A notch strain calculation of a notched specimen under axial-torsion loadings

In this paper, a notch analysis model is presented for the numerical prediction of multiaxial strains of a notched 1070 steel specimen under combined axial and torsion loadings. The proposed model is based on the notion of a structural yield surface and uses a small-strain cyclic plasticity model to describe stress–strain relations. A notch load–strain curve is calculated with Neuber’s rule and incremental nonlinear finite element analysis. The presented model is applied to simulate the notch root deformations of a circumferentially notched specimen under cyclic tension–compression–torsion loading histories. The model predictions are evaluated with strain measurements at the notch root of the specimen in a comprehensive set of cyclic tests. The computed strain loops were in accord with experimental data and matched qualitatively with measured shear–axial strain histories irrespective of loading path of the test. In proportional balanced torsion-axial loading, the nonlinear shear strain–axial strain loops were calculated properly. The modeling errors were determined to be a function of the loading path shape, and compared to shear strains, axial strain predictions were more accurate.     

Low‐cycle fatigue/high‐cycle fatigue interactions in notched Ti‐6Al‐4V*

Combined low‐cycle fatigue/high‐cycle fatigue (LCF/HCF) loadings were investigated for smooth and circumferentially V‐notched cylindrical Ti–6Al–4V fatigue specimens. Smooth specimens were first cycled under LCF loading conditions for a fraction of the previously established fatigue life. The HCF 10⁷ cycle fatigue limit stress after LCF cycling was established using a step loading technique. Specimens with two notch sizes, both having elastic stress concentration factors of K_t = 2.7, were cycled under LCF loading conditions at a nominal stress ratio of R = 0.1. The subsequent 10⁶ cycle HCF fatigue limit stress at both R = 0.1 and 0.8 was determined. The combined loading LCF/HCF fatigue limit stresses for all specimens were compared to the baseline HCF fatigue limit stresses. After LCF cycling and prior to HCF cycling, the notched specimens were heat tinted, and final fracture surfaces examined for cracks formed during the initial LCF loading. Fatigue test results indicate that the LCF loading, applied for 75% of total LCF life for the smooth specimens and 25% for the notched specimens, resulted in only small reductions in the subsequent HCF fatigue limit stress. Under certain loading conditions, plasticity‐induced stress redistribution at the notch root during LCF cycling appears responsible for an observed increase in HCF fatigue limit stress, in terms of net section stress.     

Multi-axial fatigue behaviour of a severely notched carbon steel

The paper deals with multi-axial fatigue strength of notched specimens made of C40 carbon steel (normalised state), subjected to combined tension and torsion loading, both in-phase and out-of-phase (Φ=0 and 90°). V-notched specimens have been tested under two nominal load ratios, R=−1 and 0, while keeping constant and equal to the unity the biaxiality ratio, λ=σ_a/τ_a. All specimens have the same geometry, with notch tip radius and depth equal to 0.5 and 4 mm, respectively, while the V-notch angle is equal to 90°. The results determined are discussed together with those deduced under pure tension or torsion loading on plain and notched specimens as well as on small shafts with shoulders. The application of an energy-based approach allows all the fatigue data obtained from the notched specimens to be summarised in a single scatter band, in terms of the total strain energy density evaluated at the notch tip against cycles to failure.     

Notch fatigue life prediction considering nonproportionality of local loading path under multiaxial cyclic loading

An innovative numerical methodology is presented for fatigue lifetime estimation of notched bodies experiencing multiaxial cyclic loadings. In the presented methodology, an evaluation approach of the local nonproportionality factor F for notched specimens, which defines F as the ratio of the pseudoshear strain range at 45° to the maximum shear plane and the maximum shear strain range, is proposed and discussed deeply. The proposed evaluation method is incorporated into the material cyclic stress‐strain equation for purpose of describing the nonproportional hardening behavior for some material. The comparison between multiaxial elastic‐plastic finite element analysis (FEA) and experimentally measured strains for S460N steel notched specimens shows that the proposed nonproportionality factor estimation method is effective. Subsequently, the notch stresses and strains calculated utilizing multiaxial elastic‐plastic FEA are used as input data to the critical plane‐based fatigue life prediction methodology. The prediction results are satisfactory for the 7050‐T7451 aluminum alloy and GH4169 superalloy notched specimens under multiaxial cyclic loading.     

Multiaxial fatigue of V‐notched steel specimens: a non‐conventional application of the local energy method

The paper deals with the multi‐axial fatigue strength of notched specimens made of 39NiCrMo3 hardened and tempered steel. Circumferentially V‐notched specimens were subjected to combined tension and torsion loading, both in‐phase and out‐of‐phase, under two nominal load ratios, R=?1 and R= 0, also taking into account the influence of the biaxiality ratio, λ=τ_a/σ_a. The notch geometry of all axi‐symmetric specimens was a notch tip radius of 0.1 mm, a notch depth of 4 mm, an included V‐notch angle of 90° and a net section diameter of 12 mm. The results from multi‐axial tests are discussed together with those obtained under pure tension and pure torsion loading on plain and notched specimens. Furthermore the fracture surfaces are examined and the size of non‐propagating cracks measured from some run‐out specimens at 5 million cycles. Finally, all results are presented in terms of the local strain energy density averaged in a given control volume close to the V‐notch tip. The control volume is found to be dependent on the loading mode.     

Fatigue life estimation of notched specimens of modified 9Cr-1Mo steel under uniaxial cyclic loading

Accuracy in the estimation of low cycle fatigue life of modified 9Cr-1Mo steel notched specimen by different analytical methods such as linear rule, Neuber’s rule, strain energy density method and numerical method such as finite element analysis have been studied in this investigation. The fatigue tests on notched specimens having notch radius of 1.25 mm, 2.5 mm and 5.0 mm were carried out at 823 K with net stress amplitudes of 250 MPa, 300 MPa and 350 MPa. The fatigue tests on smooth specimens were carried out with strain amplitudes ranging from ±0.3% to ±0.8% with a strain rate of 3 × 10^?3 s^?1 at 823 K to evaluate the fatigue life of notched specimen through strain-life approach. In order to predict the cyclic stress response of the material, Chaboche non-linear hardening model was employed considering two back stress components. Predicted hysteresis loops for smooth specimen were well in agreement with experimental results. Estimated fatigue lives of notched specimens by analytical methods and finite element analysis were within a factor ±16 and ±2.5 of the experimental lives respectively.     

Analysis on the fatigue damage evolution of notched specimens with consideration of cyclic plasticity

This paper presents a damage mechanics method applied successfully to assess fatigue life of notched specimens with plastic deformation at the notch tip. A damage‐coupled elasto‐plastic constitutive model is employed in which nonlinear kinematic hardening is considered. The accumulated damage is described by a stress‐based damage model and a plastic strain‐based damage model, which depend on the cyclic stress and accumulated plastic strain, respectively. A three‐dimensional finite element implementation of these models is developed to predict the crack initiation life of notched specimens. Two cases, a notched plate under tension‐compression loadings and an SAE notched shaft under bending‐torsion loadings including non‐proportional loadings, are studied and the predicted results are compared with experimental data.     

NOTCHED FATIGUE BEHAVIOUR OF TWO COLD ROLLED STEELS

Abstract— A SAE1010 plain carbon steel and a SAE945X HSLA steel were cold rolled to various thickness reductions. Centre notched specimens were tested under stress control at a stress ratio of—1. The effect of loading direction on the fatigue strength was examined. The notched specimen fatigue strength was only slightly increased by cold rolling, since two opposing factors: the smooth specimen fatigue strength and the notch sensitivity, were increased by cold rolling. The notched specimen fatigue strength in the transverse direction was approximately the same as that in the longitudinal direction. An empirical equation and equations derived from fracture mechanics and Neuber's rule were applied to predict the fatigue notch factor for the sharp and blunt notch geometries examined. A reasonable agreement between the predictions and the experimental results was observed for the sharp notches. For the blunt notches, the predicted fatigue notch factors were conservative.     

FATIGUE STRENGTH OF A ROTOR STEEL SUBJECTED TO TORSIONAL LOADING SIMULATING THAT OCCURRING DUE TO CIRCUIT BREAKER RECLOSING IN AN ELECTRIC POWER PLANT

Abstract— The fatigue strength of notched specimens of a rotor steel was examined under variable torsional loading which simulates turbine-generator oscillations resulting from the high speed reclosing of transmission-line circuit breakers. The local stress-strain response at a notch root was analysed using Neuber's rule and the resulting complex strain sequences applied to smooth specimens. Using the rain flow analysis and the linear summation rule, fatigue lives of the smooth specimens were successfully predicted from constant amplitude fatigue life data in association with the cyclic stress-strain curve obtained by the incremental step method. Experimental crack initiation lives for notched specimens subjected to variable torsional loading were in excellent agreement with the theoretical curves derived from results on smooth specimens. According to the view that fatigue damage is equated to crack length, the propagation life of a mode II crack along the notch root was predicted to be actually coincident with the life to crack initiation at the notch root denned in this study, i.e. the life at the stage of finding a continuous circumferential crack.     

Low cycle fatigue life of Ti–6Al–4V alloy under non-proportional loading

Multiaxial low cycle fatigue life of Ti–6Al–4V under non-proportional loading was studied. Strain-controlled multiaxial fatigue tests at room temperature were carried out using tubular specimens. The strain paths employed were push–pull loading, reversed torsion loading, and two kinds of 90° out-of-phase loadings. The former two loadings are proportional loading tests where the principal directions of stress and strain are fixed in the cycle. The latter two are non-proportional loading tests where there is a 90° phase difference between axial and shear loadings, and the principal directions are cyclically rotated continuously. Failure lives are reduced obviously by non-proportional loadings in comparison with those in proportional loading tests. This paper focuses on determining a suitable fatigue model for evaluating the failure lives of Ti–6Al–4V under multiaxial loading.     

Prediction of fatigue lifetime under multiaxial cyclic loading using finite element analysis

Life prediction for GH4169 superalloy thin tubular and notched specimens were investigated under proportional and nonproportional loading with elastic–plastic finite element analysis (FEA). A strain-controlled tension–torsion loading was carried out by applying the axial and circular displacements on one end of the specimen in the cylindrical coordinate system. Uniaxial cyclic stress–strain data at high temperature were used to describe the multi-linear kinematic hardening of the material. The comparison between FEA and experimental results for thin tubular specimen showed that the built model of FE is reliable. A fatigue damage parameter was proposed to predict the fatigue crack initiation life for notched specimen. The results showed that a good agreement was achieved with experimental data.     

Fatigue strength of notched specimens made of 40CrMoV13.9 under multiaxial loading

The work deals with multiaxial fatigue strength of notched round bars made of 40CrMoV13.9 steel and tested under combined tension and torsion loading, both in-phase and out-of-phase. The axis-symmetric V-notches present a constant notch root radius, 1 mm, and a notch opening angle of 90°; the notch root radius is equal to 4 mm in the semi-circular notches where the strength in the high cycle fatigue regime is usually controlled by the theoretical stress concentration factor, being the notch root radius large enough to result in a notch sensitivity index equals to unity. In both geometries the diameter of the net transverse area is 12 mm.The results from multi-axial tests are discussed together with those obtained under pure tension and pure torsion loading from notched specimens with the same geometry. Altogether more than 120 new fatigue data are summarised in the present work, corresponding to a one-year of testing programme.All fatigue data are presented first in terms of nominal stress amplitudes referred to the net area and then re-analysed in terms of the mean value of the strain energy density evaluated over a given, crescent shape volume embracing the stress concentration region. For the specific steel, the radius of the control volume is found to be independent of the loading mode.     

A Coupled Armstrong-Frederick Type Plasticity Correction Methodology for Calculating Multiaxial Notch Stresses and Strains

Based on the pseudo-strain method, a computational modeling technique coupling with Armstrong-Frederick type nonlinear kinematic hardening rule (Jiang-Sehitoglu model) is developed to calculate the multiaxial stress-strain responses of notched components. The pseudo-strain-true notch stress curve is determined using Neuber’s rule. The material constants in Jiang-Sehitoglu model are calculated using the Ramberg-Osgood curve. The presented method is applied to simulate the notch-tip deformations of circumferentially notched 1070 steel and S460N steel shafts subjected to various loadings, including box, circle, V-shape, zigzag-shape, and butterfly-shape loading paths. The calculated strain loops are in accord with experimental data and show reasonable accuracy.     

非比例载荷下缺口件疲劳寿命预测

针对Mod.9Cr-1Mo铁素体钢缺口件进行了一系列非比例载荷低周疲劳试验,采用直流电位差法测量裂纹萌生寿命,比较了缺口半径和应变路径对疲劳裂纹萌生寿命的影响。结果表明,缺口件裂纹萌生寿命占总寿命的比例与材料类型、应变路径相关,更与缺口半径尺寸直接相关。同一路径下,随着缺口半径增加,裂纹萌生寿命所占比例增大。采用Neuber律进行缺口局部应力-应变损伤的计算,结合Smith-Watson-Topper (SWT)模型和Kandil-Brown-Miller (KBM)模型进行疲劳寿命预测。结果表明,除单轴路径和比例路径外,SWT模型得到的预测结果偏于不安全;KBM模型除对单轴预测偏于保守外,其他预测值较好,总体预测结果位于2倍分散带内。     

Notch effect on creep–fatigue life for Sn–3.5Ag solder

This paper studies the creep–fatigue crack initiation and failure lives of Sn–3.5Ag solder notched specimens focused on the multiaxial strain at the notch root. Push–pull creep–fatigue tests were performed using three circumferential notched specimens using four kinds of creep–fatigue strain waveforms. Multiaxial strains at the notched section were calculated by finite element (FE) analysis under four kinds of creep–fatigue loading. Creep–fatigue damage laws were applied for evaluating the crack initiation and failure lives using the multiaxial strains obtained by the FE analysis. von Mises equivalent strain at the notch root estimated the crack initiation lives with a large scatter as well as the failure lives. Instead, the mean value of von Mises equivalent strain over the cross section of the notch root estimated the crack initiation and failure lives with a small scatter.     

Vergleichende Untersuchungen zur Anrisslebensdauervorhersage gekerbter Proben mit dem Örtlichen Konzept und dem Nennspannungskonzept am Beispiel des Stahls Cm15

Comparative Investigations on Service Life Assessment of Notched Specimens Based on the Local Strain and the Nominal Stress Approach to Fatigue for a Steel SAE 1017 It is still unclear whether the strain based approach to fatigue or the stress based approach to fatigue should be preferred for service life assessment of notched components. In order to clarify the similarities and differences between these concepts stress and strain controlled fatigue experiments have been performed with notched specimens. It has been found, that stress and strain controlled fatigue testing results in the same number of cycles until failure. Essential for this correlation is that the cyclic stable strain amplitude at the notch root is taken for the entry into the strain‐life diagram in both cases. Starting from an elastic‐plastic analysis of the material behaviour at the notch root it is shown, how the strain‐life curve can be converted into a stress‐life curve. Based on that result service‐life is calculated from both approaches mentioned above. The calculation gives nearly the same service‐lives for both cases, but overestimates the measured data. It becomes obvious, that a S‐N curve determined under one‐level loading doesn’t provide a proper basis for service life assessment. While strain or stress‐life curves always contain crack initiation phase as well as crack propagation phase, the fatigue process under irregular loads is mainly governed by crack propagation. As a consequence, the damage per cycle is underestimated for loads near the fatigue limit, if Miner’s rule is used.     

Energy approach to fatigue under combined cyclic bending with torsion of smooth and notched specimens

We present the results of fatigue tests of smooth and notched round specimens made of 10HNAP steel under the combined action of cyclic bending and torsion. The experimental results are analyzed by using the well-known energy models proposed by Neuber and Molski-Glinka and a new model proposed by the authors and based on the analysis of the amplitude of the strain-energy density. The accumulation of fatigue damage in the stage of crack initiation was observed only in the active part of the cross section of the specimen where the level of stresses is higher than the fatigue limit. The proposed model enables one to determine the fatigue life of smooth and notched specimens under the combined action of cyclic bending and torsion by using standard characteristics of uniaxial fatigue and the relationship between cyclic stresses and strains. Department of Mechanics and Machine Design, Technical University of Opole, Opole, Poland. Published in Fizyko-Khimichna Mekhanika Materialiv, Vol. 34, No. 5, pp. 34–42, September–October, 1998.     

Local stress–strain field intensity approach to fatigue life prediction under random cyclic loading

According to the characteristic of the local behavior of fatigue damage, on the basis of stress field intensity approach, a theory of local stress–strain field intensity for fatigue damage at the notch is developed in this paper, which can take account of the effects of the local stress–strain gradient on fatigue damage at the notch. In order to calculate the local stress–strain field intensity parameters, an incremental elastic-plastic finite element analysis under random cyclic loading is used to determine the local stress–strain response. A local stress–strain field intensity approach to fatigue life prediction is proposed by means of elastic-plastic finite element method for notched specimens. This approach is used to predict fatigue crack initiation life, and good correlation was observed with U-shape notched specimens for normalized 45 steel.     

FAILURE MECHANISMS IN IMPACT FATIGUE OF METALS

Abstract Impact fatigue tests were performed with smooth and notched specimens of low carbon steels under various impact loading conditions. The characteristic failure mechanisms in impact fatigue was discriminated by comparison with those in non-impact, ordinary fatigue. The fatigue life of smooth specimens was uniquely related to the range of plastic strain at the middle of the fatigue life in both impact and non-impact fatigue, although the characteristics of micro-structural deformation and cyclic stress-strain relationships were markedly different. The growth rate of a fatigue crack in impact fatigue of notched specimens was higher than that in non-impact fatigue when compared at the same stress intensity factor. Fractographic observations with scanning electron microscopy and the X-ray diffraction technique revealed more abundant cleavage facets and a smaller spread of the plastic zone beneath the fracture surface made by impact fatigue. Both nucleation and propagation lives in notched specimens were much shorter in impact fatigue than in non impact fatigue when compared at the same values of nominal stress and stress concentration factor.