Au/Ni/Al/Ti/AlxGa1-xN/GaN和Au/Pt/Al/Ti/AlxGa1-xN/GaN欧姆接触研究

研究并对比了Ti/Al/Ni/Au和Ti/Al/Pt/Au多层金属膜与未掺杂的Al0 .2 2 Ga0 .78N/GaN(i AlGaN/GaN)异质结构之间的欧姆接触性质。在退火温度低于 70 0℃时 ,两种接触样品上都不能得到欧姆接触。随着退火温度的升高 ,85 0℃快速退火后 ,在Ti/Al/Ni/Au接触上获得了 1.2 6×10 - 6 Ω·cm2 的比接触电阻率 ,在Ti/Al/Pt/Au接触上获得了 1.97× 10 - 5Ω·cm2 的比接触电阻率。研究结果表明 ,金属与半导体接触界面和Al0 .2 2 Ga0 .78N异质结构界面载流子沟道之间适当的势垒的存在对高质量欧姆接触的形成起重要作用 ,势垒的宽度取决于退火温度以及退火的具体进程。对Ti/Al/Ni/Au和Ti/Al/Pt/Au欧姆接触比接触电阻率的差异进行了解释。     

Effect of metal doping into Ce0.5Zr0.5O2 on catalytic activity of MnOx/Ce0.5–xZr0.5–xM0.2xOy/Al2O3 for benzene combustion

The research investigated the effect of doping two metals separately or together into Ce0.5Zr0.5O2 on the catalytic activity of MnOx/Ce0.5-xZr0.5-xM0.2xOy/Al2O3 （M=Y, Mn, Y and Mn） for catalytic combustion of benzene. The prepared catalysts were characterized by X-ray diffraction （XRD）, surface area analysis, oxygen storage capacity （OSC）, and H2-temperature programmed reduction （H2-TPR）. Catalytic test was performed on a conventional fixed bed flow reactor. The characterization results revealed that Y and Mn ions entered into the ceria-zirconia mixed oxides framework, which improved the textural properties and greatly promoted the MnOx dispersion on the support surface. The complete conversion temperature of benzene on MnOx/Ce0.4Zr0.4Y0.1Mn0.1Oy/Al2O3 was 563 K, and the selectivity of carbon dioxides was 99%. This catalyst could be applied in a wide range of GHSV and wide concentration condition, showing great potential for application.     

Superconducting Transition Temperature in YBa2Cu4O8/La2/3 Ca1/3 MnO3 / YBa2 Cu4O8 Heterostructure

YBa2Cu4O8/La2/3 Ca1/3 MnO3/YBa2Cu4O8 （ Y-124/LCMO/Y- 124） heterostructure was prepared by facing-target sputtering technique. The oscillatory superconducting transition temperature was observed when the thickness of LCMO d L is larger than critical thickness d L^CR. The metal-insulator transition temperature can only be detected at d L 〉 d L^CR. The dependence on the spacer layer in LCMO/Y-124 systems suggests strongly the interplay of ferromagnetic and superconducting couplings.     

热压烧结制备Li3/8Sr7/16Ta3/4Hf1/4O3钙钛矿型固体电解质

采用热压烧结制备了Li_3/8Sr_7/16Ta_3/4Hf_1/4O₃钙钛矿型固体电解质, 研究了不同烧结方式对样品性能的影响。通过X射线衍射仪表征材料的晶体结构, 扫描电子显微镜观察组织形貌, 交流阻抗仪测试电化学性能。结果表明:样品为立方KTaO₃相, 热压烧结成功合成了钙钛矿结构固体电解质, 相对于常压烧结, 热压烧结制备的样品孔隙更少, 晶粒之间结合更加紧密, 致密度高达94.0%, 离子电导率为4.33×10-4S·cm(T=298K).      

LiNi1/3Co1/3Mn1/3O2正极材料的合成与性能

采用共沉淀-高温固相法制备LiNi_1/3Mn_1/3Co_1/3O₂正极材料,利用XRD和SEM对所制试样的晶体结构和形貌进行表征,研究了烧结温度对材料电化学性能的影响.结果表明,焙烧温度为850 ℃制备的材料具有较好电化学性能,在25 ℃,电压范围为2.75~4.2 V,1 C充电6 C放电下首次放电比容量为124.2 mAh/g,50次循环后容量保持率为95.2 %.      

Effect of Zn Doping on Transport Properties of La2/3 Sr1/3 Mn1 - x Znx O3 Films

La2/3 Sr1/3 Mn1-x ZnxO3films （x =0.05, 0.1,0.3, and 0.5） were prepared using magnetron sputtering method, and the effect of Zn doping on transport properties of the films was studied. An analysis of X-ray diffraction showed that the main phase of the bulk target was orthorhombic and the films had better epitaxial character. It was found that the films with x =0.05 and x =0.1 exhibited typical insulator-metal transition. No transition of the films with x≥0.3 was observed and the dominant transport was variable-range hopping due to observable secondary phase ZnO. These could be attributed to the Zn doping effect on manganites.     

锂过量对钙钛矿型Li3/8Sr7/16Ta3/4Hf1/4O3固体电解质性能的影响

固相烧结法合成钙钛矿型Li_3/8Sr_7/16Ta_3/4Hf_1/4O₃(LSTH) 固体电解质材料,制备过程中分别加入过量的碳酸锂,质量分数分别为(0~30 %).通过XRD、SEM、ICP-OES以及EIS测试,表征不同锂过量LSTH固体电解质材料成相、显微形貌以及室温电导率的影响.实验结果表明,配料时,过量一定质量百分数的碳酸锂,能够有效减少烧结过程中因锂挥发而生成的SrTa₂O₆杂相,提高样品密度和室温电导率.样品最佳锂过量质量百分数为20 %,20 %锂过量样品1 300 ℃烧结10 h为钙钛矿纯相,密度6.5 g/cm3,室温电导率达到3.12×10-4 S/cm.      

锂离子电池正极材料LiNi1/3Co1/3Mn1/3O2研究进展

介绍了比容量高、循环性能优异、成本较低的LiNil/3Co1/3Mnl/3O2正极材料近年来在合成技术及其掺杂改性、表面修饰等方面所取得的成果和进展,并对其未来的发展趋势进行了展望。     

Antigenic drift between the haemagglutinin of the Hong Kong influenza strains A/Aichi/2/68 and A/Victoria/3/75

A DNA copy of the gene coding for the influenza A/Aichi/2/68 haemagglutinin protein was cloned in the plasmid pBR322 and the complete nucleotide sequence determined. Comparison of this primary structure and the deduced amino acid sequence with the haemagglutinin gene and protein of strains belonging to the same (H3) subtype and to different subtypes, of both human (H2) and avian (Hav1) origin, documents further at the molecular level the two independent modes of antigenic variation of the virus--drift and shift.     

Index/Volume 14/1975

Abstract

A microscopic study has been made of the dissolution of lead and copper sulphides from blast furnace mattes by bioleaching.

The results of the experiments demonstrate the preferential corrosion sites and the degradation of the surface of the sulphides caused by the oxidation catalyzed by bacteria (Tiobacillus ferrooxidans). This degradation of the solid leads to its breakdown and increases the reaction surface.

In addition, it is shown that a two-stage bioleaching treatment (800 h retention time) is required to achieve at least 80% copper extraction.     

Catalytic combustion of diesel soot over K2NiF4-type oxides La2-xKxCuO4

Nanostructure K2NiF4 type oxides La2-xKxCuO4 complex oxides were prepared using the Sol-Gel method, characterized by X-Ray Diffraction （XRD）, Fourier Transform Infrared （FT-IR）, and Scanning Electron Microscopy （SEM）. The catalytic activity for soot combustion was evaluated by the Temperature-Programmed Reaction （TPO） technique. The results demonstrated that the substitution quality of K^＋ for La^3＋ at the A-site would increase the catalytic activities of La2-xKxCuO4 for soot combustion greatly; the substitution quality affected the structure and catalytic activity obviously. The La1.8K0.2CuO4 complex oxides with tetrahedral structures had the best catalytic activity for soot combustion, and the ignition temperature of soot combustion was lowered from 490 to 320 ℃.     

Al2O3La2O3Y2O3/Cu复合材料的电弧侵蚀特性研究

采用喷射沉积和内氧化法制备出Al₂O₃La₂O₃Y₂O₃/Cu复合材料,研究该材料在直流20 V/20 A的工作条件下触点的电弧侵蚀特性,并与Al₂O₃/Cu材料进行了对比分析.利用电子天平、扫描电镜等方法分析电弧侵蚀后触点的质量变化和表面微观结构.结果表明,通过添加Y₂O₃、La₂O₃稀土氧化物颗粒,可有效降低触头材料的材料转移量.Al₂O₃La₂O₃Y₂O₃/Cu材料的抗熔焊性和抗烧损性优于Al₂O₃/Cu材料的性能.在直流阻性负载条件下Al₂O₃La₂O₃Y₂O₃/Cu阳极触头表面形成凹坑,阴极触头表面形成凸起,触点表面显示出浆糊状凝固物和喷发坑等电弧侵蚀形貌特征.      

Crystal Structures and Thermoelectric Properties of Sm-Filled Skutterudite Compounds Smy Fex Co4 - x Sb12

Polycrystalline samples of Sm partially filled skutterudites SmyFexCo4-xSb12 were prepared by melting and Spark Plasma Sintering technique. The results of Rietveld refinement showed that the obtained SmyFexCo4-xSb12 samples possessed filled skutterudite structures. The thermal parameter （B） of Sm is larger than that of Sb, Fe, and Co, indicating that Sm ＂rattled＂ in Sb-icosahedron voids. The effects of filling atom Sm on thermoelectric properties of these compounds were investigated. With the increase of Sm filling fraction （y）, electrical conductivity decreased, Seebeck coefficient increased and had a maximum value when y was 0.38; thermal conductivity reduced and had a minimum value when y was 0. 32. At 750 K, the highest figure of merit of 0.68 was obtained for Sm0.32Fe1.47Co2.53Sb12.     

Index/Volume 11/1972

Abstract

Samples of Magpie titaniferous iron ore – deposits totalling one billion tons – are already known and have been systematically studied by chemical analysis, X-ray diffraction and electron microprobe. The main constituents of this ore, expressed as oxides, are: FeO 26.6%, Fe₂O₃ 36.4%, TiO₂ 12%. The main minerals are magnetite, ilmenite and a spinel; their composition has been determined with an electron microprobe. Results of magnetic concentration of the ore are presented and interpreted with the help of the electron microprobe data.

Résumé

Des échantillons du minerai de Magpie dont les gisements atteignent 1 milliard de tonnes ont été étudiés de façon systématique par analyse chimique, diffraction des rayons X et microsonde électronique. Les principaux constituants de cette magnétite titanifère, exprimés sous forme d'oxydes sont: FeO 26.6%, Fe₂O₃ 36.4%, TiO₂ 12%. Les principaux minéraux présents sont la magnétite, l'ilménite et un spinelle; leur composition a été déterminée par microsonde électronique. Les résultats des études de concentration magnétique du minerai sont également présentés et interprétés grace aux résultats de l'analyse par microsonde.     

TbCu7型SmCo7-xHfx合金的结构及磁性能

采用熔体快淬法在40 m/s制备了SmCo_7-xHf_x （x=0, 0.1, 0.15, 0.2, 0.3）合金薄带,研究Hf取代量对SmCo_7-xHf_x合金的相组成、组织结构及磁性能的影响.结果表明:随Hf取代量的增加,均可获得TbCu₇型结构的亚稳相,晶格常数a和c也随之增加,c/a比值在0.82~0.83,晶粒平均尺寸减小,且更加均匀;在性能方面,Hf取代量为0.2时,可获得最优磁性能B_r为0.55 T和H_c为1 084 kA/m. Hf的添加还可有效改善合金高温性能,在27~400 ℃温度区间,矫顽力温度系数由未添加时-0.21 %/℃改善到-0.18 %/℃,提升14.3%.