Kinetics and Microstructural Evolution of Heterogeneous Transformation of θ-Alumina to α-Alumina

Ultrafine (<0.1 μm) high-purity θ-Al₂O₃ powder containing 3–17.5 mol%α-Al₂O₃ seeds was used to investigate the kinetics and microstructural evolution of the θ-Al₂O₃ to α-Al₂O₃ transformation. The transformation and densification of the powder that occurred in sequence from 960° to 1100°C were characterized by quantitative X-ray diffractometry, dilatometry, mercury intrusion porosimetry, and transmission and scanning electron microscopy. The relative bulk density and the fraction of α phase increased with annealing temperature and holding time, but the crystal size of the α phase remained ∼50 nm in all cases at the transformation stage (≤1020°C). The activation energy and the time exponent of the θ to α transformation were 650 ± 50 kJ/mol and 1.5, respectively. The results implied the transformation occurred at the interface via structure rearrangement caused by the diffusion of oxygen ions in the Al₂O₃ lattice. A completely transformed α matrix of uniform porosity was the result of appropriate annealing processes (1020°C for 10 h) that considerably enhanced densification and reduced grain growth in the sintering stage. The Al₂O₃ sample sintered at 1490°C for 1 h had a density of 99.4% of the theoretical density and average grain size of 1.67 μm.     

Synthesis of Magnesium Aluminate Spinel Platelets from α-Alumina Platelet and Magnesium Sulfate Precursors

Spinel platelets were formed from a powder mixture of 3–5 μm wide and 0.2–0.5 μm thick α-Al₂O₃ and 1–8 μm (average 3 μm) MgSO₄ heated 2 h at 1200°C. The hexagonal platelet shape of the original α-Al₂O₃ platelet was maintained in the spinel, although their size was slightly increased and their surface roughened. When a mixture of α-Al₂O₃ platelets and MgO powder was heated 3 h at 1400°C, the spinel formed lost the platelet morphology of the alumina.     

Mg–Cu–Zn Ferrites for Multilayer Inductors

Mg–Cu–Zn ferrites can be sintered at T ≤950°C to sufficient density and display adequate permeability profiles for application in multilayer ferrite inductors. The permeability and Curie temperature have to be optimized by proper selection of composition. Ferrites with <50 mol% Fe₂O₃ reveal enhanced densification behavior. Submicrometer powders prepared by fine milling show good sintering activity and density after firing at 900°C. Nano-size ferrite powders prepared by coprecipitation or flame synthesis lead to high density; maximum shrinkage already occurs at T <800°C. The use of Bi₂O₃ as a sintering additive further improves the densification, but also affects the microstructure and, hence, the permeability. A maximum permeability of μ_i=450–500 is obtained.     

Influences of Particle Size of Alumina Filler in an LTCC System

A low temperature co-fired ceramics system consisting of a typical calcium aluminoborosilicate glass and alumina filler was used to investigate the effects of four different sizes, 13 nm, 0.5, 3, and 39 μm, of a commercially available alumina filler on the resultant densification, crystallization, and dielectric properties. There was definitely a proper range of alumina particle size, which leads to desirable densification and enhanced dielectric properties. The onset temperatures of densification and crystallization depended strongly on the filler particle size. The 3 μm sample as an optimum filler size exhibited a promising performance of k ∼8.1 and Q ∼160 at a resonant frequency of 14.8 GHz, which results from early densification and intensive crystallization of the anorthite CaAl₂Si₂O₈ phase. Particularly, the use of nano-sized alumina (13 nm) retarded both densification by ∼200°C and crystallization by ∼80°C compared with the results of the 3 μm alumina case. The dependence of the filler particle size was postulated as being related to the wetting and connectivity behavior of glass through consequent inter-reactions between glass and ceramic.     

Seeding of the Reaction-Bonded Aluminum Oxide Process

The effect of the initial α-Al₂O₃ particle size in the reaction-bonded aluminum oxide (RBAO) process on the phase transformation of aluminum-derived γ-Al₂O₃ to α-Al₂O₃, and subsequently densification, was investigated. It has been demonstrated that if the initial α-Al₂O₃ particles are fine (∼0.2 μm, i.e., 2.9 × 10¹⁴γ-Al₂O₃ particles/cm³), then they seed the phase transformation. The fine α-Al₂O₃ decreases the transformation temperature to ∼962°C and results in a finer microstructure. The smaller particle size of the seeded RBAO decreases the sintering temperature to as low as ∼1135°C. The results confirm that seeding can be utilized to improve phase transformations and densification and subsequently to tailor final microstructures in RBAO-derived ceramics.     

Rapid Sintering of Stoichiometric Zinc-Modified Lead Magnesium Niobate

A rapid thermal-processing technique was used to densify zinc-modified lead magnesium niobate (PMZN30) of the form Pb(Mg_0.7Zn_0.3)_1/3Nb_2/3O₃. This dielectric composition showed relaxor behavior with a maximum permittivity near room temperature. Rapid densification was observed at temperature. Rapid densification was observed at temperatures of 1100°C and above, whereas lower temperatures showed a significant reduction of densification and electrical properties. A sintering schedule of 4 min at 1100°C with no prevention of PbO volatilization resulted in densification on the order of 90% of theoretical density and a weak field dielectric constant in excess of 14 000. Perovskite grain size was consistently in the range of 1 μm or less. The formation of pyrochlore on sample surfaces showed a direct relation to time and temperature.     

Creep Deformation in an Alumina–Silicon Carbide Composite Produced via a Directed Metal Oxidation Process

Flexural creep studies were conducted in a commercially available alumina matrix composite reinforced with SiC particulates (SiC_p) and aluminum metal at temperatures from 1200° to 1300°C under selected stress levels in air. The alumina composite (5 to 10 μm alumina grain size) containing 48 vol% SiC particulates and 13 vol% aluminum alloy was fabricated via a directed metal oxidation process (DIMOX(tm))† and had an external 15 μm oxide coating. Creep results indicated that the DIMOX Al₂O₃–SiC_p composite exhibited creep rates that were comparable to alumina composites reinforced with 10 vol% (8 (μm grain size) and 50 vol% (1.5 μm grain size) SiC whiskers under the employed test conditions. The DIMOX Al₂O₃–SiC_p composite exhibited a stress exponent of 2 at 1200°C and a higher exponent value (2.6) at ≥ 1260°C, which is associated with the enhanced creep cavitation. The creep mechanism in the DIMOX alumina composite was attributed to grain boundary sliding accommodated by diffusional processes. Creep damage observed in the DIMOX Al₂O₃-SiC_p composite resulted from the cavitation at alumina two-grain facets and multiple-grain junctions where aluminum alloy was present.     

Low-Temperature Sintering of Seeded Sol—Gel-Derived, ZrO2-Toughened Al2O3 Composites

Seeding a mixture of boehmite (AIOOH) and colloidal ZrO₂ with α-alumina particles and sintering at 1400°C for 100 min results in 98% density. The low sintering temperature, relative to conventional powder processing, is a result of the small alumina particle size (∼0.3 μm) obtained during the θ-to α-alumina transformation, homogeneous mixing, and the uniform structure of the sol-gel system. Complete retention of pure ZrO₂ in the tetragonal phase was obtained to 14 vol% ZTA because of the low-temperature sintering. The critical grain size for tetragonal ZrO₂ was determined to be ∼0.4 μm for the 14 vol% ZrO₂—Al₂O₃ composite. From these results it is proposed that seeded boehmite gels offer significant advantages for process control and alumina matrix composite fabrication.     

Sintering of Zinc Oxide Doped with Antimony Oxide and Bismuth Oxide

The phase change, densification, and microstructure development of ZnO doped with both Bi₂O₃ and Sb₂O₃ are studied to better understand the sintering behavior of ZnO varistors. The densification behavior is related to the formation of pyrochlore and liquid phases; the densification is retarded by the former and promoted by the latter. The pyrochlore phase, whose composition is Bi_3/2ZnSb_3/2O₇, appears below 700°C. The formation temperature of the liquid phase depends on the Sb/Bi ratio: about 750°C for Sb/Bi < 1 by the eutectic melting in the system ZnO—Bi₂O₃, and about 1000°C for Sb/Bi > 1 by the reaction of the pyrochlore phase with ZnO. Hence, the densification rate is determined virtually by the Sb/Bi ratio and not by the total amount of additives. The microstructure depends on the sintering temperature. Sintering at 1000°C forms intragrain pyrochlore particles in ZnO grains as well as intergranular layers, but the intragrain particles disappear at 1200°C by the increased amount of liquid phase, which enhances the mobility of the solid second phase.     

Suppression of Rhombohedral-Phase Appearance and Low-Temperature Sintering of Scandia-Doped Cubic-Zirconia

Inhibition of cubic-rhombohedral phase transformation and low-temperature sintering at 1000°C were achieved for 10-mol%-Sc₂O₃-doped cubic-ZrO₂ by the presence of 1 mol% Bi₂O₃. The powders of 1-mol%-Bi₂O₃–10-mol%-Sc₂O₃-doped ZrO₂ were prepared using a hydrolysis and homogeneous precipitation technique. No trace of rhombohedral-ZrO₂ phase could be detected, even after sintering at 1000°–1400°C. The average grain size of the ZrO₂ sintered at 1200°C was >2 μm because of grain growth in the presence of Bi³⁺. Cubic, stabilized Bi-Sc-doped ZrO₂ sintered at 1200°C had sufficient conductivity at 1000°C (0.33 S/cm) to be used as an electrolyte for a solid-oxide fuel cell (SOFC) and at 800°C (0.12 S/cm) for an intermediate-temperature SOFC.     

Densification of Nanocrystalline Yttria by Low Temperature Spark Plasma Sintering

We investigated the densification of undoped, nanocrystalline yttria (Y₂O₃) powder by spark plasma sintering (SPS) at sintering temperatures between 650°C and 1050°C at a heating rate of 10°C/min and an applied stress of 83 MPa. In spite of the low sinterability of the undoped Y₂O₃, a remarkable densification of the powder started at about 600°C, and a theoretical density of more than 97% was achieved at a sintering temperature of 850°C with a grain size of about 500 nm. The low temperature SPS is effective for fabricating dense Y₂O₃ polycrystals.     

Mechanical-Activation-Triggered Gibbsite-to-Boehmite Transition and Activation-Derived Alumina Powders

Mechanical activation of monoclinic gibbsite (Al(OH)₃) in nitrogen led to the formation of nanocrystalline orthorhombic boehmite (AlOOH) at room temperature. The boehmite phase formed after merely 3 h of mechanical activation and developed steadily as the mechanical-activation time increased. Forty hours of mechanical activation resulted in essentially single-phase boehmite, together with α-alumina (α-Al₂O₃) nanocrystallites 2–3 nm in size. The sequence of phase transitions in the activation-derived boehmite was as follows: boehmite to γ-Al₂O₃ and then to α-Al₂O₃ when flash-calcined at a heating rate of 10°C/min in air. γ-Al₂O₃ formed at 520°C, and flash calcination to 1100°C led to the formation of an α-Al₂O₃ phase, which exhibited a refined particle size in the range of 100–200 nm. In contrast, the gibbsite-to-boehmite transition in the unactivated gibbsite occurred over the temperature range of 220°–330°C. A flash-calcination temperature of 1400°C was required to complete the conversion to α-Al₂O₃ phase, with both δ-Al₂O₃ and θ-Al₂O₃ as the transitional phases. The resulting alumina powder consisted of irregularly shaped particles 0.4–0.8 μm in size, together with an extensive degree of particle agglomeration.     

Sintering of Si3N4 with the Addition of Rare-Earth Oxides

The effect of rare-earth oxide additives on the densification of silicon nitride by pressureless sintering at 1600° to 1700°C and by gas pressure sintering under 10 MPa of N₂ at 1800° to 2000°C was studied. When a single-component oxide, such as CeO₂, Nd₂O₃, La₂O₃, Sm₂O₃, or Y₂O₃, was used as an additive, the sintering temperature required to reach approximate theoretical density became higher as the melting temperature of the oxide increased. When a mixed oxide additive, such as Y₂O₃–Ln₂O₃ (Ln=Ce, Nd, La, Sm), was used, higher densification was achieved below 2000°C because of a lower liquid formation temperature. The sinterability of silicon nitride ceramics with the addition of rare-earth oxides is discussed in relation to the additive compositions.     

Transformation, Microstructure Development, and Densification in α-Fe2O3-Seeded Boehmite-Derived Alumina

Addition of α-Fe₂O₃ seed particles to alkoxide-derived boehmite sols resulted in a 10-fold increase in isothermal rate constants for the transformation of γ- to α-Al₂O₃. Changes in porosity and surface area with sintering temperature showed no effect of seeding on coarsening of the transition alumina gels, but the 200-fold decrease in surface area associated with transformation to α-Al₂O₃ occurred ∼ 100°C lower in seeded gels compared with unseeded materials. As a result of high nucleation frequency and reduced microstructure coarsening, fully transformed seeded alumina retained specific surface areas >22 m²/g and exhibited narrow pore size distributions, permitting development of fully dense, submicrometer α-Al₂O₃ at ∼ 1200°C.     

Seeding with γ-Alumina for Transformation and Microstructure Control in Boehmite-Derived α-Alumina

The dehydration, transformation, and densification of boehmite (γ-AlOOH) are enhanced by addition of γ-Al₂O₃ seed particles. α-Al₂O₃ microstructures with uniform 1- to 2-μm grain size and sintered densities 98% of theoretical are achieved at 1300°C Thermal analysis shows that γ-Al₂O₃ seed particles transform to α-Al₂O₃ before the matrix, thus controllably nucleating the transformation of θ-AI₂O₃ to α-Al₂O₃.     

Mechanism of Alumina-Enhanced Sintering of Fine Zirconia Powder: Influence of Alumina Concentration on the Initial Stage Sintering

The isothermal shrinkage behavior of 2.9 mol% Y₂O₃-doped ZrO₂ powders with 0–1 mass% Al₂O₃ was investigated to clarify the effect of Al₂O₃ concentration on the initial sintering stage. The shrinkage of the powder compact was measured at constant temperatures in the range of 950°–1050°C. The Al₂O₃ addition increased the densification rate with increasing temperature. The values of apparent activation energy ( nQ ) and apparent frequency-factor term (β₀ ⁿ ), where n is the order depending on the diffusion mechanism, were estimated at the initial sintering stage by applying a sintering-rate equation to the isothermal shrinkage data. The diffusion mechanism changed from grain-boundary diffusion (GBD) to volume diffusion (VD) by Al₂O₃ addition and both nQ and β₀ ⁿ increased with increasing Al₂O₃ concentration. The kinetic analysis of the sintering mechanism suggested that the increase of densification rate by Al₂O₃ addition largely depends on the increase of β₀ ⁿ , that is, the increases of n with GBD→VD change and β₀ with an increase in Al₂O₃ content, although the nQ also increases with Al₂O₃ addition. This enhanced sintering mechanism is reasonably interpreted by the segregated dissolution of Al₂O₃ at ZrO₂ grain boundaries.     

Enhancement of Densification and Thermal Conductivity in AlN Ceramics by Addition of Nano-Sized Particles

The effect of addition of nano-sized particles on densification and thermal conductivity of AlN ceramics was investigated. The commercially available AlN powder (∼0.9 μm) was mixed with 1.89 mass% nano-sized AlN particles (<0.1 μm), 3.53 mass% Y₂O₃, and 2.0 mass% CaO as sintering aid. The mixture was fired at 1500° and 1600°C in a tungsten resistance furnace under flowing N₂ atmosphere. The results showed that a fully densified specimen was obtained at the lower temperature of 1600°C by addition of nano-sized particles. The thermal conductivity of the resulting product was 133 W/m°C. The value is much higher than the 52 W/m°C for the sample prepared without adding the nano-sized AlN powder. This study indicates a strong potential for the use of nano-sized particles as additives in the densification of AlN ceramics.     

Influence of Yttria–Alumina Content on Sintering Behavior and Microstructure of Silicon Nitride Ceramics

The present study investigates the influence of the content of Y₂O₃–Al₂O₃ sintering additive on the sintering behavior and microstructure of Si₃N₄ ceramics. The Y₂O₃:Al₂O₃ ratio was fixed at 5:2, and sintering was conducted at temperatures of 1300°–1900°C. Increased sintering-additive content enhanced densification via particle rearrangement; however, phase transformation and grain growth were unaffected by additive content. After phase transformation was almost complete, a substantial decrease in density was identified, which resulted from the impingement of rodlike β-Si₃N₄ grain growth. Phase transformation and grain growth were concluded to occur through a solution–reprecipitation mechanism that was controlled by the interfacial reaction.     

Effect of Bi2O3 Addition on the Sintering Temperature and Microwave Dielectric Properties of Zn2SiO4 Ceramics

Bi₂O₃ was added to a nominal composition of Zn_1.8SiO_3.8 (ZS) ceramics to decrease their sintering temperature. When the Bi₂O₃ content was <8.0 mol%, a porous microstructure with Bi₄(SiO₄)₃ and SiO₂ second phases was developed in the specimen sintered at 885°C. However, when the Bi₂O₃ content exceeded 8.0 mol%, a liquid phase, which formed during sintering at temperatures below 900°C, assisted the densification of the ZS ceramics. Good microwave dielectric properties of Q × f =12,600 GHz, ɛ_r=7.6, and τ_f=−22 ppm/°C were obtained from the specimen with 8.0 mol% Bi₂O₃ sintered at 885°C for 2 h.     

Submicrometer Transparent Alumina by Sinter Forging Seeded γ-Al2O3 Powders

Seeding boehmite with α-Al₂O₂, followed by calcination at 600°C, results in an agglomerated alumina powder (<53 μm) that can be sinter forged to full density at 1250°C. Compressive strains as high as ɛ_x=−0.9, and radial flow (ɛ_x= 1.0) during sinter forging remove large, interagglomerate pores. The fully dense alumina has a grain size of 0.4 pm and is visually transparent. It is proposed that deformation of dense agglomerates is the primary mecha- nism responsible for large pore elimination and compact densification. The sinter forging of sol-gel-derived alumina powders offers a new technology to prepare highly transparent, optical ceramics at lower temperatures than conventional routes.