固溶温度对Custom 465钢组织与性能的影响

在510 ℃时效条件下,研究了固溶温度在700～1 050 ℃范围内变化对Custom 465钢晶粒度、奥氏体和力学性能的影响.采用扫描电镜对不同固溶温度下冲击试样的断口进行了分析.结果表明,Custom 465钢的最佳固溶温度在900～950 ℃温度范围内;时效态钢中奥氏体主要为逆转变奥氏体.     

冷轧变形对Custom 465钢组织和性能的影响

 研究了冷轧变形对Ti强化马氏体时效不锈钢Custom 465时效析出、逆转变奥氏体相变和力学性能的影响。结果表明：①在510 ℃时效过程中,杆状Ni3Ti金属间化合物持续析出、长大,致使快速发生硬化;②510 ℃时效过程中,发生逆转变奥氏体相变,冷轧变形使逆转变奥氏体相变滞后;③析出Ni3Ti金属间化合物的同时,马氏体基体发生部分回复。     

合金元素对马氏体时效不锈钢Ms温度影响的定量分析

在现有各钢种马氏体转变开始温度 (Ms)经验计算公式的基础上 ,分析了合金元素对钢的Ms的影响 ,经验算提出马氏体时效不锈钢的Ms(℃ ) =5 5 0 - 330C - 35Mn - 1 7Ni - 1 2Cr - 2 1Mo - 1 0Cu - 5W - 1 0Si-0Ti+1 0Co +30Al。用该经验公式得出马氏体时效不锈钢Ms计算值与试验值符合较好 ,误差范围± 2 0℃ ,平均误差 1 1 .2 2℃。     

时效温度对马氏体时效不锈钢延迟断裂行为的影响

借助于缺口慢拉伸试验研究了马氏体时效不锈钢延迟断裂倾向对时效温度的敏感性。研究结果表明,正常冶炼和加工的材料氢的质量分数在2×10-6以下,420和440℃欠时效处理的试样仍发生氢致延迟断裂;而460℃以上时效的缺口试样慢拉伸(0.001 5mm/min)的抗拉强度和断裂行为类似于快拉伸(0.15mm/min),即不发生延迟断裂。     

钛含量对00Cr13Co9Ni5Mo5马氏体时效不锈钢冲击韧性的影响

通过具有不同钛含量的3炉试验钢,研究了钛含量对00Cr13Co9Ni5Mo5马氏体时效不锈钢的力学性能、金相组织和奥氏体含量的影响。研究结果表明:添加较多的Ti可显著降低基体组织中的有效C、N含量,大幅降低固溶、时效处理后残余/逆转变奥氏体含量,最终使冷脆转化温度显著上升,在提高强度的同时降低了钢的韧性。     

高强度马氏体时效不锈钢的晶粒细化及其力学性能的研究

研究了一种高强度马氏体时效不锈钢逆转变奥氏体再结晶规律、细化晶粒工艺及细晶组织对力学性能的影响.研究表明,通过循环相变a'(→)γ可得到7 um的等轴晶粒,新生晶粒内的板条马氏体块又重新被分割而成为若干个亚晶粒,同时部分单一的马氏体板条束又被夹角略大于60°方向上的若干个小马氏体板条束所分割,从而进一步细化了马氏体组织;与传统热处理工艺1050℃×1h相比,在同样时效处理规程下进行时效处理,钢的屈服强度提高了130 MPa,A、Z分别提高了7.5%、11%,循环相变细化晶粒是同时提高该钢的强度和韧塑性的有效手段.     

时效温度对马氏体沉淀硬化不锈钢0Cr15Ni5WMoVNb力学性能的影响

0Cr15Ni5WMoVNb钢(%:0.068C、14.54Cr、5.32Ni、0.88W、0.92Mo、0.20V、0.10Nb)经5 t中频感应炉+2 t真空电渣重熔炉冶炼,经锻造、热轧成Φ45 mm棒材,试样经1 000℃30 min固溶空冷+-70℃2 h冷处理后进行400～600℃4 h时效空冷。试验结果表明,在450℃时效0Cr15Ni5WMoVNb钢的强度最大,以准解理断裂为主,冲击功低为40 J,随时效温度上升,冲击功显著上升,强度下降,在510℃时效该钢有良好的强韧性,抗拉强度R_m 1300 MPa,屈服强度R_(p0.2)1100 MPa,冲击能A_(KV) 100 J。     

时效温度对贝氏体型冷作强化非调质钢力学性能的影响

 研究了时效温度对一种低碳Mn-B-Ti系贝氏体型冷作强化非调质钢力学性能的影响。结果表明：试验料的强度随时效温度的升高先是增加,并在250℃时存在一个峰值,随后强度又随时效温度的升高而降低,当温度升高到400℃以上时强度明显降低;试验料的塑性和屈强比则随时效温度的升高逐渐增加,其中后者增加的幅度更显著。与未充氢试样相比,试验料拉拔并充氢后的延迟断裂性能显著降低。随着时效温度的升高,充氢试样中的氢含量降低,缺口抗拉强度RBN和延迟断裂强度比R缓慢增加,当时效温度大于200℃时,RBN和R则明显增加。因此,在满足保载永久伸长变形量及强度和塑性要求的前提下,应选择合适的时效温度,以保证材料的延迟断裂性能。     

不同热处理制度对T250钢性能的影响

在不同的固溶温度、时效温度和时效时间的条件下,时真空感佑行热处理,研究不同热处理制度对其性能的影响.结果显示:在750～975 ℃不同的固溶温度下,固溶温度的变化对T250钢性能的影响很小;在450～570 ℃不同的时效温度下,T250钢的抗拉强度、屈服强度、冲击韧性和断裂韧性受到时效温度的显著影响,时效温度的变化对T250钢其他性能指标影响不大;时效时间大于5 h后,延长时效时间对T250马氏体时效钢性能的影响很小,T250钢在时效时间5 h时具有最佳的力学性能.     

Formation of Reversed Austenite in High Temperature Tempering Process and its Effect on Mechanical Properties of Cr15 Super Martensitic Stainless Steel Alloyed with Copper

Formation mechanism of the reversed austenite of Cr15 super martensitic stainless steel (SMSS) alloyed with copper after high temperature tempering was investigated by means of thermo‐calc software, transmission electron microscope (TEM), and X‐ray diffraction (XRD). The mechanical properties of the SMSS were also tested. The experimental results show that the reversed austenite with low dislocation density is formed at high temperature tempering processing. The transformation of the martensite to reversed austenite is a diffused phase transformation, and the growth of the reversed austenite is closely related to the diffusion process of Ni. The bulk reversed austenite with large amount of stacking faults is formed with the increase of the tempering temperature. The volume fraction of reversed austenite increases at first and then decreases with increasing tempering temperature, and the maximum amount of the reversed austenite is obtained at 650°C. The reversed austenite is unstable at the tempering temperature above 650°C and the martensitic phase transformation will occur at the following cooling process. The mechanical properties of Cr15 super martensitic stainless steel are significantly influenced by the volume fraction of reversed austenite.     

时效温度对S32101双相不锈钢组织和力学性能的影响

利用光学显微镜、铁素体仪进行了硬度和拉伸实验,研究了S32101双相不锈钢不同时效态下组织与力学性能之间的关系。研究结果表明,随着时效温度的升高,S32101双相不锈钢的屈服强度、抗拉强度和硬度减小,延伸率增大;析出相的产生是造成力学性能变化的主要原因,700℃为最敏感析出温度,900℃时析出相开始逐渐消失。     

时效温度对K487合金组织和性能的影响

 研究了不同时效温度对K487合金组织和性能的影响。结果表明,随时效温度提高,合金组织中γ′相尺寸增大,针状μ相减少,不规则块状和条状μ相边缘尖角变圆钝,合金强度下降,塑性提高。经900 ℃×5 h时效后,合金可获得较好的综合性能,其屈服强度约685 MPa,伸长率和断面收缩率分别达到105%和155%。     

回火温度对Mn-Ni钢亚稳奥氏体形貌及其力学性能的影响

 利用了X射线衍射仪（XRD）、电子背散射衍射（EBSD）和透射电子显微镜（TEM）研究了回火温度对一种Mn-Ni钢亚稳奥氏体形貌及其力学性能的影响。结果表明,随着回火温度的升高,室温亚稳奥氏体的体积分数逐渐升高。当回火温度为600和625 ℃时,亚稳奥氏体主要以片层状在回火马氏体板条间析出,且排列方向与周围的马氏体板条平行,这种片层状亚稳奥氏体分布较为均匀,尺寸较小,约为60～100 nm,且稳定性较高;当回火温度为650 ℃时,试验钢中出现尺寸较大的块状奥氏体在回火马氏体界面的交叉处不均匀析出。分析表明,块状奥氏体有利于提高钢的塑性,不利于改善钢的低温韧性;而片层状奥氏体能大幅度的改善钢的低温韧性。     

淬火温度对Q-P钢组织和性能的影响

 采用盐浴的方法模拟Q-P钢的热处理工艺,对钢的组织和性能进行分析和研究。其结果表明,淬火配分组织主要为板条马氏体和残留奥氏体,并随淬火温度升高马氏体含量降低,奥氏体含量升高,从而降低钢的强度,提高塑性,拉伸断口呈现典型的韧窝状形貌,当淬火温度为250℃时,得到最高的强塑积为26224MPa·%。     

C300焊缝金属3种状态的组织和性能

采用光学显微镜、扫描电镜及透射电镜等分析了C300焊缝金属焊态、焊后固溶态及焊后固溶时效态的微观组织变化、强韧性特征及断口裂纹扩展路径.结果表明,经过时效处理,在马氏体基体上析出了金属间化合物强化相,同时伴随着软相逆转变奥氏体的产生.时效态焊缝的强、硬度提高,塑、韧性降低,断口的韧窝尺寸和裂纹扩展路径相对较小,裂纹扩展阻力较低.