Electroconductive Al2O3–NbN Composites

Electroconductive Al₂O₃–NbN ceramic composites were prepared by hot pressing. Dense sintered bodies of ball-milled Al₂O₃–NbN composite powders were obtained at 1550°C and 30 MPa for 1 h under a nitrogen atmosphere. The bending strength and fracture toughness of the composites were enhanced by incorporating niobium nitride (NbN) particles into the Al₂O₃ matrix. The electrical resistivity of the composites decreased with increasing amount of NbN phase. For a 25 vol% NbN–Al₂O₃ composite, the values of bending strength, fracture toughness, Vickers hardness, and electrical resistivity were 444.2 MPa, 4.59 MPa·m^1/2, 16.62 GPa, and 1.72 × 10⁻²Ω·cm, respectively, making the composite suitable for electrical discharge machining.     

Preparation of Al2O3–AlN–Ni Composites

A method is proposed to prepare Al₂O₃-AlN-Ni composites. The composites are prepared by sintering Al₂O₃/NiAl powder mixtures at 1600°C in a mixture of nitrogen and carbon monoxide. The presence of NiAl particles raises the green density of Al₂O₃/NiAl powder compacts. During sintering, NiAl reacts with nitrogen to form AlN and Ni inclusions. A volume expansion accompanies the reaction. Because of the high green density and the reaction, the volume shrinkage of the Al₂O₃-AlN-Ni composite decreases with the increase of added NiAl content.     

Fabrication and Evaluation of Al2O3–AgCl–Agl Composites by Use of Electrochemical Deposition

Al₂O₃–AgCl–AgI composites were fabricated by an electrochemical deposition technique utilizing porous α–Al₂O₃ ceramics as a matrix. The growth process was presumed to be dominated by the diffusion rate of the Ag⁺ ion. The phases identified in the composites were α-Al₂O₃, AgCl, and β-AgI. The deposited AgCl and AgI showed enhanced conductivity compared with the reported bulk values. The deposited mixture exhibited enhanced conductivity compared with pressed polycrystalline AgCl or AgI. The enhancement was explained using a model that a deposit with a high conductivity grows much faster than that with a low conductivity.     

Sliding Wear of Al2O3–SiC–(Al,Si) Composites against a Steel Counterface

The sliding-wear behavior of Al₂O₃–SiC–Al composites prepared by melt oxidation against a steel counterface has been recorded in a pin-on-disk machine. At high speeds and pressures (10 m/s, 20 MPa), friction and wear appear to be principally controlled by the in-situ formation of an interfacial film that consists of a layer of Fe₃O₄. The formation of this film is examined as a function of sliding speed, lubrication, and composite microstructure. A model is proposed in which high surface temperatures cause the preferential extrusion of aluminum from the composite onto the pin/disk interface. This promotes the adhesive pickup of iron and its oxidation to form a stable tribologically beneficial layer of Fe₃O₄.     

Homogeneous Fabrication of Al2O3–ZrO2–SiC Whisker Composite by Surface-Induced Coating

Al₂O₃–ZrO₂–SiC whisker composites were prepared by surface-induced coating of the precursor for the ZrO₂ phase on the kinetically stable colloid particles of Al₂O₃ and SiC whisker. The fabricated composites were characterized by a uniform spatial distribution of ZrO₂ and SiC whisker phases throughout the Al₂O₃ matrix. The fracture toughness values of the Al₂O₃–15 vol% ZrO₂–20 vol% SiC whisker composites (∼12 MPa.m^1/2) are substantially greater than those of comparable Al₂O₃–SiC whisker composites, indicating that both the toughening resulting from the process zone mechanism and that caused by the reinforced SiC whiskers work simultaneously in hot-pressed composites.     

Properties of (Y)ZrO2–Al2O3 and (Y)ZrO2–Al2O3–(Ti or Si)C Composites

The effect of Al₂O₃ and (Ti or Si)C additions on various properties of a (Y)TZP (yttria-stabilized tetragonal zirconia polycrystal)–Al₂O₃–(Ti or Si)C ternary composite ceramic were investigated for developing a zirconia-based ceramic stronger than SiC at high temperatures. Adding Al₂O₃ to (Y)TZP improved transverse rupture strength and hardness but decreased fracture toughness. This binary composite ceramic revealed a rapid loss of strength with increasing temperature. Adding TiC to the binary ceramic suppressed the decrease in strength at temperatures above 1573 K. The residual tensile stress induced by the differential thermal expansion between ZrO₂ and TiC therefore must have inhibited the t - → m -ZrO₂ martensitic transformation. It was concluded that a continuous skeleton of TiC prevented grain-boundary sliding between ZrO₂ and Al₂O₃. In contrast, for the ternary material containing β-SiC in place of TiC, the strength decreased substantially with increasing temperature because of incomplete formation of the SiC skeleton.     

Al2O3–Ni Composites with High Strength and Fracture Toughness

Al₂O₃–Ni composites were prepared by the reactive hot pressing of Al and NiO. The composites had a two-phase, interpenetrating microstructure and contained ∼35 vol% Ni. They exhibited an impressively high combination of strength and toughness at room temperature; the four-point bending strength was in excess of 600 MPa with a fracture toughness of more than 12 MPa·m^1/2. Examination of fracture surfaces showed that Ni ligaments underwent ductile deformation during fracture. SEM analysis revealed knife-edged Ni ligaments with a limited amount of debonding around their periphery (i.e., at the Ni–Al₂O₃ interface), indicating a strong Ni–Al₂O₃ bond.     

Homogeneous ZrO2–Al2O3 Composite Prepared by Nano-ZrO2 Particle Multilayer-Coated Al2O3 Particles

ZrO₂–Al₂O₃ nanocomposite particles were synthesized by coating nano-ZrO₂ particles on the surface of Al₂O₃ particles via the layer-by-layer (LBL) method. Polyacrylic acid (PAA) adsorption successfully modified the Al₂O₃ surface charge. Multilayer coating was successfully implemented, which was characterized by ξ potential, particle size. X-ray diffraction patterns showed that the content of ZrO₂ in the final powders could be well controlled by the LBL method. The powders coated with three layers of nano-ZrO₂ particles, which contained about 12 wt% ZrO₂, were compacted by dry press and cold isostatically pressed methods. After sintering the compact at 1450°C for 2 h under atmosphere, a sintered body with a low pore microstructure was obtained. Scanning electron microscopy micrographs of the sintered body indicated that ZrO₂ was well dispersed in the Al₂O₃ matrix.     

Mechanical Properties and Oxidation Behavior of Al2O3–AlN–TiN Composites

The study examines the effect which the composition of hot-pressed electroconductive ceramics has on their structure, mechanical properties, and oxidation behavior, for ceramics of the type AIN–Al₂O₃–42 wt% TiN, differing in the AIN/Al₂O₃ ratio. The results are physico-mechanical property data, including density, hardness, strength, fracture toughness, and wear resistance. A correlation was found between the wear resistance and fracture toughness. The analysis of oxidation products revealed the formation of α-Al₂O₃ and rutile in the temperature range from 600° to 1100°C and aluminum titanate above 1200°C. The spallation of the oxide layer caused low oxidation resistance of Al₂O₃-rich composites above 1250°C. The oxidation of composites was compared with the oxidation of pure TiN. The relationship is discussed between material properties, composition, phases, and processing parameters.     

Phase Relations in the System Al2O3–B2O3–Nd2O3

The phase relations at a temperature below "subsolidus" in the system Al₂O₃–B₂O₃–Nd₂O₃ are reported. Specimens were prepared from various compositions of Al₂O₃, B₂O₃, and Nd₂O₃ of purity 99.5%, 99.99%, and 99.9%, respectively, and fired at 1100°C. There are six binary compounds and one ternary compound in this system. The ternary compound, NdAl₃(BO₃)₄ (NAB), has a phase transition at 950°C ± 15°C. The high-temperature form of NAB has a second harmonic generation (SHG) efficiency of KH₂PO₄ (KDP) of the order of magnitude of the form which has been used as a good self-activated laser material, and the low-temperature form of NAB has no SHG efficiency.     

Influence of the Characteristics of Spinels on the Slag Resistance of Al2O3–MgO and Al2O3–Spinel Castables

The XRD patterns at ambient temperature and at 1500°C showed that the spinel in the Al₂O₃–MgO castables fired at 1500°C for 3 h has the higher peak intensity, compared to those in Al₂O₃–spinel castables; the interplanar distance in the set (311) is 2.43 Å for the spinel in Al₂O₃–MgO castables as well as the spinels in Al₂O₃–spinel castables using spinels containing 73, 90, and 94 wt% Al₂O₃, respectively. The corresponding alumina contents of the spinels in these castables were estimated to be around 75 wt%. The smaller grain size of the spinel in Al₂O₃–MgO castables compared to that in Al₂O₃–spinel castables is evidenced by the recrystallization of the in situ spinel only occurring in Al₂O₃–MgO castables as revealed by the XRD patterns at ambient temperature and at 1500°C. The larger amount and smaller grain size of the in situ spinel in the matrix mostly account for the better slag resistance of Al₂O₃–MgO castables, compared to Al₂O₃–spinel castables.     

Microstructure Development in Al2O3-Platelet-Reinforced Ce-ZrO2/Al2O3 Composites

Composites containing Ce-ZrO₂, Al₂O₃, and aligned Al₂O₃ platelets were produced by centrifugal consolidation and pressureless sintering, followed by heat treatments at 1600°C for varied duration. Constituents in the consolidated microstructures were either uniformly distributed throughout or segregated into gradient layers, depending critically on platelet content. Quantitative image analysis was used to examine microstructure development with heat treatment. Changes in the volume fraction, dimensional anisotropy, and gradient of pores and platelets, as well as changes in the phase gradient, were quantified. Microstructure development was strongly dependent on the initial microstructure design attained from suspension processing.     

Structure Formation in the Combustion Synthesis of Al2O3–TiC Composites

Structure formation in the combustion synthesis of Al₂O₃–TiC composites from TiO₂, Al, and graphite powders was investigated using cylindrical samples and cone-shaped "quenching samples." It is shown that the phases Ti and Ti₃Al exist as intermediates in the combustion synthesis process. Titanium carbide forms in a secondary step through reactions between graphite and liquid Ti or Ti₃Al, then nucleates from a liquid mixture of the three phases Ti, Ti₃Al, and alumina. The nucleated particles grow in the postcombustion stage. Liquid alumina, containing TiC as a dissolved phase, solidifies into corundum grains in the postcombustion stage. Moreover, it is shown that the temperature gradient in the postcombustion stage markedly affects the microstructures of the products. Higher-temperature gradients, typical at the surface of the samples, give rise to the formation of corundum whiskers and TiC agglomerates. In contrast, lower gradients, typical in the center of the samples, lead to the formation of relatively large TiC particles and corundum grains.     

Tensile Ductility of Superplastic Al2O3–Y2O3–Si3N4/SiC Composites

Si₃N₄/SiC composites are ceramic materials that exhibit excellent performance for high-temperature applications. Prepared from an ultrafine amorphous Si-C-N powder, sintered materials are constituted mainly of a β -Si₃N₄ matrix with SiC inclusions and have a very small grain size (less than 1 μm). Such a microstructure is propitious for superplastic forming. Superplasticity has been studied in tension, from 1550° to 1650°C, under nitrogen atmosphere. Elongations over 100% have been achieved. In many cases, at the highest temperatures and slowest strain rates, materials are damaged by different processes, including microcracking, cavitation, and chemical decomposition. A map of the most suitable (strain-rate/temperature) domain has been established. It allows the prevention of any structural alteration by selecting carefully the testing conditions. Since specimens suffered considerable strain-induced hardening, sources for this phenomenon are examined. Although the experiments have involved high temperature and extensive strain, neither static nor dynamic grain growth has occurred. Crystallization of the amorphous grain-boundary phase, which is reported in most cases, may be invoked. However, based on microstructural observations, it is not the unique origin for flow hardening.     

Subsolidus Phase Relationships in the Ga2O3–Al2O3–TiO2 System

Subsolidus phase relationships in the Ga₂O₃–Al₂O₃–TiO₂ system at 1400°C were studied using X-ray diffraction. Phases present in the pseudoternary system include TiO₂ (rutile), Ga_{2−2 x} Al_{2 x} O₃ ( x ≤0.78 β-gallia structure), Al_{2−2 y} Ga_{2 y} O₃ ( y ≤0.12 corundum structure), Ga_{2−2 x} Al_{2 x} TiO₅ (0≤ x ≤1 pseudobrookite structure), and several β-gallia rutile intergrowths that can be expressed as Ga_{4−4 x} Al_{4 x} Ti _{n −4}O_{2 n −2} ( x ≤0.3, 15≤ n ≤33). This study showed no evidence to confirm that aluminum substitution of gallium stabilizes the n =7 β-gallia–rutile intergrowth as has been mentioned in previous work.     

Sintering and Crystallization of CaO–Al2O3–ZrO2–SiO2 Glasses Containing Different Amount of Al2O3

In this work several complementary techniques have been employed to carefully characterize the sintering and crystallization behavior of CaO–Al₂O₃–ZrO₂–SiO₂ glass powder compacts after different heat treatments. The research started from a new base glass 33.69 CaO–1.00 Al₂O₃–7.68 ZrO₂–55.43SiO₂ (mol%) to which 5 and 10 mol% Al₂O₃ were added. The glasses with higher amounts of alumina sintered at higher temperatures (953°C [lower amount] vs. 987°C [higher amount]). A combination of the linear shrinkage and viscosity data allowed to easily find the viscosity values corresponding to the beginning and the end of the sintering process. Anorthite and wollastonite crystals formed in the sintered samples, especially at lower temperatures. At higher temperatures, a new crystalline phase containing ZrO₂ (2CaO·4SiO₂·ZrO₂) appeared in all studied specimens.     

Effect of Alkali Metal Oxide Addition on the Sinterability of MgO–B2O3–Al2O3 Glass–Al2O3 Filler Composites

The sintering of a composite of MgO–B₂O₃–Al₂O₃ glass and Al₂O₃ filler is terminated due to the crystallization of Al₄B₂O₉ in the glass. The densification of a composite of MgO–B₂O₃–Al₂O₃ glass and Al₂O₃ filler using pressureless sintering was accomplished by lowering the sintering temperature of the composite. The sintering temperature was lowered by the addition of small amounts of alkali metal oxides to the MgO–B₂O₃–Al₂O₃ glass system. The resultant composite has a four-point bending strength of 280 MPa, a coefficient of thermal expansion (RT—200°C) of 4.4 × 10⁻⁶ K⁻¹, a dielectric constant of 6.0 at 1 MHz, porosity of approximately 1%, and moisture resistance.     

Novel Fabrication Route to Al2O3–TiN Nanocomposites Via Spark Plasma Sintering

A novel method for the preparation of Al₂O₃–TiN nanocomposites was developed. A mixture of TiO₂, AlN, and Ti powder was used as the starting material to synthesize the Al₂O₃–TiN nanocomposite under 60 MPa at 1400°C for 6 min using spark plasma sintering. X-ray diffractometry, scanning electron microscopy, and transmission electron microscopy were used for detailed microstructural analysis. Dense (up to 99%) nanostructured Al₂O₃–TiN composites were successfully fabricated, the average grain size being less than 400 nm. The fracture toughness ( K _{I C} ) and bending strength (σ_b) of the nanostructured Al₂O₃–TiN composites reached 4.22±0.20 MPa·m^1/2 and 746±28 MPa, respectively.