Properties of Ce-doped ITO films deposited on polymer substrate by DC magnetron sputtering

Ce-doped indium tin oxide (ITO:Ce) films were deposited on flexible polyimide substrates by DC magnetron sputtering using ITO targets containing various CeO₂ contents (CeO₂ : 0, 0.5, 3.0, 4.0, 6.0 wt.%) at room temperature and post-annealed at 200 °C. The crystallinity of the ITO films decreased with increasing Ce content, and it led to a decrease in surface roughness. In addition, a relatively small change in resistance in dynamic stress mode was obtained for ITO:Ce films even after the annealing at high temperature (200 °C). The minimum resistivity of the amorphous ITO:Ce films was 3.96 × 10^− 4 Ωcm, which was deposited using a 3.0 wt.% CeO₂ doped ITO target. The amorphous ITO:Ce films not only have comparable electrical properties to the polycrystalline films but also have a crystallization temperature > 200 °C. In addition, the amorphous ITO:Ce film showed stable mechanical properties in the bended state.     

Room temperature crystallization by RF plasma

The crystallization of amorphous thin films was achieved by radiofrequency (RF) plasma treatment. Although various amorphous films are crystallized after 2 min or so, the sample temperature is lower than 150 °C without compulsory cooling even when the films are treated for 1 h. This treatment works on amorphous films of various materials, independently of the film preparation method and substrate materials. Sol-gel-derived TiO₂ films were densified and simultaneously crystallized to anatase structure by the plasma treatment and the obtained films indicate almost the same photocatalytic activities as that of thermally crystallized TiO₂ films. Plasma-crystallized sputtered indium tin oxide (ITO) films have a bixbite structure and the resistivity reached to 1.6 × 10^− 4 Ω cm while the crystallization condition was not optimized. Amorphous silicon films with a small mount of crystallites were deposited by sputtering method and were crystallized by the plasma treatment.     

Polycrystalline films of tungsten-doped indium oxide prepared by d.c. magnetron sputtering

Electrical and optical properties of polycrystalline films of W-doped indium oxide (IWO) were investigated. These films were deposited on glass substrate at 300 °C by d.c. magnetron sputtering using ceramic targets. The W-doping in the sputter-deposited indium oxide film effectively increased the carrier density and the mobility and decreased the resistivity. A minimum resistivity of 1.8 × 10^− 4 Ω cm was obtained at 3.3 at.% W-doping using the In₂O₃ ceramic targets containing 7.0 wt.% WO₃. The 2.2 at.% W-doped films obtained from the targets containing 5.0 wt.% WO₃, showed the high Hall mobility of 73 cm² V^− 1 s^− 1 and relatively low carrier density of 2.9 × 10²⁰ cm^− 3. Such properties resulted in novel characteristics of both low resistivity (3.0 × 10^− 4 Ω cm) and high transmittance in the near-infrared region.     

Temperature dependence of the microstructure and resistivity of indium zinc oxide films deposited by direct current magnetron reactive sputtering

Indium zinc oxide (IZO) films were deposited as a function of the deposition temperature using a sintered indium zinc oxide target (In₂O₃:ZnO = 90:10 wt.%) by direct current (DC) magnetron reactive sputtering method. The influence of the substrate temperature on the microstructure, surface roughness and electrical properties was studied. With increasing the temperature up to 200 °C, the characteristic properties of amorphous IZO films were improved and the specific resistivity was about 3.4 × 10^− 4 Ω cm. Change of structural properties according to the deposition temperature was also observed with X-ray diffraction patterns, transmission electron microscopy, X-ray photoelectron spectroscopy, and atomic force microscopy. IZO films deposited above 300 °C showed polycrystalline phases evolved on the amorphous IZO layer. Very flat surface roughness could be obtained at lower than 200 °C of the substrate temperature, while surface roughness of the films was increased due to the formation of grains over 300 °C. Consequently, high quality IZO films could be prepared by DC magnetron sputtering with O₂/Ar of 0.03 and deposition temperature in range of 150-200 °C; a specific resistivity of 3.4 × 10^− 4 Ω cm, and the values of peak to valley roughness and root-mean-square roughness are less than 4 nm and 0.5 nm, respectively.     

Transparent conducting indium oxide thin films grown by low-temperature metal organic chemical vapor deposition

We have grown indium oxide thin films on silicon substrates at low temperature by metal organic chemical vapor deposition. Polycrystalline film growth could only be obtained at temperatures below 400 °C. Above 400 °C, metallic indium deposition dominated. We have investigated the effect of substrate temperature and reactor pressure on the film growth and structural properties in the range of 250-350 °C and 5 ^? 10³-4 ^? 10⁴ Pa. The film grown at 300 °C exhibited a resistivity of about 3.6 × 10^− 3 Ω cm and a maximal optical transmittance of more than 95% in the visible range. The film showed an optical band gap of about 3.6 eV.     

Thin film deposition and characterization of pure and iron-doped electron-beam evaporated tungsten oxide for gas sensors

Pure tungsten oxide (WO₃) and iron-doped (10 at.%) tungsten oxide (WO₃:Fe) nanostructured thin films were prepared using a dual crucible Electron Beam Evaporation (EBE) technique. The films were deposited at room temperature under high vacuum onto glass as well as alumina substrates and post-heat treated at 300 °C for 1 h. Using Raman spectroscopy the as-deposited WO₃ and WO₃:Fe films were found to be amorphous, however their crystallinity increased after annealing. The estimated surface roughness of the films was similar (of the order of 3 nm) to that determined using Atomic Force Microscopy (AFM). As observed by AFM, the WO₃:Fe film appeared to have a more compact surface as compared to the more porous WO₃ film. X-ray photoelectron spectroscopy analysis showed that the elemental stoichiometry of the tungsten oxide films was consistent with WO₃. A slight difference in optical band gap energies was found between the as-deposited WO₃ (3.22 eV) and WO₃:Fe (3.12 eV) films. The differences in the band gap energies of the annealed films were significantly higher, having values of 3.12 eV and 2.61 eV for the WO₃ and WO₃:Fe films respectively. The heat treated films were investigated for gas sensing applications using noise spectroscopy. It was found that doping of Fe to WO₃ produced gas selectivity but a reduced gas sensitivity as compared to the WO₃ sensor.     

Effect of annealing on molybdenum doped indium oxide thin films RF sputtered at room temperature

Thin films of molybdenum doped indium oxide (IMO) were deposited on glass at room temperature using an in-built three-source RF magnetron sputtering. The films were studied as a function of oxygen volume percentage (O₂ vol. %; ranging from 0.0 to 17.5%) in the sputtering chamber. The as-deposited amorphous films were crystallized on post-annealing. The as-deposited films are low conducting and Hall coefficients were undetectable; whereas post-annealed films possess fairly high conductivity. The lowest transmittance (11.96% at 600 nm) observed from the films deposited without oxygen increased to a maximum of 88.01% (3.5 O₂ vol. %); whereas this transmittance was decreased with the increasing O₂ vol. % to as low as 81.04% (15.6 O₂ vol. %); a maximum of 89.80% was obtained from the films annealed at 500 °C in open air (3.5 O₂ vol. %). The optical band gap of 3.80 eV obtained from the films deposited without oxygen increased with increasing O₂ vol. % to as high as 3.91 eV (17.5 O₂ vol. %). A maximum of 3.92 eV was obtained from the films annealed at 300 °C in N₂:H₂ gas atmosphere (17.5 O₂ vol. %).     

Electrical and optical properties of indium tin oxide films prepared on plastic substrates by radio frequency magnetron sputtering

The influence of deposition power, thickness and oxygen gas flow rate on electrical and optical properties of indium tin oxide (ITO) films deposited on flexible, transparent substrates, such as polycarbonate (PC) and metallocene cyclo-olefin copolymers (mCOC), at room temperature was studied. The ITO films were prepared by radio frequency magnetron sputtering with the target made by sintering a mixture of 90 wt.% of indium oxide (In₂O₃) and 10 wt.% of tin oxide (SnO₂). The results show that (1) average transmission in the visible range (400-700 nm) was about 85%-90%, and (2) ITO films deposited on glass, PC and mCOC at 100 W without supplying additional oxygen gas had optimum resistivity of 6.35 × 10⁻⁴ Ω-cm, 5.86 × 10⁻⁴ Ω-cm and 6.72 × 10⁻⁴ Ω-cm, respectively. In terms of both electrical and optical properties of indium tin oxide films, the optimum thickness was observed to be 150-300 nm.     

Composition, structural and electrical properties of thin films prepared by laser ablation of neodymium-doped potassium gadolinium tungstate

Thin films were grown on (001) SiO₂, SiO₂/(100) Si or (100) MgO substrates by laser ablation of neodymium-doped potassium gadolinium tungstate (Nd:KGW) single crystal target. The films were deposited at temperatures between room temperature and 750 °C and pressures between 1 × 10^− 4 Pa and 50 Pa of oxygen ambient. The influence of the deposition conditions on the composition, structure, morphology and electrical properties of the films was investigated. Special attention was paid to the films deposited in vacuum (1 × 10^− 4 Pa) or at very low oxygen pressures. Under such conditions, the potassium (K), gadolinium (Gd) and oxygen (O) content decreased strongly as the temperature was increased. At room temperature, the films were K and O stoichiometric, in contrast with Gd, which showed a concentration twice higher. The films were polycrystalline, with the exception of those deposited at temperatures below 500 °C, which were amorphous. However, all were smooth and dense. The films grown in vacuum and at temperatures between 500 and 700 °C consist mainly of “â-tungsten” - tungsten oxide (W₃O) phase. The films grown on SiO₂/Si possessed the best surface quality with nano-size relief. The resistivity measurements as a function of the temperature showed that the films produced in vacuum and at temperatures below 500 °C were highly insulating, whereas at 600 °C they exhibited semiconducting behavior or a metallic one at 700 °C. This behavior can be attributed to the existence of various valence states for tungsten below W⁶⁺ in the films and to their crystal structure.     

Influence of deposition parameters and heat treatment on the NO2 sensing properties of nanostructured indium tin oxide thin film

Highly oriented and transparent indium tin oxide (ITO) films have been deposited onto glass substrates by radio frequency magnetron sputtering at 648 K, under an oxygen partial pressure of 1 Pa. The effect of the sputtering power and annealing was studied. Transmission was measured with a double beam spectrometer and electrical analysis using four probe and Hall effect setup. Structural characterization of the films was done by X-ray diffraction. Characterization of the coatings revealed an electrical resistivity below 6.5 × 10^− 3 Ω cm. The ITO films deposited at 648 K were amorphous, while the crystallinity improved after annealing at 700 K. The optical transmittance of the film was more than 80% in the visible region. The surface morphology examined by scanning electron microscopy appears to be uniform over the entire surface area, after annealing. The NO₂ sensing properties of the ITO films were investigated. At a working temperature of 600 K, the ITO sensor showed high sensitivity to NO₂ gas, at concentrations lower than 50 ppm.     

Preliminary studies on molybdenum-doped indium oxide thin films deposited by radio-frequency magnetron sputtering at room temperature

Thin films of molybdenum-doped indium oxide (IMO) were prepared by a 3-source, cylindrical radio-frequency magnetron sputtering at room temperature. The films were post-annealed and were characterized by their structural (X-ray diffraction) and optical (UV-VIS-NIR spectrophotometer) properties. The films were studied as a function of oxygen volume percentage (O₂ vol.%) ranging from 3.5 to 17.5. The structural studies revealed that the as-deposited amorphous films become crystalline on annealing. In most cases, the (222) reflection emerged as high intensive peak. The poor visible transmittance of the films as-deposited without oxygen was increased from ∼ 12% to over 80% on introducing oxygen (3.5 O₂ vol.%). For the films annealed in open air, the average visible transmittance in the wavelength ranging 400-800 nm was varied between 77 and 84%. The films annealed at high temperatures (> 300 °C) decreased the transmittance to as low as < 1%. The optical band gap of the as-deposited films increased from the range 3.83-3.90 to 3.85-3.98 eV on annealing at different conditions.     

Structural and electrical properties of sputtered indium-zinc oxide thin films

In this study, indium-zinc oxide (IZO) thin films have been prepared at a room temperature, 200 and 300 °C by radio frequency magnetron sputtering from a In₂O₃-12 wt.% ZnO sintered ceramic target, and their dependence of electrical and structural properties on the oxygen content in sputter gas, the substrate temperature and the post-heat treatment was investigated. X-ray diffraction measurements showed that amorphous IZO films were formed at room temperature (RT) regardless of oxygen content in sputter gas, and micro-crystalline and In₂O₃-oriented crystalline films were obtained at 200 and 300 °C, respectively. From the analysis on the electrical and the structural properties of annealed IZO films under Ar atmosphere at 200, 300, 400 and 500 °C, it was shown that oxygen content in sputter gas is a critical parameter that determines the local structure of amorphous IZO film, stability of amorphous phase as well as its eventual crystalline structure, which again decide the electrical properties of the IZO films. As-prepared amorphous IZO film deposited at RT gave specific resistivity as low as 4.48 × 10^− 4 Ω cm, and the highest mobility value amounting to 47 cm²/V s was obtained from amorphous IZO film which was deposited in 0.5% oxygen content in sputter gas and subsequently annealed at 400 °C in Ar atmosphere.     

Study on inverse spinel zinc stannate, Zn2SnO4, as transparent conductive films deposited by rf magnetron sputtering

Inverse spinel zinc stannate (Zn₂SnO₄, ZTO) films were deposited onto fused quartz glass substrates heated at 800 °C by rf magnetron sputtering using a ceramic ZTO target (Zn:Sn = 2:1). H₂ flow ratios [H₂/(Ar + H₂)] were controlled from 0 to 30% during the depositions. ZTO films deposited at 800 °C possessed a polycrystalline inverse spinel structure. The lowest resistivity of 1.1 × 10^− 2 Ω cm was obtained for a ZTO film deposited at 20% H₂ flow ratio. The transmittance of the ZTO film was approximately 80% in the visible region.     

Fabrication of TiO2-based transparent conducting oxide on glass and polyimide substrates

We report on preparation and properties of anatase Nb-doped TiO₂ transparent conducting oxide films on glass and polyimide substrates. Amorphous Ti_0.96Nb_0.04O₂ films were deposited at room temperature by using sputtering, and were then crystallized through annealing under reducing atmosphere. Use of a seed layer substantially improved the crystallinity and resistivity (ρ) of the films. We attained ρ = 9.2 × 10^− 4 Ω cm and transmittance of ~ 70% in the visible region on glass by annealing at 300 °C in vacuum. The minimum ρ of 7.0 × 10^− 4 Ω cm was obtained by 400 °C annealing in pure H₂.     

Evolution of structure and properties of multi-component (AlCrTaTiZr)Ox films

(AlCrTaTiZr)O_x films were deposited at 350 °C by DC magnetron sputtering from high-entropy alloy target. Oxygen concentration increases with oxygen flow ratio, and saturates near 67 at.%. As-deposited films have an amorphous structure. Their hardness fall in the range of 8-13 GPa. All amorphous oxide films maintain their amorphous structure up to 800 °C for at least 1 h. After 900 °C 5 h annealing, crystalline phases with the structures of ZrO₂, TiO₂, or Ti₂ZrO₆ form. Annealing enhances mechanical properties of the films. Their hardness and modulus attain to the values about 20 and 260 GPa, respectively. The resistivity of the metallic films is around 10² μΩ cm but drastically rises to 10¹² μΩ cm when oxygen concentration increases.     

Transparent conducting ZnO thin films deposited by vacuum arc plasma evaporation

A high rate deposition of co-doped ZnO:Ga,F and ZnO-In₂O₃ multicomponent oxide thin films on large area substrates has been attained by a vacuum arc plasma evaporation method using oxide fragments as a low-cost source material. Highly transparent and conductive ZnO:Ga,F and ZnO-In₂O₃ thin films were prepared on low temperature substrates at a deposition rate of approximately 375 nm/min with a cathode plasma power of 10 kW. A resistivity of 4.5×10⁻⁴ Ω cm was obtained in ZnO:Ga,F films deposited at 100 °C using ZnO fragments co-doped with 1 wt.% ZnF₂ and 1 wt.% Ga₂O₃ as the source material. In addition, the stability in acid solution of ZnO films was improved by co-doping. It was found that the Zn/(In+Zn) atomic ratio in the deposited ZnO-In₂O₃ thin films was approximately the same as that in the fragments used. The ZnO-In₂O₃ thin films with a Zn/(In+Zn) atomic ratio of approximately 10-30 at.% deposited on substrates at 100 °C exhibited an amorphous and smooth surface as well as a low resistivity of 3-4×10⁻⁴ Ω cm.     

Investigation on structural, electrical and optical properties of tungsten-doped tin oxide thin films

Tungsten-doped tin oxide (SnO₂:W) transparent conductive films were prepared on quartz substrates by pulsed plasma deposition method with a post-annealing. The structure, chemical states, electrical and optical properties of the films have been investigated with tungsten-doping content and annealing temperature. The lowest resistivity of 6.67 × 10^− 4 Ω cm was obtained, with carrier mobility of 65 cm² V^− 1 s^− 1 and carrier concentration of 1.44 × 10²⁰ cm^− 3 in 3 wt.% tungsten-doping films annealed at 800 °C in air. The average optical transmittance achieves 86% in the visible region, and approximately 85% in near-infrared region, with the optical band gap ranging from 4.05 eV to 4.22 eV.     

Structural and optical studies of nanocrystalline V2O5 thin films

We report the structural and optical properties of nanocrystalline thin films of vanadium oxide prepared via evaporation technique on amorphous glass substrates. The crystallinity of the films was studied using X-ray diffraction and surface morphology of the films was studied using scanning electron microscopy and atomic force microscopy. Deposition temperature was found to have a great impact on the optical and structural properties of these films. The films deposited at room temperature show homogeneous, uniform and smooth texture but were amorphous in nature. These films remain amorphous even after postannealing at 300 °C. On the other hand the films deposited at substrate temperature T_S > 200 °C were well textured and c-axis oriented with good crystalline properties. Moreover colour of the films changes from pale yellow to light brown to black corresponding to deposition at room temperature, 300 °C and 500 °C respectively. The investigation revealed that nanocrystalline V₂O₅ films with preferred 001 orientation and with crystalline size of 17.67 nm can be grown with a layered structure onto amorphous glass substrates at temperature as low as 300 °C. The photograph of V₂O₅ films deposited at room temperature taken by scanning electron microscopy shows regular dot like features of nm size.     

Electrical, optical, and structural properties of InZnSnO electrode films grown by unbalanced radio frequency magnetron sputtering

We have investigated the electrical, optical, structural, and annealing properties of indium zinc tin oxide (IZTO) films prepared by an unbalanced radio frequency (RF) magnetron sputtering at room temperature, in a pure Ar ambient environment. It was found that the electrical and optical properties of unbalanced RF sputter grown IZTO films at room temperature were influenced by RF power and working pressure. At optimized growth condition, we could obtain the IZTO film with the low resistivity of 3.77 × 10^− 4 Ω cm, high transparency of ~ 87% and figure of merit value of 21.2 × 10^− 3Ω^− 1, without the post annealing process, even though it was completely an amorphous structure due to low substrate temperature. In addition, the field emission scanning electron microscope analysis results showed that all IZTO films are amorphous structures with very smooth surfaces regardless of the RF power and working pressure. However, the rapid thermal annealing process above the temperature of 400 °C lead to an abrupt increase in resistivity and sheet resistance due to the transition of film structure from amorphous to crystalline, which was confirmed by X-ray diffraction examination.     

Advantages of using amorphous indium zinc oxide films for window layer in Cu(In,Ga)Se2 solar cells

The advantages of using indium zinc oxide (IZO) films instead of conventional Ga-doped zinc oxide (ZnO:Ga) films for Cu(In,Ga)Se₂ (CIGS) solar cells are described. The electrical properties of IZO are independent of film thickness. IZO films have higher mobility (30-40 cm²/Vs) and lower resistivity (4-5 × 10^− 4 Ω cm) compared to ZnO:Ga films deposited without intentional heating, because the number of grain boundaries in amorphous IZO films is small. The properties of a CIGS solar cell using IZO at the window layer were better than those obtained using a conventional ZnO:Ga at the window layer; moreover, the properties tended to be independent of thickness. These results indicate that use of IZO as a transparent conducting oxide layer is expected to increase the efficiency of CIGS solar cells.