OMMT/NR纳米复合材料的性能研究

采用两种有机蒙脱土(OMMT)通过机械混炼法制备OMMT/NR纳米复合材科,并对复合材料的各项性能进行研究.结果表明,与NR相比,OMMT/NR纳米复合材料的加工性能、物理性能、热稳定性能和动态力学性能均有明显改善;以N,N'-二甲基-烷烃铵盐作为蒙脱土改性剂制备的OMMT/NR纳米复合材料的加工性能和物理性能较好.     

PUR/OMMT纳米复合材料的制备及性能研究

采用预聚法和原位插层聚合两种方法制备出了聚氨酯(PUR)/有机蒙脱土(OMMT)纳米复合材料,考察了复合材料的力学性能、热稳定性和阻燃性能。结果表明,两种方法制备的复合材料的硬度、拉伸与撕裂强度、断裂伸长率均高于纯PUR。与纯PUR相比,原位插层聚合法制备的复合材料的热分解温度提高了20℃,氧指数提高了23.5%;预聚体法制备的复合材料的分解温度提高了15℃,氧指数提高了13.5%。对比可知,原位插层聚合法制备的复合材料的热稳定性和阻燃性能明显提高,韧性得到增强。     

OMMT/NBR纳米复合材料结构与性能的研究

采用熔体插层法制备有机蒙脱土（OMMT）／NBR纳米复合材料，并对其微观结构及性能进行研究。结果表明，采用熔体法制备的OMMT／NBR复合材料，NBR大分子链插入OMMT片层中，OMMT在NBR基体中呈纳米级分散;与未加OMMT的NBR硫化胶相比，OMMT／NBR纳米复合材料的物理性能明显改善，相同剪切变形下的OMMT／NBR纳米复合材料的储能剪切模量较大；随着OMMT用量的增大，OMMT／NBR纳米复合材料的物理性能提高。     

HDPE/OMMT纳米复合材料制备及性能研究

采用熔融共混法制备了高密度聚乙烯/有机蒙脱土(HDPE/OMMT)纳米复合材料,并对其性能进行了研究。结果表明:OMMT在HDPE/OMMT复合材料中的分散效果良好;当OMMT用量为3份时,冲击强度提高了22.8%;OMMT用量为8份时,热分解温度比纯HDPE提高了28.5℃。     

PVC/PA1212/OMMT纳米复合材料的结构与性能

采用熔融插层法制备了聚氯乙烯(PVC)/聚酰胺1212(PA1212)/有机蒙脱土(OMMT)纳米复合材料,通过X射线衍射、透射电镜、扫描电镜等分析方法研究了OMMT在聚合物基体中的分布及其对PVC/PA1212复合材料分散相形态和力学性能的影响。结果表明:OMMT以剥离态选择性分布于PA1212相中;OMMT在PVC/PA1212复合材料中起到了细化PA1212的作用,促使PA1212分散更加均匀;适量OMMT的加入提高了PVC/PA1212复合材料的力学性能。     

PP/PP-g-MAH/OMMT纳米复合材料流变性能

采用自制聚丙烯(PP)接枝马来酸酐(PP-g-MAH)作为相容剂,与经有机化改性的蒙脱土(OMMT)通过熔融插层法制备了PP/PP-g-MAH/OMMT纳米复合材料,对其加工和流变性能进行了研究.结果发现,随着OMMT用量增加,PP/OMMT和PP-g-MAH/OMMT纳米复合材料的熔体流动速率(MFR)有下降的趋势;...     

机械混炼法OMMT/PVC/NBR纳米复合材料的结构与性能

分别采用3种不同的机械混炼法制备了有机蒙脱土(OMMT)/PVC/NBR纳米复合材料,并对其结构和性能进行表征.结果表明:采用将NBR与OMMT预混再与PVC混合的方法制备的纳米复合材料具有最佳的物理性能;当OMMT用量较小时,复合材料的物理性能随OMMT用量的增大而增大;所制得的纳米复合材料为插层型纳米复合材料.     

BR/CB/OMMT纳米复合材料的结构与性能研究

采用溶液插层法与双辊混炼法制备了顺丁橡胶/炭黑/有机蒙脱土（BR/CB/OMMT）纳米复合材料,用透射电子显微镜（TEM）以及X射线衍射（XRD）方法对复合材料的亚微观结构进行了表征,并研究了复合材料的力学特性、耐磨耗性能以及硫化特性。结果表明：BR/CB/OMMT为插层型纳米复合材料;在OMMT含量小于4份时,BR/CB/OMMT纳米复合材料具有优异的力学性能和耐磨耗性能;OMMT起到了硫化促进剂的作用,降低了BR的焦烧时间（TS）和正硫化时间（T90）;低填充量OMMT可提高复合材料的交联密度。     

NBR/PVC/OMMT纳米复合材料的结构与性能研究

采用乳液共沉法和直接混炼法制备NBR/PVC/有机蒙脱土（OMMT）纳米复合材料,研究纳米复合材料的硫化特性、微观结构、动态力学性能和热稳定性.结果表明,OMMT能够显著促进NBR的硫化反应,使NBR/PVC/OMMT纳米复合材料的焦烧时间和正硫化时间明显缩短;乳液共沉法和直接混炼法NBR/PVC/OMMT纳米复合材料是插层型纳米复合材料,乳液共沉法NBR/PVC/OMMT纳米复合材料中的OMMT分散更为均匀,其储能模量、玻璃化温度和热分解温度均高于NBR/PVC共混物和直接混炼法NBR/PVC/OMMT纳米复合材料,具有较好的动态力学性能和热稳定性.     

OMMT/PU/HTV硅橡胶纳米复合材料的制备与性能研究

采用硅烷偶联剂对钠基蒙脱土进行表面改性,制备有机蒙脱土(OMMT)/PU/热硫化(HTV)硅橡胶纳米复合材料,并对其性能进行研究.试验结果表明,与HTV硅橡胶相比,OMMT/PU/HTV硅橡胶纳米复合材料的热稳定性提高;当OMMT/PU用量为2份时,纳米复合材料的拉伸强度和拉断伸长率达到最大值.     

机械混炼法制备氟橡胶/有机蒙脱土纳米复合材料的结构与性能

选择实验室自制的3种有机蒙脱土，采用双辊混炼法制备了氟橡胶／有机蒙脱土复合材料。力学性能测试结果表明，氟橡胶／2^#有机蒙脱土复合材料具有优异的力学性能。研究了复合材料的微观结构及其应力应变行为、动态力学性能和热稳定性能。结果表明，实验制备出了一种插层型纳米复合材料；该复合材料具有较小的滚动阻力和优异的热稳定性能。     

Preparation and properties of HDPE/CaCO3/OMMT ternary nanocomposite

A series of binary composites based on HDPE (high density polyethylene) and nanoinorganic particles such as nano‐CaCO₃ and OMMT (organic montmorillonite) were prepared. Their properties including tensile, impact strength, and some thermal properties were tested. The results showed that binary composite has partial improvement in mechanical properties compared with pure HDPE. A ternary composite nano‐CaCO₃/OMMT/HDPE was prepared and characterized. It was found that the mechanical and thermodynamic properties of this ternary composite have been enhanced greatly compared with both pure HDPE and binary composites. The tensile strength, Young's modulus, flexural strength, elastic modulus, and impact strength of nano‐CaCO₃/OMMT/HDPE were increased 124.6%, 302.7%, 73.86%, 58.97%, and 27.25%, respectively. The DMA test results showed that the mechanical properties of ternary composite were increased because of the limitation on the movement of HDPE due to inorganic particles. The synergistic effect introduced by nanoparticles may play an important role in all these processes. POLYM. ENG. SCI., 2010. © 2009 Society of Plastics Engineers     

PP/黏土纳米复合材料的结构与性能

采用熔体插层法制备聚丙烯（PP）/有机黏土（OMMT）纳米复合材料。XRD和TEM的测试结果表明,采用熔体插层法制备的PP/OMMT复合材料是剥离型纳米复合材料。力学性能实验结果表明,相容剂的加入提高了PP与OMMT之间的相互作用,使其各项力学性能都得到了提高;PP/OMMT纳米复合材料的各项力学性能在有机黏土含量较小的情况下,就可以有较大幅度的提高;与纯PP相比,相容剂含量为10 phr、有机黏土用量为1 phr的聚丙烯基纳米复合材料具有最好的各项力学性能。     

OMMT/BIIR纳米复合材料的结构与性能研究

采用熔体插层法制备有机蒙脱土(OMMT)/BIIR纳米复合材料.结果表明,OMMT/BIIR纳米复合材料是有序插层型纳米复合材料,在OMMT用量(0～15份)较小的情况下,其物理性能随着OMMT用量的增大明显提高;与BIIR胶料相比,其气密性优异.     

OMMT/IIR纳米复合材料结构与性能的研究

采用熔体插层法制备有机蒙脱土(OMMT)／IIR纳米复合材料。试验结果表明，OMMT／IIR纳米复合材料是插层型纳米复合材料；与无机粘土／IIR微米复合材料及IIR相比，OMMT／HR纳米复合材料具有良好的物理性能，且其物理性能均随OMMT用量的增大而明显提高；与IIR相比，OMMT／HR纳米复合材料具有优异的气密性。     

BSBBR/OMMT纳米复合材料的结构与性能

采用机械共混法分别制备了BSBBR(星形支化溴化丁基橡胶)/OMMT(有机蒙脱土)纳米复合材料、BIIR(溴化丁基橡胶)/OMMT纳米复合材料,并着重探讨了OMMT掺量对两者结构和性能的影响。研究结果表明:BSBBR、BIIR中的部分橡胶大分子链可插入至OMMT的片层结构中,并且OMMT可良好分散在BSBBR、BIIR基体中;当w(OMMT)=10%(相对于纳米复合材料质量而言)时,BSBBR/OMMT纳米复合材料的拉伸强度相对最优,并且比纯BSBBR提高了73%,而且是BIIR/OMMT纳米复合材料的1.35倍;与BIIR/OMMT纳米复合材料相比,BSBBR/OMMT纳米复合材料具有更优异的耐热性和气体阻隔性。     

SBR/有机蒙脱土纳米复合材料的结构与性能研究

通过控制加入芳烃油、相容剂，采用乳液插层法制得了2种不同亚微观结构的SBR／有机蒙脱土（0MMT）纳米复合材料。透射电镜显示制得了插层型和半剥离型纳米复合材料。实验结果表明：炭黑N330的加入，降低了复合材料的延迟硫化现象，改善了复合材料的加工性能；SBR／OMMT／N330纳米复合材料具有优异的力学性能，其耐磨性能下降。