涂层硬质合金刀具车削50钢的切削力与刀具磨损机理研究

涂层工艺可以提高硬质合金刀具的切削性能。以发动机主轴、锻造齿轮和轧辊等机械零件上广泛应用的50正火钢作为研究对象,采用多层涂层硬质合金刀具进行车削加工试验,研究切削参数对切削力的影响规律以及高速干车削条件下刀具的磨损机理。研究结果表明：切削速度v<250m/min时,三向切削力随着切削速度的增大而减小,随着切削深度的增大而增大,随着进给量的增大先减小后增大。涂层硬质合金刀具的主要磨损形态有硬质点磨损和黏结磨损,其中硬质点磨损贯穿刀具磨损全过程;刀具在不同磨损阶段有不同程度的扩散磨损和氧化磨损。涂层硬质合金刀具破损时出现崩刃、涂层剥落、裂纹破损和积屑瘤等现象。     

高速铣削AISI 4340合金结构钢时涂层刀具磨损机理研究

针对AISI 4340合金结构钢难加工的特点,选用PVD硬质合金涂层刀具进行高速干铣削试验,选用扫描电子显微镜(SEM)观察失效刀具表面的磨损形貌特征,选用能谱分析仪(EDS)分析磨损刀具表面的元素分布及含量,揭示刀具的磨损机理。研究结果表明:刀具寿命与切削参数选取有关,随着切削速度的增加,刀具磨损加快,刀具寿命降低。硬质合金涂层刀具的主要磨损形式是前刀面磨损和后刀面磨损,前刀面磨损机理主要是粘结磨损、涂层剥落、切削刃微崩刃;后刀面磨损机理主要是磨粒磨损、粘结磨损、扩散磨损、微裂纹。     

高速车削300M高强度钢涂层刀具失效机理研究

选用不同涂层刀具进行高速切削300M钢试验,利用工具显微镜和电子扫描显微镜(SEM)观察刀具磨损形貌,并利用线扫描进行元素扩散分析,揭示刀具失效机理。研究结果表明:金属陶瓷基涂层刀具高速切削时,切削速度不宜超过240m/min;硬质合金基涂层刀具可在300m/min以上高速切削300M钢,其中CVD-Ti CNAl2O3厚涂层的高速切削性能更高,切屑塑形变形较小;涂层刀具切削300M钢的主要磨损形式是前刀面磨损和后刀面磨损,涂层剥落、崩刃、微裂纹、粘结磨损、磨粒磨损、氧化磨损、扩散磨损是刀具失效的主要原因。     

不同材料和刀尖圆弧半径刀具加工TC4钛合金的表面质量及刀具磨损行为

采用聚晶立方氮化硼(PCBN)、TiAlN涂层硬质合金(2种刀尖圆弧半径)和Al_2O_3+TiC涂层硬质合金等3种刀具车削TC4钛合金工件,测试了刀具后刀面磨损宽度和工件表面粗糙度,观察了刀具的磨损形貌并分析了磨损机制;同时,研究了刀尖圆弧半径对工件表面粗糙度和切屑形貌的影响。结果表明:TiAlN涂层硬质合金刀具具有比其他2种刀具更长的使用寿命,且加工后工件的表面粗糙度最小、表面质量最好,其磨损形式主要为磨粒磨损和黏结磨损;PCBN刀具的失效形式主要为前刀面和后刀面崩塌,而Al_2O_3+TiC涂层硬质合金刀具的磨损形式主要为扩散磨损;刀尖圆弧半径的增大有利于提高TiAlN涂层硬质合金刀具的断屑能力以及加工工件的表面质量。     

PCD刀具微细铣削硬质合金刀具磨损研究

使用PCD刀具进行微细铣削硬质合金的刀具磨损试验,研究了PCD微细铣刀的磨损形态和磨损机理。结果表明,PCD微细铣刀的磨损主要集中在刀尖和底刃上,造成刀具磨损的原因主要包括粘结磨损、磨料磨损以及微崩刃。刀具磨损导致硬质合金加工表面粗糙度逐渐增大。     

单晶金刚石刀具切削有色金属磨损机理研究

研究单晶金刚石刀具切削有色金属的磨损机理,分析切削过程影响加工工件表面粗糙度的影响因素和切削速度、进给量、背吃刀量等因素对积屑瘤生成的影响,以及积屑瘤对刀具切削力的影响。给出了切削过程中刀具与工件接触区温度和压力过高,导致金刚石刀具刃口发生石墨化、溶解、崩刃等磨损破损。前后刀面磨损、崩刃是金刚石刀具磨损主要形态。金刚石刀具磨损是微观磨损的不断积累,其磨损程度与磨损速度取决于金刚石碳原子在有色金属或在其它非金属材料原子中的溶解率。     

超细晶硬质合金刀具切削高温合金试验研究

使用普通晶粒度硬质合金YG8和超细晶硬质合金YG8UF两种材料刀具,分别对GH2132高温合金进行了干式切削试验,对比了两种刀具在不同切削速度条件下的切削力和刀-屑摩擦系数,测定了刀具后刀面的平均磨损宽度VB值,借助扫描电镜观察了刀具后刀面的磨损形貌,同时对刀具的磨损机理进行了分析.结果 表明,晶粒细化可以使切削力降低,刀-屑间平均摩擦系数减小.当切削速度达到65m/min后,超细晶硬质合金刀具YG8UF的使用寿命是普通晶粒度硬质合金刀具YG8的(3～4)倍.超细晶硬质合金刀具比通晶粒度硬质合金刀具具有更好的抗磨料磨损、粘着磨损和扩散磨损性能.     

PCBN刀具高速切削抗氢钢HR-2的性能研究

采用不同CBN含量和晶粒结构的PCBN刀具,在不同切削速度下进行了HR-2抗氢钢的高速精密切削试验。通过对PCBN刀具前、后刀面的显微形貌特征进行观测,分析了刀具的失效磨损机理,研究了不同CBN含量及不同切削速度对刀具使用寿命的影响。对刀具磨损的测量结果表明,PCBN刀具高速切削HR-2时,CBN含量高的刀具显示出更长的使用寿命,且在130-200m/min区间为最佳切削速度区域。SEM和EDS分析结果表明,高速精密切削HR-2的磨损机理为氧化磨损、扩散磨损、粘结磨损,同时存在磨粒磨损以及引起的微崩刃现象。     

涂层硬质合金刀具高速车削300M刀具磨损机理研究

以在飞机、汽车、轮船等领域的关键承力件上广泛应用的超高强度合金钢300M作为研究对象,采用涂层硬质合金刀具进行高速干车削加工,并对切屑变形、刀具寿命及刀具磨损机理进行分析。研究表明:高速切削300M时,切屑的塑性变形严重;涂层刀具主要的磨损形式为正常的前、后刀面磨损,以及非正常的剥落和崩刃;刀具在稳定磨损阶段形成了次生粘结层起着隔热、减摩的作用,有效提高了刀具寿命,但在急剧磨损阶段,大块状的粘结、崩刃、涂层剥落、微裂纹等致使刀具磨损加剧;高速车削300M涂层硬质合金刀具主要的磨损机理为粘结磨损、磨粒磨损、涂层剥落、微崩刃、微裂纹。该研究可望在高性能涂层刀具设计、刀具寿命预测等方面推广应用。     

PCBN刀具断续切削高强度钢的实验研究

通过整体PCBN刀具硬态切削淬硬钢58SiMn实验,研究了切削速度和进给量对切削力及表面粗糙度的影响.实验结果表明:切削力和表面粗糙度值都随进给量增加而增大;在较低切削速度时切削力随切削速度提高而减小,当切削速度达到一定程度时出现拐点,继续提高切削速度切削力逐渐增大.在实验条件下,切削速度低于569 m/min时刀片以磨损为主;当速度为768 m/min时,以崩刃为主.     

叶切面最大厚度数值计算与应用

以叶切面最大厚度的数值计算方法为基础,探讨叶切面最大厚度计算的计算机实现,介绍叶切面厚度数值计算法的应用实例.     

Natural frequencies of vibration of a class of solids composed of layers of isotropic materials

In a recent paper, the Ritz method with simple algebraic polynomials as trial functions was used to obtain an eigenvalue equation for the free vibration of a class of homogeneous solids with cavities. The method presented is here extended to the study of a class of non-homogeneous solids, in which each solid is composed of a number of isotropic layers with different material properties. The Cartesian coordinate system is used to describe the geometry of the solid which is modelled by means of a segment bounded by the yz, zx and xy orthogonal coordinate planes and by two curved surfaces which are defined by fairly general polynomial expressions in the coordinates x, y and z. The surface representing the interface between two material layers in the solid is also described by a polynomial expression in the coordinates x, y and z. In order to demonstrate the accuracy of the approach, natural frequencies are given for both a two- and three-layered spherical shell and for a homogeneous hollow cylinder, as computed using the present approach, and are compared with those obtained using an exact solution. Results are then given for a number of two- and three-layered cylinders and, to demonstrate the versatility of the approach, natural frequencies are given for a five-layered cantilevered beam with a central circular hole as well as for a number of composite solids of more general shape.     

盘丝极心偏对三爪自定心卡盘找标精度影响的分析

三爪自定心卡盘作为机床的主要附件,已有一百多年的发展历史,尽管目前随着数控技术的不断发展,越来越多地需求高速动力卡盘,但三爪自定心卡盘目前仍有一定的市场。 要保证卡盘可靠地夹紧工件,必须使其有可靠的夹持精度;要保持卡盘的精度,必须要严格控制各零部件公差及误差,如盘丝的极心偏。 　　极心偏是形成圆的渐开线的基圆圆心 (极心 )与盘丝内孔中心不同心所造成的偏差值。它对卡盘精度的影响分两种情况,一是卡爪夹持弧采用配磨,二是卡爪夹持弧采用单磨。本文主要探讨配磨时的影响。 　　卡爪夹持弧采用配磨,即每台卡盘整体…     

双丝杠驱动机构同步分析

介绍了双丝杠驱动机构工作原理,论述了双丝杠运动产生不同步的原因以及如何判定与解决同步问题。     

圆柱面素线的直线度公差带解析

详细分析了圆柱面素线的直线度公差带在新旧标准中定义和解释的区别，并从对圆柱面素线实际要素检测的角度，提出了推行新标准的实际意义。     

膨胀套导向机构的设计

通过分析膨胀套在实际使用产生滑移受阻现象、卡死现象原因的实质,并在分析产生问题原因的基础上提出了改进措施即：增加导向机构。     

广州地铁APM列车制动机理分析

根据广州市珠江新城旅客自动运输系统(APM)列车的运行特点,介绍APM列车制动系统的制动方式及其特点,分析APM列车动态制动和摩擦制动的工作机理及其区别和联系,阐明APM列车制动系统的电控制过程和气控制过程,从而为APM列车制动系统的维护和管理提供一定的依据.     

活塞销孔加工工艺的改进

我公司于８０年代末引进Aspera公司年产８０万台冰箱（冷柜）压缩机生产线及软件技术，在压缩机加工中，活塞销孔（如图１所示）的加工是难点之一。用镗床加工，质量一直难以达到要求，废品率很高。后来我们将Aspera公司的加工工艺即精镗后滚光改为精镗后用金刚石铰刀粗、精铰孔，由此解决了这个技术难题。（１）原意大利Aspera公司工艺简述其工艺流程为：钻６．５通孔→扩孔至７＋０．１→粗镗７．４７３＋０．０３６、圆柱度０．０１→精镗至７．９３５＋０．００６、圆柱度０．００２→滚光７．９３８＋０．００６、圆柱度０…     

磨粉机快辊轴承座加工工艺设计

设计了磨粉机快辊轴承座的加工工艺和具体的工装夹具.利用卧式加工中心加工磨粉机快辊轴承座,辅以能够高效快速夹紧的夹具,既可以保证加工精度,又能够提高加工效率.     

Development of sclerometric method of studying activation of parameters of damage and fracture of friction deformable surfaces

The article presents a brief review of the wear models based on the kinetic thermofluctuation approach. The materials were developed using SamGTU sclerometric programming software and a set of instruments developed at Samara Engineering University for assessing the parameters of kinetic thermoactivation for surface fracture deformed by friction. The first obtained results of assessments and the estimated prediction of wear resistance exemplified by tribocouple of the aircraft chassis are presented.