ML45Mn2冷镦钢盘条的研究与开发

120 t转炉-LF-VD-350 mm x430 mm铸坯-150 mm x 150 mm轧坯-轧制流程生产的ML45Mn2钢Φ16 mm和Φ18 mm盘条采用的主要工艺为:碱度1.5-2.0精炼渣,52 t中间包,电磁搅拌,轻重压下,开轧温度1 010 ~ 1 070 °C,精轧温度820 - 850°C,卷曲温度780 - 820°C,冷速0. 15 -0.4 °C/s等工艺。检验结果显示,MI45Mn2钢盘条热轧态平均抗拉强度797 MPa,平均断面收缩率50.3% ,1/4冷镦合格,金相组织为珠光体+铁素体,断面平均硬度值为92.5HRB,带状组织1.5-2.5级,满足技术要求。     

控轧控冷工艺对高强度锚杆钢组织和性能的影响

随着矿井深度的增加,对锚杆支护强韧性的要求越来越高,为了应对这一情况,需要研发出更高强度的锚杆钢。利用锚杆钢研究了轧制工艺、冷却工艺与珠光体、铁素体相比例,析出相析出行为及力学性能的关系。研究结果表明,在中轧后、精轧前采用适当水冷+回复段处理的复合工艺可使晶粒更细小、组织更均匀。对超高强度锚杆钢进行热压缩变形试验,由热模拟试验结果确定相转变温度为A_c1=737 ℃、A_c3=886 ℃。最终筛选出入精轧温度为810 ℃、回复段温度为800 ℃时,可获得的晶粒尺寸达4 μm,珠光体体积分数为66.8%,铁素体体积分数为33.2%,珠光体片层间距达200 nm;另外调整V、Cr、N等析出以提高锚杆钢的强韧性,较低的回复温度有利于细小、弥散、V(C/N)析出相的析出,V(C/N)的析出可进一步改善锚杆钢的力学性能。由该控轧控冷工艺轧制的锚杆钢屈服强度为780 MPa、抗拉强度为930 MPa、硬度为291HV、伸长率为20%。     

控轧控冷工艺对900 MPa级热轧带钢组织和性能的影响

通过动态CCT曲线测试和实验室控轧控冷试验,分析了900 MPa级热轧带钢连续冷却过程中的相变过程以及不同卷取温度下显微组织、析出相和力学性能的关系。试验结果表明:随着冷却速度提高,显微组织中多边形铁素体比例下降,贝氏体组织比例升高,冷速大于15℃/s时,显微组织全部为贝氏体;随着卷取温度升高,显微组织中针状铁素体比例下降,多边形铁素体比例升高;当卷取温度为600℃时,组织为铁素体+少量珠光体,此时析出相细小弥散,可获得抗拉强度达到1 000 MPa,延伸率17%的热轧产品。     

建邦HRB500E高强抗震钢筋生产实践

介绍建邦集团采用微钒合金化技术,在转炉连铸各工序均匀成分、保护浇铸,轧钢工序控轧控冷,最终得到珠光体＋铁素体组织的高强抗震钢筋HRB500E,其性能满足国家标准,符合市场需求,为企业创造了较好的效益。     

控轧控冷工艺对高强度锚杆钢组织和性能的影响

随着矿井深度的增加,对锚杆支护强韧性的要求越来越高,为了应对这一情况,需要研发出更高强度的锚杆钢。利用锚杆钢研究了轧制工艺、冷却工艺与珠光体、铁素体相比例,析出相析出行为及力学性能的关系。研究结果表明,在中轧后、精轧前采用适当水冷+回复段处理的复合工艺可使晶粒更细小、组织更均匀。对超高强度锚杆钢进行热压缩变形试验,由热模拟试验结果确定相转变温度为A_c1=737 ℃、A_c3=886 ℃。最终筛选出入精轧温度为810 ℃、回复段温度为800 ℃时,可获得的晶粒尺寸达4 μm,珠光体体积分数为66.8%,铁素体体积分数为33.2%,珠光体片层间距达200 nm;另外调整V、Cr、N等析出以提高锚杆钢的强韧性,较低的回复温度有利于细小、弥散、V(C/N)析出相的析出,V(C/N)的析出可进一步改善锚杆钢的力学性能。由该控轧控冷工艺轧制的锚杆钢屈服强度为780 MPa、抗拉强度为930 MPa、硬度为291HV、伸长率为20%。     

Mn含量对低碳冷镦钢SWRCH22A组织和性能的影响

分析研究了 Mn含量0.78％～0.92％对0.20％碳冷镦钢Φ20 mm热轧盘条组织和力学性能的影响.盘条热轧的终轧温度为880℃,缓冷.结果表明,Mn含量由0.78％增加至0.92％时,盘条抗拉强度由485 MPa升高至508 MPa,增加了 23 MPa,伸长率由31％降至28％,下降了 3个百分点,断面收缩率由...     

TMCP工艺对高性能桥梁钢Q370qE-HPS组织性能的影响研究

为了研究TMCP工艺对Q370q E-HPS高性能桥梁钢组织和性能的影响,达到替代正火工艺的目的,对终轧温度、开冷温度、返红温度及冷却速率等TMCP关键工艺参数与组织、力学性能的关系进行分析。结果表明:采用两阶段控轧控冷工艺生产Q370q E-HPS钢时,随终轧温度升高、开冷温度降低、返红温度升高及冷却速度降低,铁素体晶粒尺寸增大,珠光体含量增加,屈强比降低。通过工艺参数优化,可获得合适尺寸和体积分数的铁素体和珠光体,实现Q370q E-HPS钢良好的强韧性匹配和较低的屈强比。     

冷却工艺对Ti微合金化高强钢组织和硬度的影响

通过热模拟实验,研究了冷却工艺参数对Ti微合金化高强钢组织和硬度的影响.结果表明:当终冷温度为700℃时,随着冷却速度的增大,铁素体和珠光体组织得到了显著细化,实验钢硬度增加;随着终冷温度的降低,多边形铁素体晶粒尺寸呈减小趋势,铁素体和珠光体含量逐渐降低,珠光体片层间距逐渐减小,贝氏体含量增加,相变强化和细晶强化共同作...     

控轧控冷工艺对SCM435钢盘条组织和性能的影响

试验钢SCM435（/%:0.33~0.38C,0.15~0.35Si,0.60~0.85Mn,≤0.025P,≤0.025S,0.90~1.20Cr,0.15~0.30Mo）盘条的生产流程为80t BOF-LF-280 mm×325 mm铸坯-160 mm×160 mm热轧坯-热连轧成Φ16 mm盘条。试验研究了160 mm×160 mm热轧坯由常规轧制工艺（开轧1060℃,精轧930~950℃,吐丝860~900℃,冷却速度0.5~0.6℃/s）和控轧控冷工艺（开轧1060℃,精轧820~850℃,吐丝780~820℃,冷却速度0.4~0.5℃/s）对SCM435钢热轧盘条组织和力学性能的影响。结果表明,随着精轧温度的降低和冷却速度的减小,钢热轧盘条的组织得到改善,抗拉强度明显降低;常规工艺轧制SCM435钢热轧盘条的抗拉强度平均952 MPa,组织为铁素体+珠光体+贝氏体+马氏体,控轧控冷工艺轧制的SCM435钢热轧盘条的抗拉强度平均817 MPa,组织为均匀的铁素体+珠光体。结合控轧控冷工艺原理对钢的组织和性能变化进行了分析。     

控轧控冷和冷床保温工艺对42CrMo钢Φ50 mm轧材力学性能的影响

根据棒材线在生产42CrMo钢Φ50 mm轧材容易造成硬度偏高,不能满足协议要求.通过控轧控冷结合冷床保温措施,终轧温度由原967 ～970℃降到860℃,冷却速率由原0.35℃/s降低到0.17℃/s,金相组织从之前的非平衡态组织贝氏体+铁素体+珠光体优化为铁素体+珠光体,使HB硬度值由原317降至252.由此工艺生...     

Ti微合金化高强度热轧带钢组织性能及强化机理

The continuous cooling transformation behavior, the effect of coiling temperature on microstructure and mechanical properties, and strengthening mechanisms of Ti microalloyed high strength hot strip steel were systematically investigated by thermal simulation testing machine, laboratory rolling mill, SEM and HR-TEM. The dynamic CCT curve was established. The results show that the austenite to ferrite and pearlite transformation takes place when the cooling rate is less than 1??/s. The austenite to bainite transformation accompanied with austenite to ferrite and pearlite transformation takes place when the cooling rate is in the range of 5 ??/s to 10 ??/s. The bainitic transformation temperature is about 600??. The amount of granular bainite decreases, while the amount of lath bainite increases with the increase of cooling rate in the range of 20??/s to 50??/s. Furthermore, the study on the effect of coiling temperature on the microstructure and mechanical properties of experimental steel has shown that the strength and plasticity of tested steel are improved with decreasing the coiling temperature. When the coiling temperature is 550?棬the experimental steel possesses optimal mechanical properties owing to the grain refinement and precipitation of nano-scale TiC particles. And the tensile strength, yield strength and elongation of tested steel were 742MPa, 683MPa and 22??5%, respectively.     

钛微合金化热轧双相钢的工艺研究

通过模拟实验研究了钛微合金化热轧双相钢的连续冷却转变曲线及终轧温度对组织的影响规律,获得了可行的工艺窗口,并进行了验证性热轧实验.在冷却速率小于5℃·s-1及温度在625~725℃时,实验钢可以形成先共析铁素体.随着终轧温度升高,组织中铁素体及马氏体含量先升高后降低,但幅度不大.同时,当终轧温度较高时,铁素体显微硬度增加,析出强化作用增加.当终轧温度及缓冷温度分别为840℃及700℃时,获得了抗拉强度为672 MPa及屈强比为0.61的性能良好的热轧双相钢.经计算,铁素体组织中析出强化量为78.5 MPa.      

免热处理高强度低屈强比铆螺钢的研究

铆螺钢经棒材轧机控轧控冷轧成棒材,获得具有铁素体、珠光体和粒状贝氏体的混合组织,冷镦成螺栓后进行产品检验.结果表明:控轧控冷后的棒材不经过退火直接冷镦成螺栓,冷镦性能非常好.螺栓不经过最终热处理,同样可获得很高的力学性能.力学性能的提高主要是由于螺栓在拉伸变形时残余奥氏体的应变诱导马氏体相变.     

SCM435冷镦钢奥氏体连续冷却转变曲线研究

利用Gleeble-3800热模拟试验机,采用热膨胀法结合硬度测量,研究了SCM435冷镦钢的连续冷却转变过程,通过光学显微镜、电子探针分析了不同冷速下SCM435冷镦钢的组织转变行为。结果表明,SCM435冷镦钢冷速低于1℃/s时,组织主要为铁素体+珠光体+贝氏体,在1~10℃/s冷速范围内,组织主要为贝氏体和少量珠光体+铁素体或马氏体,冷速大于10℃/s时,组织为马氏体。     

超细晶粒38SiMnVB弹簧钢的控制轧制

高强韧性弹簧钢 38SiMnVB(% :0.39C ,1.48Mn ,1.21Si ,0.09V ,0.0019B)经750～820℃温度精轧 ,终轧温度700～720℃轧后缓冷 ,控制轧制后得到的组织为珠光体 +铁素体 ,晶粒度≥ 10级 ,HRC硬度值26 ,抗拉强度 925～1010 MPa ,延伸率45 %～58% ,可以直接进行冷拔。经控制轧制的轿车弹簧用超细晶粒38SiMnVB弹簧钢经 870℃淬火 ,320℃回火后具有极好的综合力学性能 :抗拉强度 2030～2140 MPa ,屈服强度1900～2010 MPa ,延伸率12 %～15 % ,断面收缩率48%～55 %。     

MULPIC冷却装置在品种钢研发中的生产实践

 舞钢新宽厚板生产线MULIPIC在线快冷装备具有高冷却速度等技术特点,结合控制轧制和在线快冷装备对船板、管线钢进行了开发研究,采用直接淬火工艺研究开发了高强工程机械用钢。结果表明： 60 mm厚度E36级TMCP船板钢,组织全部为铁素体＋珠光体,晶粒度10级以上,－40 ℃夏比横向冲击功在183 J以上;X70管线钢的组织为针状铁素体,力学性能合格率达98％;利用直接淬火（DQ）和离线回火工艺,生产出30 mm厚的WQ960D调质钢,屈服强度达到960 MPa,抗拉强度1030 MPa,－20 ℃纵向冲击功在43 J以上。     

北极海洋平台用Q355E热轧H型钢连续冷却转变规律

在实验室利用Gleeble-3500热模拟试验机对3种Nb、V微合金化Q355E热轧H型钢进行了连续冷却转变规律测试,研究了冷却速度对试验钢组织与硬度的影响。结果表明:在冷速为0.5℃/s时,组织中开始出现贝氏体;冷速大于7℃/s时,珠光体转变即终止。在中等冷速下,Nb的加入促进了贝氏体的形成,抑制了铁素体与珠光体的形核;并且Nb的加入使铁素体转变区右移。Cr的加入降低了较高冷速下铁素体与珠光体相变点,并促进了高冷速下马氏体的形成。由于受V析出的影响,含V试验钢在冷速为1℃/s时其硬度曲线有一个"波谷"。3种试验钢的冷速在0.5~3℃/s之间时,试验钢可获得强韧性较好的细小准多边形铁素体、少量珠光体与贝氏体的复合组织。     

初始组织对一种Nb-Mo微合金化中锰TRIP钢组织演变与力学性能的影响

研究了热轧后冷却方式和冷轧压下量对一种Nb-Mo微合金化中锰TRIP钢临界退火过程中组织演变与力学性能的综合影响规律.结果表明:当热轧后冷却方式由油淬变为炉冷时,在冷轧压下量一定的条件下,退火组织中长条状铁素体的体积分数增加,且长轴/短轴比增大,而等轴铁素体的晶粒尺寸变化不明显;对于热轧后油淬试样,当冷轧压下量由50%增至75%时,退火组织中长条状铁素体的体积分数减少,铁素体的平均晶粒尺寸由400~500 nm减至300~400 nm.综合分析,增加热轧后的冷却速率,可在较小的冷轧压下量条件下获得一种综合性能良好的超细晶中锰TRIP钢,其性能指标为:屈服强度为976 MPa,抗拉强度为1 165 MPa,延伸率可达34.1%,强塑积接近40 GP·%.     

高强度非调质冷镦钢研究和开发现状

根据国内外高强度非调质冷镦钢的研究和开发现状,分析和讨论了800～1 200 MPa高强度非调质冷镦钢的化学成分、工艺特点、组织和力学性能。高强度非调质冷镦钢应具有高的强度和有良好的冷成形性,其热轧材的强度和硬度应控制在一个合适的范围内。采用低碳高锰及微合金化的成分系列,通过热机轧制工艺,该钢种能获得良好的组织和力学性能。     

钛微合金化HRB400E钢筋组织性能及强化机理

为系统研究含钛钢连续冷却相转变和强化机理,利用热模拟试验机、高分辨透射电镜及金相显微镜等设备进行试验。结果表明,低冷速下(0.5~1 ℃/s),组织主要为铁素体和珠光体;冷速逐步增加(1~5 ℃/s),贝氏体组织出现,且贝氏体比例逐渐增加;高冷速后(5~10 ℃/s),组织以贝氏体为主。含钛试验钢强化机制为析出强化和细晶强化。晶粒内部弥散析出10~20 nm的TiN。优化冷速为(1.5±0.5) ℃/s开展20 mm HRB400E钢筋工业试制,屈服强度不小于430 MPa,断后伸长率不小于20%,最大力总伸长率不小于15%,强屈比不小于1.4。