Fatigue crack growth in fibre metal laminates with multiple open holes

The fatigue crack growth behaviour of hybrid S2‐glass reinforced aluminium laminates (Glare) with multiple open holes was investigated experimentally and analytically. It was observed that the presence of multiple‐site fatigue damage would increase crack growth rates in the metal layers as two propagating cracks converged. An analytical crack growth model was established for predicting crack growth rates based on empirical Paris equation. The effective stress intensity factor at crack tips is a function of mode I far‐field stress intensity factor, crack opening stress intensity factor and effective non‐dimensional stress intensity factor that incorporated the crack‐bridging effect in fibre metal laminates. The predicted results under different applied stress can capture the trend of averaged crack growth rates in experiments, although deviation exists in the predictions.     

Off-axis fatigue cracking behaviour in notched fibre metal laminates

The off‐axis fatigue cracking behaviour of notched fibre metal laminates under constant amplitude loading conditions was investigated experimentally and numerically. It was found that the off‐axis fatigue crack initiation life decreased as the off‐axis angles increased. This indicated that the off‐axis laminates raised the applied stress level in the aluminium (Al) layer and subsequently resulted in earlier cracking in the Al layer. The off‐axis fatigue crack initiation lives of notched fibre metal laminates were predicted using lamination theory and an energy‐based critical plane fatigue damage analysis from the literature. After a crack initiated in the Al layer, it was observed that the crack path angles of the off‐axis specimens were neither perpendicular to the fibre nor to the loading direction. A finite‐element model was established for predicting the crack path angles.     

Fatigue crack growth in hybrid boron/glass/aluminium fibre metal laminates

The crack growth behaviour of hybrid boron/glass/aluminium fibre metal laminates (FMLs) under constant‐amplitude fatigue loading was investigated. The hybrid FMLs consist of Al 2024‐T3 alloy as the metal layers and a mixture of boron fibres and glass fibres as the fibre layers. Two types of boron/glass/aluminium laminates were fabricated and tested. In the first type, the glass fibre/prepreg and the boron fibre/prepreg were used separately in the fibre layers, and in the second type, the boron fibres and the glass fibres were uniformly mingled together to form a hybrid boron fibre/glass fibre prepreg. An analytical model was also proposed to predict the fatigue crack growth behaviour of hybrid boron/glass/aluminium FMLs. The effective stress intensity factor at a crack tip was formulated as a function of the remote stress intensity factor, crack opening stress intensity factor, and the bridging stress intensity factor. The bridging stress acting on the delamination boundary along the crack length was also calculated based on the crack opening relations. Then, the empirical Paris‐type fatigue crack growth law was used for predicting the crack growth rates. A good correlation between the predicted and experimental crack growth rates has been obtained.     

Fatigue behaviour and life prediction of fibre reinforced metal laminates under constant and variable amplitude loading

ABSTRACT Fatigue crack growth of fibre reinforced metal laminates (FRMLs) under constant and variable amplitude loading was studied through analysis and experiments. The distribution of the bridging stress along the crackline in centre‐cracked tension (CCT) specimen of FRMLs was modelled numerically, and the main factors affecting the bridging stress were identified. A test method for determining the delamination growth rates in a modified double cracked lap shear (DCLS) specimen was presented. Two models, one being fatigue‐mechanism‐based and the other phenomenological, were developed for predicting the fatigue life under constant amplitude loading. The fatigue behaviour, including crack growth and delamination growth, of glass fibre reinforced aluminium laminates (GLARE) under constant amplitude loading following a single overload was investigated experimentally, and the mechanisms for the effect of a single overload on the crack growth rates and the delamination growth rates were identified. An equivalent closure model for predicting crack‐growth in FRMLs under variable amplitude loading and spectrum loading was presented. All the models presented in this paper were verified by applying to GLARE under constant amplitude loading and Mini‐transport aircraft wing structures (TWIST) load sequence. The predicted crack growth rates are in good agreement with test results.     

Experimental characterization of the crack-tip-opening angle in fibre metal laminates

Although the crack-tip-opening angle (CTOA) has been shown to be well suited for modelling stable crack growth in monolithic sheet aluminium alloys, its applicability for fibre metal laminates has not been fully analyzed yet. Fracture test were performed on M(T) panels made of Glare 2-3/2-0.4, Glare 3-3/2-0.4 and laminated 2024-T3 3/2-0.4. Different fatigue pre-crack lengths were created to study the effect of bridging fibres on the CTOA measured on the external layer. The effect of bridging fibres resulted in small deviations of the CTOA vs. crack extension curve with respect to the reference panel made of metal laminate. The CTOA criterion could be successfully used for predicting the residual strength in fibre metal laminates.     

拉压加载下纤维增强铝合金层板疲劳裂纹扩展的压载荷效应与预测模型

基于增量塑性损伤理论与纤维增强金属层板疲劳裂纹扩展唯象方法, 推导出在拉-压循环加载下, 纤维增强金属层板疲劳裂纹扩展速率预测模型。并通过玻璃纤维增强铝合金层板在应力比R=-1,-2的疲劳裂纹扩展实验对预测模型进行验证。结果表明, 纤维增强铝合金层板疲劳裂纹扩展的压载荷效应分为两种情况: 在有效循环应力比R_C>0时, 表现为压载荷对铝合金层所承受残余拉应力的抵消作用; 当R_C<0时, 表现为压载荷抵消残余拉应力后, 对纤维增强铝合金层板金属层的塑性损伤, 对疲劳裂纹扩展存在促进作用。纤维铝合金层板疲劳裂纹扩展的压载荷效应不可忽略, 本文中得出的在拉-压循环加载下疲劳裂纹扩展速率预测模型与实验结果符合较好。     

Fracture mechanisms and fracture mechanics at ultrasonic frequencies

Performing fatigue tests at ultrasonic frequencies, e.g. 20 000  Hz, allows one to perform experiments beyond 10⁹ and 10¹⁰ cycles within half a day or a week, respectively. The testing technique has led to the construction of fatigue machines of high technical standard. Use of the ultrasound technique to study the mechanisms of crack initiation in pure metal single crystals, in cast alloys with voids being crack initiation sites, and in complicated fibre-reinforced laminates is reported. Likewise, use of ultrasonic loading to study the mechanisms of crack propagation is discussed, as well as LEFM principles; especially when these principles cannot be applied. It is shown how crack growth retardation with increasing crack length is attained in fibre-reinforced laminates by the effect of fibre bridging. Additional experimental possibilities, e.g. random loading, variation of mean load, superposition of shear loads, variation of temperature and environment, and not only axial but also torsional loading at ultrasonic frequency, and recent research results are discussed.     

Response of fibre reinforced aluminium–lithium laminates to different fatigue conditions

Under fatigue conditions fibre reinforced aluminium–lithium laminates do not respond in the same manner as monolithic aluminium alloys. The variation of fatigue crack growth rates with initial loading condition has been examined for both carbon and glass fibre reinforced laminates, and compared with the behaviour of unreinforced 8090 aluminium–lithium alloy for a range of conditions (different initial nominal stress intensity factor range, load range and reversed loading). During fatigue, cracks grow in the metal layers of these laminates whilst the fibres in the crack wake remain intact, bridging the crack faces. The fibre bridging mechanism, inherent in this laminate system, reduces the fatigue crack growth rate. The magnitude of the bridging effect appears to be inversely related to the applied load range. This relationship can account for the behaviour observed in the performed experiments. This revised version was published online in November 2006 with corrections to the Cover Date.     

Fatigue crack propagation in welded joints under variable-amplitude loading in synthetic sea water

Fatigue crack propagation rates and the fatigue threshold in transverse butt-welded joints of centre crack type were measured in synthetic sea water under variable-amplitude loading. The fatigue threshold was about a half of that in air, and the propagation rates near the fatigue threshold were high compared with those in air. The propagation rate for each cycle under variable-amplitude loading could be estimated from the constant-amplitude data, which were obtained in the crack-closure-free condition.     

Fatigue crack growth and delamination mechanisms of Ti/CFRP fibre metal laminates at high temperatures

Ti/CFRP (titanium/carbon fibre reinforced polymer) fibre metal laminates (FMLs) are composed of titanium sheets and carbon fibres reinforced PMR (polymerization of monomeric reactants) type polyimide resin. Due to the outstanding heat resistance of the material, it can be used in hypersonic aircraft applications. Fatigue cracks in the metal layer and delamination at metal/fibre interface may occur in long‐term high‐temperature use processes. However, the behaviour of the fatigue failure at high temperatures has not been investigated. A temperature‐dependent equation has not been presented to predict the crack growth behaviour at high temperatures. In this study, to investigate the crack propagation and delamination behaviours, fatigue crack growth rate tests using tension‐tension loads at 25°C, 80°C, 120°C, and 150°C were conducted in accordance with ASTM E647‐15e1. The results indicated that the variation in fatigue crack growth rate could be described by a modified temperature‐dependent Paris equation. Interfacial strength and tensile strength may influence fatigue failure at high temperatures. Hence, these strength values were also obtained to analyse the mechanism of fatigue behaviour. The delamination area increased exponentially with temperature due to the weakening of the Ti/CFRP interface, and delamination was invariably generated on the microcracks of the titanium layers.     

Fatigue and Damage Tolerance of Glare

Methods have been developed to describe the fatigue initiation and propagation mechanisms in flat panels as well as mechanically fastened joints and to determine the residual strength of large flat panels. Glare shows excellent crack growth characteristics due to the mechanism of delamination and fibre bridging. The fatigue insensitive fibres restrain the crack opening and transfer load over the crack in the metal layers. During the initiation phase fibre bridging does not occur and the behaviour is dominated by the metal initiation properties. Mechanically fastened joints introduce additional effects such as secondary bending, load transfer and aspects related to the fastener installation. The residual strength of Glare is dependent on the amount of broken fibres and the delamination size and can be described with the R-curve approach.The impact resistance of Glare is related to the aluminium and glass/epoxy properties and is significantly higher than the impact resistance of monolithic aluminium. The same has been proven for fire resistance. Depending on the Glare grade and thickness, the outer aluminium layer will melt away, whereas the other layers will remain intact due to carbonisation of the glass/epoxy layers and delamination of the laminate. The air in the delaminations will act as insulation, keeping the temperatures at the non-exposed side relatively low.     

变幅载荷下纤维金属层板的疲劳与寿命预测

文章建立了纤维金属层板等幅疲劳载荷下的疲劳裂纹扩展速率与寿命预测模型。在此基础上对玻璃纤维-铝合金层板（GLARE）的疲劳裂纹扩展与分层扩展行为进行了试验研究,探讨了层板过载疲劳行为的机理,提出了纤维金属层板变幅载荷下疲劳寿命预测的等效裂纹闭合模型,并在GLARE层板上得到了验证。     

Effect of LCF on HCF crack growth of Ti-17

An improved understanding of fatigue crack growth phenomena applicable to titanium engine disks was developed through complimentary experimental and analytical investigations of Ti-17. The effect of low cycle fatigue (LCF) on the high cycle fatigue (HCF) threshold and rate of crack propagation was studied. A simplified variable-amplitude spectrum, consisting of high-R cycles, corresponding to HCF loading, and periodic R=0.1 cycles, corresponding to LCF loading, was used to demonstrate a load-interaction effect. When the ratio of HCF to LCF cycles was 100 or more the fatigue crack growth lifetimes were significantly lower than predicted using linear damage summation methods assuming no load-interaction effect. Thus, it was concluded that the LCF cycle accelerated the fatigue crack growth rate of subsequent HCF cycles, even when closure was concluded to be negligible. A phenomenological model was formulated based on hypothesized changes in the propagation resistance, K_PR, and fit to the test data. The model confirmed that the periodic LCF cycles increased fatigue crack growth rates of subsequent HCF cycles.     

Characterization of fatigue crack initiation and growth in hybrid aluminium–graphite fibre composite laminates using image analysis

Hybrid aluminum–graphite-epoxy fibre–metal laminates have been tested in open hole tension–tension fatigue at several stress levels. Crack initiation and growth in the outer aluminum layers was monitored by periodic digital imaging of the specimen surface. Image analysis was used to determine the crack length throughout the experiment. Crack growth results were consistent between specimens for each test configuration. A relationship between the crack growth results and stress level was developed using linear elastic fracture mechanics; this successfully characterized the data. The effect of shot peening and alternate hole finishing techniques were considered for fatigue behaviour improvement.     

A theoretical study of fatigue behaviour in unidirectional Ti-based metal matrix composites

The Fatigue Damage Map (FDM) has been used to define the different damage mechanisms operating during fatigue loading of fibre reinforced metal matrix composites (MMCs). Matrix cracking, fibre failure, fibre bridging and interfacial debonding have been suggested as being the dominant factors in fatigue crack growth of MMCs. The FDM has been used to provide information regarding the contribution of these mechanisms to fatigue failure and their dependency on load history. The application of FDM is shown not only to define design limits but also to provide vital information for maintenance engineering. Fatigue, MMCs, fatigue damage map, crack safe conditions, fail safe conditions, crack arrest, crack instability, maximum bridging, micromechanical modelling.     

On the hysteretic nature of variable-amplitude fatigue crack growth

Local Stress–Strain (LSS) approach as applied in notch fatigue analysis is extended to the fatigue crack in order to simulate the effect of variable-amplitude loading on near-tip stress and strain. Simulated near-tip stress–strain response appears to explain load sequence sensitivity of near-threshold fatigue crack growth. This observation is supported by fractographic evidence of near-threshold variable-amplitude fatigue crack in an Al–Cu alloy under closure-free conditions.     

High-cycle fatigue characteristics of quasi-isotropic CFRP laminates over 10 cycles (Initiation and propagation of delamination considering interaction with transverse cracks)

High-cycle fatigue features of over 10⁸ cycles, particularly the initiation and propagation of edge delamination considering the effects of transverse cracks, were investigated using quasi-isotropic carbon-fiber-reinforced plastic (CFRP) laminates with a stacking sequence of [45/0/−45/90]_s in this study. In the relationship between a transverse crack density and initiation and growth of edge delamination, it was found that fatigue damage growth behavior varied depending on applied stress. It was observed that edge delamination initiated and grew at parts where transverse cracks were dense at ordinary applied stress, whereas it was observed that edge delamination grew before or simultaneously with transverse crack propagation at a low applied stress and high-cycle loading. In addition, the critical transverse crack density where delamination begins growing was calculated to evaluate the interaction between transverse crack and edge delamination growth.     

Combined action of crack closure and residual stress under periodic overloads: A fractographic analysis

The close relationship between sequence-sensitive near-tip residual stress and threshold stress intensity raises questions about load interaction models currently in use to estimate fatigue crack growth under variable amplitude loading. In an attempt to address them, experiments were performed on an Al–Cu alloy under specially designed load sequences with periodic overloads. Fractographic evidence from these tests confirms that fatigue crack closure, together with sequence sensitive variation in threshold stress intensity appear to explain all observed results. The fractographic data provide quantitative inputs for improved modeling of variable-amplitude fatigue, particularly at near-threshold crack growth rates. This study appears to suggest that conventional approaches based on the Wheeler and Willenborg residual stress models can provide reasonable estimates only by coincidence. They model the wrong parameter at lower fatigue crack growth rates and may simply not be valid at other growth rates.     

THE EFFECT OF INTERMEDIATE HEAT TREATMENTS ON OVERLOAD INDUCED RETARDATIONS DURING FATIGUE CRACK GROWTH IN AN Al-ALLOY

Abstract— Crack growth fatigue tests were carried out on 2024-T3 specimens. Constant-amplitude loading was periodically interrupted by 10 overload cycles. Intermediate heat treatments (T4) were applied to remove the residual stress in the crack tip zone and the crack closure wake behind the crack tip. Retardation effects induced by crack closure due to the previous load history were fully erased by the heat treatments. Overload effects were easily introduced again by new overload cycles afterwards. Crack growth rate results and fractographic observations indicate that primary crack tip plastic deformation (in virgin material) is more effective for crack extension than secondary plastic deformation in an existing plastic zone. This conclusion is significant for cycle-by-cycle crack growth prediction models for variable-amplitude loading.     

A numerical analysis of constraint effects in fatigue crack growth by use of an irreversible cohesive zone model

The analysis of constraint effects in fatigue crack growth in multi-layer structures is discussed. The process of material separation under cyclic loading is described by a cohesive zone model (CZM) with an irreversible constitutive relationship. The traction–separation behavior does not follow a predefined path, but is dependent on the evolution of the damage dependent cohesive zone properties. A modified boundary layer model is used in simulations of fatigue crack growth along the centerline crack of the metal layer sandwiched between two elastic substrates. Fatigue crack growth is computed for a series of values of metal layer thickness under constant and variable amplitude loading conditions. The results of the computations demonstrate that certain combinations of load magnitude, layer thickness and material properties results in significant constrain effects in fatigue crack growth. The influence of these constraint effects on fatigue crack growth rates and on crack closure processes is determined. The evolutions of the traction–separation law, the accumulated and current plastic zones, as well as the stress fields during the crack propagation are discussed.