HT／Surlyn／PEG复合成核剂对PET结晶性能的影响

研究了水滑石(HT)/离子键聚合物(Surlyn)/聚乙二醇(PEG)复合成核剂对聚对苯二甲酸乙二醇酯(PET)非等温结晶性能的影响。通过正交实验选择最佳复合成核剂配方。差示扫描量热分析表明,HT/Surlyn/PEG复合成核剂各组分与PET的质量比为0．5/3/3/100时,PET的结晶温度提高,半结晶时间明显减少,说明PET的成核能力提高,结晶能力增强,结晶速率加快；同时,结晶放热焓和熔融吸热焓增加,说明PET的结晶度得到提高。     

结晶成核剂对PET／PE-HD共混物非等温结晶性能与力学性能的影响

研究了水滑石（HT）等四种结晶成核剂对聚对苯二甲酸乙二醇酯（PET）倩密度聚乙烯（PE-HD）共混物结晶性能和力学性能的影响。结果表明，加入HT，不仅可以提高PET／PlE—HD共混物中PET的结晶性能，而且还有助于改善共混物的力学性能；而添加离聚物（Surlyn 8920）或复合成核剂，PET结晶性能改善显著，但力学性能下降较多。     

一种新型复合成核剂对PET结晶性能和摩尔质量的影响

采用双螺杆挤出机,以熔融挤出法制备了含不同结晶成核剂的聚对苯二甲酸乙二醇酯(PET)样品.利用差示扫描昔热法(DSC)、黏度法研究了成核剂对PET结晶行为和摩尔质量的影响,并对比了复合成核剂(苯甲酸钠/酯交换剂A)与常用成核剂苯甲酸钠及乙烯/甲基丙烯酸共聚物的离聚物(Surlyn)对PET结晶行为和摩尔质量的影响.研究结果表明:在成核能力方面,复合成核剂的效果优于苯甲酸钠和Surlyn;同时,复合成核剂的加入还能有效地降低PET摩尔质馈的损失程度,加入复合成核剂的PET摩尔质量明显高于加入苯甲酸钠的PET样品,与加入Surlyn成核剂的PET样品摩尔质量接近.     

成核剂对PET非等温结晶动力学的影响

利用差示扫描量热仪(DSC)研究了滑石粉、苯甲酸钠和离子聚合物Surlyn对聚对苯二甲酸乙二醇酯(PET)非等温结晶行为的影响,并用Ozawa模型计算了非等温结晶动力学参数。结果表明:三种成核剂均是PET的良成核剂,其中苯甲酸钠的成核效果最为显著。与纯PET相比,三种成核剂的加入均使PET的结晶峰温度Tmc向高温偏移,过冷度(Tm-Tmc)明显降低,结晶速率常数K明显增大。纯PET和PET/成核剂共混体系的Ozawa指数n值介于1-4之间,均不为整数,且PET/成核剂共混体系的Ozawa指数n值小于纯PET的n值。     

纳米氧化物作为成核剂对PET结晶速率的影响

研究了成核剂纳米氧化镁和纳米氧化硅对聚对苯二甲酸乙二醇酯(PET)结晶速率的影响。通过等温结晶差热分析(DSC)研究了纳米氧化镁在不同含量、不同温度下对PET等温结晶行为的影响。用纳米氧化镁和纳米氧化硅填充PET体系的非等温结晶DSC,由所得冷结晶峰温度值和热结晶峰温度值的对比,探索纳米成核剂对PET结晶速率的影响及其规律。研究结果表明:纳米成核剂均能明显提高PET的结晶速率,而纳米氧化镁比纳米氧化硅对促进PET的结晶效果更好;添加不同含量的纳米氧化镁对PET在不同温度下的等温结晶影响不同,在所研究的范围内,1.0%的添加量较有利于PET的结晶。     

成核剂对PET/PEN共混物性能影响及其机理研究

利用差示扫描量热法、X射线衍射和转矩流变测试等手段,研究了成核剂碳酸氢钠、苯甲酸钠和乙烯-甲基丙烯酸离子键聚合物(Surlyn)对聚对苯二甲酸乙二醇酯/聚萘二甲酸乙二醇酯（PET/PEN）共混物结晶性能和力学性能的影响。结果表明,3种成核剂均能显著提高共混物的成核作用,其中,Surlyn和苯甲酸钠能明显提高共混物结晶性能,结晶峰温度提高约20 ℃,结晶速度提升近1倍;3种成核剂中,只有Surlyn在提高结晶性能的同时,还能提高共混物的力学性能;Surlyn是PET/PEN共混物理想的成核剂。     

成核剂对聚对苯二甲酸丙二醇酯结晶行为和形态的影响

用差示扫描量热分析仪、广角X射线衍射仪和偏光显微镜，研究了聚对苯二甲酸丙二醇酯（P1T）与成核剂YS-688共混物的熔融结晶行为和晶体形貌。结果表明，成核剂不仅能够提高PTT、在高温区的结晶速率，同时还可以提高PTT、在低温区的结晶速率，但同时降低了PTT、的结晶度；光透过率测试表明，随着成核剂含量的增加，PTT、透明性先增加后略有下降，最佳加入量为1％（质量分数，下同）；偏光显微镜分析表明，成核剂影响PTT、的晶体尺寸，晶体尺寸随着成核剂含量的增加而减小；广角X射线衍射分析表明，添加成核剂没有改变PTT的晶型。     

PET/纳米TiO2复合材料的结晶性能

采用光学解偏振、DSC等研究了原位聚合法制备的PET／纳米TiO2复合材料的结晶行为。结果表明：添加了锐钛型纳米TiO2之后，PET的最大晶体生长速率出现的温度有所降低，纳米TiO2对PET的结晶起到了异相成核的作用；加入锐钛型纳米TiO2时，如果添加量较少，PET纳米TiO2复合材料的结晶度升高、成核作用较明显；随着TiO2用量的增加，结晶度呈下降趋势，而加入2％的金红石型纳米TiO2对PET结晶具有良好的促进作用。     

复合成核剂对PET结晶速率和特性黏数的影响

采用差示扫描量热分析仪和乌氏黏度计研究了不同成核剂及其复配对聚对苯二甲酸乙二醇酯（PET）结晶速率和特性黏数的影响。结果表明,复合成核剂对于提高PET成核结晶速率[半结晶时间（t1/2）为32.3~45.3 s]的效果优于单一成核剂（t1/2为42.9~57.9 s）;同时部分复合成核剂能有效减小PET特性黏数的降低幅度。     

成核剂对不同特性粘数PET结晶性能的影响

研究了新型复合成核剂水滑石(HT)／离聚物(Surlyn8920)／聚乙二醇(PEG)对不同特性粘数聚对苯二甲酸乙二醇酯(PET)非等温结晶性能的影响。通过差示扫描量热仪测试了PET的结晶峰温度T_(mc)和熔融峰温度(T_m)。结果表明,复合成核剂各组分及PET的质量比为0.5:3.0:3.0:100.0时,各种PET的过冷度(T_m-T_(mc))均显著减少．半结晶时间(1gt_(1／2))也明显降低。而且,复合成核剂对不同特性粘数PET结晶性能的改善是一致的。     

Synthesis, Characterization, and Catalytic Properties of Nu-1, FU-1, and Related Zeolites

The discovery of the striking catalytic properties of the Mobil zeolite ZSM-5 has been followed by a large and intensive research effort both in catalysis promoted by ZSM-5 and in the synthesis and properties of other highly siliceous zeolites. While the distinctions between ZSM-5 and some of the claimed new zeolites are barely perceptible (it would perhaps be invidious to name these zeolites), other new. highly-siliceous zeolites differ markedly from ZSM-5/ZSM-11 in structure and consequently in other properties as well. Zeolites Nu-1 and FU-1 have now been fairly well characterized in both physical and catalytic properties. Although their crystal structures have not yet been determined, it is clear that they are different from ZSM-5 (and indeed, any other published zeolite structure).     

瓶用聚酯薄膜气体渗透性能的比较

比较了PET聚合过程中加入1^#纳米添加剂和2^#纳米添加剂的瓶用聚酯薄膜以及热灌装瓶用聚酯薄膜与普通瓶用聚酯薄膜对氧气透气量的大小,试验表明加入2^#纳米添加剂的瓶用聚酯薄膜阻隔气体渗透性能较好,热灌装瓶用聚酯薄膜次之,加入1^#纳米添加剂瓶用聚酯薄膜阻隔气体渗透性能不佳。     

常压阳离子可染聚酯熔体的流变性能研究

应用高压毛细管流变仪测试了2种常压阳离子染料可染聚酯(ECDP-1,ECDP-2)熔体的流变性能并与常规聚酯(PET)熔体的流变性能进行对比.结果表明:ECDP-1,ECDP-2与PET熔体都属于假塑性非牛顿流体,黏度随剪切速率((γ))的增大而减小;ECDP-1,ECDP-2与PET熔体的非牛顿指数都随温度的升高而增...     

Synthesis of a novel microcapsule flame retardant and flame-retardant property of its composites with poly (ethylene terephthalate)

A novel halogen-free microcapsule flame retardant, carbon microspheres coated with magnesium hydroxide microcapsule and polyethylene terephthalate (PET) (MMH@CMSs) were synthesized. Then, the prepared MMH@CMSs were introduced into PET resin to prepare MH@CMSs/PET composites. The morphology and structure of MMH@CMSs were characterized by SEM, TEM and FTIR, which showed that an organic shell layer of PET as capsule wall was coated on the surface of MH@CMSs. The prepared MMH@CMSs/PET reached the LOI of 27.4 with only 1wt.% MMH@CMSs, and UL94 test results showed that MMH@CMSs/PET reached UL94 V-0 rating when the dosage of MMH@CMSs was over 1.5wt.%. Tensile properties results showed that the microcapsule treatment of MH@CMSs significantly improved the mechanical properties of the composite, and the tensile strength of 1wt.% MMH@CMSs/PET increased by 83.9% compared with 1wt.% MH@CMSs/PET. The flame retardant mechanism was studied by cone calorimeter measurement, TGA, TGA-FTIR, SEM and FTIR. The results disclosed that MMH@CMSs enhanced the thermal stability of PET in air, and promoted PET to form a dense and continuous protective char layer that effectively blocked heat transfer and combustible gas release.     

PBT／PET共混体系相容性研究

将聚对苯二甲酸丁二醇酯(PBT)与聚对苯二甲酸乙二醇酯(PET)熔融共混,通过粘度匹配原则, 确定PBT／PET共混体系的熔体温度为275-285℃,在283℃时制得PBT／PET共混切片,并对其共混体系进行相容性研究。结果表明:PBT／PET共混体系的理论热焓均小于41．8 mJ,为热力学相容体系;由扫描电镜观察PBT／PET共混体系在PBT和PET交界处发生了相分离,当PBT与PET共混比越接近,相分离程度越明显;DSC分析表明PBT／PET共混体系在非晶区相容,晶区不相容。     

苯乙烯-甲基丙烯酸钠离聚物的合成及其对PET结晶行为的影响

采用溶液法制备苯乙烯-甲基丙烯酸钠(SMA-Na)离聚物,研究其对聚对苯二甲酸乙二酯（PET）的结晶及熔融行为的影响。结果表明：SMA-Na是PET的良成核剂,加入1wt %的苯乙烯-甲基丙烯酸钠使PET的熔融结晶温度（Tmc）提高了17.9 ℃,冷结晶温度(Tcc)降低了17.3℃,显著的提高了PET在高温区和低温区的结晶速度。加入离聚物,使得PET球晶变得更加细化完善。     

分子筛改性PET纤维的制备和性能研究

将分子筛、添加剂(分散剂、交联剂)以不同的比例和PET切片共混进行母粒法熔融纺丝,制得分子筛改性PET纤维,并测定纤维的力学性能、吸湿性能和染色性能。结果表明：当纤维中分子筛质量分数为2%时,改性PET纤维的可纺性较好;添加剂含量存在最佳值,与纯PET纤维相比,分子筛：分散剂(质量比)为1．0：1．8时,改性纤维断裂强度提高39．7%,含湿率提高30．4%,上染率提高7．7%;分子筛：分散剂：交联剂(质量比)为1．0：1．2：0．2时,改性纤维断裂强度可提高62．7%。分子筛在改性PET纤维中分散均匀,并形成了拟网状结构。     

抗紫外PET及纤维的研究开发

探讨了纳米碱式碳酸锌的制备方法。并结合聚酯的制备条件，在聚酯的聚合前加入纳米碱式碳酸锌，在聚合过程中分解生成氧化锌，实现聚酯的抗紫外性能；实验表明，聚酯的抗紫外性能随氧化锌用量的增加而增强，当氧化锌质量分数大于1％时，对聚酯的抗紫外线性能影响已不很明显。对抗紫外聚酯的相应纺丝干燥、速度、上油等条件进行了阐述。     

Kinetics of alkaline hydrolysis and morphologies of novel poly(ethylene terephthalate) micro‐porous hollow fibers and functional characteristics of fabrics

This investigation explores the kinetics of the alkaline hydrolysis of regular poly(ethylene terephthalate) (PET) solid fibers and PET micro‐porous hollow fibers, using statistical regression analysis. Statistical regression analysis results concerning the kinetics of the alkaline hydrolysis of regular PET solid fibers and PET micro‐porous hollow fibers yielded a β value of 1. The R² of the kinetic equation for α values from 1.07 to 1.16 exceeded that for α = 1. The rate constants of alkaline hydrolysis followed the order PET micro‐porous hollow fibers ? regular PET solid fibers. A morphology of large pores of diameter 0.1–3.5 μm was observed following alkali treatment of the PET micro‐porous hollow fibers. The weight loss percentage of the hollow fibers was around 20%. The hollowness of the PET micro‐porous hollow fibers after alkali treatment was between 30 and 32%. The PET micro‐porous hollow fibers exhibited simultaneous water‐absorption/release and keep‐warm functions. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

不同TiO_2含量PET的流变性能研究

采用毛细管流变仪研究了不同二氧化钛(Ti O_2)含量的聚对苯二甲酸乙二醇酯(PET)的流变性能。结果表明:添加Ti O_2质量分数为2.4%及以下的消光PET为假塑性非牛顿流体;在280℃、285℃、290℃下消光PET在低γ下的η_a高于大有光PET,且随着Ti O_2含量的提高,η_a略有增大;在280℃、285℃、290℃下,消光PET的非牛顿指数n低于大有光PET,而在295℃时,消光PET的n高于大有光PET;在γ低于3 000 s-1时,消光PET的ΔE_η高于大有光PET,而随着γ的逐渐增大,消光PET的ΔE_η又逐渐低于大有光PET;在280℃、285℃和290℃温度下消光PET的结构粘度指数Δη高于大有光PET,295℃时低于大有光PET。