Ultrafast preparation of Al2O3–ZrO2 multiphase ceramics with eutectic morphology via flash sintering

Herein, Al₂O₃–ZrO₂ multiphase ceramics with a eutectic molar ratio were prepared using the flash sintering technique at 1200 °C in 2 min. The samples were divided into two regions according to the microscopic morphology: multiphase ceramics zone and eutectic ceramics zone. The multiphase ceramics zone uniformly distributed irregular Al₂O₃ and ZrO₂ phases. The eutectic zone presented typical eutectic morphology, where different morphologies of ZrO₂ was uniformly embedded in the Al₂O₃ matrix, mainly showing fine lamellar, rod-like and irregular network morphology. Overall, flash sintering is a promising route to prepare high-performance multiphase ceramics.     

Effect of solidification path on the microstructure of Al2O3–Y2O3–ZrO2 ternary oxide eutectic ceramic system

The solidification path of the Al₂O₃–Y₂O₃–ZrO₂ ternary oxide eutectic composite ceramic is determined by a high temperature DTA and laser floating zone (LFZ) directional solidification method to investigate the effect of solidification path on the microstructure of the ternary oxide. The DTA and microstructure analyses show that the YAG or Al₂O₃ tends to form as primary phase under the unconstrained solidification conditions, and then the system enters ternary eutectic solidification during cooling from 1950 °C at rate of 20 °C/min. The as-solidified composite ceramic shows a divorced irregular eutectic structure consisting of Al₂O₃, YAG and ZrO₂ phases with a random distribution. The primary phases are however completely restrained at the directional solidification conditions with high temperature gradient, and the ternary composite by LFZ presents well coupled eutectic growth with ultra-fine microstructure and directional array. Furthermore, the eutectic transformation and growth mechanism of the composite ceramic under different solidification conditions are discussed.     

Superplastic deformation of directionally solidified nanofibrillar Al2O3–Y3Al5O12–ZrO2 eutectics

Nanofibrillar Al₂O₃–Y₃Al₅O₁₂–ZrO₂ eutectic rods were manufactured by directional solidification from the melt at high growth rates in an inert atmosphere using the laser-heated floating zone method. Under conditions of cooperative growth, the ternary eutectic presented a homogeneous microstructure, formed by bundles of single-crystal c-oriented Al₂O₃ and Y₃Al₅O₁₂ (YAG) whiskers of ≈100 nm in width with smaller Y₂O₃-doped ZrO₂ (YSZ) whiskers between them. Owing to the anisotropic fibrillar microstructure, Al₂O₃–YAG–YSZ ternary eutectics present high strength and toughness at ambient temperature while they exhibit superplastic behavior at 1600 K and above. Careful examination of the deformed samples by transmission electron microscopy did not show any evidence of dislocation activity and superplastic deformation was attributed to mass-transport by diffusion within the nanometric domains. This combination of high strength and toughness at ambient temperature together with the ability to support large deformations without failure above 1600 K is unique and shows a large potential to develop new structural materials for very high temperature structural applications.     

Sintering,microstructure and mechanical properties of Al2O3–Y2O3–ZrO2 (AYZ) eutectic composition ceramic microcomposites

We report on how the mechanical properties of sintered ceramics (i.e., a random mixture of equiaxed grains) with the Al₂O₃–Y₂O₃–ZrO₂ eutectic composition compare with those of rapidly or directionally solidified Al₂O₃–Y₂O₃–ZrO₂ eutectic melts. Ceramic microcomposites with the Al₂O₃–Y₂O₃–ZrO₂ eutectic composition were fabricated by sintering in air at 1400–1500 °C, or hot pressing at 1300–1400 °C. Fully dense, three phase composites of Al₂O₃, Y₂O₃-stabilized ZrO₂ and YAG with grain sizes ranging from 0.4 to 0.8 μm were obtained. The grain size of the three phases was controlled by the size of the initial powders. Annealing at 1500 °C for 96 h resulted in grain sizes of 0.5–1.8 μm. The finest scale microcomposite had a maximum hardness of 19 GPa and a four-point bend strength of 282 MPa. The fracture toughness, as determined by Vickers indentation and indented four-point bending methods, ranged from 2.3 to 4.7 MPa m^1/2. Although strengths and fracture toughnesses are lower than some directionally or rapidly solidified eutectic composites, the intergranular fracture patterns in the sintered ceramic suggest that ceramic microcomposites have the potential to be tailored to yield stronger, tougher composites that may be comparable with melt solidified eutectic composites.     

Gelcasting and pressureless sintering of silicon carbide ceramics using Al2O3–Y2O3 as the sintering additives

In this paper, silicon carbide ceramics were prepared by aqueous gelcasting and pressureless sintering using Al₂O₃ and Y₂O₃ as the sintering additives. In order to develop well dispersed SiC slurries in the presence of sintering additives, the Al₂O₃ and Y₂O₃ powder was treated in the citric acid solution in advance. Zeta potential measurement showed that the isoelectric point (IEP) of Al₂O₃ and Y₂O₃ powder moved toward low pH region after treatment. Rheological measurement confirmed that the addition of as-treated powder showed very limited influence on the slurry properties as compared to that of untreated powder. SiC slurries with solid content of 54 vol% and enough fluidity can be developed. After gelcasting and pressureless sintering, SiC ceramics with nearly full density, fine grained and homogeneous microstructure can be obtained. Results showed that the surface treatment of Al₂O₃ and Y₂O₃ with citric acid is effective for the gelcasting process of SiC.     

Pore formation model for direct laser deposition of Al2O3–ZrO2 ceramic

Pores are some of the most common defects that form during direct laser deposition of ceramic materials. A mathematical model of pore formation for Al₂O₃-ZrO₂ ceramic was developed. The pore formation model, which was developed from the bubble escape factor, reveals the relationship between the movement of the solid-liquid interface of the molten pool and that of the bubbles. In the frontier region of the molten pool, with increasing laser power, the proportion of bubbles that escaped and the area from which bubbles escaped increased. With increasing laser power, the actual and theoretical porosity decreased from 80 % to 40 %. At the central region of the molten pool, the bubble escape factor increased with increasing bubble diameter under the same laser power. The theoretical porosity and the actual porosity decreased with increasing laser power. The pore formation model provides a basis for fabricating high-quality Al₂O₃-ZrO₂ ceramics by direct laser deposition.     

Solidification of Al2O3–YAG eutectic composites with off-metastable eutectic composition from undercooled melt produced by melting Al2O3–YAP eutectics

It has been reported that solidification of the Al₂O₃–YAG equilibrium eutectic structure follows melting of the Al₂O₃–YAP metastable eutectic structure. Since the exothermic heat due to solidification was consumed by the endothermic heat due to melting, a fine and uniform eutectic structure was obtained. However, the composition of the Al₂O₃–YAG eutectic structure is restricted to the metastable eutectic composition. In this paper, Al₂O₃–YAG eutectic compacts with an off-metastable eutectic composition were prepared by the addition of Al₂O₃ particles to Al₂O₃–YAP eutectic particles with diameters less than 20 μm. In compositions ranging from 18.5 mol%Y₂O₃ to 13.5 mol%Y₂O₃, dense Al₂O₃–YAG eutectic compacts were formed without any Al₂O₃ segregation. The flexural strength and the fracture toughness remained almost unchanged with the increase in the Al₂O₃ phase. The addition of Al₂O₃ particles to the Al₂O₃–YAP eutectic particles enabled the matrix phase to change from the YAG phase to the Al₂O₃ phase.     

Fabrication of Si3N4 ceramics by post-reaction sintering using Si–Y2O3–Al2O3 nanocomposite particles prepared by mechanical treatment

Post-reaction sintering of a powder compact of Si and sintering aids is a useful technique for fabricating silicon nitride (Si₃N₄) ceramics at low costs. In order to inhibit the inhomogeneous and uncontrollable exothermic nitridation of Si in the powder compact, Si–Y₂O₃–Al₂O₃ nanocomposite particles are designed as an aid for post-reaction sintering. These Si–Y₂O₃–Al₂O₃ nanocomposite particles are prepared via mechanical treatment applying high shear stress. Scanning electron microscopy (SEM) observations show that Y₂O₃ and Al₂O₃ particles are homogenously dispersed, and fixed to the Si particles. A green compact prepared using the Si–Y₂O₃–Al₂O₃ nanocomposite particles results in lower electrical resistivity than that prepared using a powder mixed by wet ball-milling, which suggests that Si particles in the green compact prepared using the nanocomposite particles are isolated by Y₂O₃ and Al₂O₃ particles. The isolation of Si particles by the sintering aids successfully prevents the Si particles from melting and agglomerating during the nitridation process, resulting in a higher nitridation ratio and higher α-Si₃N₄ phase content due to the inhibition of rapid heat transfer caused by the exothermic reaction. The nitridation ratio also increases with the applied power during mechanical treatment. As a result of firing the homogeneously nitrided powder compacts at high temperatures, Si₃N₄ ceramics with homogeneous microstructure and improved density are successfully fabricated in this manner.     

Pressureless sintering of carbon nanotube–Al2O3 composites

Alumina ceramics reinforced with 1, 3, or 5 vol.% multi-walled carbon nanotubes (CNTs) were densified by pressureless sintering. Commercial CNTs were purified by acid treatment and then dispersed in water at pH 12. The dispersed CNTs were mixed with Al₂O₃ powder, which was also dispersed in water at pH 12. The mixture was freeze dried to prevent segregation by differential sedimentation during solvent evaporation. Cylindrical pellets were formed by uniaxial pressing and then densified by heating in flowing argon. The resulting pellets had relative densities as high as ～99% after sintering at 1500 °C for 2 h. Higher temperatures or longer times resulted in lower densities and weight loss due to degradation of the CNTs by reaction with the Al₂O₃. A CNT/Al₂O₃ composite containing 1 vol.% CNT had a higher flexure strength (～540 MPa) than pure Al₂O₃ densified under similar conditions (～400 MPa). Improved fracture toughness of CNT–Al₂O₃ composites was attributed to CNT pullout. This study has shown, for the first time, that CNT/Al₂O₃ composites can be densified by pressureless sintering without damage to the CNTs.     

Y3Al5O12-α-Al2O3 composites with fine-grained microstructure by hot pressing of Al2O3-Y2O3 glass microspheres

Yttrium aluminate glass microspheres with the eutectic composition 76.8 mol. % Al₂O₃ and 23.2 mol. % Y₂O₃ were prepared by combining the sol-gel Pechini method with flame synthesis. The sol-gel method was applied to achieve the desired composition homogeneity of the prepared glass and hence, improve the microstructure homogeneity and mechanical properties of bulk polycrystalline materials. The latter were prepared by hot pressing, more specifically pressure assisted sintering, at 1050 °C, 1300 °C and 1600 °C using pressures of 30 MPa and 80 MPa and holding times between 0 and 30 min. This also led to the crystallization of the glass. A composite with the Vickers hardness 18.0 ± 0.7 GPa and an indentation fracture toughness 4.9 ± 0.3 MPa.m^1/2 was obtained by sintering at 1600 °C, at the pressure of 80 MPa and with 30 min isothermal heating at the maximum temperature. Improved mechanical properties were observed when increasing the temperature of sintering and the holding time. This can be attributed to the formation of a unique microstructure consisting of α-Al₂O₃ grains in the μm-scale embedded in a YAG (yttrium-aluminium garnet) matrix in the hot-pressed samples.     

Pure perovskite BiFeO3–BaTiO3 ceramics prepared by reaction flash sintering of Bi2O3–Fe2O3–BaTiO3 mixed powders

In this work, the 0.67BiFeO₃-0.33BaTiO₃ ferroelectric ceramic was prepared by Reaction Flash Sintering (RFS). This preparation technique combines synthesis and sintering in a single Flash experiment. The starting oxides reacted during the flash to produce a stoichiometric well-sintered solid solution at a temperature of 858 °C by applying a modest field of 35 V cm⁻¹. The process takes place in a matter of seconds, which allows obtaining a pure perovskite structure without secondary phases. X-ray diffraction (XRD) results show the mixture of rhombohedral and pseudocubic phases expected for a composition that lies within a morphotropic phase boundary (MPB) region, since a significant splitting is observed in the reflections at 2θ values of 39° and 56.5°. The microstructure exhibit a peculiar bimodal grain size distribution that determines the electrical properties. As compared with previous results, flash-prepared 0.67BiFeO₃-0.33BaTiO₃ evidences smaller grain size, as well as slightly lower remanent polarization (P_r) and smaller coercive field (E_c) under similar electric fields. It is also demonstrated that the preparation by RFS provides benefits regarding electrical energy consumption.     

Formation of Al2O3–GdAlO3 eutectic ceramics with a fine anisotropic structure in a flash event

An Al₂O₃–GdAlO₃ (GAP) composite with a fine eutectic microstructure was obtained through local melting and rapid solidification during a flash event. An AC field of 1 kV/cm at a frequency of 1 kHz was applied to a calcined Al₂O₃–GAP body at a furnace temperature of 1400°C to induce the flash event. The Al₂O₃–GAP body exhibited local melting through the current path. Solidification proceeded with the maximum cooling rate of about 140°C/s just after the power supply was turned off. Using this flash treatment, a refined eutectic structure with rodlike GAP phases in the Al₂O₃ matrix was obtained within 1 min. The interphase spacing of the obtained structure was approximately 170 nm, comparable with the finest Al₂O₃–GAP eutectic material obtained in previous studies. A flash event and subsequent rapid cooling can contribute to forming fine eutectic ceramics with a relatively low furnace temperature and short processing time.     

Effects of Al2O3–Y2O3/Yb2O3 additives on microstructures and mechanical properties of silicon nitride ceramics prepared by hot-pressing sintering

Silicon nitride (Si₃N₄) ceramics doped with two different sintering additive systems (Al₂O₃–Y₂O₃ and Al₂O₃–Yb₂O₃) were prepared by hot-pressing sintering at 1800℃ for 2 h and 30 MPa. The microstructures, nano-indentation test, and mechanical properties of the as-prepared Si₃N₄ ceramics were systematically investigated. The X-ray diffraction analyses of the as-prepared Si₃N₄ ceramics doped with the two sintering additives showed a large number of phase transformations of α-Si₃N₄ to β-Si₃N₄. Grain size distributions and aspect ratios as well as their effects on mechanical properties are presented in this study. The specimen doped with the Al₂O₃–Yb₂O₃ sintering additive has a larger aspect ratio and higher fracture toughness, while the Vickers hardness is relatively lower. It can be seen from the nano-indentation tests that the stronger the elastic deformation ability of the specimens, the higher the fracture toughness. At the same time, the mechanical properties are greatly enhanced by specific interlocking microstructures formed by the high aspect ratio β-Si₃N₄ grains. In addition, the density, relative density, and flexural strength of the as-prepared Si₃N₄ ceramics doped with Al₂O₃–Y₂O₃ were 3.25 g/cm³, 99.9%, and 1053 ± 53 MPa, respectively. When Al₂O₃–Yb₂O₃ additives were introduced, the above properties reached 3.33 g/cm³, 99.9%, and 1150 ± 106 MPa, respectively. It reveals that microstructure control and mechanical property optimization for Si₃N₄ ceramics are feasible by tailoring sintering additives.     

Microwave sintering of IR-transparent Y2O3–MgO composite ceramics

A method for preparation of dense Y₂O₃–MgO composite ceramics by the microwave sintering was developed. The initial powders were obtained by glycine-nitrate self-propagating high-temperature synthesis (SHS) with different oxidant-to-fuel ratio. Density and IR-transmission of microwave sintered Y₂O₃–MgO ceramics increase with respect to dispersity of the SHS-powders and reach its maximum values for the powder prepared in a 20% fuel excess. The sintering behavior of Y₂O₃–MgO compacts was investigated by optical dilatometry and measuring an electric conductivity upon heating. Significant microwave radiation power surges at temperatures of 900–1000 °C, caused by the decomposition of magnesium carbonate, have been found. As a result of matching the conditions for the synthesis of powders and sintering modes, a transmission of composite ceramics of 78% at a wavelength of 6 μm was achieved at a maximum processing temperature of 1500 °C.     

Optical and mechanical properties of amorphous bulk and eutectic ceramics in the HfO2–Al2O3–Y2O3 system

Bulk glasses containing HfO₂ nano-crystallites of 20–50 nm were prepared by hot-pressing of HfO₂–Al₂O₃–Y₂O₃ glass microspheres at 915 °C for 10 min. By annealing at temperatures below 1200 °C, the bulk glasses were converted into transparent glass-ceramics with HfO₂ nano-crystallites of 100–200 nm, which showed the maximum transmittance of ～70% in the infrared region. An increase of annealing temperature (>1300 °C) resulted in opaque YAG/HfO₂/Al₂O₃ eutectic ceramics. The eutectic ceramics contained fine Al₂O₃ crystallites and showed a high hardness of 19.8 GPa. The fracture toughness of the eutectic ceramics increased with increasing annealing temperature, and reached the maximum of 4.0 MPa m^1/2.     

High temperature sintering of SiC with oxide additives: I. Analysis in the SiC–Al2O3 and SiC–Al2O3–Y2O3 systems

The vaporization behaviour of pure Al₂O₃, Y₂O₃ and SiC as well as SiC–Al₂O₃ and SiC–Al₂O₃/Y₂O₃ mixtures has been analysed by thermodynamic calculations in an open system. Pure Al₂O₃ and Y₂O₃ evaporate congruently in the 1200–2300 K temperature range. Pure SiC vaporizes in a non-congruent manner leading to graphite formation as by-product. A SiC–Al₂O₃ mixture evaporates congruently according to the main vaporization reaction, 2 SiC(s) + Al₂O₃(s) +Al₂O(g) ⇆ 2 SiO(g) + 2 CO(g) +4 Al(g), but the overall composition changes: for SiC rich samples, the mixture tends towards pure SiC in time, and for Al₂O₃ rich samples towards pure Al₂O₃. A SiC–Al₂O₃/Y₂O₃ mixture shows similar behaviour.     

High-strength AlN ceramics by low-temperature sintering with CaZrO3–Y2O3 co-additives

Aluminum nitride (AlN) ceramics with the concurrent addition of CaZrO₃ and Y₂O₃ were sintered at 1450-1700 °C. The degree of densification, microstructure, flexural strength, and thermal conductivity of the resulting ceramics were evaluated with respect to their composition and sintering temperature. Specimens prepared using both additives could be sintered to almost full density at relatively low temperature (3 h at 1550 °C under nitrogen at ambient pressure); grain growth was suppressed by grain-boundary pinning, and high flexural strength over 630 MPa could be obtained. With two-step sintering process, the morphology of second phase was changed from interconnected structure to isolated structure; this two-step process limited grain growth and increased thermal conductivity. The highest thermal conductivity (156 Wm⁻¹ K⁻¹) was achieved by two-step sintering, and the ceramic showed moderate flexural strength (560 MPa).     

Melt extraction processing of structural Y2O3–Al2O3 fibers

Compounds in the system Y₂O₃-Al₂O₃ are promising materials for optical, electronic and structural applications. In this study, a melt extraction process with a new approach to making ceramic fibers was used to produce amorphous fibers in the Y₂O₃–Al₂O₃ system within the 20–30-micron size range. Smooth and uniform cross section fibers with relatively high tensile strength were obtained depending on the wheel velocity. X-ray diffraction of as-extracted fibers revealed the non-crystalline nature of the yttria-alumina compositions. The crystallization and glass transition temperatures of non-crystalline fibers were determined using differential thermal analysis (DTA). Crystalline phases were identified by X-ray diffraction in the fibers after heat treatment.     

Microstructure and thermal expansion of Al2TiO5–MgTi2O5 solid solutions obtained by reaction sintering

Solid solutions Mg_0.1Al_1.8Ti_1.1O₅ and Mg_0.5AlTi_1.5O₅ were obtained by reaction sintering of mixtures of the binary oxides at 1350–1600 °C using different precursor powders. For the composition Mg_0.1Al_1.8Ti_1.1O₅, ceramics sintered at 1400–1500 °C have high relative density (⩾90%), reduced grain size (2–6 μm), low thermal expansion (−0.8 to 0.3×10⁻⁶ K⁻¹ in the range 200–1000 °C) and reproducible expansion behaviour. At higher temperature, grain size rapidly increases owing to anisotropic and exaggerated grain growth (EGG) resulting in severe microcracking. Microstructure evolution is affected by the nature of the starting oxides, in particular for what concerns the onset temperature of EGG, the size and the fraction of abnormal grains. For the composition Mg_0.5AlTi_1.5O₅, EGG already takes place at 1350 °C and materials with grain size < 5 μm are difficult to obtain by conventional reaction sintering. Large grained samples (>10 μm) of both compositions show a reduced hysteresis and complex thermal expansion behaviour. In particular, heating to 1000 °C results in a significant increase in specimen size on return to room temperature. Repeated thermal cycling leads to an increase of the hysteresis.