喷雾转换法制备超细晶WC-12Co复合粉末HVOF涂层性能研究

采用超音速火焰喷涂(HVOF)技术,以喷雾转换法制备的超细晶WC-12Co复合粉末为热喷涂粉末原料,在45#钢基体上制备WC-12Co涂层,并测试涂层的显微硬度、开裂韧性及抗磨粒磨损性能,利用XRD对复合粉末及涂层进行相结构分析,用SEM对复合粉末及涂层截面进行显微观察。结果表明,在喷涂过程中,多孔空壳球形复合粉末中WC颗粒有明显的脱碳分解发生,涂层中含有W2C、Co2W4C、W和非晶相;涂层组织呈典型的层状结构,WC晶粒有圆润化和长大现象;涂层显微硬度HV0.3/10平均值为1 084、开裂韧性平均值为5.24 MPa·m1/2,涂层表面抗磨损性能随粗糙度降低和硬度增加而提高,平均磨损质量损失为0.783mg/min。     

HVOF喷涂超细结构WC-12Co涂层磨粒磨损性能

以喷雾转换法制备的球壳形WC-12Co复合粉为原料,采用超音速火焰喷涂(HVOF)在45~#钢上制备超细结构WC-12Co涂层,并测试涂层的显微硬度、开裂韧性。利用XRD、SEM和磨损试验机分析涂层物相组成、微观结构和耐磨损性能。结果表明:多孔球壳形WC-12Co复合粉在HVOF喷涂过程中发生了中度脱碳,涂层中不仅含有WC、W_2C相,还有少量W相;涂层微观结构致密,组织呈岩层状,截面平均显微硬度HV_(0.3)为1 205.5、平均开裂韧性为4.96 MPa·m~(1/2);磨损过程中,粘结相被SiO_2犁削出非连续状槽沟,WC晶粒剥离或裂解出的细小WC晶粒成为新的磨粒,对粗大晶粒产生磨削或积于裂纹处加剧开裂。     

大气等离子喷涂WC-12Co涂层的组织结构与性能研究

采用大气等离子喷涂(APS)方法在45钢基体上制备了WC-12Co涂层。用扫描电子显微镜(SEM)、X射线衍射仪(XRD)对涂层的微观形貌和成分进行了分析;采用显微硬度计和万能试验机分别测定了涂层的显微硬度和结合强度;并用SRV-Ⅳ摩擦磨损试验机测试了涂层的摩擦磨损性能。结果表明:WC-12Co涂层组织均匀致密,在喷涂过程中仅少量的WC发生了氧化分解,生成W_2C和Co_3W_3C相。涂层力学性能优异,结合强度平均值为50.63 MPa,涂层表面平均硬度为85.7 HR15N,截面平均显微硬度为1 053.8 HV0.3。相对于304不锈钢,等离子喷涂WC-12Co涂层具有十分优良的耐磨损性能,在室温(25℃)至300℃范围内,WC-12Co涂层的磨损机制为磨粒磨损。     

HVAF 制备 WC 基涂层结构与滑动摩擦磨损性能研究

采用HVAF超音速火焰喷涂制备三种WC基金属陶瓷复合涂层以及金属涂层Ni60,对比分析了各涂层的微观形貌、硬度、沉积速率、滑动摩擦磨损性能。结果表明:HVAF超音速火焰喷涂制备的各涂层与基体结合良好、涂层结构致密,孔隙率1.5%;随着复合涂层中碳化物陶瓷增强颗粒的增加,各涂层的显微硬度增大,沉积速率降低;摩擦磨损试验显示WC-10Co-4Cr、WC-12Co涂层磨损量仅为金属涂层Ni60的1/20,表现出优异的耐滑动磨损性能。     

WC-Co(Cr)超音速火焰喷涂粉末和涂层性能

采用喷雾造粒和真空烧结工艺制备粒度15~45μm的WC-12%Co(WC12Co)、WC-17%Co(WC17Co)、WC-10%Co-4%Cr(WC10Co4Cr)球形喷涂粉末,并采用超音速火焰喷涂(HVOF)法在同一喷涂参数下制备WC12Co,WC17Co,WC10Co4Cr涂层,应用金相显微镜、X-射线衍射仪、扫描电镜、显微硬度计等表征粉末和涂层的结构和性能。结果表明:制备的3种碳化钨基喷涂粉末球形度高,流动性好(~13s/50g),松装密度接近(4.8~5.0 g/cm3),粉末物相均为WC和Co相,各粉末微观结构和物理性能均满足液体燃料HVOF喷涂要求;3种粉末制备的涂层的沉积率高(52%~55%)、孔隙率低(1.1%)、显微硬度高(1200~1 300 HV300g);各涂层脱碳程度小,涂层物相均为WC、W2C和非晶或纳米晶相;相同喷涂工艺下WC17Co、WC12Co、WC10Co4Cr涂层的耐磨粒磨损性能依次增强,同时WC10Co4Cr涂层具有较强的耐盐雾腐蚀性能。     

微纳米 涂层在 介质中的抗泥沙冲蚀性能研究

采用超音速火焰喷涂 (HVOF) 工艺制备了微纳米、 纳米和普通结构 WC-10Co4Cr 金属陶瓷涂层, 测量了涂层的显微硬度、 孔隙率和开裂韧性, 分析了三种 WC-10Co4Cr 涂层在 3.5wt% NaCl 溶液中的腐蚀电位和腐蚀电流密度, 研究了喷涂层在 NaCl 介质中的抗泥沙冲蚀性能, 并探讨了涂层在 NaCl 介质中的泥沙冲蚀机理。 结果表明： 微纳米 WC-10Co4Cr 涂层具有最优异的电化学性能; 相比于纳米、 微米涂层, 微纳米涂层的抗泥沙冲蚀磨损性能分别提高了 38% 和 78%。 微纳米 WC-10Co4Cr 涂层致密的组织结构、 高显微硬度 (1126HV0.3) 和高开裂韧性 (4.66MPa·m1/2) 有效减弱了泥沙冲蚀过程中的机械冲刷作用和电化学腐蚀作用。     

M152钢基体超音速火焰喷涂WC-17Co涂层性能研究

采用超音速火焰喷涂技术在M152钢上制备了WC-17Co涂层。对WC-17Co涂层的耐磨性能和耐蚀性能进行了研究。结果表明超音速火焰喷涂WC-17Co涂层显著提高了M152钢基体的抗盐雾腐蚀性能,同时WC-17Co涂层具有优异的抗氧化性能和耐磨性能,可用于M152钢零件中温区域的耐磨、耐蚀防护。     

超音速火焰喷涂WC-10Co4Cr涂层在含Cl~-环境中的腐蚀行为

在Q235钢表面,采用超音速火焰喷涂(HVOF)技术制备了WC-10Co4Cr金属陶瓷涂层。利用扫描电镜(SEM)、能谱仪(EDS)、万能试验机、显微维氏硬度计等设备对涂层的显微组织、成分、力学性性能进行研究。采用盐雾试验和电化学极化测试技术研究了WC-10Co4Cr涂层在含Cl~-环境中的腐蚀行为与电化学特性。结果表明,WC-10Co4Cr涂层组织均匀致密,涂层力学性能优异,结合强度平均值为71.03MPa,涂层平均显微硬度为1290.74HV0.3。盐雾试验384h后WC-10Co4Cr涂层表面生成了致密的腐蚀产物层,有效阻止了腐蚀介质的侵入,具有良好的长期防护效果。电化学测试结果表明,在含Cl~-环境中,WC-10Co4Cr涂层具有优异的耐腐蚀性能,能够对基体起到有效的保护作用。     

WC粒度对超音速火焰喷涂WC-10Co-4Cr涂层耐腐蚀性能的影响

采用制粒?高温快速烧结法制备两种分别含亚微米级和微米级WC粒径的WC-10Co-4Cr喷涂粉末,并用超音速火焰喷涂(HVOF)技术在45#钢基体上制备涂层;利用扫描电子显微镜和电化学工作站分别对涂层的显微形貌及耐腐蚀性能进行分析检测,探讨WC粒度对涂层耐腐蚀性能的影响和涂层的电化学腐蚀机理。研究结果表明：两种涂层组织致密,界面结合良好;含亚微米级WC粒径的涂层具有相对较低的孔隙率,使其涂层的耐腐蚀性能优于含微米级WC粒径的涂层。在3.5%NaCl溶液中涂层的硬质相WC和粘结相Co发生电偶腐蚀,且低电位的Co相优先腐蚀,导致WC颗粒脱落,出现凹坑及点蚀现象。     

微纳米WC-10Co4Cr涂层在NaCl介质中的抗泥沙冲蚀性能研究

采用超音速火焰喷涂(HVOF)工艺制备了微纳米、纳米和普通结构WC-10Co4Cr金属陶瓷涂层,测量了涂层的显微硬度、孔隙率和开裂韧性,分析了三种WC-10Co4Cr涂层在3.5wt%NaCl溶液中的腐蚀电位和腐蚀电流密度,研究了喷涂层在NaCl介质中的抗泥沙冲蚀性能,并探讨了涂层在NaCl介质中的泥沙冲蚀机理。结果表明:微纳米WC-10Co4Cr涂层具有最优异的电化学性能;相比于纳米、微米涂层,微纳米涂层的抗泥沙冲蚀磨损性能分别提高了38%和78%。微纳米WC-10Co4Cr涂层致密的组织结构、高显微硬度(1126HV_(0.3))和高开裂韧性(4.66MPa·m~(1/2))有效减弱了泥沙冲蚀过程中的机械冲刷作用和电化学腐蚀作用。     

The Corrosion and Wear Performance of Microcrystalline WC-10Co-4Cr and Near-Nanocrystalline WC-17Co High Velocity Oxy-Fuel Sprayed Coatings on Steel Substrate

The study of near-nanocrystalline cermet composite coating was performed by depositing near-nanocrystalline WC-17Co powder using the high velocity oxy-fuel spraying technique. The WC-17Co powder consists of a core with an engineered near-nano-scale WC dispersion with a mean grain size 427 nm. The powder particle contains 6 wt pct of the ductile phase Co matrix mixed into the core to ensure that the reinforcing ceramic phase WC material is discontinuous to limit debridement during wear, while the remainder of the binding phase (11 wt pct) is applied as a coating on the powder particle to improve the ductility. The tribological properties of the coating, in terms of corrosion resistance, microhardness, and sliding abrasive wear, were studied and compared with those of an industrially standard microcrystalline WC-10Co-4Cr coating with a WC mean grain size 3 μm. Results indicated that the WC-17Co coating had superior wear and corrosion resistance compared to the WC-10Co-4Cr coating. The engineered WC-17Co powder with a duplex Co layer had prevented significant decarburization of the WC dispersion in the coating, thereby reducing the intersplat microporosity necessary for initiating microgalvanic cells. The improved wear resistance was attributed to the higher hardness value of the near-nanocrystalline WC-17Co coating.     

等离子喷涂WC-12Co涂层制备及耐磨耐蚀性研究

采用等离子喷涂方法,在不同送粉量和喷涂距离下制备WC-12Co涂层,研究了喷涂工艺参数变化对涂层显微结构、结合强度、表面硬度及耐磨耐蚀性能的影响.利用扫描电子显微镜（SEM）、能谱仪（EDS）测试分析了涂层的形貌和成分;利用显微硬度计测定了涂层的显微硬度;利用万能试验机测定了涂层的抗拉强度;利用高速环块磨损实验机测试了涂层的耐磨性能;利用CHI660D电化学工作站和三电极体系测试了涂层的电化学性能.结果表明,喷涂过程中送粉量和喷涂距离的改变对WC-12Co涂层的结合强度和硬度影响显著,喷涂过程中有新相产生,合理喷涂工艺参数的优选可使涂层的抗拉强度和表面硬度显著提高,涂层孔隙分布均匀,耐磨耐蚀性能良好.     

HVAF喷涂La2O3改性WC-20Cr3C2-11NiMo涂层的耐磨耐蚀性能

为进一步提升高质量WC涂层的耐磨性、耐海水腐蚀性和耐海水气蚀性。采用大气超音速火焰喷涂(HVAF)在0Cr13Ni5Mo基体上制备稀土La₂O₃改性WC-20Cr₃C₂-11NiMo涂层。通过显微硬度测试、平面孔隙测试、摩擦磨损实验、电化学实验和模拟海水超声波气蚀实验,测试涂层的显微硬度、孔隙率、摩擦因数、摩擦磨损性能、耐海水腐蚀性能和耐海水气蚀性能,分析La₂O₃对WC-20Cr₃C₂-11NiMo涂层耐磨耐蚀性能的影响。结果表明,改性后的涂层显微硬度提升到1400 HV0.2左右,平均孔隙率降低约48.6%;涂层磨损质量降低约33%,摩擦因数降低约30%,摩擦磨损表面微凹坑和微裂纹明显减少;电化学自腐蚀电位明显右移,电化学自腐蚀电流密度明显减小;涂层的气蚀质量损失减少约20%,气蚀坑洞明显减少和变小。HVAF喷涂La₂O₃改性后的WC-20Cr₃C₂-11NiMo涂层硬度略微提升,致密性、耐磨性、耐海水腐蚀性和耐海水气蚀性得到明显提升,除表面疲劳磨损外,表面摩擦磨损机理从严重磨粒磨损转变为轻微磨粒磨损,气蚀机理主要为流体冲击波侵蚀。     

超音速火焰喷涂WC-10Co4Cr涂层对30CrMnSiA钢防护性能的影响

为增强30CrMnSiA钢的耐磨与防腐性能,采用超音速火焰喷涂制备WC-10Co4Cr防护涂层,并与传统硬铬镀层进行性能对比。扫描电镜观察显示,WC-10Co4Cr涂层孔隙率低,结构均匀致密。显微硬度与摩擦磨损测试表明,WC-10Co4Cr涂层较硬铬镀层硬度提高了1.4倍,耐磨性提高4倍以上;耐蚀性测试表明,WC-10...     

Ag含量对WC-12Co/Ag涂层高温摩擦性能的影响

采用超音速火焰喷涂技术制备了三种不同Ag含量(10%,15%和20%)的WC-12Co/Ag涂层,将其高温摩擦性能与WC-12Co涂层进行对比。通过微观检测手段分析了Ag在涂层中的分布形态;检测了500℃,不同载荷(50N,100N,150N和200N)条件下,WC-12Co/Ag涂层摩擦因数随摩擦行程增加而变化的情况;并观察了涂层高温摩擦试验后磨痕微观形貌以及Ag元素的分布状态。试验结果表明:Ag元素在涂层中均匀分布,涂层中的Ag主要以单质的形式存在;在500℃条件下,当Ag含量大于15%时,Ag元素在磨损界面处形成一定厚度的连续润滑膜,起到良好的自润滑作用。     

热喷涂WC-10Co4Cr涂层的研究现状

WC陶瓷涂层以其较高的硬度和优良的耐磨性能而被广泛的应用于各种耐磨保护涂层。文章综述了热喷涂WC-10Co4Cr涂层的主要制备方法及工艺现状;指出了其中最为适合制备WC-10Co4Cr粉末和涂层的技术方法,并总结了近年来热喷涂技术特别是超音速火焰喷涂技术制备WC-10Co4Cr涂层的主要研究进展;同时,通过对影响涂层组织和性能的主要因素和影响机理的分析,对热喷涂WC-10Co4Cr陶瓷涂层的研究趋势进行了展望,提出值得关注稀土元素对WC-10Co4Cr涂层的改性作用。     

低温超音速火焰喷涂纳米WC-10Co4Cr涂层的显微结构和性能

以纳米和微米WC-10Co4Cr粉末为热喷涂粉末,采用低温超音速火焰喷涂（LT-HVOF）和超音速火焰喷涂（HVOF）技术制备了WC-10Co4Cr涂层,采用SEM、XRD、和显微硬度仪等对LT-HVOF WC涂层显微结构和性能进行了表征.结果表明：n-WC涂层、lm-WC涂层的显微结构与普通超音速火焰喷涂WC涂层没有明显的区别,其主晶相为WC; m-WC涂层呈明显的层状结构,涂层中WC颗粒尖端发生了钝化和部分熔化,粒径变小,并形成了WC/的核壳结构;其主晶相为.n-WC涂层显微硬度较lm-WC涂层低,但其韧度高而使涂层的磨损失重最低;m-WC涂层的显微硬度和韧度最低,磨损失重最大.     

HVAF喷涂超细WC-10Co-4Cr粉末涂层的耐腐蚀性研究

对比研究超细和常规粒度WC-10Co4Cr粉末喷涂制备涂层的性能,根据显微形貌、力学性能与电化学特性比较两种涂层的耐腐蚀性并分析机理。在304不锈钢基体上,利用空气助燃高速(High Velocity Air Fuel, HVAF)热喷涂技术制备WC-10Co-4Cr涂层。采用SEM和XRD分析了涂层的物相组成和显微形貌,采用维氏硬度仪和万能拉伸试验机分别测试了涂层的显微硬度与结合强度以表征力学性能,在质量分数为3.5%的NaCl溶液中对涂层进行电化学分析。结果表明：两种WC-10Co-4Cr粉末涂层均具有优异的耐腐蚀性能,超细粉末涂层自腐蚀电位(-0.199 V)高于常规粉末粒径涂层(-0.267 V);超细粉末粒径涂层腐蚀电流密度(1.996×10^-7 A/cm2)小于常规粉末粒径涂层(3.123×10^-6 A/cm²),对基体能起到良好的保护作用。超细粉末与常规粉末WC-10Co-4Cr涂层电位腐蚀的机理主要是WC与粘结相的电偶腐蚀、Cl-对涂层表面钝化膜的破坏引起的孔蚀,腐蚀机理基本一致,主要差异在于,超细粉末涂...