P(BA-g-MMA)/纳米蒙脱土复合粒子的制备及其增韧PVC的研究

采用种子乳液聚合法制备了纳米蒙脱土(MMT)改性聚丙烯酸丁酯甲基丙烯酸甲酯核壳接枝共聚物P(BA-g-MMA)增韧剂并用于增韧聚氯乙烯（PVC）树脂,分析了MMT含量对共混物力学性能的影响,用X射线衍射仪、扫描电子显微镜观察了蒙脱土的插层和分散效果。结果表明,丙烯酸丁酯(BA)单体在MMT层间发生聚合反应,使MMT层间距由1.25 nm增大至1.5 nm;当P(BA-g-MMA)核壳比(BA∶MMA)为85∶15,100 份（质量份,下同） PVC中加入9份P(BA-g-MMA)时,PVC/P(BA-g-MMA)共混物冲击强度为1106 J/m,是典型的韧性断裂,综合性能好。     

聚丙烯／BA原佐聚合改性MMT纳米复合材料的DSC分析与力学性能

通过原位聚合制备了聚丙烯酸丁酯(PBA)改性蒙脱土(MMT)，与聚丙烯(PP)熔融复合制成P／MMT纳米复合材料，系统地研究了复合材料的熔融、结品行为和力学性能。结果表明：随着处理MMT的BA用量的增加，PP／MMT纳米复合材料中PP相的结晶度、熔点和结晶温度明显提高，结晶速度加快；复合材料的拉伸强度变化不大，但拉伸横量和冲击强度有显著提高。当BA／0MMT质量比为1／12左右时，复合材料的韧性趋于平衡值，而拉伸横量出现最大值。     

蒙脱土对sPS/PET复合材料性能的影响

以蒙脱土(MMT)为增强刺、磺化间规聚苯乙烯锌盐(SsPS-Zn)为增容剂来改性间规聚苯乙烯(sPS)／聚对苯二甲酸乙二酯(PET)复合材料,复合材料的综合力学性能和耐热性较未填充MMT时显著提高。当MMT用量为2份时,复合材料的冲击强度达到最大值14．7kJ／m^2,约是纯sPS的3．5倍,约是未加入MMT时的1．5倍,而拉伸强度和弯曲强度同时也相应提高了约30MPa。材料发生较大形变的终止温度比未加入MMT时提高了20℃以上,形变量减小,起始粘流温度提高了10℃以上。动态热机械分析结果表明,加入MMT后复合材料的玻璃化转变温度提高。     

MMA-BA自由基共聚物的结构及性能

采用本体聚合法制备了甲基丙烯酸甲酯(MMA)/丙烯酸丁酯(BA)无规共聚物，考察了引发剂、单体配比对聚合物材料力学、光学及其他性能的影响。借助氢谱核磁共振、动态力学分析、扫描电子显微镜对共聚物的结构和性能进行了表征分析。结果表明，随着BA含量的增加，共聚物的损耗模量降低，链段的内摩擦阻力减小，链段运动能力加强；当MMA/BA质量比为75/25时，材料的冲击强度提高了43 %，同时透光率保持在92 %以上。     

多单体固相接枝共聚物对废聚丙烯/稻糠复合体系结构与性能的影响

用固相接枝法接枝合成了聚丙烯(PP)与甲基丙烯酸甲酯(MMA)／马来酸酐(MAH)／丙烯酸丁酯(BA)的多单体接枝共聚物(GPP)，将其应用于废聚丙烯(RPP)／稻糠(RC)复合体系，研究了接枝共聚物对体系的力学性能、微观形态、热性能的影响。结果表明，在RPP／RC复合体系中加入固相接枝共聚物，可有效提高复合材料的拉伸强度、弯曲强度、弯曲模量和维卡软化点。     

PVC／木粉复合材料抗冲改性研究

用甲基丙烯酸、丙烯酸丁酯、甲基丙烯酸甲酯三元共聚物P（MAA—BA—MMA）对木粉进行预处理,再利用CPE、ACR和nano—CaCO3对PVC／木粉复合材料进行增韧改性。结果表明,木粉经P（MAA—BA—MMA）预处理后,使用ACR增韧时效果最好,其拉伸强度、弯曲强度、冲击强度和断裂伸长率分别提高了7．97％、5．26％、68．85％和571．26％。SEM结果表明,木粉预处理后再增韧,复合材料界面模糊,断面呈一定的韧性断裂特征。     

聚丙烯/BA原位聚合改性MMT纳米复合材料的DSC分析与力学性能

通过原位聚合制备了聚丙烯酸丁酯 (PBA )改性蒙脱土 (MMT ) ,与聚丙烯 (PP)熔融复合制成PP/MMT纳米复合材料 ,系统地研究了复合材料的熔融、结晶行为和力学性能。结果表明 :随着处理MMT的BA用量的增加 ,PP/MMT纳米复合材料中PP相的结晶度、熔点和结晶温度明显提高 ,结晶速度加快 ;复合材料的拉伸强度变化不大 ,但拉伸模量和冲击强度有显著提高。当BA/OMMT质量比为 1/ 12左右时 ,复合材料的韧性趋于平衡值 ,而拉伸模量出现最大值     

BADCy/MMA半互穿网络的制备及性能表征

在加热熔融的氰酸酯树脂(BADCy)中加入甲基丙烯酸甲酯(MMA)单体(同步合成法)或MMA预聚体(异步合成法)并引发使其发生本体聚合,制备了具有半互穿聚合物网络结构的氰酸酯树脂/聚甲基丙烯酸甲酯(BADCy/MMA-SIPN),通过力学性能测试,红外及DSC分析研究了MMA含量对体系力学性能和热性能的影响。结果表明,互穿网絡的形成使氰酸酯树脂体系的力学性能和耐热性能都有较大的提高,冲击强度、弯曲强度及玻璃化温度分别提高了97.8%、58.6%和65℃。     

聚合后期加入纳米复合材料制备改性PVC树脂

在纳米水滑石（HT）表面共聚适量的丙烯酸六氟丁酯（HfA）和甲基丙烯酸甲酯（MMA）,制得HfA／MMA／HT纳米复合材料（以下简称纳米复合材料）,并对纳米复合材料的组成进行了优化;还研究了VCM聚合时纳米复合材料的用量对试样热稳定性和抑烟性能的影响。结果表明：①不同HfA、MMA含量的纳米复合材料均能提高试样的冲击强...     

PP/MMT复合材料的制备与性能研究

以聚丙烯(PP)回收料为基体,改性蒙脱土(MMT)为填充剂,通过熔融共混的方法制备了PP/MMT复合材料,探讨了MMT用量对PP/MMT复合材料的热行为、机械性能及流动性能的影响。结果表明:少量MMT的加入可明显提高复合材料的力学性能,其拉伸强度提高26%,断裂伸长率提高520%,冲击强度提高11%。MMT的加入可提高复合材料的结晶温度,但对其熔点的影响不大;随着MMT的添加,PP/MMT复合材料的流动性能得到了很好的改善,当MMT的含量为1 wt%时,其熔融指数达到最大值,体系的粘度变小。     

Properties of na‐montmorillonite and cellulose nanocrystal reinforced poly(butyl acrylate‐co‐methyl methacrylate) nanocomposites

Poly(butyl acrylate‐co‐methyl methacrylate) (BA‐co‐MMA) nanocomposite latexes were synthesized in the presence of sodium montmorillonite (Na‐MMT) and cellulose nanocrystal (CNC) as fillers. Nanocomposite preparation with 3 wt% Na‐MMT based upon the total monomer amount was conducted by semi‐batch emulsion polymerization. Furthermore, direct blending of neat copolymer latex with Na‐MMT was performed for comparison. CNC/BA‐co‐MMA nanocomposites were obtained via blending process with varying CNC content (1, 2, and 3 wt %). Good dispersion of both Na‐MMT and CNC within the copolymer matrix was achieved as demonstrated by X‐ray diffraction and transmission electron microscope. Particle size of the nanocomposite latexes was around 120 nm. Thermal, mechanical, and barrier properties of the copolymer showed great improvement with the addition of both Na‐MMT and CNC. CNC nanocomposites displayed enhanced properties with increasing CNC level. Tensile strength of copolymer latex with 3 wt% CNC reached 262.5% of the pristine latex, while tensile strength of Na‐MMT nanocomposite at the same content was 187.5% of the pristine latex. POLYM. ENG. SCI., 55:2922–2928, 2015. © 2015 Society of Plastics Engineers     

高固含量苯丙微乳液的制备与性能研究

以苯乙烯(St)、甲基丙烯酸甲酯(MMA)和丙烯酸丁酯(BA)为共聚单体,丙烯酸(AA)为功能单体,反应型乳化剂(DNS-86)、十二烷基硫酸钠(SDS)和壬基酚醚磺基琥珀酸酯钠盐(OS)为复合乳化剂,采用种子乳液聚合法制备了粒径小、耐水性好且固含量为50%的苯丙微乳液。研究结果表明:当w(引发剂)=0.7%、m(MMA+St)∶m(BA)∶m(AA)=5.0∶4.7∶0.3、w(St)=15%~25%、m(DNS-86)∶m(SDS+OS)=3∶2且w(复合乳化剂)=5%时,高固含量苯丙微乳液的综合性能良好。     

Novel method to measure the shear strength of exfoliated montmorillonite/polymer nanocomposite films

Shear fracture of exfoliated montmorillonite/poly(methyl acrylate‐co‐methyl methacrylate) (MMT/P(MA‐co‐MMA)) nanocomposite films fabricated via soap‐free emulsion polymerization was studied using a unique test fixture that is capable of controlling the inclined angle between the loading axis and the shear fracture plane. It was found that fracture of the films depended on both shear and normal stresses and could be described by the Mohr–Coulomb criterion. The effects of MMT content on the intrinsic shear strength (i.e. the shear strength at zero normal stress) τ_s were also examined. The obtained τ_s increased from 1.66 to 2.78 MPa as 1 wt% MMT was incorporated into P(MA‐co‐MMA) and then increased almost linearly to 5.32 MPa when the content of MMT increased to 15 wt%. Also, the fracture‐surface morphology of the composite film depended on both the MMT content and the inclined angle (and hence the normal‐to‐shear stress ratio). For low MMT contents and low normal‐to‐shear stress ratios, striations normal to the shear direction appeared on the fracture surface. As the MMT content or the stress ratio increased, the fracture surface became rough accompanied by the presence of interfacial micro‐cracking between MMT nanoplatelets and the matrix. With further increase in MMT content and high stress ratio, the MMT nanoplatelets were compressed into large flakes on the fracture surface. Copyright © 2011 Society of Chemical Industry     

PDCPD/PS/MMT纳米复合材料的制备与性能研究

采用反应注射成型工艺,使用钨系双组分催化剂WCl6/Et2AlCl进行双环戊二烯单体原位聚合反应,制备出聚双环戊二烯/聚苯乙烯/蒙脱土(PDCPD/PS/MMT)纳米复合材料。运用XRD、SEM对聚合物进行表征,测定了其拉伸强度、冲击强度及弯曲强度等力学性能。结果表明:MMT片层被完全剥离开,形成了真正的纳米复合材料,PS、MMT质量分数分别为1%、2%时,纳米复合材料的各项性能最好。     

Synthesis of CaCO3–P(MMA–BA) nanocomposite and its application in water based alkyd emulsion coating

As part of broader effort to synthesize a new class of water-based composite, hybrid emulsion polymerization was carried out with acrylic monomers [methyl methacrylate (MMA), n-butyl acrylate (BA)]. Nanocomposite of P(MMA–BA)/nano CaCO₃ was synthesized by in situ emulsion polymerization. Water-based alkyd coating with various proportions nano CaCO₃, P(MMA–BA) and its nanocomposite was formulated. Extent of polymerization with and without nano CaCO₃ was measured using gravimetric method. Thermal properties of neat polymer, nanocomposite and coating films were evaluated by TGA and DSC, DTA analysis. Uniform dispersion of nano CaCO₃ in polymer matrix was ensured from SEM/TEM images. Incorporation of nanoparticles to hybrid polymer and nanocomposite to alkyd emulsion showed significant enhancement in mechanical and thermal properties. Dual role of nanocomposite in coating; as a partial binder and a filler to improve property profile of neat coating has been reported.     

聚丙烯酸酯涂料印花黏合剂的合成与性能研究

以过硫酸铵(APS)为引发剂、甲基丙烯酸甲酯(MMA)为硬单体、丙烯酸丁酯(BA)和丙烯酸异辛酯(EHA)为软单体、丙烯酸(AA)为功能单体和N-羟甲基丙烯酰胺(NMA)为交联单体,采用预乳化法合成出一种聚丙烯酸酯涂料印花黏合剂。讨论了单体滴加方式、预乳化液滴加时间、阴/非离子型乳化剂配比及用量、交联剂和各单体用量等对该黏合剂乳液性能的影响。结果表明:当w(BA)=15%、w(EHA)=8%、w(MMA)=20%、w(NMA)=3.0%、滴加时间为2.5 h、复合乳化剂中m(SDS):m(OP-10)=1:2且w(复合乳化剂)=6%时,该黏合剂乳液具有优良的综合性能,能够满足织物印花的使用要求。     

新型高吸油树脂的制备

以丙烯酸正丁酯(BA)和甲基丙烯酸甲酯(MMA)为单体,采用改进的悬浮聚合法合成高吸油树脂。考察了单体配比、引发剂和交联剂用量、AIBN加入量及加入时间对树脂吸油性能的影响。结果表明,最佳合成条件为:单体配比BA∶MMA质量比为4∶1,引发剂BPO用量为单体质量的0.4%,交联剂N,N’-亚甲基双丙烯酰胺为单体质量的0.15%,发泡剂偶氮二异丁腈(AIBN)为单体质量的18%,在此条件下合成的树脂对甲苯的吸油率最高可达40.17 g/g,速率也明显提高。     

PEG改性天然钠基蒙脱土及其与PET纳米复合材料的结构与性能

采用环境友好、热稳定性较高且与聚对苯二甲酸乙二醇酯(PET)有良好相容性的聚乙二醇(PEG)改性天然钠基蒙脱土(Na+-MMT)与PET熔融共混制备了PET/Na+-MMT纳米复合材料。结果表明,经PEG改性的Na+-MMT的层间距增加,与PET熔融共混后其层间距进一步加大,TEM分析证实了MMT片层存在插层型纳米结构。相对传统的有机蒙脱土,PEG改性Na+-MMT的热稳定性有显著改善,满足了PET的高温加工要求。此外,PEG改性的Na+-MMT比未处理Na+-MMT对PET有更低的冷结晶温度和更高的熔融结晶温度,显著改善了PET的结晶能力。所制的纳米复合材料具有良好的力学性能,其拉伸强度可达59.8MPa,缺口冲击强度可达3.13kJ/m2。     

不同工艺制备的PP/蒙脱土纳米复合材料的性能

选择一种新型有机蒙脱土（MMT）,分别通过直接注塑法和挤出一注射法（简称挤出法）将聚丙烯（PP）与有机MMT复合,制备出高抗冲PP／MMT纳米复合材料。透射电子显微镜观察表明。挤出法制备的复合材料为全插层型结构,MMT分散均匀,尺寸小;而直接注塑法制备的复合材料为部分插层型结构．MMT明显分散不均匀,尺寸较大,且有少量团聚产生。力学性能测试表明,随着MMT的增加．2种试样的缺口冲击强度都有显著提高,均在ω（MMT）为4％时达到极大值。此时,挤出法试样缺口冲击强度比纯PP提高102％。屈服拉伸强度、弹性模量也略有提高;直接注塑法试样的缺口冲击强度比纯PP提高82．6％,但屈服拉伸强度、弹性模量都明显降低。