微反应器制备纳米硫酸钡研究

采用微反应器技术对硫酸钠和氯化钡为原料制备纳米硫酸钡进行了研究,考察了反应物浓度、流量、反应温度对产品颗粒粒径的影响.实验结果表明,随着反应浓度增加,随着流量增大,随着反应温度的降低,制得的硫酸钡粒子粒径减小.当温度低于60℃时,平均粒径随反应温度的变化缓慢;当反应物浓度为0.9 mol/L、流量为10 L/h、室温条件下制备硫酸钡颗粒平均粒径为32 nm,且粒度分布窄,纳米硫酸钡颗粒的形貌为椭球状.釜式搅拌反应器制得的硫酸钡粒径明显比用微反应器制得的硫酸钡大5～7倍.     

有机硅-丙烯酸酯弹性乳液的制备与研究

采用有机硅氧烷与丙烯酸酯单体共聚制备有机硅改性丙烯酸酯弹性乳液,研究了有机硅单体、乳化剂用量及配比等因素对乳液的影响,并对涂膜进行了兀'一IR表征.研究结果表明有机硅与丙烯酸酯单体能很好地聚合,且制备出的乳液性能优异,可以作为高性能外墙弹性涂料的基体树脂.     

核壳型苯乙烯-丙烯酸酯共聚乳液的制备研究

采用预乳化、半连续种子聚合法工艺,选用功能乳化剂,以丙烯酸丁酯、丙烯酸异辛酯、苯乙烯为主体,甲基丙烯酸缩水甘油酯、丙烯酸为交联单体,乙烯基三甲氧基硅烷为功能单体合成了一种具有核壳结构的交联苯丙乳液.以此配制低VOC内墙乳胶漆,重点讨论了乳化剂用量、单体配比的影响.     

溶胶-沉淀法疏水纳米二氧化硅的制备及其在硅橡胶中的应用

采用溶胶-沉淀法在醇介质中以氨催化水解正硅酸甲酯生成缩聚产物纳米二氧化硅,经六甲基二硅氮烷原位改性制备疏水纳米二氧化硅,并研究疏水纳米二氧化硅在甲基乙烯基硅橡胶中的补强效果.结果表明,在恒温20℃,水、六甲基二硅氮烷,氨水和正硅酸甲酯的摩尔比为3.55:0.65:0.36:1,表面活性剂与絮凝剂适量,搅拌反应时问为2 h,陈化时间为4 h的条件下,制备的疏水纳米二氧化硅比表面积大、平均粒径小、粒径分布窄,对甲基乙烯基硅橡胶补强效果好,并可使材料保持光学透明性.     

有机蒙脱土/BS乳液接枝改性制备粉末橡胶及在PVC中的应用

在丁苯（BS）乳液插层有机蒙脱土（OMT）过程中加入一定量的甲基丙烯酸甲酯（MMA）和二乙烯苯（DVB）进行反应制得接枝丁苯乳液（MMA—g—BS）,破乳后制得改性粉末丁苯胶（m-PSBR）,以质量分数为15％的OMT、25％MMA和1.2％DVB制得的m-PSBR粒径小于1mm．m—PSBR的热分解温度比粉末丁苯有明显提高。用该方法制得m—PSBR,用量为聚氯乙烯20％,共混制得m-PSBR／PVC复合材料,其拉伸强度比丁苯／OMT制得的粉末橡胶与聚氯乙烯的复合材料提高了25％、冲击强度提高了150％。     

定-转子反应器气液传质特性实验研究

采用氮气-水脱氧体系,在转子转速为300～1450 r·min-1、水流量为0.75～2.0 m3·h-1、氮气流量为1.5～4.0 m3·h-1的实验条件下,研究了定-转子反应器(RSR)的气液传质特性,初步考察了操作参数及结构参数对RSR气液传质性能的影响.实验结果表明:液体出口氧含量随转子转速(N)、气体流量(Gv)的增加而降低,随液体流量(GL)的增加而升高,液相体积传质系数(kxa) 随N,GL和GV的增加而增大.结构参数对定-转子反应器的气液传质特性具有显著的影响,定-转子反应器内部的转子层数越多,传质单元数NTU越大,传质效果越好.最后采用因次分析法推导出了定-转子反应器液相体积传质系数关联式,且进行了统计检验,所得关联式与实验数据拟合较好.     

乳状液膜包酶制备6-APA的研究

Production of 6-aminopenicillanic acid (6-APA) by hydrolysis using penicillin acylase (PA) was studied as a model of an enzymatic emulsion liquid membrane (ELM) process. The loss of PA activity was examined for various membrane compositions (organic solvent, surfactant, carrier). The effects of some experimental variables on the stability of emulsion were investigated. It was found that the choice of organic solvent greatly affected tilestability of the emulsion. Increasing the concentration of the carrier in the membrane phase increases the transfer rate of substrate and products but also has a destabilizing effect on the emulsion. The recovery of 6-APA obtained by a di-carrier system (N263-N1923) was much higher than those when either of the di-carriers was used separately.The whole process was controlled both by the enzymatic reaction rate and by the transfer rate of the substrate and the products, however, the ratio of them could be changed by varying the composition of the system. For an optimum condition, it was obtained that the recovery ratio of 6-APA was over 80% and the conversion of benzyl penicillin (PG) was up to 90% in the external phase after 30 minutes. Meanwhile, the breakage percentage of the emulsion was less than 2%.     

耐水性白乳胶的制备研究

以醋酸乙烯酯为主单体,聚乙烯醇为保护胶体,在适当比例下合成了稳定的白乳胶。该白乳胶的贮存稳定性好,但耐水性较差。通过加入共聚丙烯酸改性单体对白乳胶进行共聚改性,得到性能稳定、粘接力强的高耐水性白乳胶。     

陶瓷膜乳化系统制备单分散乳状液的研究--集成式膜乳化反应器的前期研究

A new reactor with integrated conventional slurry stirred reactor and ceramic external membrane emulsification system, was introduced in this paper. Toluene and toluene containing surfactant was separately used as dispersed phase for preparation of emulsions. Two kinds of emulsions were prepared and compared. The volume average sizes of prepared emulsions were 3.53μm and 3.6μm respectively. The results showed that the droplet sizes of two kinds of emulsions were similar, but the monodispersed emulsion was only obtained with addition of surfactant into the dispersed phase.     

不同内部结构定-转子反应器气液传质实验研究

采用氮气-水脱氧实验体系,在常温常压下、转子转速(N)为500～1450 r·min-1、水流量(L)为0.1～0.5 min3·h-1,气量(G)为0.2～1.0 m3·h-1的条件下考察了不同内部结构对定-转子反应器传质性能的影响,建立了液相体积传质系数关联式,计算结果与实验结果拟合较好.研究结果表明:不同的内部结构定.转子反应器内,液相体积传质系数KXa均随着液量、气量、转速的增大而增大,脱除率ε随着气量、转速的增加而增大,随着液量的增加而降低.但相比较而言,SS-RH和SC-RH这两种组合的定.转子反应器传质性能较好.     

乙烯基聚硅氧烷乳液的制备及性能研究

以十六烷基三甲基溴化铵(CTAB)和辛基酚聚氧乙烯醚(OP-10)为复合乳化剂、KOH为催化剂、八甲基环四硅氧烷(D<,4>)和四甲基四乙烯基环四硅氧烷(D<'Vi><,4>)为单体,制备了乙烯基聚硅氧烷乳液.考察了CTAB用量、CTAB与OP-10的质量比、聚合温度对乳液性能的影响,并对制备的聚硅氧烷进行了红外(IR)与热失重(TG)表征.结果表明,D<,4>与D<'Vi><,4>发生了共聚反应;当CTAB用量为单体质量的3.2%,CTAB与OP-10的质量比为1:6,聚合温度为80℃时,可制得单体转化率为88.5%、乳胶粒粒径为74.82 nm、机械、高温、稀释与电解质稳定性都较好的乙烯基聚硅氧烷乳液.热失重分析(TGA)表明,292℃以前乙烯基聚硅氧烷的质量损失率为17.2%,然后快速分解至442℃,乙烯基聚硅氧烷的质量损失率为97.2%.     

聚氨酯-聚丙烯酸酯复合乳液合成工艺的研究

采用种子乳液聚合法制备了聚氨酯-聚丙烯酸酯(PUA)复合乳液。比较了4种不同合成工艺对PUA复合乳液性能的影响。试验结果发现，单体中和合成工艺的PUA复合乳液的贮存稳定性、机械性能和耐水性好，具有工艺简单、污染小、成本低的特点。     

改性聚醋酸乙烯酯乳液的研制

以聚乙烯醇(PVA)为保护胶体,过硫酸铵(APS)为引发剂,叔碳酸乙烯酯(Veo Va10)、双丙酮丙烯酰胺(DAAM)为醋酸乙烯酯的共聚单体,当Veo Va10占单体总量的20%,DAAM占单体的2.0%时,合成出具有良好耐水性和粘接强度的聚醋酸乙烯酯乳液。     

有机硅改性丙烯酸酯接枝共聚乳液的研制

由乙烯基硅油采用接枝共聚法对丙烯酸酯乳液进行改性,合成了性能优良的硅丙乳液。讨论了引发剂、乳化剂、聚合反应温度及有机硅单体对乳液性能的影响。