Effect of acetylation on dimensional stability,mechanical, and dynamic properties of jute board

Jute slivers were acetylated in pilot scale following a no catalyst‐no solvent method at 120°C for 2 h. The weight % gain was found to be 11.37. Different jute boards were pressed under heat and pressure using acetylated jute sliver and urea formaldehyde resin. Neutral salt (NaCl), acid salt (NH₄Cl), and melamine powder were used separately for curing urea formaldehyde. For comparison purposes, control boards were also prepared using nonacetylated slivers. The boards were tested for water soaking, cyclic water soaking, and cyclic humidity to see the effect of acetylation on dimensional stabilization. This chemical modification was found to improve the dimensional stability to a great extent for NaCl and NH₄Cl cured boards and to a less extent for a melamine‐cured one. Tensile and flexural strengths were tested by Instron before and after the cyclic tests. Retention values were found to be as high as 60% after cyclic water tests for acetylated boards and the same was as low as 24% for control boards. Dynamic parameters, such as storage flexural modulus (E′), loss flexural modulus (E"), and loss factor or damping efficiency (tan δ) were determined in a fixed‐frequency mode. Dynamic mechanical study revealed that tan δ peaks were lowered due to increased bulkiness of the fiber after acetylation and thus restricted mobility. A tiny additional peak was also visible at ∼90°C beside the main peak at ∼125°C for boards with modified slivers. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 72: 935–944, 1999     

Pultruded fiber-reinforced poly(methyl methacrylate) composites. II. Static and dynamic mechanical properties,environmental effect,and postformability

This paper presents a novel process developed to manufacture poly(methyl methacrylate) (PMMA) pultruded composite. The mechanical, thermal, and dynamic mechanical properties, environmental effect, postformability of various fiber (glass, carbon, and Kevlar 49 aramid fiber) reinforced pultruded PMMA composites have been studied. Results show mechanical properties (i.e., tensile strength, specific tensile strength, tensile modulus, and specific flexural strength) and thermal properties (HDT) increase with fiber content. Kevlar fiber/PMMA composites possess the highest specific tensile strength and HDT, carbon fiber/PMMA composites show the highest tensile strength and tensile modulus, and glass fiber/PMMA composites show the highest specific flexural strength. Pultruded glass-fiber-reinforced PMMA composites exhibit good weather resistance. These composite materials can be postformed by thermoforming under pressure, and mechanical properties of postformed products can be improved. The dynamic shear storage and loss modulus (G′, G″) of pultruded glass-fiber-reinforced PMMA composites increased with decreasing pulling rate, and their shear storage moduli are higher than those of pultruded Nylon 6 and polyester composites.     

Property investigation of polypropylene/multiwall carbon nanotube nanocomposites prepared via in situ polymerization

In this study, polypropylene/carbon nanotube nanocomposites were prepared via in situ polymerization using a bi‐supported Ziegler ? Natta catalytic system. In this system, magnesium ethoxide and multiwall carbon nanotubes (MWCNTs) are jointly used as catalyst supports. SEM images reveal the distribution and quite good dispersion of MWCNTs throughout the polypropylene (PP) matrix. The thermal properties of the samples were examined using DSC and TGA tests. The results show that the crystallization temperature of the nanocomposites significantly increases while the melting point is not markedly affected. In addition, the thermal stability is improved. The melt rheological properties of PP/MWCNT nanocomposites in the linear and nonlinear viscoelastic response regions were studied. An increment of the complex viscosity (η^*), storage modulus (G′) and loss modulus (G′′) and a decrement of the loss factor (tan δ) compared with neat PP are observed. Steady shear flow experiments show an increase in shear viscosity with increasing the MWCNT content. © 2013 Society of Chemical Industry     

Effect of natural fibers on thermal and mechanical properties of natural fiber polypropylene composites studied by dynamic mechanical analysis

The present study deals with the effects of natural fibers on thermal and mechanical properties of natural fiber polypropylene composites using dynamic mechanical analysis. Composites of polypropylene and various natural fibers including kenaf fibers, wood flour, rice hulls, and newsprint fibers were prepared at 25 and 50% (by weight) fiber content levels. One and two percent maleic anhydride grafted polypropylene was also used as the compatibilizer for composites containing 25 and 50% fibers, respectively. Specimens for dynamic mechanical analysis tests were cut out of injection‐molded samples and were tested over a temperature range of ?60 to +120°C. Frequency of the oscillations was fixed at 1 Hz and the strain amplitude was 0.1%, which was well within the linear viscoelastic region. The heating rate was 2°C/min for all temperature scan tests. Storage modulus (E′), loss modulus (E″), and mechanical loss factor (tan δ) were collected during the test and were plotted versus temperature. An increase in storage and loss moduli and a decrease in the mechanical loss factor were observed for all composites indicating more elastic behavior of the composites as compared with the pure PP. Changes in phase transition temperatures were monitored and possible causes were discussed. Results indicated that glass transition was slightly shifted to lower temperatures in composites. α transition temperature was higher in the case of composites and its intensity was higher as well. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 4341–4349, 2006     

Mechanical,thermal and dynamic‐mechanical behavior of banana fiber reinforced polypropylene nanocomposites

Natural fiber‐reinforced nanocomposites based on polypropylene/nanoclay/banana fibers were fabricated by melt mixing in a twin‐screw extruder followed by compression molding in this current study. Maleic anhydride polypropylene copolymer (MA‐g‐PP) was used as a compatibilizer to increase the compatibility between the PP matrix, clay, and banana fiber to enhance exfoliation of organoclay and dispersion of fibers into the polymer matrix. Variation in mechanical, thermal, and physico‐mechanical properties with the addition of banana fiber into the PP nanocomposites was investigated. It was observed that 3 wt% of nanoclay and 5 wt% of MA‐g‐PP within PP matrix resulted in an increase in tensile and flexural strength by 41.3% and 45.6% as compared with virgin PP. Further, incorporation of 30 wt% banana fiber in PP nanocomposites system increases the tensile and flexural strength to the tune of 27.1% and 15.8%, respectively. The morphology of fiber reinforced PP nanocomposites has been examined by using scanning electron microscopy and transmission electron microscopy. Significant enhancement in the thermal stability of nanocomposites was also observed due to the presence of nanoclay under thermogravimetric analysis. Dynamic mechanical analysis tests revealed an increase in storage modulus (E′) and damping factor (tan δ), conforming the strong interaction between nanoclay/banana fiberand MA‐g‐PP in the fiber‐reinforced nanocomposites systems. POLYM. COMPOS., © 2011 Society of Plastics Engineers.     

硫磺改性聚丙烯纤维材料及其流变行为的研究

采用熔融接枝法制备了相容剂硫磺接枝聚丙烯(PP-g-S),同时制备了不同硫磺(S)含量的聚丙烯(PP)/PP-g-S/S改性纤维材料。分别用哈克转矩流变仪、红外光谱仪、核磁共振仪、熔体流动速率仪、扫描电子显微镜对接枝相容剂进行对比分析,再用旋转平板流变仪研究了S含量对PP/PP-g-S/S改性纤维材料的动态流变行为的影响。结果表明,在过氧化二异丙苯的引发下可以通过熔融接枝法制得相容剂PP-g-S,而且相容剂PP-g-S对PP/PP-g-S/S改性纤维材料起到了明显的增容作用;随着S含量的增加,PP/PP-g-S/S改性纤维材料的复数黏度、储能模量、损耗模量及损耗因子均增大,Cole-Cole曲线圆弧半径增大,零剪切黏度增大、S呈均相均匀分散。     

Dynamic mechanical properties of nanoclay filled TPU/PP blends with compatibiliser

Abstract

Blends of thermoplastic polyurethane (TPU) and polypropylene (PP) are highly incompatible because of large differences in polarities and high interfacial tensions. On one hand, PP is added to TPU to improve TPU's thermal stability, chemical properties, mechanical properties (modulus, strength and hardness) and processing performance and to reduce TPU's cost. On the other hand, TPU is blended with PP to improve PP's properties (e.g. abrasion, flexibility, tear strength, shock absorbing capabilities, impact strength, adhesion and paintability/printability). Earlier works in polyurethane/organoclay nanocomposites, PP/organoclay nanocomposites and TPU/PP blends were studied. In our experimental work, both ester and ether based TPU nanocomposites were prepared by melt blending using 3?wt-% Cloisite 10A (organically modified montmorillonite clay) as the nanoscale reinforcement and blended with PP with/without PP-graft-maleic anhydride as the compatibiliser. Blends of nanoclay filled TPU/PP were evaluated for dynamic mechanical properties such as storage modulus E′, loss modulus E″ and dissipation factor tanδ.     

A rheological and morphological study of treated PVC

This article reports a rheological and morphological study of poly(vinyl chloride) (PVC) that was subjected to a treatment capable of decreasing the simultaneous mass transfers occurring between liquid food (or simulant) and PVC packaging. The storage modulus (G′), loss modulus (G″), and the loss angle (tan δ), have been used to determine the glass transition temperature using a Rheometric Scientific Dynamic Analyzer. Young's modulus was measured on a dynamometer, and a morphological characterization was carried out with an optical microscope. The obtained results show that treated PVC behaves like a composite material, which is in agreement with a previously established model. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 3497–3502, 2003     

Preparation and characterization of poly(vinylidene fluoride) nanocomposites containing multiwalled carbon nanotubes

Poly(vinylidene fluoride) (PVDF) nanocomposites with different loadings of multiwalled carbon nanotubes (MWNT) were prepared by melt‐compounding technique. A homogeneous dispersion of MWNT throughout PVDF matrix was observed on the cryo‐fractured surfaces by scanning electron microscopy. Thermogravimetric analysis results indicated that the thermal stability of neat PVDF was improved with the incorporation of MWNT. Dynamic mechanical analysis showed a significant improvement in the storage modulus over a temperature range from ?125 to 75°C with the addition of MWNT. The melt‐rheological studies illustrated that incorporating MWNT into PVDF matrix resulted in higher complex viscosities (|η*|), storage modulus (G′), loss modulus (G″), and lower loss factor (tan δ) than those of neat PVDF. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Mechanical and thermal properties of toughened polypropylene composites

The mechanical, thermal, and structural properties of a new flexible composite containing polypropylene fiber (PP) in a random poly(propylene‐co‐ethylene) (PPE) matrix with ethylene–propylene elastomer (EP) was investigated with emphasis on the effect of EP elastomer concentration. The intrinsic composition of the composites, toughening of the matrix with EP and the fiber–matrix interface determined the properties of the composites. Through the incorporation of EP elastomer into the polypropylene–poly (propylene‐co‐ethylene) (all‐PP) composite, tensile and storage modulus (E′) decreased, flexural modulus and loss modulus (E″, damping) increased slightly to 0.15 EP and then decreased. There was an increase in impact resistance for the toughened composites, with about 100% increase in comparison with an untoughened all‐PP composite. The composition corresponding to 0.20 weight fraction EP gave optimum impact and mechanical properties. Creep resistance of the composite decreased with increasing EP content, but recovery showed an increase with increasing EP content up to 0.20. Fracture surfaces of composites after impact tests were studied with scanning electron microscopy. Moreover, the use and limitation of theoretical equations to predict the tensile and flexural modulus of the flexible PP composite is discussed. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

Effect of interface affinity on the performance of a composite of microcrystalline cellulose and polypropylene/polylactide blends

The effects of compatibilizer and fillers on the mechanical properties and dispersion state of droplets of polypropylene (PP)/polylactide (PLA) blends were investigated. Two blended composite systems, i.e. PP‐rich (80/20) containing microcrystalline cellulose (MCC) modified with silane (m‐MCC) and PLA‐rich (20/80) containing MCC were prepared by melt compounding using a twin‐screw extruder. The structural differences between MCC and m‐MCC were confirmed using Fourier transform infrared spectra. Universal testing machine results revealed that the tensile strength and Young's modulus increased with the addition of compatibilizer and filler, respectively. These results were supported by the reduction of domain size observed by scanning electron microscopy. Differential scanning calorimetric analysis showed a change of the melting and crystallization behavior of blends according to the presence of compatibilizer or filler. An increase of the dynamic storage modulus and a decrease in tan δ with addition of compatibilizer indicated that the interfacial adhesion between PP and PLA improved. © 2019 Society of Chemical Industry     

Effects of swelling on the viscoelastic properties of polyester films made from glycerol and glutaric acid

Viscoelastic properties have been determined for poly(glycerol‐co‐glutaric acid) films synthesized from Lewis acid‐catalyzed polyesterifications. The polymers were prepared by synthesizing polymer gels that were subsequently cured at 125°C to form polymer films. The polymers were evaluated for the extent of reaction before and after curing by Fourier transform infrared spectroscopy. They were subsequently immersed in dimethylsulfoxide, tetrahydrofuran, water, methanol, and hexane for 24 h. The amounts of solvent absorbed were monitored and recorded. Dependent up the solvent used, the polymers were able to absorb 9.5–261% of its weight. The effects of the solvent absorption on the viscoelastic properties of the polyester films were evaluated by determining their elastic modulus (G′), viscous modulus (G″), tan δG″/G′, and complex viscosity (η*) by performing oscillatory frequency sweep experiments. The elastic modulus (G′) and viscous modulus (G″) were both higher for the dry polymers than the solvent‐absorbed polymers. However, the polymer films were all higher in elastic (G′) character than viscous (G″) character. Therefore, tan δG″/G′ < 1 before and after immersion in solvents. Values for η* decreased with angular frequency for all of the polyesters tested in this study. © 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

Dynamic rheological behavior of poly(ether ketone ketone) from solid state to melt state

High performance thermoplastic poly(ether ketone ketone) (PEKK) polymers with various meta phenyl links ratio were investigated by dynamical mechanical analysis. Analyses were carried out in a wide range of temperature from solid state (torsion rectangular mode) to the melt state (torsion parallel plates mode) as function of thermal history and environmental conditions. In the solid state, this study was focused on the secondary relaxations in the vitreous state. A complementary investigation conducted with different poly(aryl ether ketones) allowed us to propose a molecular interpretation of PEKK sub‐vitreous relaxations. In the molten state, storage modulus (G′), loss modulus (G″), storage viscosity (η′), and loss viscosity (η″) were studied to determine zero shear‐rate viscosity (η₀) and thermal activation energy E_a. Master curves were built and the shift factor a_T was determined. Thermal activation energies were extracted from an Arrhenius model on the shift factor temperature's dependency. Finally, E_a and η₀ were determined thanks to the dynamic viscosity fit with Cross model and Cole–Cole representation. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 46456.     

Rheological behavior of high‐density polyethylene (HDPE) filled with paper mill sludge

A comparative study was conducted of composites made with sludge from three different paper mills. Sludges were obtained from a thermomechanical pulp (TMP), a chemico‐TMP (CTMP), and a Kraft mill with a feedstock of primarily black spruce. The primary sludge (PS) and secondary sludge (SS) were mixed at two different ratios (PS:SS = 7:3 and 9:1) and blended with high‐density polyethylene (HDPE) at 20%, 30%, and 40% proportion. The blends were tested using plate–plate geometry before subjection to frequency sweep by oscillation rheometry. The storage modulus (G′), loss modulus (G″), and complex viscosity (η*) increased with increasing paper sludge content. Decreasing the PS:SS ratio from 9:1 to 7:3 decreased G′, G″, and η*. Differential scanning calorimetry showed that sludge addition increased both the melting and crystallization temperature, for a positive effect on crystallinity. Although the behavior of sludge–high‐density polyethylene blends differed from that of traditional wood plastic composite made with wood flour, they obtained G′, G″, and η* values of the same magnitude. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 46484.     

Interfacial,dynamic mechanical,and thermal fiber reinforced behavior of MAPE treated sisal fiber reinforced HDPE composites

The present article summarizes an experimental study on the mechanical and dynamic mechanical behavior of sisal fiber reinforced HDPE composites. Variations in mechanical strength, storage modulus (E′), loss modulus (E″), and damping parameter (tan δ) with the addition of fibers and coupling agents were investigated. It was observed that the tensile, flexural, and impact strengths increased with the increase in fiber loading up to 30%, above which there was a significant deterioration in the mechanical strength. Further, the composites treated with MAPE showed improved properties in comparison with the untreated composites. Dynamic mechanical analysis data also showed an increase in the storage modulus of the treated composites The tan δ spectra presented a strong influence of fiber content and coupling agent on the α and γ relaxation process of HDPE. The thermal behavior of the composites was evaluated from TGA/DTG thermograms. The fiber–matrix morphology in the treated composites was confirmed by SEM analysis of the tensile fractured specimens. FTIR spectra of the treated and untreated composites were also studied, to ascertain the existence of type of interfacial bonds. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3306–3315, 2006     

Characterization of highly filled wood flour–polyvinyl chloride composites: Dynamic mechanical and dielectric analysis

Viscoelastic and dielectric properties of composites with polyvinyl chloride as major matrix constituent, ethylene vinyl acetate (EVA) as polymeric plasticizer, and wood flour (WF) and fly ash (FA) as filler have been studied. The effect of variation of WF, FA, and EVA on storage modulus E′, loss modulus E″, and glass transition temperature, T_g has been evaluated using dynamic mechanical analysis (DMA). Effect on permittivity ε′ and conductivity is evaluated using dielectric analysis. The results show considerable influence of constituents of the composite on the properties evaluated. DMA shows that WF contributes to an increase in T_g, E′, and E″ and a decrease in loss tangent, tan δ. The FA content has insignificant effect on these properties. Increasing WF content increases ε′. POLYM. ENG. SCI., 2010. © 2010 Society of Plastics Engineers     

Dynamic mechanical properties of sisal fiber reinforced polyester composites fabricated by resin transfer molding

The dynamic mechanical properties of sisal fiber reinforced polyester composites fabricated by resin transfer molding (RTM) were investigated as a function of fiber content, frequency, and temperature. Investigation proved that at all temperature range the storage modulus (E′) value is maximum for the composites having fiber loading of 40 vol%. The loss modulus (E″) and damping peaks (tan δ) were lowered with increasing fiber content. The height of the damping peaks depends upon the fiber content and the fiber/matrix adhesion. The extent of the reinforcement was estimated from the experimental storage modulus, and it has been found that the effect of reinforcement is maximum at 40 vol% fiber content. As the fiber content increases the T_g from tan δ curve showed a positive shift. The loss modulus, storage modulus, and damping peaks were evaluated as a function of frequency. The activation energy for the glass transition increases upon the fiber content. Cole–Cole analysis was made to understand the phase behavior of the fiber reinforced composites. Finally, attempts were made to correlate the experimental dynamic properties with theoretical predictions. POLYM. COMPOS., 2009. © 2008 Society of Plastics Engineers     

Influence of interfacial adhesion on the structural and mechanical behavior of PP‐banana/glass hybrid composites

Hybrid composites of polypropylene (PP), reinforced with short banana and glass fibers were fabricated using Haake torque rheocord followed by compression molding with and without the presence maleic anhydride grafted polypropylene (MAPP) as a coupling agent. Incorporation of both fibers into PP matrix resulted in increase of tensile strength, flexural strength, and impact strength upto 30 wt% with an optimum strength observed at 2 wt% MAPP treated 15 wt% banana and 15 wt% glass fiber. The rate of water absorption for the hybrid composites was decreased due to the presence of glass fiber and coupling agent. The effect of fiber loading in presence of coupling agent on the dynamic mechanical properties has been analyzed to investigate the interfacial properties. An increase in storage modulus (E′) of the treated‐composite indicates higher stiffness. The loss tangent (tan δ) spectra confirms a strong influence of fiber loading and coupling agent concentration on the α and β relaxation process of PP. The nature of fiber matrix adhesion was examined through scanning electron microscopy (SEM) of the tensile fractured specimen. Thermal measurements were carried out through differential scanning calorimetry (DSC) and the thermogravimetric analysis (TGA), indicated an increase in the crystallization temperature and thermal stability of PP with the incorporation of MAPP‐treated banana and glass fiber. POLYM. COMPOS., 31:1247–1257, 2010. © 2009 Society of Plastics Engineers     

Influence of organically modified nanoclay on the performance of pineapple leaf fiber‐reinforced polypropylene nanocomposites

Polypropylene/Pine apple leaf fiber (PP/PALF)‐reinforced nanocomposites were fabricated using melt blending technique in a twin‐screw extruder (Haake Rheocord 9000). Variation in mechanical properties, crystallization behavior, water absorption, and thermal stability with the addition of nanoclay in PP/PALF composites were investigated. It was observed that the tensile, flexural, and impact properties of PP increase with the increase in fiber loading from 10 to 30 wt %. Composites prepared using 30 wt % PALF and 5 wt % MA‐g‐PP exhibited optimum mechanical performance with an increase in tensile strength to 31%, flexural strength to 45% when compared with virgin PP. Addition of nanoclay results in a further increase in tensile and flexural strength of PP/PALF composites to 20 and 24.3%, which shows intercalated morphology. However, addition of nanoclay does not show any substantial increase in impact strength when compared with PP/PALF composites. Dynamic mechanical analysis tests revealed an increase in storage modulus (E′) and damping factor (tan δ), confirming a strong influence between the fiber/nanoclay and MA‐g‐PP. Differential scanning calorimetry, thermogravimetric analysis thermograms also showed improved thermal properties when compared with the virgin matrix. TEM micrographs also showed few layers of agglomerated clay galleries along with mixed nanomorphology in the nanocomposites. Wide angle X‐ray diffraction studies indicated an increase in d‐spacing from 22.4 Å in Cloisite 20A to 40.1 Å in PP/PALF nanocomposite because of improved intercalated morphology. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Influence of fly ash cenospheres on performance of coir fiber‐reinforced recycled high‐density polyethylene biocomposites

Recycled high‐density polyethylene (RHDPE)/coir fiber (CF)‐reinforced biocomposites were fabricated using melt blending technique in a twin‐screw extruder and the test specimens were prepared in an automatic injection molding machine. Variation in mechanical properties, crystallization behavior, water absorption, and thermal stability with the addition of fly ash cenospheres (FACS) in RHDPE/CF composites were investigated. It was observed that the tensile modulus, flexural strength, flexural modulus, and hardness properties of RHDPE increase with an increase in fiber loading from 10 to 30 wt %. Composites prepared using 30 wt % CF and 1 wt % MA‐g‐HDPE exhibited optimum mechanical performance with an increase in tensile modulus to 217%, flexural strength to 30%, flexural modulus to 97%, and hardness to 27% when compared with the RHDPE matrix. Addition of FACS results in a significant increase in the flexural modulus and hardness of the RHDPE/CF composites. Dynamic mechanical analysis tests of the RHDPE/CF/FACS biocomposites in presence of MA‐g‐HDPE revealed an increase in storage (E′) and loss (E″) modulus with reduction in damping factor (tan δ), confirming a strong influence between the fiber/FACS and MA‐g‐HDPE in the RHDPE matrix. Differential scanning calorimetry, thermogravimetric analysis thermograms also showed improved thermal properties in the composites when compared with RHDPE matrix. The main motivation of this study was to prepare a value added and low‐cost composite material with optimum properties from consumer and industrial wastes as matrix and filler. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42237.