壳聚糖微球固定化脂肪酶催化性质研究

以壳聚糖微球为载体制备固定化脂肪酶制剂并研究其催化性质.首先,制备壳聚糖微球,用2%醋酸溶液溶解壳聚糖,以液体石蜡为分散剂制成壳聚糖微球;然后,通过戊二醛交联制备固定化脂肪酶制剂,并研究其催化性质.结果表明:壳聚糖微球在2%戊二醛浓度下常温下交联9 h,脂肪酶固载率可达60%.与游离脂肪酶相比,壳聚糖微球固定化脂肪酶的最适底物、最适p H值及最适温度分别转变为4-硝基苯基辛酸酯,p H 8.57及50℃.固定化脂肪酶重复实验6次后仍保留有47.7%的催化活性,置于60℃下4 h酶活保留73%,其金属离子K+和Mg2+最适浓度分别为0.15 mol/L,0.10 mol/L.     

纳米TiO2固载脂肪酶及其固载界面表征

以3种不同形貌的纳米TiO2为载体固定化脂肪酶,研究载体形貌、酶添加量、pH值、温度和时间对固载酶活性的影响.研究结果表明,纳米线形貌TiO2固定化效果最好,最优固定化条件为加酶量0.25g/25mL溶液、pH 7.0、固载温度40℃、固载时间6.3h.利用SEM、XRD、FT-IR等对固载酶及其界面进行表征,SEM和XRD结果表明,脂肪酶吸附于纳米线TiO2载体表面,且未改变纳米线TiO2的晶型结构;FT-IR表征表明固载酶含有脂肪酶的特征吸收峰;比表面积分析显示固定化后样品的BET明显减小,表明脂肪酶在纳米线TiO2表面进行物理型吸附.     

仿生合成SiO2载体及其固定脂肪酶的条件研究

采用L-脯氨酸为模板,仿生制备用于固定脂肪酶的二氧化硅载体．SEM、IR表征得知,制备的仿生载体为粒径约3um的SiO2微球,氮气吸附表征得知,SiO2微球内部孔径大小约16．8nm．载体固定脂肪酶的实验结果表明,固定化脂肪酶的相对最佳条件：酶液质量浓度5mg／mL,反应温度40℃,反应时间7h,pH=8,最高固载率可达82．3％,酶活1067U／g载体．     

羟基磷灰石表面改性对PET过滤布固载效果的影响（英文）

采用热熔法将表面改性的羟基磷灰石固载到PET过滤布上,探讨了未改性、甲基丙烯酸酯化改性和甲基丙烯酸甲酯接枝聚合改性的羟基磷灰石在不同热熔温度、热熔时间和颗粒量条件下对PET过滤布颗粒固载率及孔径大小影响。通过镉离子吸附测试评价了不同方法制备的过滤布对重金属吸附性能。结果表明,PET过滤布固载接枝改性的羟基磷灰石时能获得更高固载率和更大孔径及镉离子吸附量。     

聚合物刷改性的纳米纤维在固定化脂肪酶中的应用

基于静电纺丝技术制备甲基丙烯酸甲酯-丙烯酸共聚纳米纤维(PMMA-co-PAA),利用壳聚糖(CTS)和甲基丙烯酸钠对纳米纤维改性.以该纳米纤维作为载体固定脂肪酶,研究改性纳米纤维对酶的固载量及稳定性的影响.试验表明,改性纳米纤维的亲水性和纤维直径得到提高,当甲基丙烯酸钠浓度为0.1mol/L时,酶的固载量达到165mg/g.此外,相比于游离酶,固定化脂肪酶有较高的温度和pH值稳定性,pH值在5~9,温度在20~60℃变化时,固定化酶在最低点的相对活性相比游离酶提升了325%和400%;60℃保温10h后,固定化酶的相对活性比游离酶提升170%.     

表面复合修饰磁性颗粒固定化脂肪酶效能研究

以表面复合修饰的纳米超顺磁性Fe_3O_4颗粒聚集体为载体固定胰脂肪酶,比较分析固定化脂肪酶的固载效能及酶学特性,研究了固定化及游离脂肪酶的最适温度和pH值、不同环境下的操作稳定性等应用特性及基本动力学特征。结果表明:在室温下脂肪酶质量浓度为4.01 mg/mL时具有最大的固载酶量0.72 mg/10 mg,固定化脂肪酶最适作用pH为6,最适温度35℃,与游离脂肪酶相比,对酸性环境pH的变化更敏感,但具有更广泛的温度耐受性。固定化脂肪酶催化水解Lineweaver-Burk曲线线性相关,米氏常数K_m值为9.65 g/mL,远高于游离脂肪酶,亲和性弱于游离脂肪酶。固定化脂肪酶重复催化反应7次,相对酶活力仍剩余51.6%,半衰期为6.2次,重复操作较稳定。     

离子交换树脂固定化脂肪酶催化合成蔗糖乙酯

南极假丝酵母(Candida rugosa)脂肪酶具有优良的催化性能,对其进行固定化可以很方便地实现酶的回收和再利用.采用4种离子交换树脂为载体,对来源于南极假丝酵母的脂肪酶进行了吸附固定化,并对固定化酶催化合成蔗糖乙酯的活性进行考察.结果表明,以弱碱性丙烯酸系阴离子交换树脂214为载体的固定化酶活性最高.固定化酶制备过程中缓冲液的最适宜pH值为8.4,最佳固定化时间为3h,最佳酶液浓度为8mg/mL,最适固定化温度为35℃.所得固定化酶催化合成蔗糖乙酯,酯化率达57.12%,蔗糖-6-乙酯的选择性达到51.21%.10批反应后,该固定化酶仍有较高的酶活力.     

改性玻璃纤维填充聚丙烯复合材料的制备与力学性能

为比较不同改性剂对填充聚丙烯用玻璃纤维表面改性的优劣及改性剂的最佳用量,使用熔融共混法研究了两种硅烷偶联剂、钛酸酯偶联剂以及马来酸酐接枝聚丙烯改性玻璃纤维对玻璃纤维填充聚丙烯复合材料的力学性能的影响．并用扫描电子显微镜观察了几种不同的表面处理对聚丙烯／玻璃纤维复合材料断面形貌影响．结果表明,所使用的几种改性剂都能改善聚丙烯的力学强度和模量．扫描电镜照片显示聚丙烯与玻璃纤维间的界面相互作用的强弱与聚丙烯／玻璃纤维复合材料的力学性能之间有着紧密的关系．此外,力学数据结果表明,使用８％ 的马来酸酐接枝聚丙烯相容剂对聚丙烯／玻璃纤维复合材料的增强效果最佳,硅烷偶联剂的效果次于马来酸酐接枝聚丙烯,钛酸酯偶联剂的改性效果最差．     

玻璃纤维布增强造纸脱墨污泥纤维板性能研究

研究造纸污泥资源化利用,分析偶联剂对玻璃纤维布增强造纸脱墨污泥纤维板物理性能的影响.结果表明,随着偶联剂的加入,纤维板的各项性能均有明显提高,但偶联剂的加入量超过1.0%后,纤维板性能的改善不再显著.红外光谱分析发现,偶联剂改善玻璃纤维表面极性,使得玻璃纤维与酚醛树脂胶产生共价连接.扫描电镜观察发现,偶联剂能增加玻璃纤维表面粗糙度,由于酚醛树脂对玻璃纤维表面是润湿的,改善了玻璃纤维表面的润湿性,有利于胶合.     

氮表面修饰活性炭纤维的脱硫性能

为了研究氮表面修饰活性炭纤维脱硫性能,将活性炭纤维（ACF）浸渍在不同浓度尿素溶液中,然后在不同温度下进行热处理,对ACF进行含氮官能团表面修饰改性处理。评价了其脱除模拟烟气中二氧化硫的性能,并通过SEM、XPS和TG等手段研究了改性处理对ACF的表面含氮官能团的影响。实验结果表明：热处理温度为750℃、尿素溶液浓度为2.4mol/L制备条件下得到的样品具有最佳脱硫性能, 其平台阶段脱硫效率达到了60%;浸渍尿素热处理改性ACF可以增加表面含氮官能团的数量,其中对脱硫性能起主要作用的吡啶氮增加最多,含量是未改性的近5倍。     

中空玻璃微珠填充环氧树脂复合材料

讨论了用发电厂固体废料中的中空玻璃微珠填充Ｅ－４４环氧树脂制备轻质复合材料，实验详尽地考察了微珠填料，ＫＨ－５００偶联剂，固化剂（三乙基四胺，Ｔ－３１，三乙醇及液体四氢苯酐）及低聚酰胺等增韧剂等对所得的复合材料为力学性能的影响，并通过扫描电镜（ＳＥＭ）观察了材料的形态，其结果表明，偶联剂和增韧剂对复合材料的力学性能影响较大，中空玻璃微珠填充环氧树脂赋予基轻质，高强，价廉等特性。     

Tribological Properties of Polytetrafluoroethylene Composites Filled with Rare Earths Modified Glass Fibers

1Introduction Polytetrafluoroethyleneisakindofperfectself lubri catingmaterialduetoitsverylowfrictioncoefficient,goodhightemperaturestabilityandchemicalstability.Yetitcannotbeusedasanti wearmaterialalonebecause ofitspoormechanicalproperties,badthermalconductivi tyandhighwearrate.Therefore,variousreinforcement andmodificationofPTFEhavebeentried,andthefric tionandwearpropertiesofPTFEcompositeshavebeen extensivelystudiedbymanyinvestigators[14].Glassfiberexhibitsahightensilestrengthandten sile…     

硅烷偶联剂改性对聚丙烯纤维抗裂效果的影响

采用乙烯基三乙氧基硅烷偶联剂(SCA-1613)对聚丙烯纤维分别进行浸泡和表面接枝改性,并研究了最佳改性工艺条件;通过对开裂指数和断裂能的测试,研究了偶联剂改性对聚丙烯纤维在砂浆中的抗裂性能的影响。结果表明,与未改性纤维相比,经硅烷浸泡处理后的纤维,可明显提高水泥基材料的抗塑性开裂性能,其最佳的纤维体积掺量为0.08%,改性效果较突出。     

硅烷偶联剂改性白炭黑在丁苯橡胶中的应用

研究了硅烷偶联剂改性白炭黑在丁苯橡胶 (SBR)中的应用 ,探讨了硅烷偶联剂种类和用量对SBR胶料性能的影响。结果表明 ,在使用白炭黑的SBR胶料配方中加入硅烷偶联剂 ,可以降低胶料的门尼粘度 ,缩短硫化时间。胶料的综合力学性能都有不同程度的提高。     

Surface modification of fire-retardant asphalt with silane coupling agent

The theory and approach of the surface modified of asphalt fire-retardant with silane coupling agent were introduced.The optimum silane dosage was determined,and the structure and properties of the asphalt fire-retardant before and after the surface modification were characterized by infrared spectrum and thermo gravimetric analysis.The dispersion effect of asphalt fire-retardant was studied.The influence of the surface modification on the hydrophilicity and lipophilicity of the asphalt fire-retardant was analyzed.The experimental results showed that there were physical and chemical interactions between the silane coupling agent and the asphalt fire-retardant,which reduced the surface polarity of the asphalt fire retardant.The optimum silane coupling agent dosage was 0.95% of the asphalt fire retardant.The surface modification improved the thermal stability,dispersibility and lipophilicity of the asphalt fire retardant,which enhanced the compatibility between asphalt fire retardant and asphalt.     

A STUDY OF THE STRUCTURAL LAYERS OF COUPLING AGENTS AND THE MICROSCOPIC RHEOLOGY IN THE INTERFACES OF GF/UP SYSTEMS

The coupling agents content and thickness on glassfiber (GF) surfaces which have been treated with silanesand titanates under different conditions are tested bymeans of XRF (X-Ray Fluorescent spectrometry). And therheological characteristics of the dispersed systemsprepared from the above glass fibers combined withunsaturated polyester resin (UP) are discussed. Theresults show that the rigidity of the internal layers ofsilane coupling agent absorbed by glass surfaces isgreater than the one of the external layers; while theeffect of the titanate coupling agents on the rheolo-gical characteristics of the system is approximatelythe same in each structural layer, that is due to thefact that both the internal and external layers oftitanates on glass surfaces have the similar flexiblestructures.     

芳纶纤维表面改性及其对芳纶纸物理性能的影响

利用磷酸、硅烷偶联剂、硝化/还原改性剂等对芳纶纤维进行改性,再以改性后的芳纶纤维配抄芳纶纸,探讨芳纶纤维表面改性及其对芳纶纸物理性能的影响.结果表明,上述3种改性方法均可以改善芳纶纤维与芳纶浆粕界面的结合,从而提高芳纶纸的强度.     

硅烷偶联剂处理对玄武岩单丝拉伸性能的影响

用硅烷偶联剂KH-550对不同品种的玄武岩纤维进行表面改性处理,采用单丝拉伸试验,结合扫描电镜和SPSS统计分析的方法,研究了硅烷偶联剂处理对玄武岩单丝拉伸性能的影响.结果表明:表面处理前后,玄武岩纤维品种2和3的拉伸强度和断裂伸长率均没有显著变化;玄武岩纤维品种1的拉伸强度和断裂伸长率明显增大,其拉伸强度提高32.8%,断裂伸长率增大31.79%.这证明用硅烷偶联剂KH-550对玄武岩纤维进行表面改性处理,可以达到表面处理的目的且不损伤玄武岩单丝的拉伸性能,一定程度上可以弥补玄武岩纤维生产工艺的不足.     

Effects of Silane Coupling Agent on Microstructure and Mechanical Properties of EPDM/Carbonyl Iron Microwave Absorbing Patch

The effects of types and amounts of silane coupling agent on mechanical properties of vuleanized rubber microwave absorbing patch （VRMAP） were studied. The mechanisms of silane coupling agent＇s effects on mechanical properties of rubber microwave absorbing patch （ RMAP ） and microvave absorbing patch＇s （MAP＇s） mierostrueture were also discussed by using SEM and FT-IR. The experimental results show that the tensile strength of RMAP could be increased through adding the filler of carbonyl iron powder （CIP） modified by silane coupling agent. RMAP fiUed with CIP, which was treated by silane coupling agent KH550, possessed a high tensile strength of 11.5 MPa, which was 448% more than that of MAP whose filler wus not modified by any coupling agent. It was found that the optimal amount of KH550 was 1.0 phr to 100.0 phr carbonyl iron powder. The effects of different modifying techniques on RMAP＇s mechanical properties were also inrestigated. It is indieated that MAP whose filler is modified by the wet process has the highest tensile strength, but it is not the optimal modiifying technique due to complieated wet process. On the contrary, the dry process was very simple, and VRMAP possessed fairly high mechanical properties, therefore, it was the perfect modifying process.     

玻璃纤维浸润性能和玻璃纤维／环氧基复合材料介电性能的研究

研究了５种偶联剂对玻璃纤维的浸润性能和玻璃纤维／环氧基复合基材料介绍性能的影响。结果表明，玻璃纤维经偶联剂处理后，其浸润活化能降低，与环氧基体的相容性及化学反应活性得到改善，从而提高了玻璃纤维／环氧基复合材料的介电性能。其提高的幅度与偶联剂的枯性和化学结构有关。同时还研究了环境温度和水煮时间对玻璃纤维／环氧基复合材料介电性能的影响，并对影响机制进行了分析讨论。