Siliconization elimination for SiC coated C/C composites by a pyrolytic carbon coating and the consequent improvement of the mechanical property and oxidation resistances

Carbon/carbon (C/C) composites have a wide application as the thermal structure materials because of their excellent properties at high temperatures. However, C/C composites are easily oxidized in oxygen-containing environment, which limits their potential applications to a great degree. Silicon carbide (SiC) ceramic coating fabricated via pack cementation (PC) was considered as an effective way to protect C/C composites against oxidation. But the mechanical properties of C/C composites were severely damaged due to chemical reaction between the molten silicon and C/C substrate during the preparation of SiC coating by PC. In order to eliminate the siliconization erosion, a pyrolytic carbon (PyC) coating was pre-prepared on C/C composites by the chemical vapor infiltration (CVI) prior to the fabrication of SiC coating. Due to the retardation effect of PyC coating on siliconization erosion, the flexural strength retention of the SiC coated C/C composites with PyC coating increased from 46.27 % to 107.95 % compared with the specimen without PyC coating. Furthermore, the presence of homogeneous and defect-free PyC coating was beneficial to fabricate a compact SiC coating without silicon phase by sufficiently reacting with molten silicon during PC. Therefore, the SiC coated C/C composites with PyC coating had better oxidation resistances under dynamic (between room temperature and 1773 K) and static conditions in air at different temperatures (1773?1973 K).     

Preparing the SiC coated C/C composites with excellent mechanical and antioxidative properties using a buffer layer

The preparation of SiC coating on C/C composites via a pack cementation method would cause serious mechanical damage to C/C substrate due to the siliconization corrosion by molten silicon during the ultra-high-temperature preparation process (2173–2373 K). In order to prepare SiC coated C/C composites with excellent mechanical and antioxidative properties, we applied a buffer layer on the surface of C/C to inhibit siliconization corrosion and densify coating. Results showed that the siliconized area ratio of the C/C substrate was decreased from 60.9% to 24.8%, and its bending strength was increased from 36.9 MPa to 60.6 MPa. Moreover, the mass loss of the modified SiC coated C/C sample has reduced by ~4.14 times after oxidation for 144 h in air at 1773 K and decreased from 2.44% to ? 0.15% after suffering 50 thermal cycles between room temperature and 1773 K.     

HfC nanowires to improve the toughness and oxidation resistance of Si-Mo-Cr/SiC coating for C/C composites

To improve the oxidation resistance of carbon/carbon (C/C) composites, a dense HfC nanowire-toughened Si-Mo-Cr/SiC multilayer coating was prepared by chemical vapor deposition (CVD) and pack cementation. The microstructure, thermal shock and isothermal oxidation resistance of the coating were investigated. HfC nanowires could improve the toughness of the coating and suppress the coating cracking. After incorporating HfC nanowires in the coating, both of the thermal shock and isothermal oxidation resistance of the coating were obviously improved. The multilayer coating with HfC nanowires could effectively protect C/C composites at 1773 K for 270 h, whose weight loss is only 0.19%. The good oxidation resistance is mainly attributed to the formation of a compound glass layer containing SiO₂ and Cr₂O₃.     

SiC nanowire-toughened MoSi2-WSi2-SiC-Si multiphase coating for improved oxidation resistance of C/C composites

To improve the oxidation resistance of carbon/carbon (C/C) composites at high temperature, a SiC nanowire-toughened MoSi₂-WSi₂-SiC-Si multiphase coating was prepared by chemical vapor deposition (CVD) and pack cementation. The microstructure, mechanical properties and oxidation resistance of the coating were investigated. After the introduction of SiC nanowires, the elastic modulus, hardness, and fracture toughness of the MoSi₂-WSi₂-SiC-Si coating were increased by 25.48%, 4.09% and 45.03%, respectively. The weight loss of the coated sample with SiC nanowires was deceased from 4.83–2.08% after thermal shock between 1773 K and room temperature for 30 cycles and the weight loss is only 3.24% after isothermal oxidation at 1773 K in air for 82 h. The good oxidation resistance of the coating is mainly attributed to that SiC nanowires can effectively inhibit the propagation of cracks in the coating by the toughening mechanisms including bridging and pull-out.     

A gradient composite coating to protect SiC-coated C/C composites against oxidation at mid and high temperature for long-life service

To improve the oxidation resistance of carbon/carbon (C/C) composites at mid and high temperature, a gradient composite coating was designed and prepared on SiC-coated C/C composites by in situ formed-SiO₂ densifying the porous SiC-ZrSi₂ pre-coating. SiO₂ gradient distribution was conducive to inhibiting the cracking of the coating. A dual-layer structure with the outer dense layer and the inner microporous layer was formed in the coating during densifying. The dense layer had excellent oxygen diffusion resistance and the microporous layer alleviated CTE mismatch between SiC inner coating and dense layer. Moreover, ZrSiO₄ particles inhibited crack propagation and stabilized SiO₂ glass. Therefore, the coating can protect the C/C composites from oxidation at 1473 K, 1573 K and 1773 K for 810 h, 815 h and 901 h, respectively. The coated samples underwent 30 thermal cycles between room temperature and 1773 K without mass loss, exhibiting good thermal shock resistance.     

SiC-Si coating with micro-pores to protect carbon/carbon composites against oxidation

To improve the oxidation resistance of carbon/carbon (C/C) composites at high temperatures, a SiC-Si coating with micro-pores was prepared by slurry and heat-treatment on the surface of C/C composites with SiC-Si inner coating acquired by pack cementation (PC). The microstructure, phase composition, element distribution, and anti-oxidation properties of the dual-layer SiC-Si coating were investigated. The results show that a SiO₂-SiC inlay structure was formed during the oxidation process, due to a large amount of SiO₂ rapidly generated by the oxidation of SiC particles in the porous coating. The coating with this structure could inhibit the cracking of SiO₂ glass and had a good resistance to oxygen diffusion. Moreover, the crack propagation was blocked by the remaining micro-pores of the coating. The coating could protect C/C composites against oxidation for 846 h only with the mass loss of 0.16 % at 1773 K in air.     

A SiC–Si–ZrB2 multiphase oxidation protective ceramic coating for SiC-coated carbon/carbon composites

In order to improve the oxidation protective ability of SiC-coated carbon/carbon (C/C) composites, a SiC–Si–ZrB₂ multiphase ceramic coating was prepared on the surface of SiC-coated C/C composite by the process of pack cementation. The microstructures of the coating were characterized using X-ray diffraction and scanning electron microscopy. The coating was found to be composed of SiC, Si and ZrB₂. The oxidation resistance of the coated specimens was investigated at 1773 K. The results show that the SiC–Si–ZrB₂ can protect C/C against oxidation at 1773 K for more than 386 h. The excellent oxidation protective performance is attributed to the integrity and stability of SiO₂ glass improved by the formation of ZrSiO₄ phase during oxidation. The coated specimens were given thermal shocks between 1773 K and room temperature for 20 times. After thermal shocks, the residual flexural strength of the coated C/C composites was decreased by 16.3%.     

A MoSi2-SiOC-Si3N4/SiC anti-oxidation coating for C/C composites prepared at relatively low temperature

In this study, SiC coating for C/C composites was prepared by pack cementation method at 1773 K, and MoSi₂-SiOC-Si₃N₄ as an outer coating was successfully fabricated on the SiC coated samples by slurry method at 1273 K. The microstructure and phase composition of the coatings were analyzed. Results showed that a porous β-SiC inner coating and a crack-free MoSi₂-SiOC-Si₃N₄ coating are formed. Effect of Si₃N₄ content on the oxidation resistance of the coated C/C composites at 1773 K in air was also investigated. The weight loss curves revealed that introducing the appropriate proportion of Si₃N₄ could improve the oxidation resistance of coating. The MoSi₂-SiOC/SiC coated C/C sample had an accelerated weight loss after oxidation in air for 20 h. However, the coating containing 45% Si₃N₄ could protect C/C composition from oxidation for 100 h with a minute weight loss of 0.63%.     

A ZrB2–SiC/SiC oxidation protective dual-layer coating for carbon/carbon composites

In order to improve the oxidation resistance of C/C composites, a ZrB₂–SiC/SiC oxidation protective dual-layer coating was prepared by a pack cementation combined with the slurry paste method. The phase and microstructure of the coating were characterised by X-ray diffraction, scanning electron microscope and energy-dispersive spectrometer analyses. The anti-oxidation and thermal shock resistance of the coating were also investigated. It was found that the ZrB₂–SiC/SiC coating could effectively improve the oxidation resistance of the C/C composites. The weight loss of the coated samples was only 1.8% after oxidation at 1773?K for 18?h in air. The coating endured 20 thermal shock cycles between 1773?K and room temperature with only 4.6% weight loss.     

A Si–SiC oxidation protective coating for carbon/carbon composites prepared by a two-step pack cementation

To prevent carbon/carbon (C/C) composites from oxidation, a Si–SiC coating has been prepared by a two-step pack cementation technique. X-ray diffraction (XRD) and scanning electron microscopy (SEM) analysis show that the coating obtained by the first step pack cementation is a porous β-SiC structure, and a dense structure consisting α-SiC, β-SiC and Si is obtained after heat-treatment by the second step pack cementation. By energy dispersive spectroscopy (EDS) analysis, a gradient C–SiC transition layer can be formed at the C/C-coating interface. The as-received coating has excellent oxidation protection ability and can protect C/C composites from oxidation for 166 h at 1773 K in air. The weigh loss of the coated C/C is due to the formation of bubble holes on the coating surface and through-coating cracks in the coating.     

Oxidation resistance of a gradient self-healing coating for carbon/carbon composites

A gradient self-healing coating consisting of three layers, SiC-B₄C/SiC/SiO₂, was examined as a multilayer protection for carbon/carbon composites. The inner layer was made of B₄C and β-SiC, the middle layer was a SiC based layer, and the outer layer was SiO₂ as an airproof layer. Both inner and middle layers were produced to be diphase structure by a pack cementation technique, and the outer airproof layer was prepared by hydrolyzing tetraethylorthosilicate. SEM and EDS investigations showed that the coating had a compositional gradient between B₄C and SiC. The coating showed great self-healing properties from 500 °C to 1500 °C. The weight loss rate of the coated composites was less than 1.3% after 50 h at 1500 °C, and coating represented excellent thermal shock resistance at 1500 °C. The oxidation kinetics of coated carbon/carbon composites showed that the Arrhenius curve consisted of three parts with two broken points at about 700 °C and 1100 °C, and the three parts corresponded to three different self-healing mechanisms in different temperature regions.     

Effect of temperature gradient on the erosion behavior of SiC coating for carbon/carbon composites in a combustion environment

SiC coating with a thickness of 50–70 µm was prepared on the surface of C/C composites by in-situ reaction method. The SiC coated C/C composites were then tested in a wind tunnel where a temperature gradient from 200 to 1600 °C could be obtained to investigate their erosion behavior. The results of wind tunnel test indicated that the service life of C/C composites was prolonged from 0.5 to 44 h after applying the SiC coating. After the wind tunnel test, three typical oxidation morphologies, including glassy SiO₂ layer, porous SiO₂ layer and clusters of honeycomb-like SiO₂ grains, were found on the SiC coated C/C composites. With the decrease of oxidation temperature, the amount of glassy SiO₂ declined and the thermal stress increased, which induced the cracking followed by the degradation of the SiC coating.     

Oxidation resistance of SiC nanowires reinforced SiC coating prepared by a CVD process on SiC‐coated C/C composites

Oxidation protective SiC nanowires‐reinforced SiC (SiCNWs‐SiC) coating was prepared on pack cementation (PC) SiC‐coated carbon/carbon (C/C) composites by a simple chemical vapor deposition (CVD) process. This double‐layer SiCNWs‐SiC/PC SiC‐coating system on C/C composites not only has the advantages of SiC buffer layer but also has the toughening effects of SiCNWs. The microstructure and phase composition of the nanowires and the coatings were examined by SEM, TEM, and XRD. The single‐crystalline β‐SiC nanowires with twins and stacking faults were deposited uniformly and oriented randomly with diameter of 50‐200 nm and length ranging from several to tens micrometers. The dense SiCNWs‐SiC coating with some closed pores was obtained by SiC nanocrystals stacked tightly with each other on the surface of SiCNWs. After introducing SiCNWs in the coating system, the oxidation resistance is effectively improved. The oxidation test results showed that the weight loss of the SiCNWs‐SiC/PC SiC‐coated samples was 4.91% and 1.61% after oxidation at 1073 K for 8 hours and at 1473 K for 276 hours, respectively. No matter oxidation at which temperature, the SiCNWs‐SiC/PC SiC‐coating system has better anti‐oxidation property than the single‐layer PC SiC coating or the double‐layer CVD SiC/PC SiC coating without SiCNWs.     

Oxidation and erosion resistance of multi-layer SiC nanowires reinforced SiC coating prepared by CVD on C/C composites in static and aerodynamic oxidation environments

A multi-layer SiC nanowires reinforced SiC (SiCnws-SiC) coating was prepared in-situ on carbon/carbon (C/C) composites by three chemical vapor deposition (CVD) processes. The microstructure and phase composition of the nanowires fabricated on the first-layer SiCnws-SiC coating and the coatings were examined by SEM, TEM, and XRD. The bamboo-like SiC nanowires with a 50?nm diameter and a length of several tens of micrometers are straight, randomly orientated and distributed like a net on the first-layer SiCnws-SiC coating. The growth direction is [111], and the growth mechanism is VS. The multi-layer SiCnws-SiC coating has three layers: the thickness of the first-layer is roughly 400?µm, and the outer two layers are about 200?µm. Each layer has a sandwich structure. The isothermal oxidation and erosion resistance of the multi-layer SiCnws-SiC coating were investigated in an electrical furnace and a high temperature wind tunnel. The results indicated that the weight loss of the multi-layer SiCnws-SiC coated C/C composites was only 1.8% after oxidation in static air at 1773?K for 361?h. Further, the coated sample failed due to fracture of the coating at the clamping position (i.e. 80?mm) after erosion at 1873?K for 130?h in the wind tunnel. The weight loss of the coated C/C composites occurred due to the formation of penetrating cracks in the coating during the oxidation thermal shock. The maximum bending moment and the larger clamping force caused the coating fracture and resulted in intense oxidation of the substrate and the failure of the specimen.     

Microstructure and anti-oxidation properties of multi-composition ceramic coatings for carbon/carbon composites

To protect carbon/carbon (C/C) composites from oxidation at elevated temperature, an effective WSi₂-CrSi₂-Si ceramic coating was deposited on the surface of SiC coated C/C composites by a simple and low-cost slurry method. The microstructures of the double-layer coatings were characterized by X-ray diffraction, scanning electron microscopy and energy dispersive spectroscopy analyses. The coating exhibited excellent oxidation resistance and thermal shock resistance. It could protect C/C composites from oxidation in air at 1773 K for 300 h with only 0.1 wt.% mass gain and endure the thermal shock for 30 cycles between 1773 K and room temperature. The excellent anti-oxidation ability of the double-layer WSi₂-CrSi₂-Si/SiC coating is mainly attributed to the dense structure of the coating and the formation of stable vitreous composition including SiO₂ and Cr₂O₃ produced during oxidation.     

Research on microstructure and oxidation resistant property of ZrSi2-SiC/SiC coating on HTR graphite spheres

ZrSi₂-SiC/SiC coating was prepared on the surface of high temperature gas-cooled reactor (HTR) matrix graphite spheres by two-step pack cementation and sintering process. The microstructure, oxidation resistance and thermal shock resistance properties of the as-prepared coatings with different original powder mixtures were investigated. Results show that dense microstructure of the ZrSi₂-SiC/SiC coating and continuous ZrSiO₄-SiO₂-ZrO₂ glass phase generated during the oxidation process were the key factors for the outstanding thermal properties. When the mole ratio of Zr:Si:C reaches 1:7:3 in the second pack cementation powders, the coated graphite spheres have optimum oxidation resistant ability. The weight gain is only 0.6 wt% after 15 times thermal shock tests and 0.12 wt% after isothermal oxidation test at 1500 °C for 20 h in air. The oxidation resistant mechanism of the coating was also discussed. The dense inner SiC layer and the outer glass layer generated during the oxidation process could protect the ZrSi₂-SiC/SiC coating from further oxidation.     

SiC/MoSi2 based coatings for Cf/C composites by two step pack cementation

In order to improve the oxidation resistance of C_f/Cs produced by chemical vapour infiltration, a multilayer coating based on silicon carbide and molybdenum disilicide was produced by two-step pack cementation technique. The inner SiC layer with a thickness up to 25 μm was obtained without promoted reaction additives by varying the composition, and thermal treatment conditions. The SiC/SiC-MoSi₂ coating was produced with a thickness up to 80 μm by two step pack cementation, considering the effect of the inner layer characteristic. The enhancement of the oxidation resistance, observed in SiC/SiC-MoSi₂ coated C_f/Cs by means of thermal analysis in flowing air up to 1500 °C, was due to the formation of SiO₂ promoted by the passive oxidation of silicon carbide and molybdenum disilicide.     

Ablation resistance of HfB2-SiC coating prepared by in-situ reaction method for SiC coated C/C composites

To improve the ablation resistance of SiC coating, HfB₂-SiC coating was prepared on SiC-coated carbon/carbon (C/C) composites by in-situ reaction method. Owing to the penetration of coating powders, there is no clear boundary between SiC coating and HfB₂-SiC coating. After oxyacetylene ablation for 60 s at heat flux of 2400 kW/m², the mass ablation rate and linear ablation rate of the coated C/C composites were only 0.147 mg/s and 0.267 µm/s, reduced by 21.8% and 60.0%, respectively, compared with SiC coated C/C composites. The good ablation resistance was attributed to the formation of multiple Hf-Si-O glassy layer including SiO₂, HfO₂ and HfSiO₄.     

Oxidation behavior of oxidation protective coatings for PIP-C/SiC composites at 1500 °C

Three-dimensional carbon fiber reinforced silicon carbide (C/SiC) composites were fabricated by precursor infiltration and pyrolysis (PIP) with polycarbosilane as the matrix precursor, SiC coating prepared by chemical vapor deposition (CVD) and ZrB₂-SiC/SiC coating prepared by CVD with slurry painting were applied on C/SiC composites, respectively. The oxidation of three samples at 1500 °C was compared and their microstructures and mechanical properties were investigated. The results show that the C/SiC without coating is distorted quickly. The mass loss of SiC coating coated sample is 4.6% after 2 h oxidation and the sample with ZrB₂-SiC/SiC multilayer coating only has 0.4% mass loss even after oxidation. ZrB₂-SiC/SiC multilayer coating can provide longtime protection for C/SiC composites. The mode of the fracture behavior of C/SiC composites was also changed. When with coating, the fracture mode of C/SiC composites became brittle. When after oxidation, the fracture mode of C/SiC composites without and with coating also became brittle.     

Oxidation and erosion resistance of MoSi2-CrSi2-Si/SiC coated C/C composites in static and aerodynamic oxidation environment

A MoSi₂-CrSi₂-Si multi-composition coating was prepared on the surface of SiC coated carbon/carbon (C/C) composites by pack cementation in argon. The crystalline structure of the multi-composition coating was measured by X-ray diffraction. The morphology and element distribution were analyzed by scanning electron microscopy and energy dispersive spectroscopy, respectively. The isothermal oxidation and erosion resistance of the multi-layer coating were investigated in electrical furnace and high temperature wind tunnel, respectively. These results indicated that the weight loss of the coated C/C composites was only 0.8% after oxidation in air at 1873 K for 500 h, and the sample was fractured after erosion at 1873 K for 32 h in wind tunnel. The weight loss of the coated C/C composites was considered due to the excessive depletion of the outer coating and the appearance of defects in the coating. The mismatch of thermal expansion coefficient between the multi-layer coating and C/C composites caused excessive local stress and resulted in the fracture of the coated C/C composites.