高岭土/聚甲基丙烯酸甲酯核壳结构复合粒子对聚丙烯动态机械性能的影响

采用乳液聚合方法,以高岭土为核,甲基丙烯酸甲酯(MMA)为壳制备了具有核壳结构的共聚物。将制得共聚物与聚丙烯共混,用动态机械分析仪测试其共混物的动态机械性能,得出共混体系中温度与内耗因子的关系,温度与储能模量的关系以及温度与损耗模量的关系,并对所得的参数进行对比分析。研究表明,该种核壳结构的共聚物粒子与聚丙烯有很好的相容性,可以提高聚丙烯材料的阻尼性能,且可降低聚丙烯材料的玻璃化温度从而改善聚丙烯的柔韧性。     

PA6/ABS共混材料的微观结构与相容性

为改善PA6/ABS共混材料的微观结构与相容性,提高该共混材料的性能,分析了聚酰胺6(polyamide 6,PA6)结晶行为、丙烯腈-丁二烯-苯乙烯共聚物(acrylonitrile-butadiene-styrene copolymer,ABS)"核-壳"结构、共混物组成和工艺等条件对PA6/ABS共混材料微观结构与相容性的影响,介绍环氧型和酸酐型反应性增容剂对PA6/ABS共混材料微观结构与性能的影响及其作用机理,并对PA6/ABS共混材料的理论研究和工程应用进行评述.分析表明,随着PA6/ABS共混材料中组分ABS含量增多,PA6的微观形貌由球晶向片晶转变,且ABS "核-壳"结构颗粒可有效增韧PA6;反应性增容剂与PA6/ABS共混材料发生的接枝反应可降低界面张力,使分散相颗粒分布均匀.     

尼龙-1010/聚丙烯共混体系相容性的研究

利用溶剂法将尼龙－１０１０和聚丙烯接枝丙烯酸共聚物制取共混材料,测试了其力学性能及其形态结构．结果表明：有聚丙烯接枝丙烯酸共聚物作增容剂的增容共混体系中,尼龙－１０１０和聚丙烯两相相容性好,力学性能优于无增容剂的共混体系,形态结构观察亦证实了这一点．     

尼龙—1010／聚丙烯共混体系相容性的研究

利用溶剂法将尼龙－１０１０和聚丙烯烯接枝丙烯酸共聚物制取共混材料,测定了其力学性能及其形态结构,结果表明：有聚丙烯接枝丙烯酸共聚物作增容剂的增容共混体系中,尼龙－１０１０和聚丙烯两相相容性好,力学性能优于无增容剂的共混体系,形态结构观察亦证实了这一点。     

核壳型含氟丙烯酸酯聚合物的共混成膜研究

为了得到表面性能和内部结构优异而成本较低的含氟丙烯酸酯聚合物共混乳胶膜,采用半连续种子乳液聚合法制备了核相为MMA和BA、壳相中F6MBA含量不同的核壳型含氟丙烯酸酯聚合物乳液,通过动态光散射、透射电镜检测了乳液的稳定性、单分散性和乳胶粒的核壳结构,并合成了普通丙烯酸酯聚合物乳液(PMMA-co-BA)。将含氟核壳乳液与普通丙烯酸酯聚合物乳液共混成膜并热处理,得到共混乳胶膜样品,通过静滴接触角、红外、拉曼、扫描电镜能谱等表征膜的结构和性能,研究氟含量对共混乳胶膜结构与性能的影响。结果表明:随着氟含量的增加,膜与空气界面(F-A)的表面能降低,且下降幅度随着退火时间的延长而变大;共混膜的体系含氟量仅约为16.7%时,其F-A面表面能可低至18.75mN/m;壳相含氟50%的共混膜的断面具有氟的浓度梯度结构。     

核壳结构丙烯酸酯共聚物乳液的合成研究

以丙烯酸丁酯为核单体,甲基丙烯酸甲酯和丙烯酸乙酯为壳单体,十二硫醇为壳层聚合的链转移剂,采用种子乳液共聚方法制备核壳结构的丙烯酸酯共聚物.研究单体、链转移剂的用量对壳层聚合物的玻璃化温度、黏流温度和熔体流动速率的影响,用扫描电子显微镜对乳胶粒结构进行研究.实验结果表明:加入丙烯酸乙酯或十二硫醇,可以降低壳层聚合物的玻璃化温度和黏流温度,增加熔体流动速率,加入质量分数为0.1%的十二硫醇可以使壳层共聚物(m(MMA)/m(EA)=80/20)的熔体流动速率提高到0.863 g/min,提高了2个数量级,核壳聚合物乳胶粒径在100～200nm之间,粒径分布较窄.     

聚丙烯酸/聚乙烯醇共混物结构研究

将丙烯酸／丙烯酰胺二元共聚物与聚乙烯醇共混后经热交联处理得到吸水性较好的聚丙烯酸／聚乙烯醇共混树脂，利用傅立叶红外光透射谱图(FT-IR)、热重谱图(TG-DTA)和动态力学分析温度谱图(DMA)详细分析了树脂的结构和热性能、结果表明，共混物大分子间形成了有效的化学交联点且二元共聚物与聚乙烯醇间存在相互作用、     

动态交联热塑性弹性体增韧聚丙烯合金

用动态交联方法制备聚烯烃热塑性弹性体（ＴＰＯ）增韧聚丙烯，制备了具有低温冲击性能良好、综合力学性能比较均衡的聚丙烯合金。同时，研究了ＴＰＯ组成、工艺及基体组成与ＴＰＯ增韧聚丙烯共混物力学性能的关系。并通过差热扫描量热计和扫描电镜考察了共混物的形态结构。     

碳酸钙和乙烯-辛烯共聚物对废旧聚丙烯塑料的改性

研究了废旧聚丙烯塑料的共混工艺、增强增韧改性及共混物的流动性能.以废旧聚丙烯塑料为研究对象,加入无机填料碳酸钙,增韧剂乙烯-辛烯共聚物及适量相容剂马来酸酐接枝聚丙烯对其进行增强增韧改性,通过熔融共混法制备了聚丙烯/碳酸钙、聚丙烯/碳酸钙/乙烯-辛烯共聚物两种复合材料.结果表明:碳酸钙和乙烯-辛烯共聚物对废旧聚丙烯塑料均有良好的的增韧效果,马来酸酐接枝聚丙烯作为聚丙烯/碳酸钙复合体系的界面改性剂能有效改善分散相碳酸钙在连续相聚丙烯中的分散状态,但乙烯-辛烯共聚物的加入会降低复合材料的拉伸强度,且共混体系的流动性能也有明显的降低趋势.当聚丙烯/碳酸钙/乙烯-辛烯共聚物质量份数比为100/15/10时,两种复合材料的悬臂梁缺口冲击强度均达到最大值,增韧效果最佳,弯曲强度和模量也有一定程度的提高,复合材料表现出良好的综合力学性能.     

共混对聚丙烯力学性能的影响

研究了不同牌号的聚丙烯共混后的产物的力学性能,并以DCP为硫化剂,TAIC为硫化促进剂,以自制的聚酯型超支化聚合物为流动促进剂,利用动态硫化技术制备了聚丙烯树脂/三元乙丙橡胶(EPDM)热塑弹性体.研究表明:高熔融指数的聚丙烯、共混材料中橡胶的用量以及超支化树脂的比例对共混材料的力学性能和高温流动性有很大影响.     

包覆Fe_2O_3超微粒复合共聚物的动态力学性能研究

采用种子乳液聚合法将Ｆｅ２Ｏ３超微粒包覆在苯乙烯／丙烯酸／丙烯酸丁酯（Ｓｔ／ＡＡ／ＢＡ）核－壳型复合共聚物中，形成包覆有无机粒子的有机高分子核－壳型复合微球，从微观的分子尺寸上改变了复合共聚物的性能，并着重研究Ｆｅ２Ｏ３的含量对这种复合共聚物的动态力学性能的影响。结果表明，随着Ｆｅ２Ｏ３含量的增加，复合共聚物的内耗明显增加，刚性显著下降。因而Ｆｅ２Ｏ３加入对复合共聚物有增韧作用，改善了复合共聚物的力学性能。     

PP-g-（MAH-CO-St）对PP／SMA相容性及力学性能影响的研究

为预测接枝物PP-g（MAH-CO-St）对PP／SMA共混物增容效果和力学性能的影响,采用分子动力学模拟法在COMPASS力场下对PP、SMA、PP／SMA和PP／SMA／PP-g-（MAH-CO-St）的玻璃化温度、聚合物结合能、聚合物均方位移和力学性能进行模拟计算,同时采用实验方法测定聚合物的力学性能、水接触角以及缺口断裂形貌。通过比较共混体系加入增容剂前后的玻璃化温度、聚合物结合能和均方位移的变化预测其增容效果,比较拉伸模量和剪切模量和体积模量的变化预测其力学性能的影响。结果表明,PP-g-（MAH-CO-St）可作为PP／SMA很好的增容剂且可明显提高其韧性和断裂强度,有效改善其力学性能。     

基于DMA方法的沥青胶浆微观结构

采用动态力学分析(DMA)方法对沥青胶浆的微观结构进行了研究,通过对沥青胶浆的动态黏弹性能的变化规律以及Han曲线的温度依赖性进行分析。比较了沥青胶浆和改性沥青胶浆的相态结构的区别,并且根据沥青及沥青矿粉胶浆的损耗因子tanδ计算出参数A,用来评价沥青与胶浆的界面粘结程度。研究结果表明了用DMA方法可以很好地研究沥青胶浆的微观结构,从而为更好地改善沥青胶浆的路用性能提供了理论依据。     

聚丙烯/乙烯-辛烯共混物的动态交联及性能

利用动态交联技术制备了动态交联聚丙烯/乙烯-辛烯共混物(PP/POE).采用哈克转矩流变仪研究了动态交联对PP/POE共混物扭矩的影响;研究了交联剂的种类和POE用量对共混物力学性能的影响;考察了动态交联共混物的流变性能.结果表明,加入过氧化二异丙苯(DCP)后,PP/POE共混物的扭矩先升后降至平衡状态;随着POE用量的增加,PP/POE共混物的冲击强度明显提高,但拉伸强度有所降低,PP/POE共混物合适配比为100∶40,DCP的添加量为POE含量的2%为优;PP/POE共混物熔体流变行为属于假塑性流体,且高温下(220℃)降解反应程度高于交联反应程度.     

Experimental investigation on dynamic mechanical characteristics and microstructure of steam-cured concrete

Steam-cured concrete is widely used to manufacture prefabricated units of high-speed railway foundation structure such as girder and track slab. The dynamic mechanical property of steam-cured concrete is one of the key properties affecting service performance of high-speed railway foundation structure. In the present paper, serial macro/micro-experiments were carried out to investigate the dynamic elastic modulus, shear modulus, damping ratio, and microstructure of steam-cured concrete. The relationships between compositions, curing regime, microstructure, and dynamic properties of steam-cured concrete as well as the corresponding mechanisms were discussed. The results indicate that steam-cured concrete in early age has a larger dynamic elastic modulus and shear modulus as well as a smaller damping ratio compared with standard-cured concrete. On the contrary, at a later age a slightly smaller dynamic elastic modulus and a larger damping ratio of steam-cured concrete are observed. Addition of mineral admixture results in a bit lower dynamic elastic modulus and damping ratio of concrete than that of the control specimen without mineral admixtures. The achievements can provide some fundamental suggestions for materials parameters selection during structural design of steam-cured concrete precast element.     

乙烯-乙烯醇与聚丙烯共混物的形态及性能

以聚丙烯接枝马来酸酐(PP-g-MAH)为增容剂,共混聚丙烯(PP)与乙烯-乙烯醇(EVOH)制备可润湿性PP.用扫描电镜(SEM)、动态粘弹谱仪(DMA)和差示扫描量热仪(DSC)分析了EVOH/PP共混物的形态结构、力学性能和热性能.用接触角测定仪表征了共混物的可润湿性.SEM结果表明共混物呈明显两相结构,EVOH...     

Z N-35硅橡胶材料的动态力学性能试验研究

针对ZN-35硅橡胶材料宽频范围下的动态力学性能问题,通过DMTA动态热机械仪测试了ZN-35硅橡胶材料在11个不同温度下低频范围内的储能模量、损耗模量、损耗因子。依照国军标GJB981—90黏弹性材料强迫非共振型动态测试方法和主曲线绘制方法,通过对测量数据的计算和处理,绘制出该种材料的主曲线。预测出了各个温度下在更高频率下的动态力学性能,为减振材料的使用及减振器件设计提供了基础数据。结果表明：相同频率下,随着温度的升高,ZN-35硅橡胶储能模量与损耗模量呈下降趋势。当温度恒定时,储能模量和损耗模量会随着频率的升高而升高,直至趋于稳定。主曲线方法可以准确地得到ZN-35硅橡胶材料的高频动态力学性能。     

Deterioration of dynamic mechanical property of concrete with mineral admixtures under fatigue loading

The dynamic mechanical property of concrete is one of the key parameters, which greatly influences durability of infrastructures subjected to continuous heavy loading, such as girder and track slab of high-speed railway foundation structure. This paper reports serials of experiments designed to investigate the deterioration of dynamic mechanical properties of different concretes under fatigue loading condition. Four parameters including relative dynamic elastic modulus (RDEM), relative dynamic shear modulus (RDSM), relative compressive strength (RCS) and water absorption (WA) of concrete were evaluated to assess the dynamic properties and microstructures of concretes. Results show that the fatigue stress levels and fatigue cycle durations significantly influence the dynamic mechanical properties of concrete including dynamic elastic modulus and dynamic shear modulus. Addition of proper mineral admixture can improve the dynamic mechanical characteristics of concrete and increase its resistance against the fatigue loading effect. Keeping the amount of mineral admixture in concrete constant, its dynamic mechanical property with fly ash is lower than that with fly ash and silica fume. The water absorption in concrete, which is an indirect parameter reflecting capillary porosity, increases evidently after bearing fatigue-loading. There is a close correlation between the deterioration of dynamic mechanical property and the increasing of water absorption of concrete. This indicates that the damage of microstructure of concrete subjected to fatigue loading is the indispensable reason for the decay of its dynamic mechanical performance.     

Anti-cracking Property of EVA-modified Polypropylene Fiber-reinforced Concrete Under Thermal-cooling Cycling Curing

In order to investigate the synergistic effect of re-dispersible powder-ethylene-vinyl acetate copolymer(EVA) and polypropylene fiber on the crack resistance of concrete under thermal fatigue loading, the compressive strength, ultimate tensile strength, ultimate tensile strain and tensile modulus of elasticity were tested. In addition, ultrasonic method and scanning electron microscope analysis were used to explain the microstructure mechanism. The results show that polypropylene fiberreinforced concrete presents a better performance on crack resistance than ordinary concrete, and the synergism of EVA and polypropylene fiber can improve the anti-cracking ability of concrete further.