轧后冷却工艺对铌钛微合金化低碳贝氏体钢组织性能的影响

利用金相显微镜、SEM、TEM方法研究了轧后冷却制度对铌钛微合金化低碳贝氏体钢微观组织结构、第二相析出及力学性能的影响.结果表明:轧后空冷(弛豫)至一定温度后加速冷却获得铁素体/贝氏体双相组织;随轧后空冷终止温度降低,铁素体含量增加,晶粒尺寸越大,第二相析出尺寸也有长大趋势,贝氏体形态发生改变,贝氏体板条边界和取向越不明显,位错密度降低,M/A形态也发生一定变化;力学性能表现为强度降低,屈强比和韧塑性得到改善.当轧后空冷终止温度在725～740℃,然后以15℃/s的冷却速度冷却至440℃,可以获得良好的综合力学性能,性能满足标准GB/T 1591中Q690要求.     

锰含量和终轧温度对低成本中钛Q345B钢组织性能的影响

 通过实验室轧制试验,研究不同锰质量分数（0.6%～1.0%）、终轧温度对低成本中钛（质量分数0.04%～0.05%）Q345B钢微观组织和力学性能的影响,同时采用透射电镜观察钢中钛的析出规律。结果表明：锰质量分数为0.8%、终轧温度为850 ℃时,试验钢的屈服强度为491 MPa,抗拉强度为625 MPa,伸长率为33.6%,在满足力学性能条件下能最大限度地降低成本,而钛的析出主要以球形纳米尺寸TiC粒子为主,有少量方形大尺寸TiN粒子。     

终轧温度对700MPa级高强板性能的影响

采用TMCP工艺生产低碳贝氏体钢时,合理的工艺制度是得到优良综合性能的保障。本文通过不同终轧温度的工艺试验,探讨了终轧温度对700MPa级高强板性能的影响。     

热轧终轧温度对冷轧无取向电工钢析出物的影响

研究了热轧终轧温度对低碳低硅无取向电工钢热轧带中第二相析出物的影响。结果发现，在高温γ相区终轧卷相后，析出物的直接较大，析出物体积分数较高；在α γ两相区终轧卷相后，析出物的直径也较大，但析出物体积分数较小；在α相区终轧卷取后，析出物的直径较小，析出物体积分数较小。     

终轧温度对高性能桥梁钢力学性能及组织的影响

利用拉伸、冲击试验机测试力学性能，采用光学显微镜、扫描电镜和透射电镜研究了终轧温度对高性能桥梁钢Q370qE力学性能和微观组织、晶界取向角度差、织构、位错和析出相形态的影响。结果表明：在875～803℃范围内降低终轧温度，钢的屈服强度和抗拉强度均提升，屈强比上升，韧脆转变温度降低，低温韧性提高。终轧温度为803℃时，钢的屈服强度、抗拉强度分别为420、542 MPa,-40℃的夏比冲击功均值为243 J。降低终轧温度有利于铁素体晶粒的细化和均匀性的提升，细化珠光体团束的尺寸，减少珠光体组织的数量，改变了珠光体形态，出现退化形态；但较低的终轧温度，珠光体组织由分散变为连续的条带，加重了钢的带状组织。同时降低终轧温度，促进了大角度晶界的形成和小角度晶界的减少，有利于晶粒<001>取向的减弱和<110>取向的增多；有利于晶内Nb/Ti碳氮化物析出相颗粒的细化及球状的形成，铁素体晶粒内部位错增多并大量缠结，也促进了Nb/Ti碳氮化物在位错上的形成。     

终轧温度对加Ti低合金Q355B钢板组织性能的影响

以钛微合金化的355 MPa级低合金高强度钢为研究对象,将试验钢分别在830、800、750、700 ℃系列温度下终轧,研究了终轧温度对显微组织和力学性能的影响。结果表明,随着终轧温度的降低,屈服强度和抗拉强度呈现不断升高的趋势,伸长率和冲击性能呈现先升高后下降的趋势,在Ar3温度附近终轧,钢板可获得最佳的综合力学性能。不同终轧温度下钢板基体组织均为铁素体+珠光体,在800 ℃终轧钢板晶粒最为均匀细小,830 ℃终轧钢板晶粒较800 ℃终轧相对粗大,750 ℃终轧钢板组织出现混晶现象,700 ℃终轧时,钢板晶粒已经拉长变形,一定程度上出现“纤维状铁素体”。充分细化晶粒可以减轻钢板中的带状组织。     

终轧温度对高强度工程机械用钢组织性能的影响

对不同终轧温度的高强度工程机械用钢热轧钢卷进行了力学性能和金相组织的测试,研究了终轧温度对其组织和性能的影响。试验结果表明,随着终轧温度的降低,试验钢的抗拉强度和屈服强度降低,延伸率升高。高温终轧试样的低温冲击值很低,随着终轧温度的降低,低温冲击值大幅度升高。高温终轧试样的金相组织是铁素体+微量的珠光体,铁素体组织均匀性较差;中温终轧和低温终轧试样的组织是铁素体+珠光体,铁素体晶粒比较规则,而且低温终轧的均匀性比中温终轧好。高温终轧试样的铁素体晶界明显存在M3C型复合条状或短棒状的碳化物。     

终轧温度对高强度工程机械用钢组织性能的影响

对不同终轧温度的高强度工程机械用钢热轧钢卷进行了力学性能和金相组织的测试,研究了终轧温度对其组织和性能的影响。试验结果表明,随着终轧温度的降低,试验钢的抗拉强度和屈服强度降低,延伸率升高。高温终轧的低温冲击值很低,随着终轧温度的降低,低温冲击值大幅度升高。高温终轧的金相组织是铁素体＋微量的珠光体,铁素体组织均匀性较差;中温终轧和低温终轧的组织是铁素体＋珠光体,铁素体晶粒比较规则,而且低温终轧的均匀性比中温终轧好。高温终轧的铁素体晶界明显存在M3C型复合条状或短棒状的碳化物。     

控轧控冷工艺对低碳铌微合金钢组织和性能的影响

用Gleeble-1500热模拟实验机测定了低碳铌微合金钢变形后的连续冷却转变曲线(CCT曲线),并在实验室对该实验钢采用不同的工艺进行了控制轧制和控制冷却的实验.研究了工艺参数对实验钢力学性能和微观组织的影响,分析了低碳铌微合金钢的强韧化机制.热模拟实验结果表明,实验钢在较宽的冷却速度范围(0.5～30 ℃/s)内可以获得贝氏体组织.控轧控冷的实验结果表明,实验钢的组织主要为铁素体和贝氏体.随着终轧温度的降低,组织得到细化,强度提高,但屈强比也随之增加;降低卷取温度使组织中的贝氏体含量略有增加,强度有所提高.初步探讨了贝氏体对实验钢性能的影响,为制定合适的生产工艺制度提供了依据.     

终轧温度对低硅含磷系TRIP钢组织性能的影响

通过实验室热轧试验,研究了不同终轧温度下低硅含磷系热轧TRIP钢的组织特征及性能特点。结果表明：终轧温度由900℃降低到790℃,铁素体体积分数增加,贝氏体体积分数降低,残余奥氏体体积分数变化不太明显;终轧温度900和820℃时,得到贝氏体为基体的室温组织;终轧温度降低到790℃时,低温变形促进了奥氏体到铁素体的相变率...     

Effect of Finish Rolling Temperature on Microstructure and Mechanical Properties of High Grade Pipeline Steel

The correlation among finish rolling temperature (FRT),microstructure and mechanical property of the high grade pipeline steel was investigated in this study.The microstructure of the steels with different finish rolling temperatures was observed with scanning electronic microscope (SEM) and transmission electronic microscope (TEM).The martensite/austenite (M/A) islands distribution was fixed by colour metallography,and the mechanical properties of the steels were tested with quasi-static tensile testing machine.The result shows that the fraction of M/A island increased with the finish rolling temperature decreasing,and when the finish rolling temperature is 800℃,the mechanical properties are the best.     

Effects of Finish Rolling Temperature on Microstructure and Mechanical Properties of Ferritic-Rolled P-Added High Strength Interstitial-Free Steel Sheets

  The steels were rolled at 3 different finishing temperatures. The mechanical properties were tested by tensile tests. The results show that as finish rolling temperature decreases from 620 to 560 ℃ in ferrite region, the deep drawability of ferritic rolled P added high strength IF steels is improved, and r value rises from 114 to 137. Finish rolling temperature (FT) has less influence on other mechanical properties, such as yield strength, tensile strength and elongation. Microstructures of hot rolled and annealed steel sheets and precipitates of annealed steel sheets were also analyzed.     

精轧入口温度对Nb-V-Ti微合金钢组织的影响

在Gleeble-3800热模拟试验机上模拟了Nb-V-Ti微合金钢不同精轧入口温度的轧制和卷取过程,并观察了最终试样的显微组织。同时进行了多道次变形的模拟试验,通过平均流变应力分析了不同应变量下的未再结晶温度。结果表明,当精轧入口温度在未再结晶温度以上时,针状铁素体和多边形铁素体相对粗大;精轧入口温度在未再结晶温度以下时,随着精轧入口温度的降低,针状铁素体和多边形铁素体均逐渐细化。     

回火对低碳贝氏体钢组织和性能的影响

研究了(250~500)℃×30 min回火热处理对低碳贝氏体钢组织和性能的影响。结果表明,TMCP状态试验钢的组织为粒状贝氏体、板条贝氏体和针状铁素体。回火温度升高,粒状贝氏体增加,板条贝氏体和针状铁素体减少,组织逐渐粗化。350℃回火时,试验钢的屈服强度(Rt0.5)为735~765 MPa,抗拉强度(Rm)为845~865 MPa,屈强比为0.87~0.88,-20℃冲击功为218~257 J,强韧性匹配最佳。300~400℃回火时,裂纹形成能(E1)、韧性裂纹扩展能(E2)及脆性裂纹扩展能(E3)+脆性裂纹扩展止裂能(E4)最大,止裂性能最佳。     

轴承钢GCr15棒材产品低温精轧的研究

采用国外引进的可实现低温精轧的生产线，对轴承钢GCr15棒材产品进行了低温精轧，通过低温精轧降低了网状碳化物级别，减少了球化退火时间。研究得到了低温精轧轧制GCr15时以控制网状碳化物级别为目标的轧制温度范围为750～840℃，轧后冷却温度范围为600～680℃，同时也研究得到了低温精轧轧制GCr15时以控制网状碳化物级别及减少球化退火时间为目标的轧制温度范围为750～800℃，轧后冷却温度范围为600～680℃。通过该研究网状碳化物级别达到了2级以下，球化退火时间由原18h减少到了11h。     

铜单一元素合金化热轧钢板的组织与性能

研究了铜单一合金化高纯净热轧钢板在时效退火前后的组织与性能的关系.结果表明,铜具有明显的时效强化作用,在时效过程中铜的析出优先于钢板的再结晶,同时高纯净基体使钢材保持了良好的塑性.分析表明,铜单一合金化高纯净钢具有良好的发展前景.     

回火温度对贝氏体/马氏体复相海洋用钢的组织和性能影响

利用扫描电镜、透射电镜等实验方法,研究不同回火温度下试验钢的组织性能变化情况.结果表明:经控轧控冷获得了贝氏体/马氏体复相海洋用钢,其中贝氏体体积分数约占30%;随着回火温度的升高,试验钢的屈服强度先上升后又略有下降,在600℃达到最大值,为983 MPa,抗拉强度明显下降,延伸率先降低后升高,在600℃回火温度达到最大值为19.6%,之后又开始降低,冲击功在400℃和600℃出现明显回火脆性;在550℃回火温度试验钢取得最佳力学性能,其中抗拉强度和屈服强度分别为1050MPa和981 MPa,延伸率为16.6%,-40℃低温冲击功为19.9 J.分析认为,回火过程中马氏体板条断裂消失,贝氏体相互合并形成准多边形铁素体,析出物逐渐回溶和重新析出,造成力学性能的变化差异.     

Effects of Rolling Processes on Bainite and Mechanical Properties of Ultra-High Strength Pipeline Steel

Ultra-high strength pipeline steels were rolled by thermal mechanical controlling process (TMCP),and effects of the volume fraction,the size and microstructure morphologies of three different bainite (AF,GB and LB) on mechanical properties were investigated by optical microscope.The results showed that,X120 ultra-high strength pipeline steel was rolled through the reasonable thermal mechanical controlling process (TMCP),and the yield strength and the low temperature charpy impact energy (-30℃) were higher than 840MPa and above 230J,respectively,meanwhile,the ratios of tensile strength to yield strength were lower below 0.82.As for X100 pipeline,of which the mechanical property were higher than that by X100 pipeline steel of ISO standard,yield strength of the steel was 715 MPa,ultimate tensile strength 963 MPa,impact energy 282J,and yield ratio 0.74.