相变保温砂浆的制备及应用

制备出相变保温砂浆,并将之应用于建筑外墙保温体系中。通过对某高校1号教学楼和第二食堂的试点项目研究,证明本相变材料保温效果良好,通过与其他保温工程对比分析,确定利用该相变保温砂浆对建筑进行外墙保温,施工工艺简单,综合费用低廉,外墙涂层强度高,耐水性好,耐候性强。     

相变膨胀石墨制备保温砂浆的试验研究

以石蜡/膨胀石墨复合相变材料为功能组分,制备出具有蓄热调温功能的保温砂浆。利用SEM分析了复合相变材料的微观形貌,测试了相变保温砂浆的抗压强度、软化系数、导热系数和调温蓄热等技术性能。结果表明,随着相变膨胀石墨掺量的提高,砂浆28d抗压强度逐渐降低,软化系数则先增加后降低;热导率较高的膨胀石墨提高了石蜡的热交换效率,使保温砂浆具有较好的调温蓄热能力。     

砌块用保温砂浆的研制

针对普通砂浆导热系数大,易造成砌块建筑产生冷桥的问题,研制出一种新型的砌块用保温砂浆。文章讨论了水泥用量、集料、粉煤灰和引气剂对砂浆性能的影响。     

相变石蜡复合膨胀珍珠岩保温隔热干粉砂浆

采用膨胀珍珠岩为担载介质,相变石蜡为储能物质,以乳化法工艺实现了相变石蜡在膨胀珍珠岩中高效、稳定与大容量的担载,比较直接吸附法提高了3.5倍.并以此复合相变膨胀珍珠岩,制备了新型相变储能保温隔热干粉砂浆.以此干粉砂浆为原料,所研制的相变储能保温隔热材料具有比热容和蓄热系数大,导热系数较小的特点,同时相变石蜡在相变储能保温隔热板材中表现出优秀的工作稳定性能和防渗出稳定性能.     

膨胀珍珠岩保温砂浆导热系数实验研究

1　引　言青岛地区原有建筑外墙主要是以 2 4 0ｍｍ厚的砖墙为主 ,通过外墙的能耗占冬季供暖耗能的 4 0 %以上 ,占夏季空调耗能的 30 %以上。本文对采用膨胀珍珠岩砂浆用于外墙内保温或屋面外保温层的保温效果进行了实验研究。对不同配比、不同含水率、不同密度的膨胀珍珠岩保温砂浆进行导热系数的实验研究 ,并得出膨胀珍珠岩保温砂浆在不同条件下导热系数的关系式。2　试验装置采用防护热板法试验装置。它是根据大平壁一维稳态导热的原理测定单层平壁均质材料的导热系数。试验装置见图 1。3　试　件分别按水泥与膨胀珍珠岩体积比 1∶1 6、1…     

发泡保温砂浆的性能研究

以普通硅酸盐水泥为胶凝材料,以聚苯颗粒为轻质骨料,研究了聚苯颗粒保温砂浆的性能。针对其界面结合不好,内部结构松散的缺点,加入适量的发泡剂进行改善,并对其表干密度、抗压强度、导热系数等性能进行研究,确定最佳配比。利用扫描电镜对聚苯颗粒保温砂浆和发泡聚苯颗粒保温砂浆进行微观结构分析,探讨发泡剂的作用机理。     

玻化微珠保温砂浆的试验研究

通过玻化微珠保温砂浆的正交试验,分析了相关因素对玻化微珠保温砂浆的导热系数和抗压强度的影响规律,为玻化微珠保温砂浆的进一步改进提供了基础数据,以促进高性能保温绝热材料的研制开发与应用。     

FTC相变保温砂浆施工技术措施

论述了FTC相变保温砂浆在建筑施工中的主要问题和质量通病,分析了产生各种问题的原因,针对主要问题及通病提出了相应的施工技术措施,以保证工程的施工质量。     

粘结剂与EPS掺量对保温砂浆性能影响

主要研究废弃EPS颗粒制备的保温砂浆力学性能与导热性能,不同粘结剂种类对EPS保温砂浆抗压强度与导热系数的影响.通过掺入对不同量的EPS聚苯颗粒,得出EPS颗粒的掺量对保温砂浆的影响.     

相变控温砂浆用于改善建筑围护结构保温性能的研究

相变控温砂浆可以借助相变材料的相变潜热和热工性能来改善建筑围护结构的保温性能,以癸酸-月桂酸二元低共熔物/改性硅藻土定形相变材料为相变蓄热介质,采用共混搅拌法掺入水泥砂浆中,制成相变控温砂浆。利用FT-IR、DSC等测试了相变砂浆化学结构及热物性,并测试了相变控温砂浆的热工参数,通过实验模拟和DesignBuilder软件模拟研究了相变砂浆用作保温材料的建筑调温效果。     

Experimental study and assessment of thermal energy storage mortar with paraffin/recycled brick powder composite phase change materials

Thermal energy storage recycled powder mortar (TESRM) was developed in this study by incorporating paraffin/recycled brick powder (paraffin/BP) composite phase change materials (PCM). Fourier transform infrared and thermogravimetric analysis results showed that paraffin/BP composite PCM had good chemical and thermal stability. The onset melting temperature and latent heat of the composite PCM were 46.49 °C and 30.1 J·g⁻¹. The fresh mortar properties and hardened properties were also investigated in this study. Paraffin/BP composite PCM with replacement ratio of 0%, 10%, 20%, and 30% by weight of cement were studied. The results showed that the static and dynamic yield stresses of TESRM were 699.4% and 172.9% higher than those of normal mortar, respectively. The addition of paraffin/BP composite PCM had a positive impact on the mechanical properties of mortar at later ages, and could also reduce the dry shrinkage of mortar. The dry shrinkage of TESRM had a maximum reduction about 26.15% at 120 d. The thermal properties of TESRM were better than those of normal mortar. The thermal conductivity of TESRM was 36.3% less than that of normal mortar and the heating test results showed that TESRM had good thermal energy storage performance.     

聚合物干粉对新拌膨胀珍珠岩保温砂浆性能的影响

主要研究聚合物干粉改性膨胀珍珠岩保温砂浆加水搅拌后的性能。研究结果表明,聚合物干粉的种类和掺量对新拌砂浆的体积密度、稠度和含气量有不同程度的影响,其中纤维素醚和引气剂对新拌砂浆性能的影响较大,而乳胶粉和淀粉醚的影响较小。此外,新拌膨胀珍珠岩保温砂浆的体积密度和含气量对其导热系数有影响。     

石蜡／膨胀珍珠岩复合相变材料的制备

利用真空吸附法制备了石蜡／膨胀珍珠岩复合相变材料,此相变材料经过差示扫描量热仪、扫描电镜和扩散-渗出圈法测试,结果显示此相变材料具有调温功能,石蜡被吸附到膨胀珍珠岩孔道中并且分布均匀,性能稳定,可以应用到建筑材料中。     

复合保温浆料外墙外保温设计厚度的计算

针对外墙外保温工程中较为广泛使用的复合保温浆料,按照相关建筑节能设计标准的要求,以外墙平均传热系数为指标,阐述了保温层设计厚度的计算过程,可为复合保温浆料的工程设计和应用提供有价值的参考。     

掺三元乙丙橡胶粉水泥砂浆性能的试验研究和分析

系统研究三元乙丙橡胶粉以20%、40%、60%、80%和100%等体积取代河砂时对新拌砂浆和硬化砂浆性能的影响程度和规律。试验结果表明,适当掺量的橡胶粉,可以改善新拌砂浆的和易性,提高硬化砂浆适应变形的能力、早期抗裂能力、抗冻融循环耐久性、抗干湿循环耐久性,降低砂浆的表观密度和导热系数。但橡胶粉的掺入也会明显降低砂浆的力学性能和增加砂浆干缩变形值,并导致橡胶粉掺量增加到一定范围时,砂浆的抗裂能力、抗冻剥蚀能力和抗干湿循环能力降低。橡胶粉砂浆性能的缺陷需要优选其他外加剂来解决。     

低熔点石蜡微胶囊掺量对相变蓄热砂浆性能的影响

以低熔点石蜡微胶囊为相变储能材料,配以水泥、砂和外加剂制成低熔点石蜡微胶囊相变蓄热砂浆。研究了低熔点石蜡微胶囊掺量对相变蓄热砂浆施工性能、力学性能以及热工性能的影响,并进行了模拟上墙试验。结果表明,石蜡微胶囊掺量对相变蓄热砂浆的性能有着重要的影响,当其掺量在6.5%～10%时,其施工性能、力学性能和热工性能达到最佳;掺量为8%时,相变蓄热砂浆上墙无开裂,适宜于工程应用。     

相变石蜡复合膨胀珍珠岩的制备与表征

通过扫描电子显微镜(SEM)与差示扫描量热仪(DSC),采用真空吸附法对复合材料微观结构及热性能进行了研究。试验结果表明:经过吸附后,膨胀珍珠岩的所有微孔基本被石蜡填充;复合相变储能材料的相变焓相对于单一石蜡的相变焓有所降低;石蜡与膨胀珍珠岩复合的最佳质量比为3∶1。     

谈住宅外墙用水泥基复合保温砂浆的质量控制

结合工程实例,介绍了水泥基复合保温砂浆建筑保温系统构造和施工工艺,阐述了保温层的施工方法,并对其施工过程中的质量控制进行了论述,以保证施工质量。