HVOF喷涂参数对WC-Co涂层力学性能的影响

目的研究HVO下在不锈钢上热喷涂WC-Co合金涂层喷涂参数如速度和靶距对涂层力学性能的影响,揭示其对表面残余应力,表面硬度的影响机理,优选最佳工艺参数.方法使用HVOF在不锈钢表面喷涂WC-Co合金形成耐磨涂层,通过使用显维硬度测量和钻孔方法来测量不同加工参数下的涂层硬度和残余应力分布.结果涂层和基体上存在3个区域,在这3个区域内硬度和残余应力完全不同的,但它们的变化趋势是一致的.涂层最大硬度并不是在表面,而是距离表面为40μm.结论通过比较不同参数下的涂层力学性能,可以确定最佳加工参数,通过试验发现喷枪速度小,靶矩小,涂层内部残余应力加大,同时显微硬度也有所提高.     

氧氩比和退火温度对AZO薄膜结构与性能的影响

在通氩气和不同比率氧氩混合气体的条件下,利用射频磁控溅射法在玻璃衬底上制备铝(Al)掺杂氧化锌(AZO)薄膜(溅射功率为180W,衬底温度为300℃),并对部分薄膜样品进行400℃或500℃退火处理.采用X射线衍射仪(XRD)、原子力显微镜(AFM)和分光光度计对薄膜的结构、表面形貌和光学性能进行测试研究.结果表明,制备的所有薄膜均呈现(002)晶面择优生长;与氩气溅射相比,当采用氧氩混合气体溅射时,生长的AZO薄膜晶粒尺寸显著增大;退火处理使2类薄膜的表面粗糙度都明显减小,晶粒也有所增大(7%~13%).其中,在氧氩比为1∶2的混合气体中制备的薄膜,经过500℃退火后,晶粒尺寸最大(39.4nm),薄膜表面更平整致密,在可见光区平均透过率接近最大(89.3%).     

临界盐浓度递减率对多孔介质微粒释放的影响

通过批量试验研究了临界盐浓度递减率对多孔介质微粒释放过程的影响,并通过胶体化学理论对其进行了微观机理探讨.研究结果表明:中性条件下,NaCl溶液临界盐浓度递减速率在0.012 mol/L左右,只有驱替溶液(低于临界盐浓度值)与被驱替溶液的浓度差高于该值时,微粒释放才会发生;临界盐浓度递减速率是一个区间值,而非单一值.     

ABS／PMMA的配比对共混物性能的影响

制备了不同配比的ABS／PMMA共混材料,对其缺口冲击强度、拉伸强度、热变形温度、熔融指数等特性进行了研究．结果表明,引入PMMA可以提高ABS耐热性能,ABS与PMMA共混能提高PMMA的力学性能特别是缺口冲击强度．当ABS／PMMA中PMMA为20％时,共混物具有最优的力学性能．     

三层复合PI薄膜厚度比对其介电性能影响

利用微乳化-热液法制备纳米分散液,制备了掺杂层与中间纯聚酰亚胺（PI）层厚度比不同的三层复合薄膜.在相同环境条件下通过透射电镜（TEM）、击穿场强和耐电晕测试分别对三层复合薄膜的微观结构和纳米掺杂层厚度比例的变化与介电性能的影响进行了分析.TEM测试结果表明纳米粒子在有机基体中的分散均匀;介电强度测试和耐电晕测试表明随掺杂层厚度比例的增加,击穿场强逐渐下降,耐电晕性能呈先上升后下降趋势.     

Effect of Salt Spray Corrosion on Tribological Properties of HVOF Sprayed NiCr-Cr_3C_2 Coating with Intermediate Layer

The objective of the present work was to determine the influence of the neutral salt spray corrosion on the wear resistance of HVOF sprayed NiCr-Cr_3C_2 coating with intermediate layer. Ni-Zn-Al_2O_3 coatings as interlayers were prepared by low pressure cold spray(LPCS) between NiCr-Cr_3C_2 cermet coatings to form a sandwich structure to enhance the corrosion resistance properties. The tribological properties were examined using the UMT-3 fricition and wear tester by line-contact reciprocating sliding under dry and salt spray one week corrosion. The morphology, element distribution, and phase compositions of the coating and worn sufaces were analyzed by using scanning electron microscopy, energy dispersive spectrometry, and X-ray diffraction respectively. The corrosion behavior of the coating was studied by the open-circuit potential, the electrochemical impedance spectroscopy, potentiodynamic polarization, and salt spray corrosion methods. It is found that the sandwich structured coating has better corrosion resistance than the single layer coating. The results show that under dry wear conditions, the wear mechanism is abrasive and adhesive wear, whereas under salt spray corrosion conditions it becomes corrosion wear. The friction coefficient of the sandwich structured coating after salt spray corrosion is slightly lower than the dry friction coefficient, but the weight of the wear loss is lower than that under dry condition.     

颗粒分布对活性粉末混凝土性能及微观结构影响

从活性粉末混凝土(RPC)原材料的粒径分布来研究颗粒堆积物的密实度,并通过量热分析、X射线衍射、扫描电镜等手段研究了RPC的水化速度、水化产物及微观结构。分析了RPC的性能与原材料的粒径分布和微观结构之间的关系,并用“中心质假说”对其高强、高韧性机理进行探讨。由图象分析可知,RPC原材料的比例及颗粒度符合密实堆积原理,堆积物的孔隙率达到最小;差示扫描量热分析表明,RPC的水化反应速度很快,主要的水化过程集中在较短时间内;扫描电镜及X衍射试验表明,RPC硬化体的结构非常致密,主要由一些不规则状的扁平粒子紧密堆积在一起,水化产物主要是Ⅲ型C—S—H,Ca(OH)2晶体的量稀少且没有钙矾石。     

预交联聚合物凝胶颗粒对乳状液稳定性影响

用界面张力仪、表面粘弹性仪和Zeta 电位仪测定了胜利孤东原油模拟油与含预交联聚合物凝胶颗粒 溶液间的界面特性, 并研究了预交联聚合物凝胶颗粒浓度对这些界面特性及乳状液稳定性的影响。结果表明, 去离 子水中加入预交联聚合物凝胶颗粒后, 去离子水及模拟水与原油模拟油间的界面张力和界面剪切粘度及油滴表面 的Ze ta 电位绝对值均增大, 原油与预交联聚合物凝胶颗粒溶液间所形成的W/ O 型和O/W 型乳状液稳定性均随聚 合物凝胶颗粒浓度增加而增强。     

氧气气氛对氧化铪薄膜性能的影响

在有氧和无氧气氛条件下,采用真空电子束热蒸发技术在P-Si(100)硅衬底上制备了HfO2薄膜.利用X射线光电子能谱,对薄膜的化学组分进行表 征,利用椭偏法对薄膜的膜厚和折射率进行测定,利用紫外可见光谱测量了薄膜的在200 nm～1 200 nm范围内的光透过率,并计算出其光学能隙,利用C-V测试系统对退火后薄膜的介电性能进行测试.结果表明,有氧和无氧条件下制备的薄膜中组分含量存在明显差异,相比于无氧条件下制备的薄膜,有氧条件下制备的薄膜中含有较少的铪单质,因而在可见光范围内具有较高透光率和光学能隙,较低的折射率和更优异的介电性能.