制备工艺对Cf/SiC复合材料力学性能的影响

分别采用先驱体裂解-热压和先驱体浸渍-裂解方法制备出了Cf/SiC复合材料.重点探讨了不同制备工艺对复合材料纤维/基体间界面和力学性能的影响.研究表明,采用先驱体裂解-热压工艺制备复合材料时,由于制备温度较高,复合材料中纤维与基体间的界面结合强,同时纤维本身性能的退化严重,因此复合材料表现为脆性断裂,具有较低的力学性能.而采用先驱体浸渍-裂解法制备复合材料时,由于致密化温度较低,复合材料中纤维与基体的界面结合较弱,而且纤维的性能保留率较高.因此,纤维能够较好地发挥补强增韧作用,复合材料具有较好的力学性能, 其抗弯强度和断裂韧性分别为573.4MPa和17.2 MPa*m1/2.     

聚硅氧烷先驱体转化制备三维Cf/Si-O-C复合材料的研究

研究了含氢聚硅氧烷(PSO)与二乙烯基苯(DVB)的交联与裂解。结果表明:只有在氯铂酸的催化作用下,PSO与DVB才能完全交联。DVB/PSO质量比对陶瓷产率的影响较大,DVB/PSO＝0.5时陶瓷产率最高,达到76%。裂解产物中Si,C,O的含量分别为38.3wt%,34.3wt%,27.4wt%。以质量比为0.5的DVB/PSO体系为先驱体,采用先驱体转化法制备出三维C_f/Si-O-C复合材料。研究发现:第一次裂解时采用热压辅助可以明显提高材料的力学性能。第一次在1600℃,10MPa的条件下热压裂解5min,后续真空浸渍-常压裂解处理六个周期所制得的材料具有较高的力学性能,其弯曲强度和断裂韧性分别为502MPa,23.7MPa·m 1/2。理想的界面结合状态是其具有高性能的主要原因。     

SiCf/SiC复合材料的制备与力学性能

分别采用先驱体裂解-热压和先驱体浸渍-裂解方法制备出了SiCf/SiC复合材料.重点探讨了不同制备工艺对复合材料纤维/基体间界面和断裂行为的影响.研究表明,采用先驱体裂解-热压工艺制备复合材料时,虽然烧结液相可以促进复合材料的致密化,但其同时导致纤维与基体间的界面结合强以及纤维本身性能的退化,因此复合材料表现为脆性断裂,具有较低的力学性能.而采用先驱体浸渍-裂解法制备复合材料时,由于致密化温度较低,复合材料中纤维与基体的界面结合较弱,而且纤维的性能保留率较高,因此,纤维能够较好地发挥补强增韧作用,复合材料具有较好的力学性能,其抗弯强度和断裂韧性分别为703.6MPa和23.1Pa.m1/2.     

热模压辅助先驱体浸渍裂解制备Cf/SiC复合材料研究

以聚碳硅烷为先驱体,采用热模压辅助先驱体浸渍裂解工艺制备3D-B C_f/SiC复合材料,研究了热模压辅助对3D-B C_f/SiC复合材料致密度和力学性能的影响。结果表明:先驱体浸渍裂解制备陶瓷基复合材料第一次浸渍后引入高温热模压工艺可以改善材料微观结构,显著提高材料的致密度和力学性能。其中1600℃,10MPa,1h下热模压辅助先驱体浸渍裂解6次制备的3D-B C_f/SiC复合材料的密度为1.79g/cm3,弯曲强度高达672MPa,断裂韧性达18.9MPa·m1/2,剪切强度接近50MPa,且具有较好的抗热震性和高温抗氧化性。     

聚钛碳硅烷先驱体转化法制备3DCf/Si-Ti-C-O复合材料研究

以一种新型先驱体,聚钛碳硅烷(PTC)为原料制备了3D Cf/Si-Ti-C-O材料,考察了其力学性能和抗氧化、抗热震性能.结果表明,PTC在1200℃时裂解的陶瓷产率达到63.37%,材料的弯曲强度和断裂韧性分别达到485.3MPa和19.95MPa·m1/2.在1300℃马弗炉中氧化10min后,材料的弯曲强度为306.2MPa,强度保留率为63.06%.1300℃五次热震试验后的弯曲强度为408.9MPa,强度保留率为85.13%.表明3D Cf/Si-T-C-O材料具有较好的力学性能和抗氧化、抗热震性能,PTC是一种优异的适合制备陶瓷基复合材料的先驱体.     

两种先驱体低温裂解制备石英纤维增强氮化硅复合材料

以全氢聚硅氮烷( PHPS) 和聚甲基硅氮烷( PHMS) 为陶瓷先驱体, 通过循环浸渍和600 ℃低温裂解分别制备了三维石英纤维增强氮化硅复合材料, 对比研究了复合材料的力学性能和微观结构。结果表明: 由PHPS 制备的复合材料密度为1. 83 g/ cm3 , 气孔率10 % , 弯曲强度45. 4 MPa , 材料断口平整, 纤维基体界面结合强; 而由PHMS 制备的复合材料密度仅为1. 66 g/ cm3 , 气孔率16 % , 却具有更高的弯曲强度56. 3 MPa , 材料断面较粗糙,界面结合较弱。先驱体活性不同是导致复合材料界面结合强弱及力学性能不同的主要原因。      

威碳纤维及其SiC基复合材料的性能分析

以聚碳硅烷(PCS)为先驱体,国产光威(Gw)碳纤维为增强体,采用先驱体浸渍-裂解工艺(PIP)制备了Cf/SiC复合材料.结果表明,所制备Gw碳纤维复合材料的力学性能优异,抗弯强度达到405.3MPa,断裂韧性15.7 MPa·m1/2.并对GW纤维制备复合材料的表面和断口进行了显微形貌分析,复合材料断口纤维拔出较多,Gw碳纤维在复合材料中很好地发挥了补强增韧作用.     

裂解碳涂层对碳纤维增强碳化硅复合材料力学性能的影响

采用先驱体裂解－热压烧结方法制备出Cf/SiC复合材料,探讨了裂解碳涂层和烧结温度对复合材料纤维／基体界面和力学性能影响,烧结温度为1800度时,由于其中由富碳界面相构成的纤维／基体界面相使纤维／基体界面结合适中,具有较好的力学性能。     

聚硅氧烷先驱体转化制备低成本Si—O—C陶瓷基复合材料

研究了廉价聚硅氧烷的交联与裂解情况，并以其为先驱体转化制备Si-O-C陶瓷基复合材料，结果表明，在氯铂酸的催化下，聚硅氧烷与二乙烯基苯可以交联固化，当聚硅氧烷／二乙烯基苯摩尔比为1：0．5时，陶瓷产率达60．52％，经6次浸渍－交－裂解过程制备出碳纤维三维编织物增强陶瓷基复合材料，其密度达到1.59g/cm^3，弯曲强度达到321MPa，断裂韧性达到9.38MPa.m^1/2.     

裂解工艺对先驱体转化制备Cf/SiC材料结构与性能的影响

以聚碳硅烷(PCS)/二乙烯基苯(DVB)为先驱体,经8个周期的反复真空浸渍-交联-裂解处理制备出三维编织碳纤维增强碳化硅(3D-B C_f/SiC)复合材料,考察了裂解工艺对材料结构与性能的影响。结果表明:提高裂解升温速率可以提高材料密度,形成较理想的界面结合,从而提高材料的力学性能。裂解温度对材料性能也有较大的影响,C_f/SiC复合材料在第6个周期采用1600℃ 裂解可以弱化纤维与基体之间的界面,提高材料致密度,材料的力学性能也得到较大改善。裂解升温速率为15℃/min,第6个周期采用1600℃裂解制备的C_f/SiC材料性能较好,弯曲强度达到556.7 MPa。      

Insertion of triangulated surfaces into a meccano tetrahedral discretization by means of mesh refinement and optimization procedures

In this paper, we present a new method for inserting several triangulated surfaces into an existing tetrahedral mesh generated by the meccano method. The result is a conformal mesh where each inserted surface is approximated by a set of faces of the final tetrahedral mesh. First, the tetrahedral mesh is refined around the inserted surfaces to capture their geometric features. Second, each immersed surface is approximated by a set of faces from the tetrahedral mesh. Third, following a novel approach, the nodes of the approximated surfaces are mapped to the corresponding immersed surface. Fourth, we untangle and smooth the mesh by optimizing a regularized shape distortion measure for tetrahedral elements in which we move all the nodes of the mesh, restricting the movement of the edge and surface nodes along the corresponding entity they belong to. The refining process allows approximating the immersed surface for any initial meccano tetrahedral mesh. Moreover, the proposed projection method avoids computational expensive geometric projections. Finally, the applied simultaneous untangling and smoothing process delivers a high‐quality mesh and ensures that the immersed surfaces are interpolated. Several examples are presented to assess the properties of the proposed method.     

Certification Institutions Expected to Update and Transfer Information on Present Standards

Standards are the basis for production enterprises to organize production, ex-factory inspection, trade (delivery) and technical exchanges, product certification, quality arbitration and supervision.……     

Flow calorimeter for enthalpy increment measurements on condensed gases

A flow calorimeter for enthalpy increment measurements on condensed gases is presented. A better knowledge of the properties of the liquefied natural gas is needed, and therefore a liquid loop has been designed for our flow calorimeter. The fluid loop in the calorimeter is designed in order to avoid the two-phase region, since two phases would give compositional disturbances in the measurements. The avoidance of the two-phase region is made possible by increasing the pressure of the test fluid after the measurement section, then heating the fluid at super-critical pressure past the critical point. Finally, the fluid is throttled to the low-pressure gas state at the inlet condition of the compressor that circulates the fluid. To perform the pressure increase, a new cryogenic pump has been designed. To evaluate the new equipment, measurements were taken on liquid ethane over the temperature range 146–256 K at pressure between 0.9 and 5.1 MPa.     

Refrigerators Enter a New Era of Health Preservation Frestech initiates the establishment of China's first standard for household sterilization refrigerators

On November 30, 2007, the China Association for Standardization (CAS) held a press conference at Beijing Diaoyutai State Guest House. Leaders from the China Household Electric Appliance Research Institute, the China Household Electric Appliance Association, and the China Consumers' Association attended and made speeches.……     

Optimum-Simulation von Ernteprozessen

Zusammenfassung Bei der Gestaltung von Ernteprozessen — beispielsweise des Prozesses Mähdrusch, Körnertransport und -abnahme — als transportverbundene Fließarbeitsverfahren mit mindestens zwei verschiedenen Arbeitsmitteln gibt es einen großen Optimierungsspielraum. Solche Prozesse sind mehrstufige Bedienungsprozesse mit gemischter Anordnung der Bedienungseinrichtungen. Außerdem besitzen sie stark ausgeprägte räumliche Aspekte. Es wird vor allem gezeigt, welche Merkmale solcher Prozesse in Simulationsmodellen abgebildet sein müssen, welche Zielgrößen in Abhängigkeit von welchen Einflußgrößen unter Berücksichtigung welcher Prozeßbedingungen ermittelt werden sollten und wie der Bewertungsprozeß zur Ermittlung der gewünschten Informationen gestaltet werden muß.     

A study of centrifugal cast high boron high speed steel

In the present study a high‐boron high speed steel (HSS) roll material was designed. Many expensive alloy elements have been substituted by cheap boron alloy, and high‐boron high speed steel roll has been manufactured by centrifugal casting method. The microstructures, mechanical properties and wear resistance of centrifugal casting high‐boron high speed steel roll have been investigated by optical microscopy (OM), scanning electron microscopy (SEM), and X‐ray diffraction (XRD) analysis, hardness test, impact test and wear test. The results indicated that the solidification microstructures of high‐boron high speed steel roll consisted of M₂(B,C), (W,Mo)₂(B,C), M₃(B,C), M₂₃(B,C)₆ type borocarbides and martensite, a small amount of retained austenite. Borocarbides were continuously distributed over the grain boundary. After quenching from 1050 °C, local broken network appeared in partial borocarbides, and fine secondary borocarbide precipitated from the matrix. After tempering from 525 °C, the amount of precipitated borocarbide increased significantly. After heat treatment, the hardness of high‐boron high speed steel roll excelled 60 HRC, and its impact toughness excelled 8.0 J/cm². The single groove steel rolling amount of high‐boron high speed steel rolls increases by 500% than that of bainite cast iron roll, when the rolls are used in K₁ mill housing of bar mill.     

Brainstorming for ISO Strategy 2016-2020

正Responding to ISO’s appeal for survey for the to-be-developed ISO Strategy Plan for 2016-2020,SAC hosted a special workshop over the needs and comments of various fi elds on June 8 in Beijing.The workshop was attended by ISO President-elect and Ansteel General Manager Zhang Xiaogang,SAC Vice-Administrator Yu Xinli,and 30 experts from     

CNAS Passes APLAC's PTP Review

正The review group of Asia Pacific Laboratory Accreditation Cooperation(APLAC)carried out a 4-day peer review of the proficiency testing provider(PTP)for China National Accreditation Service for Conformity Assessment(CNAS)from July 28 to 31,2014.CNAS passed the PTP review with excellent performance.Two senior peer reviewers of APLAC made a comprehensive,rigorous and detailed review of CNAS’s PTP accreditation activities,and made the on-spot inspection of the review groups in Shanghai and Shenzhen respectively.     

新闻(英文)

正China and Greece Sign the Standardization Cooperation Agreement Witnessed by Chinese Premier Li Keqiang and Greek Prime Minister Antonis Samaras,AQSIQ Minister Zhi Shuping and ELOT Chairman and Executive Director Angelos Tolkas signed the SAC-ELOT Standardization Cooperation Agreement.The Agreement is one of the critical cooperation documents signed during Li Keqiang’s visit in Greece,encouraging China and Greece to