Effect of post-welding heat treatment on microstructure and mechanical properties of 1Crl8Ni9Ti and 2Cr13 steel welded joints

通过钨极氩弧焊方法,对1Cr18Ni9Ti与2Cr13钢实施焊接,并对焊接接头整体进行焊后热处理。采用OM、SEM对2Cr13与1Cr18Ni9Ti钢热处理前后的焊接接头组织进行分析,利用显微硬度计、电子万能拉伸机测量了焊接接头的力学性能。结果表明,1Cr18Ni9Ti和2Cr13钢焊接接头热处理前焊缝组织为典型的柱状晶,组织为板条马氏体＋残留奥氏体＋碳化物;热处理后焊缝组织为回火索氏体,而且碳化物析出量也明显增多。拉伸时,热处理前后焊接接头断裂的部位都发生在奥氏体不锈钢热影响区一侧,热处理前后焊接接头的抗拉强度分别约为635.56、649.44 MPa;焊缝区的显微硬度分别约为276、222 HV0.5,热处理后焊接接头的整体显微硬度比热处理前的明显降低。     

热处理对1Cr18Ni9Ti与2Cr13钢焊接接头断口组织形貌的影响

通过钨极氩弧焊方法,在一定工艺条件下对1Cr18Ni9Ti与2Cr13实施焊接,后对焊接接头进行焊后热处理。通过万能拉伸机对热处理前后的焊接接头进行拉伸试验,采用OM、SEM对1Cr18Ni9Ti与2Cr13钢热处理前后的焊接接头进行断口组织形貌观察及分析。结果表明,1Cr18Ni9Ti和2Cr13焊接接头热处理前焊缝组织为典型的柱状晶,组织为板条马氏体+残余奥氏体+碳化物;热处理后焊缝组织转变为回火索氏体。拉伸时,热处理前后焊接接头断裂部位都发生在奥氏体不锈钢热影响区一侧,均属于韧性断裂,热处理前韧窝大小、分布不均匀;热处理后韧窝变小,分布均匀,大小尺寸均等。热处理前,焊接接头的抗拉强度约为635 MPa,伸长率约为26%,断面收缩率约为44%;热处理后,焊接接头的抗拉强度约为645 MPa,伸长率约为24%,断面收缩率约为44%。     

热处理对1Cr18Ni9Ti与2Cr13钢板焊接接头耐腐蚀性的影响

通过填丝钨极氩弧焊方法对1Cr18Ni9Ti与2Cr13钢板进行焊接,并对焊接接头进行焊后热处理.采用SEM对焊接接头热处理前后的组织进行观察及分析;采用模拟海水浸泡试验,测量了焊接接头的交流抗阻和极化曲线.结果表明,1Cr18Ni9Ti和2Cr13钢板焊接接头热处理前焊缝为典型的柱状晶,组织为板条马氏体+奥氏体+第二...     

半导体激光焊接85Cr17与0Cr18Ni9不锈钢的组织与性能

采用半导体激光作为焊接热源,对高碳马氏体不锈钢85Cr17和奥氏体不锈钢0Cr18Ni9进行对接焊试验,分析了焊接接头的显微组织并测试了显微硬度和拉伸强度.结果表明:采用半导体激光焊接工艺可实现85Cr17和0Cr18Ni9的对接焊,获得连续、平整的焊缝;焊缝中心区域主要为等轴晶,近中心区为柱状晶与树枝晶的混合组织.靠近基体侧的焊缝边缘区为柱状晶组织;焊缝区的平均硬度高于两种基材;拉伸试样均断在85Cr17侧热影响区,未焊透时,焊接接头抗拉强度达到0Cr18Ni9母材的88%,焊透时,抗拉强度达到0Cr18Ni9母材的95%以上.     

06Cr18Ni12Mo2Cu2奥氏体不锈钢焊接接头组织与力学性能

通过拉伸、弯曲、维氏硬度等试验以及金相分析,对06Cr18Ni12Mo2Cu2奥氏体不锈钢焊接接头的显微组织和力学性能进行了研究。结果表明:焊条电弧焊焊接接头有良好的抗拉性能和弯曲性能,焊缝区硬度略高于母材,而热影响区硬度略低于母材。焊缝组织为奥氏体+5%铁素体组织。焊接热影响区过热区奥氏体晶粒粗大,导致材料强度和硬度下降。     

焊后低温热处理对马氏体不锈钢组织和性能的影响

对ZG06Cr13Ni4Mo马氏体不锈钢进行了焊后低温热处理工艺试验(240、300 ℃),通过显微组织分析、拉伸及弯曲试验、硬度试验及残余应力测试对不同低温热处理下焊接接头的显微组织、力学性能、硬度和残余应力等进行了研究。结果表明,经低温热处理后,接头焊缝热影响区组织为回火马氏体及碳化物,接头焊缝区的组织为低碳马氏体+块状马氏体+碳化物,接头的抗拉强度变化不大,硬度略有下降,经240 ℃低温热处理后,焊接接头焊缝处的残余应力消除了69.1%。     

1Cr17与1Cr18Ni9Ti异种钢搭接焊接接头的显微组织分析

本文进行1Cr17和l Cr18Ni9Ti异种不锈钢搭接氩弧焊接,采用钨极焊炬偏向lCr18Ni9Ti奥氏体不锈钢侧的焊接工艺,以减少铁素体不锈钢1Cr17的熔化量和降低其热影响区铁素体晶粒粗化,采用光学显微镜、扫描电镜和室温拉伸对其焊接接头的显微組织和性能进行了研究。结果表明,搭接焊缝金属主要为细小的条块状奥氏体组织及少量的块状铁素体。1Cr17钢侧热影响区铁素体晶粒粗化得到抑制,试样拉伸断口位于搭接区的奥氏体焊缝金属而不是铁素体不锈钢的热影响区。     

1Cr13与1Cr18Ni9Ti不锈钢焊接接头组织及性能研究

通过钨极氩弧焊方法,在一定工艺条件下对1Cr18Ni9Ti与1Cr13实施焊接,并采用LOM、SEM对1Cr13马氏体型与1Cr18Ni9Ti奥氏体型不锈钢焊接接头进行金相组织、断口形貌观察及分析,利用显微硬度计、电子万能拉伸机测量了焊接接头的力学性能.结果表明,通过手工钨极氩弧焊,采用直流正接法(焊接电流为80 A,焊接速度为110 mm/min)能够获得外观平整、组织均匀,力学性能满足要求的焊接接头.     

3Cr13与1Cr18Ni9Ti异种钢高压管焊接

在分析3Cr13与1Cr18Ni9Ti各自焊接性的基础上,根据异种钢接头焊缝金属成分与组织,选择不同焊接材料进行工艺试验,依据试验结果选定A307焊条成功地焊接了异种钢接头。     

热处理对9Ni钢焊接接头组织与性能的影响

对9Ni钢焊接接头分别进行了QT处理和IHT处理,采用拉伸、硬度、冲击试验,断口电镜扫描等方法研究了两种热处理对焊接接头显微组织及性能的影响。结果表明,未经热处理时焊缝的组织为细晶铁素体+针状铁素体;QT处理后焊缝的组织为马氏体+奥氏体;IHT处理后焊缝组织为马氏体+奥氏体+铁素体。QT与IHT处理均能使9Ni钢焊接接头的强度、硬度下降,塑性上升;IHT处理后焊接接头的伸长率达到29.0%,塑性优于QT态。经QT和IHT处理后,焊缝的低温冲击吸收能量分别从48 J上升至78 J和100 J;IHT处理可明显提升焊缝的低温韧性,其冲击断口为典型的韧性断裂。     

1Cr18Ni9Ti与1Cr13不锈钢的焊接试验

通过钨极氩弧焊方法,对 1Cr18Ni9Ti 与 1Cr13 实施焊接.采用光学显微镜、扫描电镜对 1Cr13 马氏体型与 1Cr18Ni9Ti 奥氏体型不锈钢焊接接头进行金相组织、断口形貌观察及分析;利用显微硬度计、电子万能拉伸机测量焊接接头的力学性能;并通过海水模拟溶液浸泡试验,测量焊接接头极化曲线和交流阻抗谱.结果表明,通过手工钨极氩弧焊,采用直流正接接法,在合适的工艺下(焊接电流为 80 A,焊接速度为 110 mm/min),能够获得外观平整、组织均匀,力学性能与电化学性能符合要求的焊接接头.

Abstract：

The stainless steels of 1Cr18Ni9Ti and 1Cr13 were welded through deterministic craft by tungsten inert-gas (TIG) welding. The microstructure and fracture pattern of weld joints of 1Cr13martensite and 1Cr18Ni9Ti austenite stainless steels were observed and analyzed by means of LOM and SEM, the mechanical properties of the weld joints were measured with micro-hardness tester and electronic universal stretcher, and the polarization curves and AC impedance spectroscopy of weld joints were tested by seawater immersion test of simulation solution. The results show that adopting manual TIG welding through electrode negative to direct current soldering machine to weld 1Cr18Ni9Ti austenite stainless steel and 1Cr13 martensite stainless steel is feasible; under suitable process (welding current is 80 A, welding speed is 110 mm/min), weld joints can obtain good appearance and uniform structure; mechanical properties and galvano-chemistry properties can meet use requirements.     

Fe-Cr-2Al-Si阻尼合金与1Cr18Ni9Ti不锈钢的钨极氩弧焊接

采用钨极氩弧焊（GTAW）和奥氏体不锈钢焊丝LNT309LSi作为填充金属,研究了Fe-Cr-2Al-Si阻尼合金和1Cr18Ni9Ti不锈钢的焊接工艺和焊接质量。借助金相显微镜分析了焊缝组织特征,采用电子探析分析了焊缝成分。按照国家标准研究了焊接接头的硬度、拉伸性能和弯曲性能。结果表明,用奥低不锈钢焊丝焊接Fe-Cr-2Al-Si阻尼合金和1Cr18Ni9Ti不锈钢,可获得理想的奥氏体＋少量的铁素体＋马氏体的焊缝组织,焊缝的抗拉强度和抗弯性能均高于阻尼合金。所采用的焊接方法、焊接工艺和焊丝能满足这两种钢的焊接要求,焊接质量可靠。     

不同热处理制度下1Cr11Ni2W2MoV闪光对焊接头的组织与性能

针对1Cr11Ni2W2MoV不锈钢开展闪光对焊试验,研究不同焊后热处理制度对其焊接接头组织和力学性能的影响。结果表明:采用闪光对焊方法焊接1Cr11Ni2W2MoV,能够获得优质的焊接接头。1Cr11Ni2W2MoV闪光焊焊态下焊缝组织为马氏体和少量的δ铁素体组织,焊接接头具有较好的拉伸性能,但塑性和韧性较差。经过淬火+回火热处理后组织表现为回火索氏体组织,焊接接头的抗拉强度、塑性和韧性等性能均得到改善。在1000℃油淬+570℃回火状态下,焊接接头具有良好的综合力学性能。     

12Cr/30Cr2Ni4MoV异质接头低周疲劳性能

文中研究了12Cr/30Cr2Ni4MoV异质焊接接头的显微组织、显微硬度和室温低周疲劳性能.结果表明,母材12Cr的显微组织是板条状回火马氏体,母材30Cr2Ni4MoV是板条状回火马氏体和粒状回火贝氏体,过渡层和焊缝的显微组织为粒状回火贝氏体,且焊缝由柱状晶区与等轴晶区交替构成.30Cr2Ni4MoV比12Cr有更...     

热处理对1Cr18Ni9Ti钢焊接接头性能的影响

试验研究了固溶+稳定化处理、固溶处理和去应力退火处理对1Cr18Ni9Ti钢焊接接头力学性能的影响。结果表明:固溶+稳定化处理试样的屈服强度、伸长率、抗拉强度均最高。扫描电镜观察结果表明:所有的断口均为韧窝型断裂。     

热处理对1Cr18Ni9Ti钢焊接接头性能的影响

试验研究了固溶＋稳定化处理、固溶处理和去应力退火处理对1Cr18Ni9Ti钢焊接接头力学性能的影响。结果表明：固溶＋稳定化处理试样的屈服强度、伸长率、抗拉强度均最高。扫描电镜观察结果表明：所有的断口均为韧窝型断裂。     

FSS/ASS厚壁异种钢“TIG冷焊 + UNGW”组合焊的接头组织与力学性能

为了有效解决铁素体不锈钢的焊接热影响区晶粒易粗化问题，以及奥氏体不锈钢焊接时在接头部分熔合区及其附近热影响区内因易形成蠕虫状δ铁素体而显著降低该区域耐腐蚀性的问题，提出了“TIG冷焊 + UNGW”的组合焊接工艺，并进行了1Cr17/1Cr18Ni9Ti厚壁异种不锈钢的焊接，同时对所得接头的显微组织、力学性能及耐腐蚀性进行了测试与分析. 结果表明，组合焊接头的1Cr17母材热影响区晶粒未发生粗化，并且1Cr18Ni9Ti母材部分熔合区及其附近热影响区内未形成蠕虫状δ铁素体；组合焊接头的抗拉强度优于1Cr17母材，并且1Cr17母材热影响区的冲击吸收能量与1Cr17母材相当；组合焊接头的熔敷层、1Cr18Ni9Ti母材、1Cr17母材、UNGW焊缝区及完整接头的耐腐蚀性呈依次下降的趋势.     

1Cr18Ni9Ti钢不同焊接接头的低温拉伸性能

采用精密多功能低温静载材料实验机和扫描电镜,系统研究了焊接方法对1Cr18Ni9Ti钢焊接接头低温拉伸性能的影响。结果表明:在77K下,1Cr18Ni9Ti钢TIG焊接头的强度、伸长率均比MMA焊接头的高;两者拉伸断口均为韧窝和撕裂棱混合型韧性断口,但TIG焊接头断口中韧窝的尺寸细小而均匀。     

1Cr18Ni9Ti+Q235复合钢板对接焊缝组织和抗腐蚀性能分析

针对内复合不锈钢焊管制造,采用4种焊接工艺对厚度为3mm+10mm的1Cr18Ni9Ti+Q235复合钢板对接焊缝进行了自动焊接,对焊接接头进行显微组织分析、拉伸、内外弯曲、冲击试验、电化学和晶间腐蚀试验.结果表明,采用TIG焊焊接复层,复层焊缝显微组织为奥氏体加少量铁素体,在1moL/L的盐酸溶液中进行电化学腐蚀试验,其抗电化学腐蚀性能与母材复层相近,无晶间腐蚀现象.基体采用TIG焊的焊接接头,基体焊缝组织为较高强韧性的板条状马氏体,满足力学性能要求.而基体采用SAW焊的焊接接头,基体焊缝力学性能和复层焊缝抗腐蚀性能均不能满足要求.