Influence of residual stresses from shot peening on fretting fatigue crack growth

One method to improve fretting fatigue life is to shot peen the contact surfaces. Experimental fretting life results from specimens in a Titanium alloy with and without shot peened surfaces were evaluated numerically. The residual stresses were measured at different depths below the fretting scar and compared to the corresponding residual stress profile of an unfretted surface. Thus, the amount of stress relaxation during fretting tests was estimated. Elastic–plastic finite element computations showed that stress relaxation was locally more significant than that captured in the measurements. Three different numerical fatigue crack growth models were compared. The best agreement between experimental and numerical fatigue lives for both peened and unpeened specimens was achieved with a parametric fatigue growth procedure that took into consideration the growth behaviour along the whole front of a semi‐elliptical surface crack. Furthermore, the improved fretting fatigue life from shot peening was explained by slower crack growth rates in the shallow surface layer with compressive residual stresses from shot peening. The successful life analyses hinged on three important issues: an accurate residual stress profile, a sufficiently small start crack and a valid crack growth model.     

Effects of shot-peening intensity on fretting fatigue crack-initiation behaviour of Ti–6Al–4V

The effects of shot‐peening intensity on fretting fatigue crack‐initiation behaviour of titanium alloy, Ti–6Al–4V, were investigated. Three intensities, 4A, 7A and 10A with 100% surface coverage, were employed. The contact geometry involved a cylinder‐on‐flat configuration. Residual stress and improvement in fretting fatigue life were directly related to shot‐peening intensity. The magnitude of compensatory tensile stress and its location away from the contact surface increased with increasing intensity. The relaxation of residual stress occurred during fretting fatigue which increased with increasing the number of cycles. An analysis using a critical plane‐based fatigue crack‐initiation model showed that stress relaxation during the fretting fatigue affects life and location of crack initiation. Greater relaxation of the residual stress caused greater reduction of fatigue life and shifted the location of crack initiation from inside towards the contact surface. Modified shear stress range (MSSR) parameter was able to predict fretting fatigue crack‐initiation location, which agreed with the experimental counterparts. Also, the computed parameter showed an appropriate trend with the experimental observations of the measured fretting fatigue life based on the shot‐peening intensity.     

Low cycle fatigue life prediction in shot‐peened components of different geometries—part I: residual stress relaxation

In this study, the residual stress relaxation behaviour occurring during low‐cycle fatigue in shot‐peened specimens with either a flat or a notched geometry has been studied. A representative low‐pressure steam turbine material, FV448, was used. The residual stress and strain hardening profiles caused by shot peening were measured experimentally and were then incorporated into a finite element model. By allowing for both effects of shot peening, the residual stress relaxation behaviour was successfully simulated using this model and correlated well with the experimental data. Although more modelling work may be required to simulate the interaction between shot peening effects and external loads in a range of notched geometries, the model predictions are consistent with the specimens tested in the current study. The novelty of this study lies in the development of such a modelling approach which can be used to effectively simulate the complex interaction between shot peening effects and external loads in notched regions. Compared with the un‐notched geometry, the notched geometry was found to be more effective in retaining the improvement in fatigue life resulting from shot peening, by restricting the compressive residual stress relaxation during fatigue loading.     

Experimental results in fretting fatigue with shot and laser peened Al 7075-T651 specimens

This work focuses on determining the effect of shot and laser peening on fretting fatigue in the Al 7075-T651 alloy. These surface treatments generate a residual compressive stress field near the treated surface where contact under fretting fatigue produces high stress levels. The fretting fatigue resistance of shot and laser peened specimens was assessed in a series of tests involving measurements of the residual stress field, residual stress relaxation under the action of cyclic loads, the friction coefficient, surface roughness and material hardness. The obtained results are compared with those for untreated specimens. The tests show the beneficial effect of the compressive residual stresses and the improvement that surface roughness causes in fretting fatigue life, especially in shot peened specimens. Another important effect observed, is the partial residual stress relaxation produced during the fretting fatigue tests.     

Crack incubation in shot peened AA7050 and mechanism for fatigue enhancement

Shot peening is a dynamic cold‐working process involving the impingement of peening media onto a substrate surface. Shot peening is commonly used as a surface treatment technique within the aerospace industry during manufacturing to improve fatigue performance of structural components. The compressive residual stress induced during shot peening results in fatigue crack growth retardation, improving the performance of shot‐peened components. However, shot peening is a compromise between the benefit of inducing a compressive residual stress and causing detrimental surface damage. Because of the relatively soft nature of AA7050‐T7451, shot peening can result in cracking of the constituent precipitate particles, creating an initial damage state. The aim of this paper is to understand the balance and fundamentals of these competing phenomena through a comparative study throughout the fatigue lifecycle of baseline versus shot‐peened AA7050‐T7451. Microstructure and surface topology characterization and comparison of the baseline and shot‐peened AA7050‐T7451 has been performed using scanning electron microscopy, electron backscatter diffraction, energy dispersive spectroscopy, and optical profilometry techniques. A residual stress analysis through interrupted fatigue of the baseline and shot‐peened AA7050‐T7451 was completed using a combination of X‐ray diffraction and nanoindentation. The fatigue life performance of the baseline versus shot‐peened material has been evaluated, including crack initiation and propagation. Subsurface particles crack upon shot peening but did not incubate into the matrix during fatigue loading, presumably due to the compressive residual stress field. In the baseline samples, the particles were initially intact, but upon fatigue loading, crack nucleation was observed in the particles, and these cracks incubated into the matrix. In damage tolerant analysis, an initial defect size is needed for lifetime assessment, which is often difficult to determine, leading to overly conservative evaluations. This work provides a critical assessment of the mechanism for shot peening enhancement for fatigue performance and quantifies how incubation of a short crack is inhibited from an initially cracked particle into the matrix within a residual stress field.     

Fretting fatigue behaviour of shot-peened Ti-6Al-4V at room and elevated temperatures

Fretting fatigue behaviour of shot‐peened titanium alloy, Ti‐6Al‐4V was investigated at room and elevated temperatures. Constant amplitude fretting fatigue tests were conducted over a wide range of maximum stresses, σ_max= 333 to 666 MPa with a stress ratio of R= 0.1 . Two infrared heaters, placed at the front and back of specimen, were used to heat and maintain temperature of the gage section of specimen at 260 °C. Residual stress measurements by X‐ray diffraction method before and after fretting test showed that residual compressive stress was relaxed during fretting fatigue. Elevated temperature induced more residual stress relaxation, which, in turn, decreased fretting fatigue life significantly at 260 °C. Finite element analysis (FEA) showed that the longitudinal tensile stress, σ_xx varied with the depth inside the specimen from contact surface during fretting fatigue and the largest σ_xx could exist away from the contact surface in a certain situation. A critical plane based fatigue crack initiation model, modified shear stress range parameter (MSSR), was computed from FEA results to characterize fretting fatigue crack initiation behaviour. It showed that stress relaxation during test affected fretting fatigue life and location of crack initiation significantly. MSSR parameter also predicted crack initiation location, which matched with experimental observations and the number of cycles for crack initiation, which showed the appropriate trend with the experimental observations at both temperatures.     

Short‐crack thresholds and propagation in an AISI 4340 steel under the effect of SP residual stresses

The effect of residual stresses induced by shot‐peening in a high‐strength AISI 4340 steel has been studied with the purpose of deriving a consistent fatigue model incorporating the results of fatigue crack growth experiments in the threshold region for a broad range of load ratio (R‐ratio ranging from ?2.5 to 0.7), and the effect of short cracks by means of a modified El‐Haddad model. The proposed model, taking into account the effect of crack closure and being capable to assess the conditions for fatigue propagation of short cracks partially embedded in the shot‐peened surface layer, was validated against constant amplitude fatigue experiments conducted in the endurance strength region, ie, for fatigue lives up to 10⁷ cycles, with micronotched specimens in the presence of shot‐peening residual stresses. The proposed model was also validated by comparing the results of fatigue crack propagation simulations with fatigue crack growth experiments under variable amplitude loading, experimentally reproducing the combined effect of service fatigue loads and shot‐peening residual stresses.     

Mechanism modelling of shot peening effect on fatigue life prediction

A new mechanism modelling is proposed in this paper to explain the shot peening effect on fatigue life predictions of mechanical components. The proposed methodology is based on the crack growth analysis of shot peened specimens, which are affected by the interaction of surface roughness and residual stress produced during the shot peening process. An asymptotic stress intensity factor solution is used to include the surface roughness effect and a time‐varying residual stress function is used to change the crack tip stress ratio during the crack propagation. Parametric studies are performed to investigate the effects of surface roughness and the residual stress relaxation rate. Following this, a simplified effective residual stress model is proposed based on the developed mechanism modelling. A wide range of experimental data is used to validate the proposed mechanism modelling. Very good agreement is observed between experimental data and model predictions.     

Prediction of 3D small fatigue crack propagation in shot-peened specimens

Shot peening has been widely applied in industrial design to improve fatigue durability of high loaded machine components. The compressive residual stress induced by shot peening is in general assumed to be responsible for the improvement of material fatigue strength. In the present work a cyclic cohesive zone model is extended to analyze three-dimensional fatigue crack growth in shot-peened specimens. Fatigue crack growth behaviors in both unpeened and peened specimens are investigated using 3D finite element analysis. The parameters of the cohesive zone model have been identified in 2D unpeened specimens and are applied to predict peened specimens directly. The results indicate that shot peening strongly affects crack initiation time and crack profiles, but has little effect on crack propagation rate. It implies that the shot peening will hardly change Paris’ law used for the damage tolerant design.     

激光喷丸强化对半圆孔件疲劳寿命的影响

为研究激光喷丸强化对7075-T6铝合金半圆孔件疲劳寿命的影响,对激光喷丸与未喷丸的试样进行了对比试验,利用X射线应力仪测定其表面残余应力,并对试样进行疲劳拉伸试验.用扫描电镜观察了两类试样疲劳断口的形貌,并采用数理统计方法对其疲劳寿命进行分析.研究表明:经激光喷丸处理区域,表面存在较大的残余压应力,幅值为310 MPa;未喷丸试样疲劳裂纹条带的宽度为0.7~0.8μm,而喷丸试样疲劳裂纹条带的宽度为0.3~0.4μm,说明喷丸试样裂纹扩展的速度比未喷丸试样慢很多;激光喷丸后半圆孔件的疲劳寿命比未喷丸的疲劳寿命提高了2.8~7.2倍.     

A stress approach model for predictions of fatigue life by shot peening of EN45A spring steel

A lot of research has been done to improve fatigue strength of materials by creating compressive residual stress field in their surface layers through shot peening. In this paper, fatigue strength of shot peened leaf springs has been calculated from laboratory samples. The axial fatigue strength of EN45A spring steel specimen is evaluated experimentally as a function of shot peening in the conditions used for full-scale leaf springs testing in industries. Optimum shot peening condition for specimen is found and S/N curves of the specimens are correlated with leaf springs curve. A mathematical model has been developed which predicts the fatigue life of leaf springs for a given stress at varying shot peening conditions. Predictions from this model are compared with experimental data. The estimation of fatigue life and relaxation of compressive residual stress field are discussed.     

The influence of hammer peening on fatigue in high-strength steel

An investigation of the influence of hammer peening on fatigue crack initiation and propagation in high-strength steel has been performed using edge notch specimens. The crack initiation time was found to decrease after peening; however, the fatigue crack growth stage remained unchanged or decreased depending upon the peening parameters. The results have been used to develop an analytical model to predict the fatigue crack growth rate in peened materials, based upon the compressive residual stress effect.     

Fatigue of shot peened 7075-T7351 SENB specimen – A 3-D analysis

As‐received or shot peened 7075‐T7351 single‐edged notch bend (SENB) specimens, 8.1‐mm thick, were fatigued at a constant maximum load and at stress ratios of R= 0.1 and 0.8 to predetermined numbers of fatigue cycles or to failure. The SENB specimens were then fractured by overload and the tunnelling crack profiles were recorded. The crack‐growth rate, da/dN, after crack initiation at the notch was determined by crack‐profile measurement and fractography at various fatigue cycles. The shot peened surface topography and roughness was also evaluated by three‐dimensional (3‐D) laser scanning microscopy. Residual stresses in the as‐received specimens and those generated by shot peening at Almen scales of 0.004A, 0.008A, 0.012A and 0.016A, were measured by an X‐ray diffraction stress analyser with an X‐ray target, CrK, every 0.1 mm to a depth of 1 mm. The 3‐D stress intensity factor of the curved crack front was determined by the superposition of the 3‐D finite element solutions of the stress intensity factor of the loaded SENB specimen without the residual stress and the stress intensity factor of the unloaded SENB specimen with a prescribed residual stress distribution. da/dN versus the resultant stress intensity factor amplitude, ΔK_I, plots showed that while the residual stress locally retarded the crack‐growth rate it had no effect on the overall crack‐propagation rate.     

EFFECT OF SHOT PEENING ON FATIGUE BEHAVIOR IN AL-ALLOYS

The individual contributions of residual compressive stresses, high dislocation densities, and surface roughness that are induced by shot peening to the improvement of fatigue life of Al 2024 are assessed. Stress amplitudes to number of fatigue cycles (S-N) curves and microcrack propagation (da/dN-ΔK curves) are determined for both underaged (T3) and peak-aged (T6) conditions. The fatigue behavior of the electropolished (which is also the reference condition), shot peened, shot peened and stress relieved, shot peened and polished, and shot peened, stress relieved, and polished condition is evaluated in fatigue tests.     

The influence of partial surface shot peening on fatigue crack growth behaviour of a high‐strength ferritic steel

The effects of partial surface shot peening on the fatigue crack growth behaviour of a ferritic steel have been experimentally investigated in this paper. Dog‐bone specimens fabricated from Optim700QL were tested under tension‐tension fatigue loads. Three distinct extents of partial shot peening, with respect to the crack tip and specimen symmetry line, were tested. The fatigue crack growth results from these experiments have been compared with those obtained from the same specimen geometry but with no peening. The results show that the residual stress fields formed ahead of the initial notch tip due to the partial peening process play a significant role in the fatigue crack growth behaviour of the material and effectively result in accelerated crack propagation at the midwidth of the specimens. It has been shown in this study that partial peening can lead to a fatigue crack growth rate around twice as fast as that of the unpeened specimen.     

Kugelstrahlen von Spaltbiegeprofilen mit ultrafeinkörnigen Gradientengefügen

Linear bend splitting and linear flow splitting are innovative methods to produce bifurcated profiles with ultrafine grained (UFG) microstructures in an integral style. Linear bend split profiles exhibit high potential for lightweight applications, due to their bifurcations and the high strength of the ultrafine grained microstructures, which develop at the surface of the work piece. The presence of the ultrafine grained microstructure is accompanied by a duplication of hardness and strength and a markedly increase of the fatigue properties, compared to the untreated material. Because of their high strength, ultrafine grained materials exhibit increased potential for the formation of compressive residual stresses. Therefore, shot peening of ultrafine grained microstructures could result in an increased fatigue resistance. The results clearly show that shot peening, despite optimized shot peening parameters, does not lead to an increase of the fatigue resistance. Compared to the untreated ultrafine grained microstructure, the fatigue resistance of shot peened material is even lower. The lower fatigue resistance is probably caused by the roughness of the shot peened surface, which overcompensates the compressive residual stresses.     

Influence of anodization on the fatigue strength of 7050-T7451 aluminium alloy

In recent years, with higher demand for improved quality and corrosion resistance, recovered substrates have been extensively used. Consequently residual stresses originated from these coatings reduce the fatigue strength of a component. Due to this negative influence occasioned by corrosion resistance protective coatings, an effective process like shot peening must be considered to improve the fatigue strength. The shot peening treatment pushes the crack sources beneath the surface in most of medium and high cycle cases due to the compressive residual stress field (CRSF) induced. The aim of this study was to evaluate the influence on the fatigue life of anodic films grown on 7050-T7451 aluminium alloy by sulphuric acid anodizing, chromic acid anodizing and hard anodizing. The influence on the rotating and reverse bending fatigue strength of anodic films grown on the aluminium alloy is to degrade the stress life fatigue performance of the base material. A consistent gain in fatigue life in relation to the base material was obtained through the shot peening process in coated specimens, associated to a residual stress field compressive near the surface, useful to avoid fatigue crack nucleation and delay or even stop crack propagation.     

Shot peening of plasma nitrided steel for fretting fatigue strength enhancement

Abstract

The potential of fretting fatigue strength enhancement by a duplex surface engineering process involving shot peening of plasma nitrided steel, termed duplex SP/PN, is demonstrated. Specimens of 709M40 steel were individually plasma nitrided, shot peened, or duplex SP/PN treated. Fretting fatigue properties of the surface engineered specimens were evaluated. Surface roughness, residual stress, and hardening effect following the various surface treatments were examined and compared. It has been found that the duplex treatment can significantly improve the fretting fatigue strength of the investigated low alloy steel. Under the present testing conditions, the duplex SP/PN treatment increased the fretting fatigue strength (at 10⁷ cycles) of 709M40 steel by more than 70% relative to the nitrided, 120% to the shot peened, and 500% to the untreated steel. The improvement has been explained in terms of the significantly increased surface hardness and compressive residual stress in the near surface region following the duplex SP/PN treatment. By analysing the stress distributions in a shot peened surface, the influence of surface roughness on fretting fatigue strength is also discussed.     

Low cycle fatigue life prediction in shot‐peened components of different geometries – part II: life prediction

This study investigates the effects of shot peening on the low‐cycle fatigue performance of a low‐pressure steam turbine blade material. The finite element model incorporating shot‐peening effects, which has been introduced in part I, has been used to predict the stabilised stress/strain state in shot‐peened samples during fatigue loading. The application of this model has been extended to different notched geometries in this study. Based on the modelling results, both the Smith–Watson–Topper and Fatemi–Socie critical plane fatigue criteria have been used to predict the fatigue life of shot‐peened samples (treated with two different peening intensities) with varying notched geometries. A good agreement between experiments and predictions was obtained. The application of a critical distance method considering the stress and strain hardening gradients near the shot‐peened surface has been found to improve the life prediction results. The effects of surface defects on the accuracy of life predictions using the proposed method were also discussed.     

The effect of residual stresses arising from laser shock peening on fatigue crack growth

Residual stresses have in the past been introduced to manipulate growth rates and shapes of cracks under cyclic loads. Previously, the effectiveness of shot peening in retarding the rate of fatigue crack growth was experimentally studied. It was shown that the compressive residual stresses arising from the shot peening process can affect the rate of crack growth. Laser shock peening can produce a deeper compressive stress field near the surface than shot peening. This advantage makes this technique desirable for the manipulation of crack growth rates. This paper describes an experimental program that was carried out to establish this effect in which steel specimens were partially laser peened and subsequently subjected to cyclic loading to grow fatigue cracks. The residual stress fields generated by the laser shock peening process were measured using the neutron diffraction technique. A state of compressive stress was found near the surface and tensile stresses were measured in the mid-thickness of the specimens. Growth rates of the cracks were observed to be more affected by the tensile core than by the compressive surface stresses.