烧结温度对高钨重合金性能的影响

研究了烧结温度对高钨含量W—Ni—Fe重合金显微组织及力学性能的影响。结果表明：钨基重合金的显微组织和力学性能与烧结温度密切相关。合适的烧结温度可以使合金具有良好的显微组织和优良的力学性能，而烧结温度较低时，合金中的粘结相分布不均匀，烧结温度较高时，合金中的钨颗粒粗大，两者都会显著降低其力学性能。     

钨合金粘结相屈服强度测量方法探讨

针对钨合金应力弛豫现象,在不同载荷作用下,对质量分数93%钨合金的应力进行测量,分析了其应力随时间变化的规律。实验结果表明:当载荷作用时间少于22 h,钨合金应力随时间下降,并在200 MPa处应力随时间变化率出现极大值,此时发生剪切屈服;当载荷时间高于22 h,钨合金应力变化趋于稳定,初步确定粘结相屈服强度范围为340～490 MPa,这一现象本质为钨合金特殊的相结构和滞弹性变形。     

石蜡在多组元粘结剂和高比重合金喂料中的低温热脱脂动力学

为了控制热脱脂过程中的缺陷,研究了石蜡（ＰＷ）在多组元粘结剂体系和高比重合金喂料中的低温热脱脂行为。研究表明,在２５０℃以下,当保温时间相当长时,ＰＷ可以全部脱完。在此温度下,石蜡在聚合物和粉末孔隙中的扩散为石蜡的脱除速度控制,脱脂率与脱脂时间、样品厚度的倒数服从指数关系,即：１－ｍ（ｔ）ｍ（０）＝１＋Ｃ′ｅＫｄｔ。脱脂过程中产生的缺陷主要由此阶段不正确的脱脂引起     

Co/Ni比对93W-Co-Ni钨合金烧结温度及力学性能的影响

以Co、Ni作黏结剂,选择不同Co/Ni比,用粉末冶金法制备出HRC硬度在30⁴3之间的93W-Co-Ni钨合金。采用光学金相、扫描电镜对合金组织形貌进行表征,采用准静态拉伸试验对合金的抗拉强度及延伸率进行测试,采用洛氏硬度计对合金硬度进行测定。结果表明:随着Co/Ni比增加,合金的烧结温度逐渐增加,其抗拉强度与延伸率急剧降低,而硬度先增加之后趋于稳定;当Co/Ni≥1.0时,合金抗拉强度很低,延伸率≤1%;当Co/Ni≥4时,其HRC硬度值稳定在4143之间的93W-Co-Ni钨合金。采用光学金相、扫描电镜对合金组织形貌进行表征,采用准静态拉伸试验对合金的抗拉强度及延伸率进行测试,采用洛氏硬度计对合金硬度进行测定。结果表明:随着Co/Ni比增加,合金的烧结温度逐渐增加,其抗拉强度与延伸率急剧降低,而硬度先增加之后趋于稳定;当Co/Ni≥1.0时,合金抗拉强度很低,延伸率≤1%;当Co/Ni≥4时,其HRC硬度值稳定在41⁴3之间,明显高于一般的W-Ni-Fe合金,这主要与Co对W基体的润湿性较差及两者之间易形成脆性化合物Co7W6有关。     

C添加对近β钛合金显微组织及性能的影响

研究了在不同热处理条件下C元素的添加量对近β钛合金Ti-4Al-5Mo-8V-2. 5Cr-1Sn-2Zr微观组织及力学性能的影响。结果表明:C元素添加对近β钛合金在不同热处理条件下的微观组织均有显著影响。C元素添加会导致β晶粒的细化,当C元素添加量由0%(体积分数,下同)增加到3%时,固溶处理后合金的β晶粒尺寸由137μm降低至25μm,且尺寸更加均匀。当C元素添加量持续增加时,β晶粒开始长大。经时效处理后,随着C元素添加量的增加,次生α相尺寸和体积分数均减小。相比于单级时效,双级时效呈现出更多的次生α相。此外,单级时效后晶界处的次生α相会随着C元素添加量的增加而逐渐消失。由于受晶粒细化、TiC颗粒和次生α相的影响,随着C元素添加量的增加,合金的显微硬度和拉伸强度明显提高,塑性降低。     

Effect of Tungsten Content and Compression on Microstructure and Texture Evolution in Liquid Phase Sintered Heavy Alloy

Metallurgical and Materials Transactions A - The crystallographic texture development in uniaxial compression tests of tungsten heavy alloys was systematically investigated by varying the tungsten...     

Al-Ti-B对AZ91D镁合金显微组织和力学性能的影响

研究了Al-Ti-B对AZ91D镁合金铸态显微组织和力学性能的影响,并探讨其化学成分与组织结构和力学性能之间的变化。研究结果表明：Al-Ti-B加入AZ91D镁合金,能明显细化组织晶粒,从而改善合金的室温力学性能。当加入Al-Ti-B时,合金晶粒细化效果较好,其室温力学性能和硬度比原来都有较大的提高。     

微量添加晶界合金对烧结Nd-Fe-B力学性能及微观结构的影响

采用双合金法制备系列烧结Nd—Fe—B磁体(保持其主合金成分不变：Ndl4．1Dy0．5Fe79.0B6.4(原子分数)，所添加的晶界合金中的B含量从0．95％(原子分数)逐步增加到6．95％(原子分数))，研究了微量添加晶界合金对烧结Nd—Fe—B力学性能及微观结构的影响。研究结果表明：微量添加晶界合金所制备的磁体，其抗弯强度值普遍高于单合金法制得的磁体；前者的抗弯强度最高可达397MPa，高于铸造，热压磁体的抗弯值，而后者的抗弯强度仅为309MPa。由相结构分析可知，当添加的晶界合金中的B含量为O．95(原子分数)，主相晶格的四方度减小，这时磁体具有最高的抗弯强度。另外，微量添加晶界合金，可使磁体中晶界相的分布更加均匀，从而基本上消除了主相晶粒直接接触的现象，使晶粒的不规则长大得到抑制。这也是微量添加晶界合金后磁体具有较高抗弯强度的原因之一。对磁性能的研究结果表明，微量添加晶界合金几乎不影响烧结Nd—Fe—B磁体的磁性能。     

Bi对AZ81镁合金组织和力学性能的影响

通过合金制备、微观分析和拉伸试验等方法,研究了Bi对AZ81镁合金组织和力学性能的影响。结果表明:在AZ81中加入适量的Bi后,细化了合金的铸态组织,同时基体中出现热稳定性较高的颗粒相Mg3Bi2。适量Bi的加入提高了合金的室温和高温力学性能,改善了合金的耐热性能。     

钨合金力学行为的计算机数值模拟─—宏观力学性能

在微观力学行为分析的基础上,对90W合金宏观力学性能及其与微观结构因素（粘结相力学参数）之间的关系进行了计算机数值模拟研究.结果表明：钨合金性能与粘结相力学参数密切相关.随着粘结相弹性模量增加,合金的抗拉强度增加,但延伸率降低.当粘结相屈服强度800MPa时,合金抗拉强度随粘结相屈服强度增加而增大,在粘结相屈服度为800MPa时达到最大值.随粘结相抗拉强度增加,合金抗拉强度和延伸率均呈近似线性规律增加.合金延伸率对粘结相应变硬化模量极为敏感.     

Effects of Tungsten Addition on the Microstructure and Mechanical Properties of Microalloyed Forging Steels

In the current study, the effects of tungsten (W) addition on the microstructure, hardness, and room/low [223 K and 173 K (?50 °C and ?100 °C)] temperature tensile properties of microalloyed forging steels were systematically investigated. Four kinds of steel specimens were produced by varying the W additions (0, 0.1, 0.5, and 1 wt pct). The microstructure showed that the addition of W does not have any noticeable effect on the amount of precipitates. The precipitates in W-containing steels were all rich in W, and the W concentration in the precipitates increased with the increasing W content. The mean sizes of both austenite grains and precipitates decreased with the increasing W content. When the W content was equal to or less than 0.5 pct, the addition of W favored the formation of allotriomorphic ferrite, which subsequently promoted the development of acicular ferrite in the microalloyed forging steels. The results of mechanical tests indicated that W plays an important role in increasing the hardness and tensile strength. When the testing temperature was decreased, the tensile strength showed an increasing trend. Both the yield strength and the ultimate tensile strength obeyed an Arrhenius type of relation with respect to temperature. When the temperature was decreased from 223 K to 173 K (from ?50 °C to ?100 °C), a ductile-to-brittle transition (DBT) of the specimen with 1 pct W occurred. The addition of W favored a higher DBT temperature. From the microstructural and mechanical test results, it is demonstrated that the addition of 0.5 pct W results in the best combination of excellent room/low-temperature tensile strength and ductility.     

Effect of Yttrium and Cerium Addition on Microstructure and Mechanical Properties of AM50 Magnesium Alloy

To develop magnesium alloy with low cost, high strength and excellent elevated temperature properties, effect of Y and Ce addition on microstructure and mechanical properties of AM50 magnesium alloy was studied. Result showed that addition of small amount of Y and Ce to AM50 alloys resulted in refinement of microstructure. Owing to the improvement of microstructure, the mechanical properties of alloys at both ambient and elevated temperature were increased. AM50 alloy containing 0.6 % Ce-0.3 % Y （mass fraction） had good refinement effect and relatively ideal mechanical properties.     

钨含量对Mo-W合金板材组织及力学性能的研究

Mo-W合金因为高熔点、低电阻率及优良的高温性能,在工业高温炉、电子光源和平板显示等诸多领域中已得到广泛应用.研究通过采用粉末冶金及轧制变形的工艺制备出Mo-W合金板材,研究了添加不同钨含量对Mo-W合金板材退火组织形貌演变及高温力学性能的影响.结果表明:轧制变形后的Mo-W合金板材与通过理论计算得到的密度值基本一致,...     

二步烧结法控制高比重合金的变形及其对组织与性能的影响

采用二步烧结法（固相烧结＋液相烧结）控制高比重合金的变形。首先在１４００℃下固相烧结,然后在粘结相的液相线温度以上进行液相烧结以达到全致密。由于在固霜烧结阶段形成了坚固的十四面体形的三维连通网络骨架,阻碍了液相烧结中钨颗粒“偏析”所引起的变形,合金的性能和显微组织的均匀性大大提高。     

高比重钨合金注射成形工艺研究

对高比重钨合金的注射成形工艺进行了研究,包括粉末的预处理,喂料制备、注射、脱脂和烧结工艺,并对材料的微观组织和机械性能进行了分析。研究表明:预处理后粉末的装载量可以达到58%,经过适当的注射工艺及热脱脂烧结工艺后,可以得到无缺陷的烧结坯。在一定的烧结温度范围内,烧结坯的密度、硬度等性能指标随着烧结温度的升高而增大。对95WNiFe材料而言,当烧结温度为1 450℃,烧结时间为120 min时,其密度可达18.02 g/cm~3,硬度为29 HRC,抗拉强度为792 MPa,屈服强度为612 MPa,延伸率为10%。     

W-Ni-Fe高比重合金断口形貌研究

通过对W-Ni-Fe高比重合金力学性能差别很大的两组断口形貌进行分析,在一些高比重合金钨颗粒内发现有W-Ni-Fe的沉淀相,该沉淀相对合金力学性能的提高有益。沉淀相形成主要与成分配比以及烧结后期的真空处理有关。断口形貌可以反应高比重钨合金的烧结状况,而材料的力学性能与合金断口形貌又有很明显的对应关系,因此,要获得很高的力学性能,烧结及热处理工艺是十分重要的工序。     

含钇银合金硫化腐蚀行为的研究及其对力学性能的影响

采用扫描电镜、能谱分析和电子力学性能等测试分析手段,研究了添加钇的银合金在常温下浸泡在0.1 mol·L-1Na2S溶液中的硫化腐蚀行为及其对合金力学性能的影响.研究表明,添加钇的银合金腐蚀层分为两层,外层为氧化层,以Cu2O为主,内层为硫化层,以Cu2S为主.添加钇的银合金在常温,16 d腐蚀预处理后,室温拉伸性能与未腐蚀的银合金相比,抗拉强度提高到275 MPa,延伸率基本保持不变.     

钨铼合金制备方法和高温力学性能的研究进展

高性能W-Re-ThO2,W-Re-HfC系钨铼合金的制备和性能研究会促进其在电子、核能、航天和测温技术等领域的应用。详细归纳了W-Re-ThO2和W-Re-HfC两种钨铼合金采用的工艺路线和工艺参数,总结了两种合金在不同成分和加工状态下时的高温力学性能,最后探讨了铼效应对钨铼合金高温性能影响的规律。钨合金的研究目前在向细化、纯化和强韧化方向发展,粉末冶金法是制备钨铼合金合适的工艺路线,因此开展第二相粒子强化的钨铼合金组织和性能的研究是非常重要的研究内容和方向。     

添加Fe对Cu-9Ni-6Sn合金组织与性能的影响

本文对真空熔铸含Ｆｅ量为０．３７～１．３６ｗｔ％的Ｃｕ－９Ｎｉ－６Ｓｎ合金的铸锭组织,时效和形变时效特征及其组织变化作了研究。实验证明：（１）０．３７～１．３６ｗｔ％Ｆｅ能完全固溶于Ｃｕ－９Ｎｉ－６Ｓｎ合金中;（２）含少量Ｆｅ的合金的铸锭组织、时效硬化、形变时效和组织变化等基本特征与不含Ｆｅ的合金相类似,但少量Ｆｅ促进合金时效、形变时效过程,增加硬化效果。