure, the joints of R01 can achieve quite good mechanical properties without preheating and post weld heat treatment (PWHT). After thermal refining, elongation (15.2%) doubled and met the DNV-OS-F101 standard. For low carbon or super low carbon pipeline steels such as 3Cr steel, the revised formula with the carbon applicable coefficient (A(c)) was quite good for predicting the maximum hardness in heat affected zone (HAZ). Compared with these two selected commercial wires, the inhouse welding wire R01 can provide the highest cost-performance ratio.     

车用TRIP590钢光纤激光焊接接头组织与性能研究

为了促进先进高强钢激光焊接技术的发展,采用光纤激光器对1.5mm厚的TRIP590钢板进行焊接,对焊接接头的微观组织、硬度以及拉伸性能进行了研究,分析了焊接速度对组织、性能的影响。结果表明:焊缝组织主要为板条状马氏体,热影响区可分为完全淬火区和不完全淬火区。焊接接头硬度分布不均匀,在热影响区或焊缝处硬度最高。随着焊接速度提高,热影响区马氏体含量增多,贝氏体含量减少,热影响区和焊缝组织变得细小。焊接速度为3~5m/min时,拉伸试样均断裂在母材,断后延伸率均超过30%,随着焊接速度提高,断后延伸率也有所提高,强塑积(PSE)均在20000MPa%以上,拉伸变形过程中相变诱发效应显著,大部分残余奥氏体转变为马氏体,在提高材料塑性的同时也提高了强度,实现了高强度和高塑性的统一。     

Q960E超高强钢焊接接头组织和性能研究

目的 对Q960E超高强钢的焊接工艺进行研究以获得高强高韧的焊接接头。方法 选择超高强钢Q960E作为母材、FK1000ER120S–G焊丝作为填充材料进行MAG焊,采用改变焊接电流的方式来研究焊接热输入对焊接接头组织和性能的影响。结果 当焊接电流为155～230 A时,均获得了全焊透无明显缺陷的焊缝。随着焊接热输入的增大,焊接接头中各亚区宽度增大,其中焊缝区变化最为显著,在最小热输入条件下焊缝宽度为3.98 mm,在最大热输入条件下焊缝宽度增至5.53 mm。对焊接接头进行组织分析发现,焊缝组织主要为针状铁素体和板条马氏体;完全相变区组织主要为板条马氏体;未完全相变区组织主要为回火马氏体和部分重结晶形成的马氏体。硬度测试表明,在热影响区的回火区发生了软化现象,最低硬度仅为290HV;在完全相变区发生了硬化现象,硬度最大值可达500HV。在不同热输入条件下,焊接接头各亚区硬度变化趋势一致,焊接接头抗拉强度为995～1 076 MPa,拉伸试验均断裂在热影响区,断后伸长率为9.33%～10.21%,断裂时存在颈缩现象,为韧性断裂。随着热输入的增加,粗晶区马氏体板条束宽度增大,未完全相变区...     

The effect of microstructure on hardness and toughness of low carbon welded steel using inert gas welding

The heat affected zone (HAZ), has a great influence on the properties of welded joints since it can alter the microstructure and residual stresses. In this paper, the effect of welding parameters and heat input on the HAZ and grain growth has been investigated. The role of grain size on hardness and toughness of low carbon steel has also been studied.     

焊接参数对铁素体不锈钢搅拌摩擦焊接头组织及性能的影响

对4mm厚T4003铁素体不锈钢进行搅拌摩擦焊接工艺实验,研究焊接参数对接头组织特征、硬度分布及常温和低温冲击韧性的影响。结果表明:接头搅拌区和热力影响区由铁素体和马氏体双相组织构成;接头搅拌区组织沿试样厚度方向存在非均质性,且随转速的降低及焊接速率的增加越发显著;转速从150r/min增加至250r/min,前进侧热力影响区组织呈现小梯度过渡趋势,无明显变形拉长特征。焊缝硬度分布相对均匀,其最高硬度为290HV,约为母材的1.87倍。焊接参数和温度对接头的冲击吸收功有较大影响:常温(20℃)下,热影响区为母材的90%～92%,搅拌区为母材的85%～103%;低温(-20℃)下,热影响区为母材的87%～97%,搅拌区为母材的82%～95%,表明焊缝区仍具有较好强韧匹配。     

Fracture toughness (J1C) of electron beam welded AA2219 alloy

AA2219 (Al–6%Cu) was butt welded in T87 temper (solution heat-treated, cold worked and precipitation hardened) and T6 temper (solution heat-treated and precipitation hardened) using electron beam welding (EBW). Variables studied were base metal temper condition and mode of EBW. Mechanical properties of the weld joint and fracture toughness at fusion zone (FZ) and heat-affected zone (HAZ) were evaluated and compared with those of the base metal. Results showed that EB welds have higher joint efficiency and fracture toughness than that of gas tungsten arc welding (GTAW). Fracture toughness of T6 base metal was found to be higher than its T87 counterpart. When welded, FZ and HAZ in T87 showed higher fracture toughness than that of T6; HAZ was the toughest. Pulsed current (PC) EB weld showed marginal reduction in toughness compared to constant current (CC) weld. Toughness variation is analyzed with the help of tensile test, Charpy impact test and scanning electron microscopy (SEM) and transmission electron microscopy (TEM).     

Gas tungsten-arc filler welding of AZ31 magnesium alloy

Optical microscopy and scanning electron microscopy (SEM) were used to examine the microstructure and fracture of AZ31 magnesium alloy joint welded by automatic gas tungsten-arc filler (GTAF) welding process with AZ61 wire. More endeavors have been put on investigating the effect of filler wire on microstructure and performance of welded joint. The result showed that the grain size in heat-affected zone (HAZ) of GTAF welded joint holds significant variety compared with that of GTA welded joint (without filler wire). The modification of microstructure in HAZ has changed the fracture location as well as the ultimate tensile strength (UTS) of joint in tensile test.     

BT20钛合金激光焊接接头的断裂韧性研究

对BT20钛合金及其激光焊接接头的断裂韧性进行了研究.同时分析了合金及激光焊接接头的硬度分布及显微组织.断裂实验表明,除了一个焊接接头紧凑拉伸(CT)试样是脆性启裂外,其它CT试样均在裂纹延性启裂并缓慢扩展后,发生脆性失稳断裂.母材的断裂韧性明显高于焊接接头,轧制方向对母材断裂韧性的影响不明显.焊接热影响区的断裂韧性介于母材和焊缝金属之间.本研究采用的焊后热处理没有改善焊接接头的断裂韧性,还有进一步恶化的趋势.添加活性剂对焊缝金属的断裂韧性没有明显作用,但对延性裂纹扩展长度有所改善.