元素Bi及稀土La、Nd对Zn-10Al-5Cu钎料性能的影响

研究了Bi及稀土添加对Zn-10Al-5Cu(mass%)基体合金的润湿性能、显微组织、力学性能的影响。结果表明:钎料合金铺展面积随Bi添加量的增加而增大;铜铝接头抗剪强度随Bi添加量的增加而先增加后降低,得到的Zn-10Al-5Cu-2Bi(mass%)是性能较为优良的钎料。在Zn-10Al-5Cu-2Bi(mass%)钎料中添加稀土La、Nd,钎料的润湿性得到改善,当稀土元素添加量为0.15%时,钎料的润湿性能最佳。随着稀土元素的添加,钎料中大块的黑色共析组织逐渐变小,基体组织得到细化;当稀土元素含量为0.1%时,基体组织最为均匀、细密,晶粒也达到最大程度的细化,铜铝钎焊接头的抗剪强度达到最大。因此稀土La、Nd元素在Zn-10Al-5Cu-2Bi(mass%)中的最佳添加量为0.1%左右。     

微量稀土镧钕对Bi5Sb8Sn力学性能影响

通过在Bi5Sb8Sn基体钎料上添加微量稀土镧钕形成Bi5Sb8SnRE新型钎料合金,研究了稀土镧钕对钎料合金力学性能的影响,同时对显微组织进行了分析.结果表明,稀土镧钕含量为0.2%时,Bi5Sb8SnRE合金抗拉强度和抗剪强度达到最大值,分别为58.30 MPa和15.50 MPa,合金抗拉强度和钎焊接头的抗剪强度较基体钎料Bi5Sb8Sn分别提高了44.2%和57.0%.显微组织分析表明,微量稀土镧钕的添加能显著细化该钎料的合金组织,改善合金的组织分布,提高钎料的力学性能;但当稀土含量超过0.2%时,稀土化合物的数量增多,钎料的力学性能下降.     

稀土镧钕对Ti15Cu15Ni钎料硬度及TC4接头抗剪强度的影响

在Ti15Cu15Ni钎料合金基础上添加微量稀土镧钕,以应用普遍的TC4为母材,研究稀土镧钕添加量对钎料合金及钎焊接头性能的影响.结果表明,稀土相分布于α-Ti及金属间化合物的相界,阻碍位错运动,使钎料硬度增加,在稀土含量为1%时达到最大40HRC.稀土镧钕对Ti15Cu15Ni抗剪强度具有较大影响,稀土含量小于0.5%时,抗剪强度随稀土含量增加而增加;稀土含量大于0.5%时,随着稀土含量增加,钎料合金抗剪强度呈下降趋势.当稀土含量等于0.5%时,抗剪强度达到最大为244.55 MPa.     

添加元素Sn,Cu对Zn-Al钎料组织性能的影响

向Zn-10Al基体中添加元素Cu,采用真空炉VF-1600M、金相显微镜、岛津AG-125KN精密万能材料试验机等,研究了Cu元素对Zn-Al钎料合金的熔化特性、润湿性能、金相组织以及力学性能的影响。结果表明,随着Cu元素的增加,钎料的熔点呈先下降后上升的趋势,在铜添加量为4%(质量分数)时,熔点最低;在铜添加量为5%时,润湿性能优良,钎料晶粒最细小,抗拉强度最好;当铜添加量继续增大时,其润湿性能下降,钎料晶粒变大,抗拉强度降低。其次研究了Sn元素的添加量对Zn-10Al-5Cu钎料性能的影响。结果表明,当Sn添加量达到3%时,其抗拉强度良好,钎料的熔化温度降低,在Cu上的润湿性能良好。当锡添加量进一步增加时,钎料合金的的润湿性能降低,基本不铺展。试验得到的Zn-10Al-5Cu-3Sn为性能较为优良的铝/铜钎焊用钎料。     

Cu、Zn、La对Al-Si基钎料钎焊性能的影响

使用正交试验法设计9组添加不同含量Cu、Zn、La元素的Al-4Si基钎料,分析了钎料对LF6铝合金润湿性的影响,并采用润湿性最好的钎料对LF6铝合金进行炉中钎焊,测试了接头剪切强度。结果表明,钎料组织由α-Al基体相、初晶Si相、Al2Cu(θ)相及La Si相组成,并且随着La含量的增加,钎料中初晶Si相成形更加良好;随着Zn含量的增加,钎料中的Al2Cu(θ)相的形状由网状转变为多边形块状。La元素对钎料的铺展性影响较大,Cu元素其次,Zn元素相对比较弱。由正交试验得出6号钎料Al-4Si-15Cu-35Zn-0.2La的铺展面积最大,为226.87 mm~2,钎料液相线为499℃,在530℃保温15 min条件下LF6铝合金钎焊接头平均剪切强度为101.03 MPa。     

稀土元素Er对Bi5Sb8Sn钎料力学性能的影响

通过向Bi5Sb8Sn钎料合金中添加适量的稀土元素铒(Er),研究了不同含量的稀土Er对Bi5Sb8Sn无铅钎料合金力学性能的影响。结果表明,微量稀土Er的添加能显著细化该钎料组织,改善合金的组织分布情况,提高钎料的力学性能;稀土w(Er)0.5%时,Bi5Sb8SnRE合金抗拉强度和钎焊接头的抗剪强度较基体钎料Bi5Sb8Sn分别提高了41.8%和83.0%.;但当稀土w(Er)0.5%时,则组织粗化,钎料力学性能下降。     

稀土元素Ce对Zn-22Al钎料组织和性能的影响

研究了稀土元素Ce的添加对Zn-22Al钎料的电阻率、熔化特性、铺展性能、显微组织以及钎焊接头抗剪强度的影响.结果表明,铈的加入对钎料的电阻率、熔化特性影响甚微,但显著改善了钎料的铺展性能,细化了钎料的基体组织,提高了钎焊接头的抗剪强度.当Ce元素的添加量达到0.05%时,钎料在铝、铜两种母材上的铺展面积取得最大值,分别较未添加时提高了21.4%和11.6%;钎焊接头抗剪强度达到最大值91.3 MPa,比未添加稀土时提高了30.3%.稀土铈含量继续增加时,其显微组织中出现脆性稀土相并且尺寸有增大的趋势,钎料铺展性能、钎焊接头强度明显恶化.     

快速凝固Al-Si基粉末钎料的研制

设计了系列铝硅基合金钎料，采用超音速气体雾化技术制备了钎料粉末。系统地研究了快凝钎料微观组织和焊接性能，优化出一种具有较高综合性能的钎料合金Al-10Si-5Cu-5Zn-0、3RE。研究表明：Al-10Si-5Cu-5Zn-0．3RE快凝粉末钎料的平均直径为0、11mm，组织细小，焊接强度达到了95．8MPa。Zn元素使快凝钎料的熔点显著降低，稀土元素明显改善钎料的润湿性。     

锆元素对Zn-15Al钎料组织和性能的影响

通过扫描电镜、X射线衍射和纳米压痕等方法研究了微量Zr元素对铝合金/不锈钢异种金属钎焊用Zn-15Al钎料显微组织和性能的影响.结果表明,微量Zr元素的添加对钎料的熔点没有明显影响.Zr元素对Zn-15Al钎料基体中η-Zn相有明显细化作用,当Zr元素的质量分数为0.2%时,细化效果最佳;Zr元素的添加量过多时,钎料中形成块状的Al₂ZnZr化合物.当Zr元素的质量分数为0.2%时,Zn-15Al-0.2Zr钎料在不锈钢和铝合金母材上的铺展面积较Zn-15Al钎料分别提高了15.9%和10.2%,钎焊接头抗剪强度达到最大值143 MPa.Zn-15Al,Zn-15Al-0.2Zr,Zn-15Al-0.3Zr 3种钎料的蠕变应力指数分别为6.64,7.35,8.07.     

锆元素对Zn-15Al钎料组织和性能的影响

通过扫描电镜、X射线衍射和纳米压痕等方法研究了微量Zr元素对铝合金/不锈钢异种金属钎焊用Zn-15Al钎料显微组织和性能的影响.结果表明,微量Zr元素的添加对钎料的熔点没有明显影响.Zr元素对Zn-15Al钎料基体中η-Zn相有明显细化作用,当Zr元素的质量分数为0.2%时,细化效果最佳;Zr元素的添加量过多时,钎料中形成块状的Al_2ZnZr化合物.当Zr元素的质量分数为0.2%时,Zn-15Al-0.2Zr钎料在不锈钢和铝合金母材上的铺展面积较Zn-15Al钎料分别提高了15.9%和10.2%,钎焊接头抗剪强度达到最大值143 MPa.Zn-15Al,Zn-15Al-0.2Zr,Zn-15Al-0.3Zr 3种钎料的蠕变应力指数分别为6.64,7.35,8.07.     

Microstructure and Property of Cu/Al Joint Brazed with Al-Si-Ge Filler MetalEI北大核心CSCD

Cu/Al brazing has good prospect for applications in the air conditioning and refrigeration industry. A suitable filler metal is the key of Cu/Al brazing. The chemical and physical properties of the filler metal have great influence on the brazing process and parameters. And the strength of the brazing joint is closely related to the properties of the filler metal and the brazing process. While the previous studies have not developed a kind of Cu/Al brazing filler metal which can achieve a tough joint at a low brazing temperature. In this work, the Al-5.6Si-25.2Ge filler metal was first used to braze Cu/Al dissimilar metals, and the melting characteristics of the filler metal, spreading wettability, Cu interfacial structure and strength of brazed joint were investigated systematically. Additionally, the common Zn-22Al filler metal was also used for comparison. The results show that the Al-5.6Si-25.2Ge filler metal possesses low melting temperature (about 541 degrees C) and excellent spreading wettability on Cu and Al base metals. The interfacial structure of Al-5.6Si-25.2Ge/Cu was CuAl2/CuAl/Cu3Al2. The thickness of planar CuAl and Cu3Al2 phases was only 1 similar to 2 mu m, and the thickness of cellular CuAl2 phase was about 3 mu m. The interfacial structure of Zn-22Al/Cu was CuAl2/CuAl/Cu9Al4, but the average thickness of the CuAl2 layer was up to 15 mm. The test results of the shearing strength show that the shearing strength of the Cu/Al joint brazed with Zn-22Al filler metal was only 42.7 MPa, but the shearing strength brazed with Al-5.6Si-25.2Ge filler metal was higher (53.4 MPa).     

Effects of Cu, Si, Ni and rare earth elements on melting temperature and properties of Al-Si filler metals

The effects of Cu,Si,Ni and RE elements (RE=La and Ce) on the melting temperature of Al-Si filler metals were studied by orthogonal design method.The wettability of the filler metals and the shear strength of 6063 aluminum alloy joints brazed with the different filler metals were measured.The results show that the copper doping content has the most obvious effect on liquidus temperature (T_L) of the Al-Si filler metals and the effect of RE content on T_L is the least.Adding suitable Cu and Si can improve the wettability of the Al-Si filler metals.The shear strength of 6063 aluminum alloy joints brazed with the filler metals S10,S15 and S20,respectively,is better than that of the joints brazed with HL401 due to the improvement of microstructure.It can improve the shear strength of the joints by brazing with the Ni- or RE-doped Al-Si-Cu filler metals.     

Sn改性Ti-Zr-Cu-Ni钎料的微观组织和力学性能

采用自制Ti-Zr-Cu-Ni-Sn钎料钎焊TA2钛合金,研究了不同Sn元素含量改性Ti-Zr-Cu-Ni钎料的熔化特性、微观组织及物相、润湿及熔蚀性、接头拉伸强度。研究表明,Sn含量增加,Ti-Zr-Cu-Ni-Sn钎料固、液相线温度基本升高,但温度差值基本变窄,可更好地抑制钎焊界面脆性化合物形成。Ti-Zr-Cu-Ni-5Sn钎料组织由Ti、Zr基体和晶体相构成,Sn倾向与Ti、Zr结合形成Ti₂Sn₃、Ti₆Sn₅、Zr₅Sn₃等低熔点共晶相。Sn≤1.5%时,随Sn含量增加,钎料对TA2钛合金的润湿性逐渐变差;继续增加Sn,钎料润湿性改善,添加5%Sn的钎料对基体润湿最佳。添加5%Sn并降低Cu、Ni总量的改性钎料对TA2钛合金熔蚀减弱。相同钎焊工艺下,添加5%Sn接头的强度和塑性均有提升。钎焊温度升高,Ti-Zr-Cu-Ni钎料产生更多强化物相,致接头强度大幅提升,而Ti-Zr-Cu-Ni-5Sn钎料产生的含Sn物相强化作用对接头强度提升有限;相...     

Effect of Ce Addition on the Microstructure and Properties of Ag17CuZnSn Filler Metal

The effect of trace amounts of rare earth element Ce on the wettability, mechanical properties and microstructure of Ag17CuZnSn filler metal was investigated systematically by means of microstructure and spectroscopic characterizations. H62 brass and 304 stainless steel were brazed with Ag17CuZnSn-xCe filler metals. The results indicate that wettability and oxidation resistance of filler metal are remarkably improved with adding trace amount of Ce. The shear strength of brazed joint increases 29% compared to that of brazed joint without adding Ce. Moreover, it is observed that the trace amount of Ce in Ag17CuZnSn filler metal refines the brazed joint matrix microstructure. The elements diffusion is examined during the brazing process. More Ce can diffuse into the stainless steel than that of either Cu or Zn. Compared to the Cu solid solution, Fe prefers to diffuse into the Ag solid solution. When the Ce content is 0.3 wt.%, some bright and brittle Ce-bearing particles appear in the bottom of dimples which deteriorate the shear strength of brazed joint. The results of this study can stimulate the use of low-silver brazing filler metals for various applications.     

铟对低银Ag-Cu-Zn钎料显微组织和性能的影响

研究了低银Ag-Cu-Zn钎料(ωAg≤20%)的熔化特性、铺展性能、钎料显微组织。以黄铜/304不锈钢作为母材,采用火焰钎焊方法,进行了搭接钎焊试验。结果表明,低银Ag-Cu-Zn钎料显微组织主要由铜基固溶体、银基固溶体、Cu Zn化合物相构成。In的添加降低了Ag-Cu-Zn钎料的固、液相线温度,改善了钎料润湿性能;添加In的低银Ag-Cu-Zn钎料在凝固过程中析出富In的银基固溶体,起到了固溶强化的效果,改善了钎焊接头的显微组织,从而提高了钎缝接头的力学性能。使用17Ag Cu Zn-1In火焰钎焊黄铜/304不锈钢,钎焊接头成形美观、组织致密、无缺陷存在,综合性能与含银量为25%的BAg25Cu Zn Sn银钎料的性能相当,节银效果显著。     

Effects of Ti on the Brazability of Zn-22Al-xTi Filler Metals as Well as Properties of Cu/Al Brazing Joints

设计并采用Zn-Al-Ti系列钎料对Cu和Al异种金属实施了钎焊,并对Zn-22Al-xTi/Cu界面处的相组成和金属间化合物形貌进行了分析。结果表明：在Zn-22Al中添加0.01%至0.05%的Ti可以显著细化钎料组织,而且Zn-22Al-0.03Ti在Cu基板上的铺展面积比Zn-22Al高出60.4%,但Ti的添加会提高Zn-22Al钎料的熔点和熔化区间。另外,在钎料中添加微量的Ti可以优化Cu/Al接头中Cu侧界面化合物的组织并减小其厚度。相比Zn-22Al钎料,Zn-22Al-0.03Ti钎焊所得Cu/Al接头强度要高出13.4%,而且接头断裂位置由化合物层转移至钎料内部。X射线衍射结果显示,钎焊过程中有CuAl2,Cu9Al4,CuZn 3种化合物产生于钎料与Cu基板界面处     

化学镀锡钎料钎焊黄铜的接头组织和力学性能

采用化学镀方法在BAg45CuZn钎料表面镀覆微米锡层,并用镀锡银钎料以火焰钎焊工艺连接H62黄铜。借助金相显微镜、扫描电镜(SEM)和X射线衍射仪(XRD)分别分析锡化学镀层、H62黄铜钎焊接头的显微组织和物相,并利用万能拉伸机和SEM表征钎焊接头的抗拉强度和断口形貌。结果表明,锡化学镀层结晶晶粒呈现明显的(110)、(210)择优取向,化学镀锡银钎料连接的接头中母材与钎缝结合紧密,接头组织中富Cu相减少,出现Cu_5Zn_8化合物相。随着基体钎料表面镀锡含量升高,钎焊接头的抗拉强度呈现先升高后降低趋势。在化学镀锡含量为6.0%(质量分数)时,钎焊接头的抗拉强度为353MPa。镀锡前后钎焊接头的拉伸断口均呈现韧性断裂。     

Zn-Al钎料钎焊Cu/Al接头组织和性能(英文)

使用不同成分的Zn-Al钎料对铜铝异种金属进行火焰钎焊,研究其力学性能。利用光学显微镜、扫描电镜和能谱研究不同Zn-Al钎料对Cu/Al钎焊接头钎焊性、力学性能及显微组织的影响。结果表明:随着Al含量的增加,Zn-Al钎料在Cu和Al上的铺展面积逐渐增大。当钎料中Al含量为15%时,Cu/Al接头的抗剪强度达到最大值88MPa;随着组织的变化,钎缝硬度值呈现HV122到HV515不等的分布。另外,钎缝组织的成分主要为富Zn相和富Al相,但是当钎料中Al含量为2%和15%以上时,靠近Cu侧的界面处会分别形成CuZn3和Al2Cu两种完全不同的金属间化合物。研究Zn-Al钎料中铝含量对Cu/Al接头界面化合物类型的影响。     

SiC纳米线对Ni-Cr-P钎料及Ni-Cr-P/Q235焊点组织与性能影响

采用具有优良高温强度、高热导率、高耐磨性能和耐腐蚀性能的SiC纳米线为Ni-Cr-P钎料的添加物,研究了钎料/焊点的组织与性能。结果表明,钎料的组织由Ni(Cr)固溶体、Ni₃P固溶体以及Ni(Cr)和Ni₃P共晶组织组成,微量的SiC纳米线可以显著细化基体组织,使焊点抗剪切强度提高29.6%。SiC纳米线的添加使钎料的熔化温度提高约4℃,显著促进钎料在Q235基板表面的润湿性,增幅达到12.5%。然而,过量添加SiC纳米线会显著粗化基体组织,降低钎料的润湿性和焊点的抗剪切强度。在不同SiC含量的Ni-Cr-P钎料中,Ni-Cr-P-0.1SiC钎料/焊点具有明显的优越性。