Effect of alumina doping on structural, electrical, and optical properties of sputtered ZnO thin films

A systematic study of the influence of alumina (Al₂O₃) doping on the optical, electrical, and structural characteristics of sputtered ZnO thin films is reported in this study. The ZnO thin films were prepared on 1737F Corning glass substrates by R.F. magnetron sputtering from a ZnO target mixed with Al₂O₃ of 0-4 wt.%. X-ray diffraction (XRD) analysis demonstrates that the ZnO thin films with Al₂O₃ of 0-4 wt.% have a highly (002) preferred orientation with only one intense diffraction peak with a full width at half maximum (FWHM) less than 0.5°. The electrical properties of the Al₂O₃-doped ZnO thin films appear to be strongly dependent on the Al₂O₃ concentration. The resistivity of the films decreases from 74 Ω·cm to 2.2 × 10^− 3 Ω·cm as the Al₂O₃ content increases from 0 to 4 wt.%. The optical transmittance of the Al₂O₃-doped ZnO thin films is studied as a function of wavelength in the range 200-800 nm. It exhibits high transparency in the visible-NIR wavelength region with some interference fringes and sharp ultraviolet absorption edges. The optical bandgap of the Al₂O₃-doped ZnO thin films show a short-wavelength shift with increasing of Al₂O₃ content.     

Effects of substrate temperature on structural, electrical and optical properties of As-doped ZnO films

As-doped ZnO films were prepared by co-sputtering ZnO and Zn₃As₂ targets on glass substrates at various temperatures from 250 to 500 °C. The effects of substrate temperature on structural, electrical and optical properties of the films were investigated. The films grown at temperatures from 250 to 400 °C were c-axis oriented and those deposited above 400 °C exhibited poor crystallinity. Hall measurement showed that p-type ZnO:As films were prepared at different temperatures. With increasing the substrate temperature from 250 to 500 °C, the optical band gap (E_g) first decreased, and then increased. The E_g changes upon the substrate temperature were due to the effect of substrate temperature on the crystallinity of ZnO films.     

Influence of annealing temperature on structural,electrical and optical properties of undoped zinc oxide thin films

The undoped zinc oxide thin films were grown on quartz substrate at a substrate temperature of 750 °C by radio frequency magnetron sputtering and post annealed at different temperatures (600–800 °C) for a period of 30 min. The influence of annealing temperature on the structure, electrical and optical properties of undoped ZnO thin films was investigated by X-ray diffraction, Hall-effect, photoluminescence and optical transmission measurements. Results indicated that the electrical properties of the thin films were extremely sensitive to the annealing temperature and the conduction type could be changed dramatically from n-type to p-type, and finally changed to weak p-type when the temperature increased from 600 to 800 °C. Electrical and photoluminescence results indicate that native defects, such as oxygen and zinc vacancies, could play an important role in determining the conductivity of these nominally undoped ZnO thin films. The conversion of the conduction type was attributed to the competition between Zn vacancy acceptor and oxygen vacancy and interstitial Zn donors. At an intermediate annealing temperature of 750 °C, the film behaves the best p-type characteristic, which has the lowest resistivity of 12 Ωcm, hall mobility of 2.0 cm²/V s and carrier concentration of 1.5 × 10¹⁷ cm^?3. The photoluminescence results indicated that the Zn vacancy might be responsible for the intrinsic better p-type characteristic in ZnO thin films.     

Influence of substrate temperature on the structural,optical and electrical properties of ZnO thin films prepared by spray pyrolysis

The influence of substrate temperature on the structural, optical and electrical properties of ZnO films prepared by the spray pyrolysis method using aqueous solution of zinc acetate has been investigated. The films are polycrystalline and X-ray diffraction measurements show a strong preferred orientation along the [002] plane which is strongly dependent on the substrate temperature. Optical absorption spectra, show high transparency of the film (90–95% transmission) in the visible range, with a sharp absorption edge around 375 nm wavelength of light which closely corresponds to the intrinsic band gap of ZnO (3.3 eV). ZnO films with the lowest resistivity, which is due to the increased mobility resulting from the improvement of the crystallinity of the films, can be prepared at a substrate temperature of 490 °C.     

Effect of substrate temperature on structural, optical and electrical properties of ZnO thin films deposited by pulsed laser deposition

ZnO thin films were grown by the pulse laser deposition (PLD) method using Si (100) substrates at various substrate temperatures. The influence of the substrate temperature on the structural, optical, and electrical properties of the ZnO thin films was investigated. All of the thin films showed c-axis growth perpendicular to the substrate surface. At a substrate temperature of 500 °C, the ZnO thin film showed the highest (002) peak with a full width at half maximum (FWHM) of 0.39°. The X-ray Photoelectron Spectroscopy (XPS) study showed that Zn was in excess irrespective of the substrate temperature and that the thin film had a nearly stoichiometrical composition at a substrate temperature of 500 °C. The photoluminescence (PL) investigation showed that the narrowest UV FWHM of 15.8 nm and the largest ratio of the UV peak to the deep-level peak of 32.9 were observed at 500 °C. Hall effect measurement systems provided information about the carrier concentration, mobility and resistivity. At a substrate temperature of 500 °C, the Hall mobility was the value of 37.4 cm²/Vs with carrier concentration of 1.36 × 10¹⁸ cm⁻³ and resistivity of 2.08 × 10⁻¹ Ω cm.     

Effect of annealing temperature on structural, electrical and optical properties of B-N codoped ZnO thin films

The B-N codoped p-type ZnO thin films have been prepared by radio frequency magnetron sputtering using a mixture of nitrogen and oxygen as sputtering gas. The effect of annealing temperature on the structural, electrical and optical properties of B-N codoped films was investigated by using X-ray diffraction, Hall-effect, photoluminescence and optical transmission measurements. Results indicated that the electrical properties of the films were extremely sensitive to the annealing temperature and the conduction type could be changed dramatically from n-type to p-type, and finally changed to weak p-type in a range from 600 °C to 800 °C. The B-N codoped p-type ZnO film with good structural, electrical and optical properties can be obtained at an intermediate annealing temperature region (e.g., 650 °C). The codoped p-type ZnO had the lowest resistivity of 2.3 Ω cm, Hall mobility of 11 cm²/Vs and carrier concentration of 1.2 × 10¹⁷ cm^− 3.     

衬底和氧分压对Cu掺杂ZnO薄膜的结构及光学特性的影响

采用射频磁控溅射方法在玻璃和硅(100)衬底上制备了不同氧分压的Cu掺杂ZnO(ZnO∶Cu)薄膜。利用X射线衍射(XRD)、原子力显微镜(AFM)和光致荧光发光(PL)等表征技术,研究了衬底和氧分压对ZnO∶Cu薄膜的结晶性能和光学特性的影响。结果显示薄膜沉积在Si衬底上比玻璃衬底上有更好c轴择优取向,两种衬底上沉积的薄膜有相同的氧分压结晶规律,且在氧氩比为10∶10时,薄膜c轴取向同时达到最好。通过对光致发光的研究表明,在低氧环境时玻璃衬底较容易制得好的发光薄膜,可在富氧环境时Si衬底上制得的薄膜发光性能较好。     

Effect of Ga doping on micro/structural, electrical and optical properties of pulsed laser deposited ZnO thin films

Undoped and Ga doped ZnO thin films (1% GZO, 3% GZO and 5% GZO) were grown on c-Al₂O₃ substrates using the 1, 3 and 5 at. wt.% Ga doped ZnO targets by pulsed laser deposition. X-ray diffraction studies revealed that highly c-axis oriented, single phase, undoped and Ga doped ZnO thin films with wurtzite structure were deposited. Micro-Raman scattering analysis showed that Ga doping introduces defects in the host lattice. The E₂^High mode of ZnO in Ga doped ZnO thin film was observed to shift to higher wavenumber indicating the presence of residual compressive stress. Appearance of the normally Raman inactive B₁ modes (B₁^Low, 2B₁^Low and B₁^High) due to breaking of local translational symmetry, also indicated that defects were introduced into the host lattice due to Ga incorporation. Band gap of the Ga doped ZnO thin films was observed to shift to higher energy with the increase in doping concentration and is explicated by the Burstein-Moss effect. Electrical resistivity measurements of the undoped and GZO thin films in the temperature range 50 to 300 K revealed the metal to semiconductor transition for 3 and 5% GZO thin films.     

Effect of Ga doping concentrations,substrate temperatures and working pressures on the electrical and optical properties of ZnO thin films

We fabricated Ga-doped ZnO (GZO) thin films on glass substrate by RF magnetron sputtering method with different conditions of Ga₂O₃ concentration, substrate temperature and working pressure. Next we investigated the electrical, optical and structural properties of the GZO thin films. At a substrate temperature of 300 °C, a working pressure of 1 mTorr, and a Ga₂O₃ concentration of 3 wt%, the GZO thin films showed the lowest resistivity of 3.16 × 10^?4 Ω cm, a carrier concentration of 7.64 × 10²⁰ cm^?3 and a Hall mobility of 25.8 cm²/Vs. Moreover, the GZO thin films exhibited the highest (002) orientation under the same conditions and the full width at half maximum of X-ray peak was 0.34°. All GZO thin films showed the optical transmittance of more than 80 % in the visible range regardless of working conditions. The Burstein–Moss effect was observed by the change of doping concentration of Ga₂O₃. The GZO thin films were fabricated to have the good electrical and optical properties through optimizing doping concentration of Ga₂O₃, substrate temperature, working pressure. Therefore, we confirmed the possibility of application of GZO thin film as transparent conductive oxide used in flat panel display and solar cell.     

Effect of growth temperature on structural, electrical and optical properties of dual ion beam sputtered ZnO thin films

ZnO epitaxial thin films were grown on p-type Si(100) substrates by dual ion beam sputtering deposition system. The crystalline quality, surface morphology, optical and electrical properties of as-deposited ZnO thin films at different growth temperatures were studied. Substrate temperature was varied from 100 to 600 °C at constant oxygen percentage O₂/(O₂ + Ar) % of 66.67 % in a mixed gas of Ar and O₂ with constant chamber pressure of 2.75 × 10^?4 mBar. X-Ray diffraction analyses revealed that all the films had (002) preferred orientation. The minimum value of stress was reported to be ?0.32 × 10¹⁰ dyne/cm² from ZnO film grown at 200 °C. Photoluminescence measurements demonstrated sharp near-band-edge emission (NBE) was observed at ~375 nm along with deep level emission (DLE) in the visible spectral range at room temperature. The DLE Peak was found to have decrement as ZnO growth temperature was increased from 200 to 600 °C. The minimum FWHM of the NBE peak of 16.76 nm was achieved at 600 °C growth temperature. X-Ray photoelectron spectroscopy study revealed presence of oxygen interstitials and vacancies point defects in ZnO film grown at 400 °C. The ZnO thin film was found to be highly resistive when grown at 100 °C. The ZnO films were found to be n-type conducting with decreasing resistivity on increasing substrate temperature from 200 to 500 °C and again increased for film grown at 600 °C. Based on these studies a correlation between native point defects, optical and electrical properties has been established.     

The effect of substrate temperature on the structural,optical and electrical properties of vacuum deposited ZnTe thin films

The present paper reports the effect of substrate temperature on the structural, optical and electrical properties of vacuum deposited zinc telluride (ZnTe) thin films. X-ray diffraction (XRD) analysis of the films, deposited on glass substrates, revealed that they have cubic structure with strong (111) texture. Room temperature deposits are tellurium rich and an increase in the substrate temperature up to 553 °K results in stoichiometric films. Electrical conductivity has been observed to increase with the increase in substrate temperature, accompanied by increase in the carrier concentration and the mobility of the carriers. The optical bandgap energy and the thermal activation energy of the films have also been evaluated.     

The effect of substrate temperature on the structural, optical and electrical properties of vacuum deposited ZnTe thin films

The present paper reports the effect of substrate temperature on the structural, optical and electrical properties of vacuum deposited zinc telluride (ZnTe) thin films. X-ray diffraction (XRD) analysis of the films, deposited on glass substrates, revealed that they have cubic structure with strong (111) texture. Room temperature deposits are tellurium rich and an increase in the substrate temperature up to 553 °K results in stoichiometric films. Electrical conductivity has been observed to increase with the increase in substrate temperature, accompanied by increase in the carrier concentration and the mobility of the carriers. The optical bandgap energy and the thermal activation energy of the films have also been evaluated.     

Investigation of structural,optical, antibacterial,and dielectric properties of V-doped copper oxide thin films: Comparison with undoped copper oxide thin films

Vanadium doped Copper oxide (CO) thin films were prepared by the sol-gel dip-coating method. The properties of thin films were examined by X-Ray Diffractometer (XRD), UV–Visible-NIR spectrophotometry, and dielectric properties analyzer. The antibacterial and photocatalytic properties were also determined. XRD spectra revealed the dual-phase of copper oxide (cuprite and tenorite) for all percentages of V with no other impurity peak. Tauc's relation is used to probe the optical band gap which is reduced from 1.96 to 1.64 eV with an increase in vanadium doping percentage. The impurity band coalesces with the conduction band of copper oxide to decrease the band gap. Dielectric constant measurements reveal that the Ac conductivity of thin films increases with an increase in V doping percentage.     

Investigation of optical and electrical properties of ZnO thin films

Zinc oxide (ZnO) thin films were deposited on Si substrates using various working pressures by magnetron sputter. The resistivity of the deposited ZnO films decreases with working pressure, and the resistivity of 4.3 × 10⁻³ Ω cm can be obtained without post annealing. According to the optical transmittance measurements, the optical transmittance above 90% in the wavelength longer than 430 nm and about 80% in the wavelength of 380 nm can be found. Using time-resolved photoluminescence measurement, the carrier lifetime increases with working pressure due to the reduction of nonradiative recombination rate. The reduction of nonradiative recombination rate is originated from the decrease of oxygen vacancies in the ZnO films deposited at a higher working pressure. This result is verified by the photoluminescence measurements. Besides, by increasing the working pressure, the absorption coefficient was decreased and the associated optical energy gap of ZnO thin films was increased.     

Correlation between structural and electrical properties of ZnO thin films

Thin ZnO films were deposited by radio frequency (r.f.) and direct current (d.c.) magnetron sputtering techniques onto glass substrates. Microstructural and electrical properties of ZnO films were studied using X-ray diffractometer (XRD), scanning electron microscope (SEM) and resistivity measurements. It was found that the size of the crystallites in the d.c. deposited films increased with increasing film thickness, while the crystallite size of r.f. deposited films remained unchanged. The d.c. deposited grains also had much stronger orientation related to the substrate than the r.f. films. XRD data indicated that the thin films with d<350 nm for r.f. and <750 nm for d.c. films have a very high degree of ZnO nonstoichiometry. This agreed well with the conductivity measurements and R(T) behaviour of the films with different resistance R. It was also found that the electrical resistivity of the samples increased exponentially with the thickness of films.     

Influence of lithium doping on the structural and electrical characteristics of ZnO thin films

Thin films of undoped and lithium-doped Zinc oxide, (Zn_1 − xLi_x)O; x = 0, 0.05, 0.10 and 0.20 were prepared by sol-gel method using spin-coating technique on silicon substrates [(111)Pt/Ti/SiO₂/Si)]. The influence of lithium doping on the structural, electrical and microstructural characteristics have been investigated by means of X-ray diffraction, leakage current, piezoelectric measurements and scanning electron microscopy. The resistivity of the ZnO film is found to increase markedly with low levels (x ≤ 0.05) of lithium doping thereby enhancing their piezoelectric applications. The transverse piezoelectric coefficient, e₃₁^? has been determined for the thin films having the composition (Zn_0.95Li_0.05)O, to study their suitability for piezoelectric applications.     

Mg掺杂ZnO薄膜的结构及其光学性能研究

利用射频磁控溅射技术在(100)Si和玻璃衬底上沉积系列Mg掺杂ZnO(x=0~0.20)薄膜,XRD分析结果表明,Zn1-xMgxO薄膜均为六角纤锌矿结构,薄膜呈现出c轴择优生长特性,但随着x值的增加,晶格常数c逐渐减小。当x=0.20时,薄膜出现(100)面衍射峰,薄膜的c轴择优生长特性减弱。SEM分析表明,x=0.10时,薄膜表面平坦光滑,晶粒大小均匀,结构更加致密,结晶质量最佳。紫外可见光透射光谱表明,Mg的掺入提高薄膜在可见光范围内的透过率;同时增大了薄膜的禁带宽度;室温PL谱分析显示所有薄膜均出现了紫外发射峰和蓝光发射带,且紫外发射峰和蓝光发光带都随x值的增加而蓝移。     

Influence of thickness and growth temperature on the optical and electrical properties of ZnO thin films

Zinc oxide transparent conductive thin films were prepared using the pulsed laser deposition technique onto Corning glass substrates and the dependences of their optical and electrical properties on the thickness and the growth temperature were investigated. As shown, the films present 90% average transmittance, their energy gap position depending on the film thickness and the growth temperature. An additional absorption band was also observed near 3.44 eV, the position of its maximum also depending on the growth parameters. Finally, the electrical properties of the films were found to be affected mainly by the growth temperature and less by the thickness.