Effect of the delignification of wood fibers on the mechanical properties of wood fiber–polypropylene composites

The effect of the delignification of hornbeam fibers on the mechanical properties of wood fiber–polypropylene (PP) composites was studied. Original fibers and delignified fibers at three levels of delignification were mixed with PP at a weight ratio of 40:60 in an internal mixer. Maleic anhydride (0.5 wt %) as the coupling agent and dicumyl peroxide (0.1 wt %) as the initiator were applied. The produced composites were then hot‐pressed, and specimens for physical and mechanical testing were prepared. The results of the properties of the composite materials indicate that delignified fibers showed better performance in the enhancement of tensile strength and tensile modulus, whereas the hardness of the composites was unaffected by delignification. Delignified fibers also exhibited better water absorption resistance. Notched impact strength was higher for delignified fiber composites, but it was reduced at higher delignification levels. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 4759–4763, 2006     

Effect of oxidized polypropylene as a new compatibilizer on the water absorption and mechanical properties of wood flour–polypropylene composites

The effect of oxidized polypropylene (OPP) as new compatibilizer on the water absorption and mechanical properties of wood flour–polypropylene (PP) composites were studied and compared with maleic anhydride grafted polypropylene (MAPP). The oxidation of PP was performed in the molten state in the presence of air. Wood flour, PP, and the compatibilizers (OPP and MAPP) were mixed in an internal mixer at temperature of 190°C. The amorphous composites removed from the mixer were then pressed into plates that had a nominal thickness of 2 mm and nominal dimensions of 15 × 15 cm² with a laboratory hydraulic hot press at 190°C. Physical and mechanical tests showed that the wood flour–PP composites with OPP exhibited higher flexural and impact properties but lower water absorption than MAPP. All of the composites with 2% compatibilizers (OPP and MAPP) gave higher flexural and impact properties and lower water absorption compared to those with 4% compatibilizers. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Effect of the talc filler content on the mechanical properties of polypropylene composites

This research examines the effect of a microsize/nanosize talc filler on the physicochemical and mechanical properties of filled polypropylene (108MF10 and 33MBTU from Saudi Basic Industries Corp. and HE125MO grade from Borealis) composite matrices. A range of mechanical properties were measured [tensile properties, bending properties, fracture toughness, notched impact strength (at the ambient temperature and ?20°C), strain at break, and impact strength] along with microhardness testing and thermal stability testing from 40 to 600°C as measured by differential thermal analysis and thermogravimetric analysis. Increasing filler content lead to an increase in the mechanical strength of the composite material with a simultaneous decrease in the fracture toughness. The observed increase in tensile strength ranged from 15 to 25% (the maximum tensile strength at break was found to be 22 MPa). The increase in mechanical strength simultaneously led to a higher brittleness, which was reflected in a decrease in the mean impact strength from the initial 18 kJ/m² (for the virgin polypropylene sample) to 14 kJ/m², that is, a 23% decrease. A similar dependency was also obtained for the samples conditioned at ?20°C (a decrease of 12.5%). With increasing degree of filling of the talc–polypropylene composite matrix, the thermooxidative stability increased; the highest magnitude was obtained for the 20 wt % sample (decomposition temperature = 482°C, cf. 392°C for the virgin polymer). © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Processing and mechanical properties of organic filler–polypropylene composites

The addition of organic fillers into thermoplastic polymers is an interesting issue, which has had growing consideration and experimentation during the last years. It can give rise to several advantages. First, the cost of these fillers is usually very low. Also, the organic fillers are biodegradable (thus contributing to an improved environmental impact), and finally, some mechanical and thermomechanical properties can be enhanced. In this study, the effect of the addition of different organic fillers on the mechanical properties and processability of an extrusion‐grade polypropylene were investigated. The organic fillers came from natural sources (wood, kenaf, and sago) and were compared to short glass fibers, a widely used inorganic filler. The organic fillers caused enhancements in the rigidity and thermomechanical resistance of the matrix in a way that was rather similar to the one observed for the inorganic filler. A reduction in impact strength was observed for both types of fillers. The use of an adhesion promoter could improve their behavior. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 96: 1906–1913, 2005     

Maleic anhydride grafted polypropylene as a coupling agent for polypropylene composites filled with ink‐eliminated waste paper sludge flour

Ink‐eliminated sludge flour (IESF), a waste residue from the recycling treatment of waste paper, is a promising new kind of filler for thermoplastic polymers with a good price/performance ratio and advantages for environmental protection. In this study, high‐impact polypropylene (PP) and maleic anhydride grafted polypropylene (MAPP) were chosen as a polymer matrix and a coupling agent, respectively, for the preparation of IESF/PP composites, and the structures and properties of the obtained composites were also investigated. The experimental results revealed that IESF not only induced the crystallization orientation of PP along the b axis but also had a restraining effect on the formation of the β phase during the recrystallization of PP from the melt; the addition of MAPP further strengthened this effect to some extent. In addition, the proper addition of MAPP was helpful for improving the thermal stability of the IESF/PP composites. With the strengthening of the interfacial interaction between the IESF and PP matrix by MAPP, the resultant efficient stress transfer from the PP matrix to the IESF particles led to increased tensile and flexural strength. However, the original greater rigidity of MAPP, with respect to PP, reduced the toughness of the composites and caused some negative effects on the impact strength and the elongation at break. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 91: 2320–2325, 2004     

Effect of wood species on the mechanical and thermal properties of wood–plastic composites

The effect of wood species on the mechanical and thermal properties of wood–plastic composites (WPCs) was explored. Various wood species, including cherry, sweet gum, hickory, yellow poplar, Osage orange, walnut, eastern red cedar, pine, maple, and red oak, were compounded with virgin isotactic polypropylene in a 50 : 50 weight ratio and injection‐molded. The tensile strength of WPCs made with cedar and hickory was higher than that of WPCs made with maple, oak, and Osage orange. The tensile modulus of WPCs made with gum and walnut was higher than that of oak WPCs. The tan δ peak temperatures and peak values from dynamic mechanical analysis indicated that pine and hickory WPCs had higher amorphous or void contents than walnut and cherry WPCs. The induction time during isothermal crystallization suggested that red cedar, cherry, and gum WPCs had higher nucleation density than walnut, pine, and oak WPCs. Dynamic mechanical properties of the WPCs appeared to be related to the crystallization behavior of the wood flour, which depends on the surface roughness. Although there were statistically significant differences in mechanical properties among the species, the differences were small, implying that wood flours from many species can be used successfully as raw materials for WPCs. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Mechanical and thermal properties of talc and calcium carbonate filled polypropylene hybrid composites

The main aim of this work was to study and compare the mechanical and thermal properties of hybrid polypropylene (PP) composites and single‐filler PP composites. With two main types of mineral fillers—calcium carbonate (CaCO₃) and talc—PP composites of different filler weight ratios (talc/CaCO₃) were compounded with a twin‐screw extruder and then injection‐molded into dumbbell specimens with an injection‐molding machine. Tensile, flexural, and impact tests were performed to determine and compare the mechanical properties of the hybrid and single‐filler PP composites. A synergistic hybridization effect was successfully achieved; the flexural strength and impact strength were highest among the hybrids when the PP/talc/CaCO₃ weight ratio was 70:15:15. The nucleating ability of the fillers and its effects on the mechanical properties were also studied with differential scanning calorimetry. Because of the influence of talc as the main nucleating agent, the hybrid fillers showed significant improvements in terms of the nucleating ability, and this contributed to the increase in or retention of the mechanical properties of the hybrid composites. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 91: 3327–3336, 2004     

Comparison of the effects of polyethylenimine and maleated polypropylene coupling agents on the properties of cellulose‐reinforced polypropylene composites

The desire to improve the properties of cellulose‐reinforced composites while producing them by methods as similar as possible to those used on an industrial scale is one of the driving forces in this field of research. In this work, extensive research for determining the mechanical, thermal, rheological, and physical properties of novel cellulose‐reinforced polypropylene composites containing a polyethylenimine (PEI) coupling agent was conducted. A comparison of their properties with those of reference composites without any coupling agent or containing a maleated polypropylene (MAPP) coupling agent was also carried out. The presence of the PEI coupling agent mainly gave rise to a substantial increase in the tensile and flexural strengths and elongations as well as the impact strength, heat deflection temperature (HDT), melt volume flow index, and water absorption of PEI‐containing composites in comparison with composites without any coupling agent added. However, the increases achieved in the tensile and flexural composite strengths and HDT were lower than those achieved with the MAPP coupling agent mainly for composites containing 50 wt % cellulose fibers. On the other hand, PEI‐containing composites exhibited, in most cases, larger elongations and energies required to break in tensile tests as well as larger impact strengths, melt volume flow indices, and water absorption percentages than MAPP‐containing composites. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Effect of epolene E‐43 as a compatibilizer on the mechanical properties of palm fiber–poly(propylene) composites

Composites of palm fibers and poly(propylene) (PP) were compounded in an extruder at 200°C. The composites were subsequently injection molded into standard tensile specimens for mechanical characterization. The fracture morphology of the specimens was analyzed by scanning electron microscopy. It was observed that the composite modulus increased with the increase of fiber content, indicating the existence of adhesion between PP and the much stiffer palm fibers. However, the adhesion was not satisfactory and resulted in a decrease in the composite tensile strength with fiber addition. The compatibilizer Epolene E‐43 was used to minimize this incompatibility between the wood fibers and the PP matrix. The maleated PP additive enhanced the fiber–matrix adhesion, resulting in an improvement in composite performance. Also, small fibers showed better mechanical properties than those of long fibers. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 92: 2581–2592, 2004     

Crosslinkable polypropylene composites made by the introduction of silane moieties

Silane‐crosslinkable polypropylene (PP) composites containing calcium carbonate (CaCO₃) as a filler have been investigated. The melt grafting of vinyl trimethoxysilane to PP with dicumyl peroxide (DCP) as a radical initiator is demonstrated. The thermal and mechanical properties of the crosslinkable products are also discussed. The results show that two reactions, that is, silane grafting and PP degradation, take place in parallel. The extents of silane grafting and PP degradation strongly depend on the reaction temperature, grafting formulation, and amount of the filler in the systems. Increasing the DCP concentration (up to 0.05 wt %) leads to an increase in the grafting degree. However, when the concentration of radicals is over a certain degree, the dominant reaction is PP chain scission. This results in a drastic decrease in the polymer viscosity. In systems containing both silane and CaCO₃, the viscosity of the polymer is higher than that of a grafted sample without CaCO₃ addition; in other words, the effect of the filler on the polymer viscosity compensates for the effect caused by PP degradation. Differential scanning calorimetry results show that the crystallization starts earlier for grafted samples. The percentage of the crystallinity of grafted PP is higher than that of the pure polymer. The incorporated silane does not have a strong effect on the mobility of the PP chains, as revealed by dynamic mechanical analysis. In comparison with ungrafted composites, the silane‐crosslinkable products show higher tensile stress and modulus. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 97: 1476–1483, 2005     

Effects of wheat straw fiber content and characteristics,and coupling agent concentration on the mechanical properties of wheat straw fiber‐polypropylene composites

Wheat straw fiber‐polypropylene (PP) composites were prepared to investigate the effects of wheat straw fiber content (10, 20, 30, 40, and 50 wt %), fiber size (9, 28, and 35 mesh), and maleic anhydride grafted polypropylene (MAPP) concentration (1, 2, 5, and 10 wt %) on the static and dynamic mechanical properties of the wheat straw fiber‐PP composites in this study. The tensile modulus and strength of the composites increased linearly with increasing wheat straw fiber content up to 40%, whereas the elongation at break decreased dramatically to 3.78%. Compared with the composites made of the longer wheat straw fiber, the composites made of the fines (>35 mesh) had a slightly higher tensile strength of 31.2 MPa and tensile elongation of 5.39% at break. With increasing MAPP concentration, the composites showed an increase in tensile strength, and the highest tensile strength of 34.0 MPa occurred when the MAPP concentration reached 10 wt %. As wheat straw fiber content increased from 0 to 40%, the flexural modulus of the composites increased gradually from 1335 to 3437 MPa. The MAPP concentration and wheat straw fiber size distribution had no appreciable effect on the static flexural modulus of the composites. The storage flexural modulus of the composites increased with increasing wheat straw fiber content. The scanning electron microscopy (SEM) observation on the fracture surface of the composites indicated that a high wheat straw fiber content (>30 wt %) resulted in fiber agglomeration and a reduction in interfacial bonding strength. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Effect of chemical treatments on the mechanical,flow, and morphological properties of talc‐ and kaolin‐filled polypropylene hybrid composites

This study was performed with commercially available phenyl trimethoxysilane (PTMS) and neoalkoxytitanate [i.e., neopentyl(diallyl)oxytri(dioctyl)phosphato titanate (LICA 12)] as coupling agents. PTMS and LICA 12 were used to treat talc and kaolin to compare their effects with untreated fillers upon incorporation into polypropylene (PP). Single‐filler PP composites (containing either talc or kaolin) and hybrid‐filler composites (containing a mix of both talc and kaolin) were compounded in a twin‐screw extruder and subsequently injection‐molded into dumbbells. The incorporation of PTMS and LICA 12 slightly decreased the tensile and flexural properties in terms of modulus and strength but increased the elongation at break for both single‐filler and hybrid‐filler composites. There was also a significant improvement in the impact strength of the composites, particularly those treated with LICA 12. The hybrid composites, through the synergistic coalescence of positive characteristics from talc and kaolin with the aid from chemical treatment provided an economically advantageous material with mechanical properties comparable to those of the single‐filler‐filled PP composites. Further investigations on flow and morphological properties were also done to correlate the mechanical properties of the single‐ and hybrid‐filler‐filled PP composites. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Comparison of the mechanical properties and interfacial interactions between talc,kaolin, and calcium carbonate filled polypropylene composites

Three types of mineral fillers—talc, calcium carbonate (CaCO₃), and kaolin (10–40 wt % filler loadings)—were compounded with polypropylene (PP) with a twin‐screw extruder. The composites were injection‐molded, and the effects of the filler loading on the mechanical, flow, and thermal properties for the three different types of filled composites were investigated. The aim was to compare their properties and to deduce prospective filler combinations that would yield hybrid PP composites in following studies. The results showed that in most cases, the strength and stiffness of the talc‐filled PP composites was significantly higher than those of the CaCO₃‐ and kaolin‐filled PP composites. However, CaCO₃, being a nonreactive filler, increased the toughness of PP. The kaolin‐filled PP composites also showed some improvement in terms of strength and stiffness, although the increases in these properties were not as significant as those of the talc‐filled PP composites. The effects of interfacial interactions between the fillers and PP on the mechanical properties were also evaluated with semiempirical equations. The nucleating ability of all three fillers was studied with differential scanning calorimetry, and the strongest nucleating agent of the three was talc, followed by CaCO₃ and kaolin. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 91: 3315–3326, 2004     

Deformation mechanism of polypropylene composites filled with magnesium hydroxide

The fracture behavior and deformation mechanism of polypropylene (PP) composites filled with magnesium hydroxide [Mg(OH)₂] were investigated. The incorporation of Mg(OH)₂ particles into the PP matrix led to an increase in Young's modulus and a significant reduction in the tensile yield strength and elongation at break. Surface modification on filler particles with stearic acid could reduce the interfacial adhesion between the filler and PP matrix and improve the stress transferability. The deformation mechanism of the Mg(OH)₂/PP composites depended on the interfacial adhesion and the deformability of ligaments between microvoids caused by debonding. The deformability of the ligaments could be significantly improved by surface modification on the particle surface. The dependence of the deformation behavior of the Mg(OH)₂/PP composites on the filler content was in accordance with percolation theory. The agglomeration of microvoids and fibrillation of ligaments in the PP composites with excessive filler content indicated the weak resistance of the polymer matrix to crack propagation and premature fracture in a brittle manner. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 97: 1922–1930, 2005     

Effect of maleic anhydride grafted polypropylene on the mechanical and morphological properties of chemically modified short‐pineapple‐leaf‐fiber‐reinforced polypropylene composites

With the rising cost of petroleum‐based fibers, the utilization of plant fibers in the manufacture of polymer–matrix composites is gaining importance worldwide. The scope of this study was to examine the perspective of the use of pineapple leaf fibers (PALFs) as reinforcements for polypropylene (PP). These fibers are environmentally friendly, low‐cost byproducts of pineapple cultivation and are readily available in the northeastern region of India. Here, both untreated and treated pineapple fibers were used. Maleic anhydride grafted polypropylene (MA‐g‐PP) was used as a compatibilizing agent. The polymer matrix of PP was used to prepare composite specimens with different volume fractions (5–20%) of fibers by the addition of 5% of MA‐g‐PP. These specimens were tested for their mechanical properties, and additional assessments were made via observations by scanning electron microscopy, thermogravimetric analysis, and IR spectroscopy. Increase in the impact behavior, flexural properties, and tensile moduli of the composites were noticed, and these were more appreciable in the treated fibers mixed with MA‐g‐PP. PALF in 10 vol % in PP mixed with MA‐g‐PP was the optimum and recommended composition, where the flexural properties were the maximum. The impact strength and the tensile modulus were also considerably high. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Effect of the polymer microstructure on the behavior of syndiotactic polypropylene/organophilic layered silicate composites

Syndiotactic polypropylenes (sPPs) with several microstructures (i.e., syndiotacticities and molecular weights) and synthesized by means of two metallocenic catalysts were melt‐blended with 1 and 3 wt % organophilic layered silicates in the presence of a compatibilizer. X‐ray diffraction and transmission electron microscopy analysis showed that the clay was well dispersed in the composites, although the filler morphology depended on the polymer microstructure. Polypropylenes with low syndiotacticities and molecular weights presented the best clay dispersion. Nonisothermal differential scanning calorimetry analysis showed that the polymer microstructure and the clay content modified the thermal behavior of the composites. The compatibilizer and the clay acted as nucleant agents to increase the crystallization temperature of the matrix. Moreover, the double endothermic peak observed during heating scan and associated with the melt/recrystallization/remelt processes of the pure polymer matrix was reduced in the composites. With regard to the mechanical properties under tensile conditions, a synergic effect of the compatibilizer and the clay was observed. In particular, the addition of the compatibilizer alone was able to increase by about 20% the elastic modulus relative to the neat samples, whereas increases between 35 and 50% were measured when the clay was also added, depending on the polymer microstructure. Our results show that the microstructure of sPPs had strong effects on the behavior of its composites with clay in the presence of a compatibilizer. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

New hyperdispersant agent for polypropylene/CaSO4 composites

A new hyperdispersant agent with Si? OH as an anchoring group and poly(butyl acrylate) as a solvatable chain was synthesized, and its effect on the properties of polypropylene (PP)/CaSO₄ composites was investigated. Fourier transform infrared spectroscopy results showed that the hyperdispersant agent reacted on the CaSO₄ surface and the modified CaSO₄ particles. The tensile strength and impact strength of the PP/CaSO₄ composites increased about 14 and 34%, respectively, versus that of PP/CaSO₄ (filled with the same unmodified fraction). According to surface analysis by scanning electron microscopy, the CaSO₄ particles were buried well in the PP matrix when CaSO₄ was coated with the hyperdispersant agent. CaSO₄ significantly increased the crystallization temperature and crystallization rate of PP by differential scanning calorimetry, but the addition of hyperdispersant‐agent‐modified CaSO₄ did not lead to the formation of crystalline PP through X‐ray diffraction. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Influence of the zeolite type on the mechanical–thermal properties and volatile organic compound emissions of natural‐flour‐filled polypropylene hybrid composites

The physicomechanical properties, thermal properties, odor, and volatile organic compound (VOC) emissions of natural‐flour‐filled polypropylene (PP) composites were investigated as a function of the zeolite type and content. The surface area and pore structure of the natural and synthetic zeolites were determined by surface area analysis and scanning electron microscopy, respectively. With increasing natural and synthetic zeolite content, the tensile and flexural strengths of the hybrid composites were not significantly changed, whereas the water absorption was slightly increased. The thermal stability and degradation temperature of the hybrid composites were slightly increased with increasing natural and synthetic zeolite content. At natural and synthetic zeolite contents of 3%, the various odors and VOC emissions of the polypropylene/rice husk flour and polypropylene/wood flour hybrid composites were significantly reduced because of the absorption of the odor and VOC materials in the pore structures of the natural and synthetic zeolites. These results suggest that the addition of natural and synthetic zeolites to natural‐flour‐filled thermoplastic polymer composites is an effective method of reducing their odor and VOC emissions without any degradation of their mechanical and thermal properties. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Flammability and mechanical properties of wood flour‐filled polypropylene composites

Polypropylene (PP) composites filled with wood flour (WF) were prepared with a twin‐screw extruder and an injection‐molding machine. Three types of ecologically friendly flame retardants (FRs) based on ammonium polyphosphate were used to improve the FR properties of the composites. The flame retardancy of the PP/WF composites was characterized with thermogravimetric analysis (TGA), vertical burn testing (UL94‐V), and limiting oxygen index (LOI) measurements. The TGA data showed that all three types of FRs could enhance the thermal stability of the PP/WF/FR systems at high temperatures and effectively increase the char residue formation. The FRs could effectively reduce the flammability of the PP/WF/FR composites by achieving V‐0 UL94‐V classification. The increased LOI also showed that the flammability of the PP/WF/FR composites was reduced with the addition of FRs. The mechanical property study revealed that, with the incorporation of FRs, the tensile strength and flexural strength were decreased, but the tensile and flexural moduli were increased in all cases. The presence of maleic anhydride grafted polypropylene (MAPP) resulted in an improvement of the filler–matrix bonding between the WF/intumescent FR and PP, and this consequently enhanced the overall mechanical properties of the composites. Morphological studies carried out with scanning electron microscopy revealed clear evidence that the adhesion at the interfacial region was enhanced with the addition of MAPP to the PP/WF/FR composites. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Synthesis of a maleic anhydride grafted polypropylene–butadiene copolymer and its application in polypropylene/styrene–butadiene–styrene triblock copolymer/organophilic montmorillonite composites as a compatibilizer

A maleic anhydride grafted propylene–butadiene copolymer (MPPB) was prepared. Fourier transform infrared spectroscopy and ¹H‐NMR results indicate that the maleic anhydride molecules reacted with the double bond in the butadiene unit of the propylene–butadiene copolymer (PPB), and the grafting percentage increased with the butadiene content in the initial copolymer. The gel permeation chromatography results show that the introduction of butadiene in the copolymer prevented the degradation of PPB. The MPPB was applied in polypropylene (PP)/styrene‐butadiene‐styrene triblock copolymer (SBS)/organophilic montmorillonite (OMMT) composites as a compatibilizer. In the presence of 10‐phr MPPB, the impact strength of the composite was improved by about 20%. X‐ray diffraction patterns indicated the formation of the β‐phase crystallization of PP in the presence of MPPB, and a significant decrease in the spherulite size was observed. Transmission electron microscopy (TEM) images showed that the OMMT was better dispersed in the matrix upon the inclusion of MPPB. A better distribution of the rubber phase and a rugged fracture surface were observed in the scanning electron microscopy images as the MPPB proportion was increased. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009