汽车轻量化发展伴随着汽车弹簧使用强度的提高,从而对钢中夹杂物的要求也越高。通过分析典型的汽车弹簧对线材中夹杂物的要求,介绍了国外弹簧钢线材先进生产企业的冶炼工艺,综述了目前国内外关于弹簧钢中夹杂物的研究报道,可为国内弹簧钢线材生产企业开发或改进汽车用弹簧钢线材提供参考。     

宽厚板立轧非均匀塑性变形机制

摘要：为探索高碳硅镇静钢中失效夹杂物的检测方法,通过大量分析切割钢丝拉拔断口明确了失效夹杂物类型,同时利用失效指数验证金相观察法、电镜分析法、极值统计法、电解法、盘条拉伸法等评价夹杂物的有效性。结果表明,以帘线钢、切割钢丝用钢为代表的高洁净度高碳硅镇静钢,失效夹杂物以高铝夹杂物为主,尺寸集中在10～40μm。断口分析是失效夹杂物的最直接评价方法,但耗时长。金相制样法评价失效夹杂物往往与实物质量不符。有机溶物电解法可以用来分析冶炼过程高铝夹杂物变化,为失效夹杂物控制提供方向。未时效盘条拉伸实验,可快速检测出高碳钢盘条中大尺寸夹杂物。     

高碳钢C72DA线材质量影响因素分析与控制

介绍了化学成分、力学性能、偏析与索氏体比例、夹杂物、氧化与脱碳、几何尺寸和表面质量等因素对高碳钢C72DA线材产品质量的影响,与国内其他生产厂家对比分析了产品质量现状。结果表明:该盘条化学成分控制范围窄、抗拉强度波动小、组织偏析度小于等于2级、索氏体比例大于等于80%,大部分夹杂物大小在10 μm以下、100 mm2面积内数量小于等于130个、但存在大于3 μm的Al2O3脆性夹杂,表面光滑无缺陷、无脱碳层、氧化皮质量分数为02%、几何尺寸均一性好。产品完全满足胎圈钢丝、胶管钢丝企业的生产要求。     

Genetic Analysis for Large TiN Inclusions in Wire Rod for Tire Cord Steel of SWRH82A

The law of element segregation of Ti, N, Mn and S, and the sequence of selective precipitation of TiN and MnS inclusions during solidification of molten steel of SWRH82A are studied on the basis of thermodynamics. The origin of large TiN inclusions which affect the titanium inclusions point penalty in SWRH82A wire rod is analyzed based on the research on the distribution characteristics of MnS and large size of TiN inclusions observed on metallographic specimen of SWRH82A steel wire rod. The solidification segregation ratio of Ti is far more than that of N, and the solidification segregation ratio of S is far more than that of Mn. In the range of cooling rate of the continuous casting production, the cooling rate of solidification has little effect on the segregation ratios of Ti, N, Mn and S. MnS inclusions will precipitate earlier than TiN inclusions during solidification of the molten steel of SWRH82A. The large TiN inclusion which is wrapped by MnS in the SWRH82A wire rod may be foreign inclusions and it is not precipitated product during solidification in the molten steel of SWRH82A.     

气门弹簧及悬架弹簧用线材现状与发展方向

简述气门弹簧、悬架弹簧用线材使用现状,指出国内弹簧钢的不足及提高其强度的发展方向,对最先进的日本弹簧钢线材的生产工艺及实物质量进行了综述,为国内开发生产高质量弹簧钢线材提供参考。     

小方坯连铸连轧生产1 860 MPa级PC钢绞线用高碳热轧盘条的研究

通过对小方坯连铸连轧工艺的调整，有效控制了高碳热轧盘条的显微组织、纯净度、表面质量和成分偏析等，生产出了满足1860MPa级PC钢绞线用Ф13．0mm热轧盘条，使其抗拉强度高于1100MPa，断面收缩率大于35％，拉丝断丝率低于1．25次／100t。     

汽车发动机气门挺柱用16MnCr5冷镦钢盘条的研发与生产

汽车发动机气门挺柱用冷镦钢16MnCr5生产流程为80t 顶底复吹转炉→LF+RH精炼→325 mm×280 mmm大方坯连铸→高速线材轧制。通过采用碱度4.8的精炼渣（/%:54.5CaO,28.5Al₂O₃,11.2SiO₂,6.2MgO,0.6FeO+MnO）、取消钙处理工艺、铸坯表面淬火技术、精轧温度880～900℃、卷取温度850～870℃等工艺,成功开发出16MnCr5钢。检验结果表明,生产的Φ30 mm盘条金相组织为均匀的铁素体+珠光体,晶粒度8级,断面收缩率71.1%～72.5%,1/3冷镦合格;氧含量0.0010%～0.0012%,N含量0.0045%～0.0047%,夹杂物尺寸均在10μm以内,无Ds类夹杂,夹杂物类型主要为单一的镁铝尖晶石夹杂。盘条具有良好的塑性变形能力和较高的纯净度,满足了客户的要求。     

硬线钢用盘条中夹杂物的调查

通过采用扫描电镜对国内外4个钢厂硬线钢用盘条中的非金属氧化物夹杂的类型、形貌、尺寸和数量以及成分分析可知,国内外各厂家的钢帘线盘条中夹杂物的类型主要是CaO- SiO2- Al2O3- MgO- MnO,国外厂家较国内厂家盘条中非金属夹杂物的Al2O3质量分数低,SiO2质量分数高。且国外两厂中的夹杂物变形性能好,呈长条状,长宽比都大于3。应尽量减少单位面积的非金属夹杂物数量和尺寸,如先进的国外甲、乙两厂夹杂物数量的控制水平为0.111~0.154个/mm2,尺寸较小的夹杂物（小于3μm）的夹杂物数量相对国内厂家偏少。国外厂家的wT［O］和wN都控制在0.0035%以内。国外厂家控制水平相对较高,wT［O］和wN分别为0.0021%左右和0.0025%左右。     

��������LX80B������������������ѧ����

In order to find out the differences between domestic and imported LX80B steel wire rods, intrinsic quality and mechanical properties were studied by OM, SEM, EPMA, tensile testing machine and other instruments. The results show that the quantity of brittle non-metallic inclusions of domestic steel wire rods is 5 times as many as imported steel wire rods. The serious carbon segregation in domestic steel wire rods results in delamination fracture during twisting. The oxide scales of domestic and imported steel wire rods are composed of inner layer (Fe1-yO) and outer layer (Fe3O4), yet the thickness of oxide scale for domestic ones is smaller than that of imported ones. The microstructure of domestic ones is composed of proeutectoid cementite and pearlite, while that of imported ones is mainly pearlite. The large variation of lamellar spacing of pearlite results in a large variation of mechanical properties of domestic ones.     

高品质预应力制品用盘条质量稳定性的控制研究

以SWRH82B盘条为例,分析了影响高品质预应力制品用盘条质量稳定性的因素并提出了控制措施。认为盘条同卷同圈性能波动大,有异常组织和大颗粒非金属夹杂物是导致盘条拉拔断裂的主要原因。通过实施窄成分冶炼,降低铸坯碳偏析指数,优化LF精炼技术、连铸机钢包长水口套管,并在盘条输送辊道下方的风口增设佳灵装置等措施,提高了高品质预应力制品用盘条质量的稳定性。     

钢帘线盘条中夹杂物形态和成分的调查

通过对国内外5个钢厂所生产的钢帘线盘条中夹杂物形态和成分的对比分析,找出了国内钢厂在夹杂物形态和成分控制上与国外钢厂的差距,尤其是在夹杂物的塑性和尺寸两个方面.同时还对盘条中T.O、N和Als含量进行了对比,结果表明国外钢厂的控制效果要明显好于国内钢厂.     

轿车悬架簧用线材的市场需求与质量要求

根据国内轿车发展趋势,分析了国内轿车工业对悬架弹簧线材的市场需求,预测悬架簧用线材今后15年的需求量.介绍轿车悬架用弹簧的冶炼、轧制和制簧深加工方面的制造工艺过程及其对线材原料的尺寸精度、表面质量、力学性能、金相组织、脱碳等实物质量要求.研究表明,发展轿车用悬架簧线材具有广阔市场前景;高质量的线材是生产优质轿车悬架簧的基础,线材制造厂应不断提高我国轿车用弹簧钢的生产技术水平和原料供应质量.     

南钢转炉流程生产高品质帘线钢的实践

介绍了南钢第二炼钢厂帘线钢NLX82A盘条的工艺情况。通过转炉出钢硅锰复合脱氧、精炼造酸性渣、优化连铸二冷参数,有效控制了钢中非金属夹杂物的含量及塑性转变,缓解了连铸方坯碳偏析。结果表明,铸坯平均总氧质量分数为0.002%,氮质量分数控制在0.004%左右,钢中铝、钛质量分数均低于0.001%,显微夹杂物均符合标准要求,中心碳偏析指数控制在1.1以下,表面无脱碳层,氧化铁皮易于脱离。其综合质量通过了重点用户的专业测评,盘条拉至0.25 mm,经捻制合股后完全满足钢帘线使用要求。     

易切削钢盘条AG1215研制开发

介绍了安钢易切削钢盘条AG1215的研制开发。通过合理的转炉终点控制、精炼工艺、增硫措施、制定关键连铸、加热、轧制工艺技术措施,获得表面及低倍质量优良的铸坯,夹杂物控制达到预期控制目标,盘条各项性能符合用户要求。     

帘线钢质量影响因素及控制措施

主要阐述了帘线钢的质量要求。对影响钢中夹杂物的尺寸及形态、热轧线材的组织及表面质量、偏析程度的因素进行了分析，提出了有效控制夹杂物形态和降低偏析程度的技术措施。     

关于特殊钢生产流程持续优化的思考

中国特殊钢的发展面临前所未有的机遇和挑战,处于结构大调整期。针对行业的共性关注,以及近期特殊钢发展特点,以多尺度理论为基础,从冶金流程中的多尺度条件、多尺度顶层设计和界面技术等方面,特殊钢企业新建和改造流程出发,对特殊钢流程持续发展作了一些思考,应加快特殊钢棒线材、特殊钢板带、特殊钢无缝管、特殊钢锻材（件）的专业化、差异化流程建设,形成中国特殊钢企业自己的流程技术。同时,以国内某特冶锻造项目新建流程为例,从产品、规模、品质定位、工艺流程、关键装备技术等方面,介绍了高洁净度特冶锻造高品质、低成本、大规格生产示范流程的情况。     

帘线钢质量影响因素及控制措施

阐述了帘线钢的质量要求，并对影响帘线用钢质量的各种因素进行了分析：主要包括钢中夹杂物的尺寸、形态，热轧线材的组织及表面质量、偏析程度等：提出了有效控制夹杂物形态、降低偏析程度的技术措施。     

钢帘线用钢C82D2盘条拉拔断丝成因分析和工艺改进

分析结果表明,连铸坯中心偏析严重,易使盘条在拉拔时,产生杯锥状断裂;盘条中的非金属夹杂物,使盘条在拉拔和捻制变形时,因应力作用而造成钢丝断裂;钢中O、N含量过高,会使钢的强度和硬度升高,塑韧性下降.合理的吐丝温度和冷却速度,能保证盘条获得理想的细索氏体组织.通过控制[O]≤20×10-6,[N]≤40 × 10-6,连...     

钙处理对硅脱氧弹簧钢55SiCr氧化物夹杂的影响

摘要：为了将硅脱氧弹簧钢中SiO2类高熔点硬质夹杂改性成低熔点夹杂物,在炼钢生产中进行了钙处理试验。利用FEI Explorer 4自动扫描电镜对硅脱氧弹簧钢55SiCr在正常工艺与钙处理工艺处理后的铸坯、盘条中氧化物夹杂的成分、尺寸、数量、形貌进行检测,统计分析2种工艺下夹杂物尺寸、夹杂物轧制变形性的差异,并通过弹簧钢丝Nakamura旋转弯曲疲劳测试对比2种工艺下夹杂物控制水平。分析结果表明：硅脱氧弹簧钢55SiCr钙处理工艺后氧化物夹杂主要为CaO SiO2 (CaS)类,尺寸较大,且此类夹杂物在盘条轧制过程中不易变形细化,最终恶化弹簧钢疲劳性能;正常工艺处理后氧化物夹杂尺寸随着夹杂物中Ca含量升高有增大倾向,CaO SiO2 Al2O3系相图中方石英、磷石英与莫来石交界区的夹杂物轧制变形性优于假硅灰石和钙长石共熔区的夹杂物。     

宝钢高速线材硬线钢夹杂物处理技术探讨

概述了高碳硬线钢夹杂物处理的几种工艺情况,通过从钢坯取样,对夹杂物尺寸,组成和形态及钢坯中夹杂物总量进行分析测定,并对几种工艺处理夹杂物效果进行评价,其结果表明：常规真空处理及喷吹高碱度粉剂可满足一般要求高碳钢丝的生产要求,采用RH和Ca处理工艺,可提高高碳钢丝的疲劳寿命,对高碳钢丝中夹杂物进行无害化处理,可满足高品质的钢丝生产要求。