Synthesis and characterization of functionalized polymer latex particles through a designed semicontinuous emulsion polymerization process

Monodispersed noncarboxylated and carboxylated poly(n‐butyl methacrylate‐co‐n‐butyl acrylate) latices were synthesized with a well‐defined semicontinuous emulsion polymerization process. A modified theory to correlate the polymerization rate to the instantaneous conversion of the monomer or comonomer mixture was developed. The resulting equation was used to determine the maximum polymerization rate only below or equal to which the polymerization could be operated in the highly monomer‐starved regime, which corresponded to an instantaneous conversion of 90% or greater. Experimental data from reaction calorimetry supported that the polymerization was under highly monomer‐starved conditions when the model latices were synthesized with the modified model. The estimation of the average number of free radicals per latex particle(n?) during the feeding stage revealed that n? was as high as 1.4 in the actual polymerization, which showed that the original selection of 0.5 as the n? value was not accurate in the developed model. From the conductimetric titration experiments, we found that most of the carboxyl groups from the methacrylic acid (MAA) were buried inside the latex particles, and the surface carboxyl group coverage increased as the MAA concentration in the comonomer feed increased. The glass‐transition temperatures of the synthesized polymers were close to the designed value from the Pochan equation, and only one glass transition was observed in the polymer samples in the differential scanning calorimetry measurements, indicating a homogeneous copolymer composition in the functionalized shell. Particle size characterization and transmission electron microscopy confirmed the uniformity in the latex particle size. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 97: 248–256, 2005     

Synthesis and characterization of model carboxylated latexes for studies of film formation from latex blends

Poly(n‐butyl methacylate‐co‐n‐butyl acylate) [P(BMA/BA)] soft latexes (carboxylated and noncarboxylated) were synthesized using a semicontinuous emulsion polymerization process that was designed on the basis of a theoretical calculation to determine the suitable surfactant [i.e., sodium dodecyl sulfate (SDS)], monomer, and water feed rates to maintain a constant particle number throughout the polymerization (guaranteeing monodispersity in the particle size), to obtain a homogeneous copolymer composition, and to independently control the particle size and carboxyl group concentration. The experimental results support the theoretical calculation. The surface coverage of the carboxyl groups present on the soft latex particles ranges from 7.6 to 21.9% for a series of latexes with particle sizes around 120 nm. In another series of latexes, the particle size was varied over a range from 120 to 450 nm. Monodisperse carboxylated polystyrene hard latexes were synthesized by shot growth (batch) and semicontinuous processes. The shot growth method is somewhat inflexible in providing more choices in surfactant, particle size, and surface carboxyl coverage. A semicontinuous process designed using a similar method used for the synthesis of P(BMA/BA) latexes successfully eliminated the drawbacks of the shot growth process. In this way, the changes in the surface carboxyl coverage (varies from 0 to 77.2%) was independent of the particle size, which was precisely controlled by the amount of styrene fed under suitable styrene and SDS feed rates. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 77: 644–659, 2000     

Role of fluorocarbon surfactant in the preparation of polytetrafluoroethylene‐modified polyacrylate emulsion

Role of fluorocarbon surfactant in the preparation of polytetrafluoroethylene‐modified polyacrylate emulsion is investigated. The fluorocarbon surfactant has an efficient preemulsification to polytetrafluoroethylene (PTFE) powder. It enables PTFE powder to be introduced into the copolymer of n‐butyl acrylate, n‐methyl methacrylate, n‐styrene, and α‐methacrylic acid. Thereby, stable PTFE‐modified polyacrylate emulsion can be formed. The effects of fluorocarbon surfactant on the surface tension, particle size and particle size distribution of the emulsion, as well as the relation between fluorocarbon surfactant and the amount of PTFE powder are fully investigated. The particle size and the surface tension of emulsion strongly depend on the fluorocarbon surfactant concentration in the reaction system. The particle size distribution becomes narrower and the stability of the emulsion is improved with the increasing of the fluorocarbon surfactant concentration. According to the experiments, a possible mechanism of fluorocarbon surfactant in polymerization is proposed. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

Morphologies of polybutylacrylate/poly(styrene‐co‐methyl methacrylate) latex prepared by starved emulsion polymerization Part I. Thermodynamics equilibrium morphology

Heterogeneous latexes were prepared by a semicontinuous seeded emulsion polymerization process under monomer starved conditions at 80 °C using potassium persulfate as the initiator and sodium dodecyl sulfate as the emulsifier. Poly(butyl acrylate) latexes were used as seeds. The second‐stage polymer was poly(styrene‐co‐methyl methacrylate). By varying the amounts of methyl methacrylate (MMA) in the second‐stage copolymer, the polarity of the copolymer phase could be controlled. Phase separation towards the thermodynamic equilibrium morphology was accelerated either by ageing the composite latex at 80 °C or by adding a chain‐transfer agent during polymerization. The morphologies of the latex particles were examined by transmission electron microscopy (TEM). The morphology distributions of latex particles were described by a statistical method. It was found that the latex particles displayed different equilibrium morphologies depending on the composition of the second‐stage copolymers. This series of equilibrium morphologies of [poly(butyl acrylate)/poly(styrene‐co‐methyl methacrylate)] (PBA/P(St‐co‐MMA)) system provides experimental verification for quantitative simulation. Under limiting conditions, the equilibrium morphologies of PBA/P(St‐co‐MMA) were predicted according to the minimum surface free energy change principle. The particle morphology observed by TEM was in good agreement with the predictions of the thermodynamic model. Therefore, the morphology theory for homopolymer/homopolymer composite systems was extended to homopolymer/copolymer systems. © 2002 Society of Chemical Industry     

Emulsion terpolymerization of dimethyl meta-isopropenyl benzyl isocyanate (TMI®) with acrylic monomers: Process development and kinetics

Dimethyl meta-isopropenyl benzyl isocyanate (TMI®) is a bifunctional monomer possessing a double bond and an isocyanate group. Emulsion terpolymerization of TMI with the acrylic monomers, methyl methacrylate and n-butyl acrylate, was studied. Polymerizations were carried out at 40°C using a redox initiator system in order to minimize the extent of hydrolysis of the isocyanate in the aqueous emulsion environment. The kinetics of the polymerization reaction were investigated. The polymerization rate was found to decrease with increasing TMI concentration. The effects of several preparative variables such as the monomer, surfactant, and initiator concentration on the polymerization kinetics was studied. Several semicontinuous polymerization processes were developed in order to enhance the incorporation of TMI at appreciable rates. These processes also allow us to control the polymer composition, latex particle size, and the locus of isocyanate groups in the latex particle. Process variables such as the mode of initiator addition (batch versus semicontinuous) were found to greatly influence the polymerization behavior. © 1996 John Wiley & Sons, Inc.     

Preparation and full characterization of cationic latex of styrene-butyl acrylate

Cationic latexes based on styrene and butyl acrylate using cetyl trimethyl ammonium bromide (CTAB) as surfactant were carried out using both batch and semicontinuous emulsion polymerization. Monomer conversion, particle size and its distribution, ζ potential, latex surface tension were determined as function of CTAB levels. Evolutions of these properties were followed, and the results from batch compared to those from semicontinuous process. It was revealed that polymerization rate in batch process was enhanced with CTAB, and the polymerization rate was controlled by addition rate of the preemulsion in semicontinuous process. Molecular adsorption area of CTAB on latex particle surface was calculated, which showed clearly that ζ potential and surface tension in the latex were directly related with surfactant adsorption on the particle surface. The molecular surface adsorption area of CTAB on latex particle could be used to explain the evolution of latex properties such as ζ potential and latex surface tension.     

Seeded emulsion terpolymerization of dimethyl meta-isopropenyl benzyl isocyanate (TMI®) with acrylic monomers

Dimethyl meta-isopropenyl benzyl isocyanate (TMI®) is a novel bifunctional monomer. It has a double bond and an isocyanate group. The seeded emulsion terpolymerization of TMI with the acrylic monomers, methyl methacrylate and n-butyl acrylate, has been studied. A copolymer of methyl methacrylate and n-butyl acrylate was used as the seed latex. In order to minimize the risk of hydrolysis of TMI, polymerizations were carried out at 40°C using redox initiators. No additional surfactant was added during the second-stage polymerization in order to avoid the nucleation of secondary particles. TMI was found to retard the polymerization kinetics. The effect of variables, such as the total number of particles, initiator concentration, and the monomer feed rate on polymerization kinetics, was investigated. The composition of the second-stage polymer could be controlled by running the polymerization under monomer-starved conditions. © 1998 John Wiley & Sons, Inc. J Appl Polym Sci 67: 685–694, 1998     

Batch and semicontinuous emulsion copolymerization of vinylidene chloride and butyl methacrylate. I. Kinetics in VDC–BMA emulsion polymerization and surface and colloidal properties of VDC–BMA latexes

Vinylidene chloride (VDC)—butyl methacrylate (BMA) comonomer mixtures with various composition (83 : 17, 60 : 40, 33 : 67 in mol %) were polymerized at 25°C using redox catalyst by batch and seeded semicontinuous emulsion copolymerization. The reactivity ratios determined in VDC (M₁)—BMA (M₂) emulsion copolymerization system were r₁ = 0.22 and r₂ = 2.41. Seven 35% solids (83 : 17 mol %) VDC–BMA copolymer latexes were prepared: one batch (G), one seeded batch (F), and 5 seeded semicontinuous polymerizations of 5 different monomer feed rates ranging from 0.27 (A) to 1.10 wt %/min (E). The kinetic studies of seeded semicontinuous polymerizations A-E showed that the rates of polymerizations (R_p) were controlled by the monomer addition rates (R_a). The conversion versus time curves for the polymerizations of 0 : 100–100 : 0 VDC–BMA mixtures by batch polymerization showed that the rate of polymerization (R_p) was a function of the number of particles, and that the rate of polymerization in a latex particle (R_pp) increased with increasing proportions of butyl methacrylate in the monomer mixture. All of the latexes had narrow particle size distributions. The greater particle number density in VDC polymerization and the greater water solubility of VDC suggest that the homogeneous nucleation mechanism is operative in VDC–BMA copolymerizations. The latex copolymers prepared by semicontinuous polymerization had lower number-and weight-average molecular weights than those of the corresponding batch copolymers, resulting from the monomer starvation occurring during the semicontinuous polymerization. The surface characterization study of the cleaned latexes showed that for the latexes by batch process, the surface charge density derived from strong-acid groups decreased with increasing proportion of VDC in the monomer mixture. On the other hand, for the latexes prepared by semicontinuous polymerization, the surface charge density derived from strong-acid groups did not depend on the monomer composition of the copolymers.     

Semicontinuous heterophase copolymerization of vinyl acetate and butyl acrylate

Vinyl acetate (VAc) and butyl acrylate (BuA) were copolymerized in heterophase by a semicontinuous process (unseeded) and compared with the seeded semicontinuous microemulsion polymerization of the same monomers. A mixture of sodium dodecyl sulfate (SDS) and poly(ethylene oxide) dodecyl ether (Brij‐35®) were used as surfactants. The effects of monomer addition rate (R_a) and surfactants concentrations (4 or 1 wt % with respect to the initial mixture of reaction) on polymer and latex properties were studied. High copolymer content latexes (24–36 wt %) with average particle diameters (D_p) from 38 to 55 nm and relatively narrow particle size distributions, high polymerization rates, weight ratios of polymer to surfactant (P/S) from 13.3 to 32.8 were obtained. The number‐average molecular weights (M_n) were between 96,000 and 188,000 g/mol. Homogeneous copolymer compositions were obtained throughout the reaction for both, seeded and unseeded processes, which is not possible by the usual batch microemulsion process. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

Morphologies and dynamic mechanical properties of core‐shell emulsifier‐free latexes and their copolymers for P(BA/MMA)/P(MMA/BA) and P(BA/MMA)/PSt systems in the presence of AHPS

Different poly(methyl methacrylate/n‐butyl acrylate)/poly(n‐butyl acrylate/methyl methacrylate) [P(BA/MMA)/P(MMA/BA)] and poly(n‐butyl acrylate/methyl methacrylate)/polystyrene [P(BA/MMA)/PSt] core‐shell structured latexes were prepared by emulsifier‐free emulsion polymerization in the presence of hydrophilic monomer 3‐allyloxy‐2‐hydroxyl‐propanesulfonic salt (AHPS). The particle morphologies of the final latexes and dynamic mechanical properties of the copolymers from final latexes were investigated in detail. With the addition of AHPS, a latex of stable and high‐solid content (60 wt %) was prepared. The diameters of the latex particles are ～0.26 μm for the P(BA/MMA)/P(MMA/BA) system and 0.22–0.24 μm for the P(BA/MMA)/PSt system. All copolymers from the final latexes are two‐phase structure polymers, shown as two glass transition temperatures (T_gs) on dynamic mechanical analysis spectra. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 86: 3078–3084, 2002     

Relationship between electrical and mechanical loss tangents of hollow glass powder reinforced epoxy composites: A pilot study

This study was focused on the synthesis of monodisperse poly(n‐butyl methacrylate‐co‐methyl methacrylate) submicrospheres via soap‐free emulsion polymerization and on their characterization. The glass‐transition temperatures of poly(n‐butyl methacrylate) and poly(methyl methacrylate) were approximately 25 and 110°C, respectively. Therefore, submicrospheres with different glass‐transition temperatures could be obtained through the variation of the copolymer composition. In addition, relationships between the monomer feed concentration (M₀) and the Mark–Houwink constant (α) for the copolymer submicrospheres were proposed. The molecular weights of the copolymer submicrospheres decreased sharply with an increase in the weight fraction of n‐butyl methacrylate. On the contrary, the particle diameter increased linearly from 277 to 335 nm with an increase in the weight fraction of n‐butyl methacrylate. The α values decreased with an increase in M₀, and this indicated that the branched structures of the copolymer submicrospheres were easily obtained when M₀ was higher than 0.11 g/mL of water. Consequently, the results of this study are expected to provide useful information for the synthesis of monodisperse copolymer submicrospheres by soap‐free emulsion polymerization. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Interfacially initiated microemulsion copolymerization: One‐stage preparation of poly(n‐butyl methacrylate)–poly(N‐vinyl pyrrolidone) core–shell nanoparticles

Interfacially initiated microemulsion copolymerizations of n‐butyl methacrylate (BMA) and N‐vinyl pyrrolidone (NVP) by the redox initiation couple of benzoyl peroxide and ferrous sulfate were carried out with Tween 80 and n‐butanol as the surfactant and cosurfactant, respectively. Fourier transform infrared spectroscopy and X‐ray photoelectron spectroscopy were recorded to analyze the chemical composition of the latex particles. Transmission electron microscopy was used to observe the particle morphology and dynamic light scattering to determine the particle size. The results demonstrated that interfacially initiated microemulsion polymerization prompted the copolymerization of the water‐soluble NVP monomer with the oil‐soluble BMA monomer to form core–shell nanoparticles. The influence of the surfactant concentration, BMA amount, and temperature on the particle size and polymerization rate was investigated. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 3751–3757, 2006     

Complexation of poly(dimethylsiloxane)/poly(methyl methacrylate‐co‐butyl acrylate‐co‐methacrylic acid) latex with poly(dimethylsiloxane)/poly(vinyl acetate‐co‐butyl acrylate) latex

Two latices—the poly(dimethylsiloxane) (PDMS)/poly(methyl methacrylate‐co‐butyl acrylate‐co‐methacrylic acid) system (PA latex) and the PDMS/poly(vinyl acetate‐co‐butyl acrylate) system (PB latex)—were prepared by seeded emulsion polymerization, and PA/PB complex latices were obtained through the interparticle complexation of the PA latex with the PB latex. In addition, for the further study of the interparticle complexation of the PA latex with the PB latex, copolymer latices [PDMS/methyl methacrylate‐co‐butyl acrylate‐co‐vinyl acetate‐co‐methacrylic acid) (PC)] were prepared according to the monomer recipe of the complex latices and the polymerization process of the component latices. The properties of the obtained polymer latices and complex latices were investigated with surface‐tension, contact‐angle, and viscosity measurements. The mechanical properties of the coatings obtained from the latices were investigated with tensile‐strength measurements. The results showed that, in comparison with the two component latices (PA latex and PB latex) and the corresponding copolymer latices (PC latices), the PA/PB complex latices had lower surface tension, lower viscosities, and better wettability to different substrates. The tensile strengths of the coatings obtained from the complex latices were higher than the tensile strengths of the coatings from the two component latices and copolymer latices. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 92: 2522–2527, 2004     

Ultrasonically initiated emulsion polymerization of n‐butyl acrylate

Ultrasonically initiated emulsion polymerization of n‐butyl acrylate (BA) without added initiator has been studied. The experimental results show that high conversion of BA can be reached in a short time by employing an ultrasonic irradiation technique with a high purge rate of N₂. The viscosity average molecular weight of poly(n‐butyl acrylate) (PBA) obtained reaches 5.24 × 10⁶ g mol^?1. The ultrasonically initiated emulsion polymerization is dynamic and complicated, with polymerization of monomer and degradation of polymer occurring simultaneously. An increase in ultrasound intensity leads to an increase in polymerization rate in the range of cavitation threshold and cavitation peak values. Lower monomer concentration favours enhancement of the polymerization rate. ¹H NMR, ¹³C NMR and FTIR spectroscopies reveal that there are some branches and slight crosslinking, and also carboxyl groups in PBA. Ultrasonically initiated emulsion polymerization offers a new route for the preparation of nanosized latex particles; the particle size of PBA prepared is around 50–200 nm as measured by transmission electron microscopy. © 2001 Society of Chemical Industry     

BA‐MMA‐POMA copolymer latexes prepared by using HMPS polymerizable emulsifier

BA‐MMA‐POMA copolymer latex was successfully prepared by soap‐free emulsion polymerization of 2‐(perfluoro‐(1,1‐bisisopropyl)‐2‐propenyl)oxyethyl methacrylate(POMA) with butyl acrylate(BA), methyl methacrylate (MMA) initiated by K₂S₂O₈ in the water. POMA was synthesized from the intermediate perfluoro nonene and 2‐hydroxyethyl methacrylate as the staring reactants. The structure of BA‐MMA‐POMA copolymer latex was investigated by Fourier transform infrared (FTIR). The characteristics of the film such as hydrophobicity and glass transition temperature were characterized with the contact angle and differential scanning calorimetry respectively. The influences of the amount of the fluorinated monomer and the initiator on the soap‐free emulsion polymerization and performance of the latex were studied. In addition, comparison with the latex prepared by the conventional emulsifier SDBS is investigated. Results show that the hydrophobicity and glass transition temperature (T_g) of the latex are increased when the fluorinated monomer is introduced to copolymerize with other monomers. The hydrophobicity can be improved further with heating. Compared with the latices prepared by using SDBS emulsifier, the latices prepared by using HMPS emulsifier have larger particle size, higher surface tension. However, the difference of their T_g is extremely minute. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Synthesis and characterization of butyl acrylate/methyl methacrylate/glycidyl methacrylate latexes

The butyl acrylate (BA)/methyl methacrylate (MMA), and glycidyl methacrylate (GMA) composite copolymer latex was synthesized by seeded emulsion polymerization technique taking poly(methyl methacrylate) (PMMA) latex as the seed. Four series of experiments were carried out by varying the ratio of BA : MMA (w/w) (i.e. 3.1 : 1, 2.3 : 1, 1.8 : 1, and 1.5 : 1) and in each series GMA content was varied from 1 to 5% (w/w). The structural properties of the copolymer were analyzed by FTIR, ¹H‐, and ¹³C‐NMR. Morphological characterization was carried out using transmission electron microscopy (TEM). In all the experiments, monomer conversion was ～99% and final copolymer composition was similar to that of feed composition. The incorporation of GMA into the copolymer chain was confirmed by ¹³C‐NMR. The glass transition temperature (T_g) of the copolymer latex obtained from the differential scanning calorimetry (DSC) curve was comparable to the values calculated theoretically. With increase in GMA content, particles having core‐shell morphology were obtained, and there was a decrease in the particle size as we go from 2–5% (w/w) of GMA. The adhesive strength of the latexes was found to be dependent on the monomer composition. With increase in BA : MMA ratio, the tackiness of the film increased while with its decrease the hardness of the film increased. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

In situ preparation and properties of high‐solid‐content and low‐viscosity poly(methyl methacrylate/n‐butyl acrylate/acrylic acid)/poly(styrene/acrylic acid) composite latexes

With monodispersed poly(methyl methacrylate/n‐butyl acrylate/acrylic acid) [P(MMA/BA/AA)] seeded latex with a particle size of 485 nm and a solid content of 50 wt % as a medium, a series of stable P(MMA/BA/AA)/poly(styrene/acrylic acid) composite latexes with a high solid content (70 wt %) and low viscosities (500–1000 mPa · s when the shear rate was 21 s^?1) was prepared in situ via simple two‐step semicontinuous monomer adding technology. The coagulum ratio of polymerization was about 0.05 wt %. The particle size distribution of such latexes was bimodal, in which the large particle was about 589 nm and the small one was about 80 nm. The latexes combined good mechanical properties with good film‐forming properties. Differential scanning calorimetry showed that the corresponding latex film had a two‐phase structure. The morphology of the latex film was characterized with atomic force microscopy and scanning electron microscopy. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 1815–1825, 2007     

Modified emulsifier‐free emulsion polymerization of butyl methacrylate with ionic or/and nonionic comonomers

A modified emulsifier‐free emulsion polymerization of butyl methacrylate (BMA) with ionic or/and nonionic comonomers was successfully used to prepare nanosized poly(butyl methacrylate) (PBMA) latices with high polymer contents. After seeding particles were generated in an initial emulsion system, consisting of a portion of BMA, water, ionic comonomer [sodium styrenesulfonate (NaSS)] or nonionic comonomer [2‐hydroxyethyl methacrylate (HEMA)] and potassium persulfate, most of the BMA monomer or the mixture of BMA and HEMA was added dropwise to the polymerizing emulsion over a period of 6–12 h. Stable latices with high PBMA contents up to 27% were obtained. It was found that the latex particle sizes (2R_h) were largely reduced (34 nm) by the continuous addition of monomer(s) compared to those (107 nm) obtained by the batch polymerization method. The effect of comonomer concentration on the particle size, the number of PBMA particles/mL of latex (N_d), and the molar mass (M_w) of copolymer during the polymerization were discussed. The surface compositions of latex particles were analyzed by X‐ray photoelectron spectroscopy, indicating that the surface of latex particles was significantly enriched in NaSS or/and HEMA. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 92: 3080–3087, 2004     

Seeded emulsion polymerization of n-butyl acrylate utilizing miniemulsions

Nucleation of polymer particles in the seeded emulsion polymerization of n-butyl acrylate (BuA) was studied through experiments designed to control the amount of new particles formed. The results show that for the batch and semicontinuous seeded polymerization of BuA, a small amount of new particles was formed in the system in which the monomer was added neat, whereas a singificant amount of new particles was formed when the monomer was added as a miniemulsion. This suggests that new particles formed in the miniemulsion process were from nucleation of the monomer droplets. These experiments also showed that monomer-droplet nucleation decreased with increasing seed concentration in the reactor. For the seeded semicontinuous polymerizations, monomer-droplet nucleation decreases with decreasing BuA miniemulsion feed rate. The results also show that monomerdroplet nucleation takes place whenever miniemulsion droplets exist in the reactor. This study suggests that miniemulsions can be used to control the particle size distribution of a polymer latex system.     

Emulsion copolymerization of vinylidene chloride and butyl methacrylate, 83:17 in mol %

Seven 35% solids, (83 : 17 in mol %), vinylidene chloride (VDC)–butyl methacrylate (BMA) copolymer latexes were prepared at 25°C using redox catalyst by batch and seeded semicontinuous emulsion copolymerization processes: one batch (G), one seeded batch (F), and five seeded semicontinuous polymerizations of five different monomer feed rates ranging from 0.27 (A) to 1.10 (E) wt %/min. All of the emulsion polymerizations gave stable latexes of almost 100% conversion with negligible coagulum and narrow particle size distributions. The kinetic studies of seeded semicontinuous polymerization A–E showed that the rates of polymerization (R_p) were controlled by the monomer addition rates (R_a), and polymerizations A–D (0.27–0.79 wt %/min) were under monomer-starved conditions; polymerization E (1.10 wt %/min) was in near-flooded condition. Significant differences were found in the physical and mechanical properties of the latex films, depending on the mode of monomer addition. Infrared spectroscopy, ¹³C solid-state NMR spectroscopy, X-ray diffraction, the T_g and T_m values by DSC, dynamic mechanical spectroscopy, and tensile strength measurement of the latex films post-heat-treated for 30 min at 70°C or aged for several months at room temperature demonstrated that batch polymerizations F and G gave copolymers of heterogeneous composition and a crystalline character. In contrast, semicontinuous polymerizations A–E gave copolymers of more uniform composition and an amorphous character.