添加剂对尼龙6铁氧体粘结磁体磁性能影响

系统研究了偶联剂和润滑剂等添加剂对注射成型尼龙6铁氧体粘结磁体磁性能的影响。结果表明,用偶联剂对磁粉进行表面处理,能够很好地改善树脂与磁粉的相容性,提高磁粉在树脂中的分散性,其中当偶联剂用量为2％（质量分数,下同）时,磁性能最好,剩磁（Br）、矫顽力（HcB）、内禀矫顽力（HcJ）以及最大磁能积（BHmax）分别达到0．23T,176．3kA／m,283．8kA／m,10．4kJ／m^3;润滑荆的使用能有效改善体系的流动性,降低共混过程中对磁粉结构的破坏,改善磁体的磁性,当润精剂用量为1％时,HcJ增加了9．3％。     

非水系中钴和镧钴合金的电沉积

研究了在含Ｃｏ（Ⅱ）或含Ｃｏ（Ⅱ）＋Ｌａ（Ⅲ）的尿素－ＮａＢｒ－ＫＢｒ－甲酰胺体系中钴和镧钴合金的电沉积过程。测定了该体系中电极反应Ｃｏ（Ⅱ）十２ｅ＝Ｃｏ的传递系数及ＣＯ（Ⅱ）的扩散系数。在铜基体上得到含镧达５０Ｗｔ％的镧钴合金电沉积层。     

专利文摘

专利文摘含磷酸型甜菜碱的化妆品淀粉磷酸酯５０和缩水甘油基三甲基氯化铵１７在６０℃反应１５ｈ，得淀粉聚［３－（Ｎ，Ｎ，Ｎ－三甲基）－２－羟丙基磷酸内铵］（Ⅰ）２７ｇ。护发剂含十八烷基三甲基氯化铵１．３、十六醇４、Ｉ５和水至１００Ｗｔ％。该剂在皮肤上保湿...     

国外期刊陶瓷文摘

国外期刊陶瓷文摘氧化铝－长石－高岭土系强化瓷坯体的组成［英］／ＫｏｂａｙａｓｈｉＹ等／／ＢｒＣｅｒａｍＴｒａｎｓ。１９９４，９３（２）．－４９～５２当Ａｌ２Ｏ３添加剂增至５０Ｗｔ％时，经１３５０℃煅烧坯体的强度成比例地提高。在使用最佳比例（４５：５５...     

混合稀土氧氯化物在冰晶石—NaF—Al2O3熔体中溶解度的研究

运用等温饱和法测定了混合稀土氧氯化物（ＲＥＯＣｌ）在冰晶石－ＮａＦ－Ａｌ２Ｏ３熔体中的溶解度。讨论了温度、冰晶石分子比、Ａｌ２Ｏ３对溶解度的影响。结果表明：ＲＥＯＣｌ的溶解度随温度的升高而增大；当有４％（Ｗｔ）Ａｌ２Ｏ３存在时，其溶解度相应减小；随着冰晶石分子比增加而增大。     

输送含颗粒物料的Y型油泵机械密封的改进

输送含颗粒物料的Ｙ型油泵机械密封的改进张钧（兰州化学工业公司合成橡胶厂）关键词Ｙ型油泵双端面机械密封结构改进兰化合成橡胶厂碳四抽提装置中两台碱液循环泵的型号为５０ＹⅡ－６０，转速２９５０ｒ／ｍｉｎ，输送介质为１０％ＮａＯＨ（Ｗｔ％）液。自１９９３年...     

聚氯乙烯树脂配方

介绍了一种加工性能有所改进、但透明度却没有降低、未胶凝物大为减少的聚氯乙烯树脂配方,由100份聚氯乙烯树脂和0.1-30份加工助剂组成。其中所用加工助剂聚合物的制备过程为：乳液聚合3－30份单体混合物（A）（由0－50％甲基丙烯酸甲酯、50％－100％丙烯酸烷基酯及0－20％另一种乙烯类可共聚单体组成）,然后聚合40－94份单体混合物（B）（由60％－100％甲基丙烯酸甲酯,0－40％至少选自一种丙烯酸烷基酯或甲基丙烯酸甲酯以外的甲基丙烯酸烷基酯的单体,0－10％另一种乙烯类可共聚单体）,再聚合3－30份单体混合物（C）（由50％－100％甲基丙烯酸甲酯、50％－100％丙烯酸烷基酯、0－20％另一种乙烯类可共聚单体组成）,（A）、（B）、（C）三种单体混合物的总量为100份。     

三元偏氯乙烯/丙烯腈/苯乙烯悬浮共聚树脂的合成

以偶氨二异丁腈（ＡＩＢＮ）作引发剂,合成了偏氯乙烯（ＶＤＣ）／丙烯腈（ＡＮ）／苯乙烯（Ｓｔ）三元悬浮共聚树脂。在聚合过程中,压力先逐步升高后下降。当悬浮聚合质量投料比为６０：１５：２５（ＶＣＤ／ＡＮ／Ｓｔ）时,其压力转变点的转化率约为５５％～６５％。聚合得到的三元ＶＤＣ－ＡＮ－Ｓｔ悬浮共聚树脂为球形半透明颗粒,重均粒径约为５０．５６μｍ。合成的悬浮液中存在数量较多的微小粒子,加入ＮａＮＯ２可减少其     

混合稀土氧氯化物在冰晶石－NaF－Al_2O_3熔体中溶解度的研究

运用等温饱和法测定了混合稀土氧氯化物（ＲＥＯＣｌ）在冰晶石－ＮａＦ－Ａｌ_２Ｏ_３熔体中的溶解度。讨论了温度、冰晶石分子比、Ａｌ_２Ｏ_３对溶解度的影响。结果表明：ＲＥＯＣｌ的溶解度随温度的升高而增大；当有４％（Ｗｔ）Ａｌ_２Ｏ_３存在时，其溶解度相应减小；随着冰晶石分子比增加而增大。     

国外专利

国外专利热熔胶粘剂ＰＣＴＩｎｔ．ＡＰＰＩ．ＷＯ９５－０２６４７（１９９５．１．２６）该胶用于制造一次性使用的软质物品，如尿布、卫生巾等，它是由含碱溶聚合物１０％一８０，聚甲基乙烯醛约０～３０％，增粘树脂约３０％～７０％及适当的增塑剂５％～３０％。作为...     

表面活性剂影响磁粉共凝聚F46乳液的研究

使用十六烷基三甲基溴化铵(CTAB)、烷基酚聚氧乙烯醚(NP)和辛基酚类聚氧乙烯醚(S-13)3种不同表面活性剂乳化铁硅铬磁粉,通过共凝聚方法制备四氟乙烯与六氟丙烯共聚物(F46)包覆乳化后磁粉(F46/铁硅铬磁粉)的复合材料。通过扫描电子显微镜(SEM)表征共凝聚粒子的形貌,通过热重分析仪(TG)测试共凝聚粒子的热稳定性,通过矢量网络分析仪(VNA)测定样品的磁介性能。结果表明:在共凝聚过程中,阳离子型表面活性剂CTAB不仅对铁硅铬磁粉进行乳化,利于磁粉分散,而且在整个共凝聚体系起到破乳作用。采用CTAB乳化磁粉的共凝聚反应,出现凝胶的时间为第12 min,整个共凝聚过程耗时33 min,相比于其他共凝聚反应,缩短了反应时间;且加入质量分数10%乳化剂的磁粉剩余质量分数为0.59%,磁粉残余量最低。F46/铁硅铬磁粉复合材料的磁导率在18.00 GHz下还能保持在1.10左右,介电常数在1.00~18.00 GHz范围内稳定在2.30以下,F46/铁硅铬磁粉复合材料的磁介性能有所改善。     

杨木粉制备泡沫的工艺研究

以杨木粉为原料,通过液化制成液化树脂,再对液化树脂采用中低温发泡法制备发泡材料,系统地考虑了液化树脂黏度和固体质量分数、发泡温度以及表面活性剂、固化剂、发泡剂用量和种类等因素对制备工艺的影响。结果表明：适宜的发泡条件为杨木粉液化树脂黏度为6 000 mPa·s、固体质量分数为75%,发泡温度75 ℃,以吐温-80与OP-10（质量比1∶1）复配作为表面活性剂,以正戊烷为发泡剂,1,4-丁内酯为固化剂,用量都在8%~12%,该条件下发泡过程稳定,制得的泡沫泡孔细腻,均匀,闭孔率高,表观质量好,泡沫的表观密度小（0.12~0.16 g/cm³）并且发泡倍率高（5~8倍）。     

A comparison of soft magnetic composites designed from different ferromagnetic powders and phenolic resins☆

Soft magnetic composites (SMCs) were prepared from three different ferromagnetic powder particles:iron powder ASC 100.29, spherical FeSi particles and vitroperm (Fe73Cu1Nb3Si16B7) flakes. Two types of hybrid organic–inorganic phenolic resins modified with either silica nanoparticles or boron were used to design a thin insulating layer perfect-ly covering the ferromagnetic particles. Fourier transform infrared (FTIR) spectrometry confirmed an incorporation of silica or boron into the polymer matrix, which manifested itself through an improved thermal stability of the hybrid resins verified by thermogravimetric-differential scanning calorimetry (TG-DSC) analysis. The core-shell particles prepared from the ferromagnetic powder particles and the modified hybrid resins were further compacted to the cylindrical and toroidal shapes for the mechanical, electrical and magnetic testing. A uniform distribution of the resin between the ferromagnetic particles was evidenced by scanning electron microscope (SEM) analysis, which was also reflected in a rather high value of the electrical resistivity. A low porosity and extraordinary high values of mechanical hardness and flexural strength were found in SMC consisting of the iron powder and phenolic resin modified with boron. The coercive fields of the prepared samples were comparable with the commercial SMCs.     

Effects of titanate coupling agent on the dielectric properties of NiZn ferrite powders–epoxy resin coatings

During ferrite powder–polymer resin slurry preparation, the ferrite particles tend to hold together, forming agglomerates, which lead to the formation of micro-structural defects in the ferrite powder–polymer coatings. These defects affect the quality of magnetic devices. In this study, the titanate coupling agent effects on the NiZn ferrites powder dispersion in an epoxy resin and solvent system and the electromagnetic properties of NiZn ferrite powders–epoxy resin composite coatings are investigated. It was observed that the dispersion of NiZn ferrite powders and the affinity of NiZn ferrites and epoxy resin can be substantially enhanced by coating a titanate coupling agent onto the ferrite powder surfaces. This coating promotes mixing homogeneity and increases the dielectric constants at low frequencies (below 100 Hz) due to the increase in phase boundary between the NiZn ferrite powders and epoxy resin.     

Performance of MUF resins for particleboard before and after spray-drying

Melamine-urea-formaldehyde (MUF) resins can be spray-dried to obtain resins in powder form and indefinite shelf-life. Application as particleboard adhesives of such resins after redissolving in water yield resins of excellent performance as particleboard adhesives if the natural advancement caused by the heat in the spray-drier chamber is taken into account. Solid-state cross-polarization/magic angle spinning ¹³C nuclear magnetic resonance (CP–MAS ¹³C NMR) analysis of the spray-dried resin in powder form and thermomechanical analysis (TMA) has shown some difference in behavior in relation to MUF resins of the same level of water tolerance which have not been spray-dried. These small but significant differences can be ascribed to differences in resin structure.     

汽车同步器齿环摩擦材料原料物相分析及表征

采用X-射线衍射、红外光谱、X射线光电子能谱等现代仪器,对汽车同步器齿环摩擦材料所选用的改性酚醛树脂、碳纤维、铁粉、铜粉、石墨、硫酸钡、硬脂酸锌等原料的组成进行了表征及分析.结果表明,改性酚醛树脂的红外光谱显示其结构中存在腰果壳油、三聚氰胺的成分.从X射线光电子能谱可知,碳纤维表面有C,O,N,Si等元素,所选用的增强纤维是PAN基碳纤维,在碳骨架的表面含有C=O及C-O-C极性基团,另有少量SiO2;X-射线衍射显示,膨胀铁粉原料中主要含有Fe3O4,还有FeO和Fe2O3,铜粉原料中主要含有Cu和Zn,另有少量Pb,石墨原料纯度较高,硬脂酸锌和BaSO4原料的纯度较低.为进一步提高汽车同步器齿环摩擦材料的性能,须对原材料进行进一步的筛选.     

无纺布专用聚丙烯树脂的工业开发

以聚丙烯(PP)粉料为基础原料,添加过氧化物生产无纺布专用PP树脂.研究发现:以熔体流动速率(MFR)为3.5～4.0 g/10 min的PP粉料为原料,使用固体过氧化物,生产MFR为40.0～50.0 g/10 min的无纺布专用PP树脂,生产过程平稳,产品质量能够满足要求.过氧化物的不同相态影响其在PP粉料中分散的均匀性,从而影响挤出造粒的稳定运行.     

Cu-SiC磨具制备及其性能表征

笔者描述了铜-碳化硅磨具的制备过程,采用热压成形法制备了Cu-SiC磨具。该磨具主要由铜粉、酚醛环氧树脂和碳化硅磨料组成。研究了树脂、碳化硅与辅助磨料的种类、组成对磨具性能的影响。结果表明:当加入适量铜粉,复合材料磨损率会下降、耐磨性能会提高,被磨削表面不易出现凹痕、孔洞;但是铜粉添加过量时,磨具磨损率会增加。较佳配方组成为:35wt%树脂、45wt%碳化硅、15.56wt%铜粉、4.44wt%白刚玉。     

包膜增韧硅微粉对环氧树脂增韧机理的研究

本文首次提出预先对硅微粉进行增韧处理来达到增韧环氧树脂的新思路,并根据断裂理论,采用循环脉冲载荷对增韧硅微粉／环氧树脂复合材料进行冲击性能试验。分析了微裂纹的形成与扩展,探讨增韧硅微粉对环氧树脂的增韧机理。