Abnormal metabolism of metal ions such as zinc may contribute to neuropathology. Complexing zinc could reduce this pathology. Thus, to examine the effectiveness of metal chelating agents in vivo, a model system was used. This involved determining the ability of chelating agents to prevent neuronal death caused by zinc chloride injected into the rat hippocampus. Significant protection against zinc toxicity was obtained with pyrithione, inositol hexakisphosphate, ethylenediamine tetraacetate (EDTA) and N,N,N',N'-tetrakis(2-pyridylmethyl)ethylenediamine (TPEN). The affinity of these agents for zinc varied between 106 M-1 and 1018 M-1. Thus, the affinity for zinc within this range does not appear to be a major factor affecting the ability of chelators to provide neuroprotection. While almost complete protection was found with EDTA and TPEN given simultaneously with zinc chloride, poor protection was obtained if TPEN was given before or after zinc chloride. Other agents either did not protect against zinc-induced neuronal death (zincon), or exacerbated zinc toxicity (BTC-5N and about 40% of rats injected with a combination of zinc chloride and diethylenetriamine pentaacetate [DTPA]). Rats showing increased damage after zinc plus BTC-5N or DTPA suffered wet dog-like shakes (WDS), suggesting that these zinc chelate complexes can induce seizures resulting in seizure-related damage. In contrast, in the 60% of rats treated with zinc chloride and DTPA that had no WDS, there was about an 80% reduction in the size of the zinc-induced lesion. The ability of chelators to cross cell membranes was examined by determining whether Timm's staining for vesicular zinc was reduced following the injection of a chelator into the hippocampus. TPEN and pyrithione reduced Timm's staining for zinc. However, cell permeability was not necessary for a chelator to protect against zinc toxicity.     

试样表面碳对红外吸收常规法测定钢中超低碳影响的研究

GB/T 20123-2006高频感应-红外吸收法（常规法）因表面碳影响,仅适用于钢中碳含量大于0.005%的测定,不能满足大生产过程中钢中超低碳测定的需求。研究表明：日常制取后直接测定的生产试样表面碳是吸附碳,标准样品试样表面碳除含吸附碳外,还含化合碳。国家标准GB/T 20126-2006（预热法）定值的标准样品事先预热冷却后用于常规法校正,可有效消除表面碳对钢中超低碳常规法测定的影响,使常规法能应用于超低碳钢日常测定。     

纯化学物质校准-高频燃烧红外吸收法测定钛及钛合金中碳

研究了纯化学物质校准-高频燃烧红外吸收法测定钛及钛合金中碳含量的分析方法。对钛及钛合金、校准样品(蔗糖) 在高频燃烧红外吸收法测定碳量中所使用的助熔剂进行了条件试验,确定二元助熔剂(050 g Sn+150 g Cu)能为钛及钛合金提供最佳释放条件。在钛及钛合金助熔剂(050 g Sn+150 g Cu)的基础上,加入0500 g纯铁有助于纯化学物质（蔗糖）中碳的释放,测定结果与加入0500 g纯钛的结果一致。采用不同碳含量的蔗糖标准溶液建立了校准曲线,测定范围为0004%～0060%(碳质量分数)。采用该校准曲线测定了10个钛及钛合金标准样品中的碳含量,测定结果与认定值吻合。方法用于实际样品分析,分析结果与重量法一致,相对标准偏差(RSD,n=8)为08%～51%。     

EDTA滴定法直接测定水氯镁石脱水产品中氧化镁

研究了用EDTA滴定法测定水氯镁石脱水产品中主体成分后用差减法求得杂质含量而间接测定水氯镁石脱水产品中Mg（OH）Cl、MgO含量（间接法）时产生很大误差的原因, 提出了通过用EDTA滴定法直接测定水氯镁石脱水产品样品的水溶渣中镁含量而得到产品中总MgO含量（直接法A）以及同时直接测定脱水产品样品的醇溶渣和水溶渣中镁含量而得到产品中Mg（OH）Cl、MgO含量(直接法B)的两种直接测定方法。醇或水溶渣中镁的测定是将渣用煮沸的5%（V/V）H₂SO₄溶解后用EDTA滴定。实验证明, 直接法测定脱水产品中氧化镁或碱式氯化镁的绝对误差很小（质量分数小于0.1%）。其中直接法A测得的脱水产品中总氧化镁含量更稳定、可靠, 具有更高的精密度和准确度（加标回收率在94%-117%）, 因此, 更适合于用盐酸苯胺(C₆H₅NH₂·HCl)作脱水剂的复盐法得到水氯镁石脱水产品中总MgO含量的准确测定。     

乙酸乙酯萃取-电感耦合等离子体质谱法测定宽范围纯度足金中的铜银铅镉

足金样品的检测有着广泛市场需求,但常用的火焰原子吸收光谱法(FAAS)、电感耦合等离子体原子发射光谱法(ICP-AES)对于铅、镉质量分数均小于0.0001%的足金样品无能为力,而电感耦合等离子体质谱法(ICP-MS)标准加入校正-内标法不能用于银、铜含量高(质量分数均大于0.001%)的足金样品检测。采用王水溶解样品后直接用乙酸乙酯萃取,以2%~5%(体积分数)硝酸为测定介质,建立了ICP-MS测定纯度为99.9%~99.999%足金中铜、银、铅、镉4种主要杂质元素的方法。干扰试验表明,足金中高含量银对测定铜、铅、镉没有干扰。在选定的实验条件下,各元素校准曲线的相关系数不小于0.9994,方法测定下限为0.01~0.19μg/g。将实验方法应用于足金实际样品分析,结果的相对标准偏差(RSD,n=6)为1.3%~2.6%,加标回收率为99%~105%。采用实验方法对3种纯度(99.9%、99.99%、99.999%)足金样品中的铜、银、铅和镉进行测定,测得结果分别与原子吸收光谱法(AAS)或ICP-MS标准加入校正-内标法基本一致。方法可实现纯度为99.9%~99.999%足金中银、铜、铅、镉的测定。     

空气-乙炔火焰原子吸收光谱法测定钐钴永磁合金中钙量

采用王水分解样品,在3%(V/V)的盐酸介质中,以标准加入法绘制校准曲线,建立了空气-乙炔火焰原子吸收光谱法(FAAS)测定钐钴永磁合金中钙的方法。分别在钐、钴单独存在以及共同存在的条件下考察了其对测定的影响,结果表明,若采用火焰原子吸收光谱法测定钐钴永磁合金中钙,钐钴基体对测定的基体效应不可忽略且情况复杂。因此,实验选择标准加入法来校正钐钴基体效应对测定的影响。方法检出限为13μg/g,方法测定下限为44μg/g。干扰试验表明,以标准加入法的校正模式进行钐钴永磁合金中钙量的测定,样品中共存元素铜、铁、锆对测定的干扰可忽略。方法应用于钐钴永磁合金中实际样品中质量分数为0.0065%钙的测定,测定值与国家标准方法GB/T 12690.15—2006(电感耦合等离子体原子发射光谱法)相符,测定结果的相对标准偏差(RSD,n=11)小于14%。方法可用于钐钴永磁合金样品中0.0050%~0.50%(质量分数)钙量的分析检测。     

粉末压片制样-X射线荧光光谱法测定土壤和水系沉积物中氯和溴

Cl和Br是土地质量调查和评价的重要指标,X射线荧光光谱法测定土壤和水系沉积物中Cl和Br的难点在于Cl容易污染,测量值易受测量时间、测量次数等因素影响,方法稳定性差;而Br的地球化学背景值低,方法准确性和稳定性较差.实验重点对Cl和Br元素的谱线选择、测量时间、基体校正以及Cl元素测量时样片的放置时间、测量次数和Br...     

电感耦合等离子体质谱法测定水系沉积物中银铜砷锑铋镉

水系沉积物中银、铜、砷、锑、铋和镉等金属元素的准确测定,对地质找矿工作具有重要的指导意义。实验采用王水于水浴条件下溶解样品,通过选择适宜的同位素以及选用干扰元素校正方程克服了质谱干扰,利用仪器软件在线校正了氯离子对砷的干扰,以2%~3%(V/V)王水为测定介质,建立了电感耦合等离子体质谱法(ICP-MS)测定水系沉积物中银、铜、砷、锑、铋和镉6种元素的方法。在优化的实验条件下,各元素校准曲线线性相关系数均在0.9990以上,方法检出限为0.0028~0.045μg/g,测定下限为0.008~0.13μg/g。采用实验方法测定水系沉积物实际样品中银、铜、砷、锑、铋和镉,测定结果分别与采用交流电弧发射光谱法(ES)测定银,原子荧光光谱法(AFS)测定砷、锑、铋,火焰原子吸收光谱法(FAAS)测定铜,石墨炉原子吸收光谱法(GF-AAS)测定镉的结果基本一致;测得结果的相对标准偏差(RSD,n=11)为0.28%~2.0%。将实验方法应用于水系沉积物标准物质分析,银、铜、砷、锑、铋和镉测定结果的相对标准偏差(n=12)为0.45%~6.0%。     

Increasing the effectiveness of your teaching program for the elderly: assessing the client''s readiness to learn

The virulent properties of V. cholerae O1 (more than 1000 strains) were studied. For this purpose the following methods were used: the determination of hemolytic activity, the express method based on the determination of the speed of mannite oxidation, complex analysis and polymerase chain reaction (PCR). The comparative analysis of the results of the in vitro determination of virulence revealed that the most frequently occurring strains among the strains isolated from humans were vct+ strains (80.5%), hemolysis-negative strains (83.9%) which were virulent (faintly virulent) as determined by complex analysis (38.2%), cholerogenic as determined by the express method (60.2%). Among the strains isolated from the environment were vct- strains (87.4%), hemolysis-negative strains (63.2%) which were virulent as determined by complex (13.1%), as well as by the express method (74.3%). The data of the determination of the vct gene did not correlate with the results obtained by complex analysis. The use of complex analysis was expedient only in the detection of strains sensitive to eltor phage in the dilution routine test of V. eltor strains. The methods for the determination of virulence, available for practical laboratories, were Grieg's method for the determination of hemolytic activity and express method. PCR proved to reliable in vitro method for the determination of the vct gene.     

氢醌滴定法测定锰铁中锰

试验并确定了氢醌滴定法测定锰铁中锰的实验条件。试样经酸溶解后,在磷酸介质中和加热条件下,用高氯酸作氧化剂, N 苯代邻氨基苯甲酸溶液作指示剂,氢醌标准溶液滴定试样中锰。用该方法对锰铁标准物质及实际试样中锰含量进行测定,结果表明：本法的测定结果与认定值或国标方法(GB/T56981-2008)的测定结果相符,测定结果的相对标准偏差小于03%（n=6）,方法也可用于锰矿石中锰含量的测定。     

燃烧碘量光电滴定法测定含氯地质样品中硫

燃烧碘量法是分析硫的经典方法,但将其应用于地质样品分析时,样品中的氯会对测定产生干扰。实验在对助熔剂、样品燃烧分解温度和滴定方式优化的基础上,以数学方程校正法消除了氯对硫的干扰,建立了燃烧碘量光电滴定法测定地质样品中硫的方法。实验表明,控制温度为1250~1300℃时样品可充分燃烧分解;采用低空白值的二氧化硅做为燃烧助熔剂有效降低了方法的检出限;利用以硒光电池电位变化指示终点的方法即光电滴定法替代传统的目视滴定法可弥补因视觉观察而产生的误差,提高了测定结果的准确性。在不同性质(水系沉积物、岩石和土壤)国家标准物质中加入优级纯氯化钠进行氯的干扰试验,结果表明,氯对硫的干扰量与氯的含量呈线性关系,据此,得到了对氯干扰进行校正的数学方程。方法检出限为17.4μg/g、测定下限为58.0μg/g。采用实验方法测定不同性质的地质国家标准物质(土壤和水系沉积物)中硫,结果与认定值的相对误差(RE)为-3.41%~+5.00%,对数差(ΔlgC)为-0.015%~+0.022%,相对标准偏差(RSD,n=12)为0.75%~2.5%。     

火花源原子发射光谱测定核电用不锈钢中硼元素

研究了火花源原子发射光谱法测定核电用不锈钢中硼元素的分析方法。讨论了硼元素的谱线和不同形态硼对硼含量测定结果的影响。延长了硼元素的校准曲线,并采用干扰系数法消除了Cr、Ni引起的谱线重叠干扰。结果表明,采用谱线B 182.64 nm进行硼元素测定,其分析上限可以达到1.6%。该方法用于核电用不锈钢标准样品和实际样品中硼元素的测定,所得结果与认定值或湿法分析结果相一致,相对标准偏差（RSD, n=7）小于3%。     

电感耦合等离子体质谱法测定钢中痕量酸溶铝

采用硝酸溶解样品,建立了电感耦合等离子体质谱法(ICP-MS)测定钢中痕量酸溶铝(Als)的方法,并对其测定条件进行了优化。实验表明:采用纯化后硝酸溶解样品可以降低对检测结果的影响;高纯铁基体效应对测定的影响不可忽略,故采用待测样品作为基体的标准加入法绘制校准曲线以消除该影响;采用石英烧杯进行样品溶解,测定结果比玻璃烧杯更稳定;采用塑料容量瓶对硅钢标准样品溶液定容,测定结果相对于玻璃容量瓶更接近认定值;对样品前处理的条件进行了优化,最终选择硝酸用量为5mL,溶解时间为10min;选择⁴⁵Sc作为内标对硅钢标准样品进行测定,结果较选用⁸⁹Y为内标更接近认定值;采用2%(体积分数)硝酸冲洗管路8s,可基本消除记忆效应。以²⁷Al质量浓度为横坐标,²⁷Al与内标元素响应值的比值为纵坐标绘制标准加入法校准曲线,校准曲线方程的相关系数为0.9998;方法对样品的测定下限为0.00006%。采用实验方法对5个钢标准样品和2个合金钢实际样品进行测定,测定值与认定值基本一致,相对标准偏差(RSD,n=5)在1.6%~4.5%之间。     

紫外脉冲荧光法测定高硬度地下水中铀

按国标GB/T 6768—986推荐的紫外脉冲荧光法直接测定高硬度地下水中铀时,加入铀荧光增强剂后溶液会变得浑浊,使得测定无法继续进行,而测定普通低硬度水样未见这种现象。实验对产生这一现象的原因进行了分析,结果表明,高硬度地下水中含量较高的钙离子与铀荧光增强剂中的磷酸盐发生化学反应生成了磷酸钙沉淀,是导致溶液浑浊的根本原因;虽然镁离子也会与磷酸根发生反应,但是按国标法选用的条件进行测定时不会与磷酸根反应,从而对铀的测定无影响。实验通过向被测水样中加入适量的乙二醇-双-(2-氨基乙醚)四乙酸(EGTA)络合剂使其与钙离子络合,即可避免由于铀荧光增强剂的加入而导致的溶液浑浊现象,从而实现了高硬度地下水中铀的紫外脉冲荧光测定。在优化的实验条件下,方法的检出限为0.02 μg/L。采用紫外脉冲荧光法测定高硬度地下水实际样品,测得结果与电感耦合等离子体质谱法(ICP-MS)基本一致,相对标准偏差(RSD,n=11)低于5%,加标回收率在99.5%～ 101%之间。     

氧瓶燃烧-离子色谱法测定铜精矿中氟

将有机质样品燃烧检测氟离子应用于铜精矿中氟测定,建立了氧瓶燃烧-离子色谱法测定铜精矿中氟的方法。由于铜精矿原样难于燃烧,通过掺杂纤维素助燃(纤维素与铜精矿最佳质量比为7:1),压片制备铜精矿试样,经改进的氧瓶燃烧后被水吸收,吸收液经0.22 μm水系微孔膜,进入离子色谱仪测定氟离子。结果表明,线性范围内(0.100～2.000 mg/L)校准曲线相关系数r>0.999,氟的检出限为2.31 μg/L;按照实验方法测定铜精矿样品中氟,结果的相对标准偏差(RSD,n=5)为1.8%～4.5%,回收率为92%～97%。将实验方法用于铜精矿标准样品氟含量测定,测定值与认定值吻合性较好;方法对照试验表明,实验方法对氟含量的测定值与国家标准GB/T 3884.5—2012的测定值基本一致。     

双氧水处理-连续滴定法测定铜电解液砷锑

为解决铜电解液中砷锑铋之间复杂化学反应所引起的砷锑分析误差大的问题,在含砷锑矿石的砷锑连续滴定方法基础上,模拟了铜电解液中砷锑的存在环境,开发出适合于铜电解液砷锑测定的双氧水预处理 连续滴定法。首先采用适量双氧水消除As,Sb对砷锑分析结果的影响,再依次加入硫酸和硫酸肼两次冒浓烟至瓶颈,冷却后于盐酸介质中,以次甲基兰 甲基橙为指示剂,先用硫酸铈标准溶液滴定Sb,再用溴酸钾标准溶液滴定As。实验表明,连续滴定法中,适宜的硫酸加入量为20 mL,发烟时间为5 min,滴定锑时的盐酸浓度为43 mol/L,温度为70 ℃,滴定砷时的盐酸浓度为18 mol/L,温度为80 ℃。采用本方法分析合成铜电解液,砷、锑的回收率分别为96 %和104 %。采用该方法分析铜电解生产线上铜电解液,测得结果与原子吸收光谱法吻合,相对标准偏差（n=6）小于12%。     

微波消解-电感耦合等离子体原子发射光谱法测定铂铑系列合金中铑

提出了试样经微波消解后用电感耦合等离子体原子发射光谱法（ICP AES）测定铂铑系列合金中铑的分析方法。对试样的微波消解条件、基体和谱线干扰等进行研究。结果表明,在230℃温度下,以盐酸和少许过氧化氢、硝酸和氢氟酸为消解试剂,试样在密闭容器中分两次进行消解60 min可以完全溶解。消解液用ICP AES测定时,通过选择合适的分析谱线可避免基体和光谱干扰。用本方法测定了系列铂铑合金的模拟试样,测定结果与行业标准方法的分析结果相一致,相对误差在010%～030%之间,相对标准偏差小于066%（n=6）。该法可以用于铂铑系列合金中铑含量的测定。     

火焰原子吸收光谱法测定铜磁铁矿中铜

采用15mL盐酸、5mL硝酸、3mL氢氟酸和5mL高氯酸分解试样,以5%(V/V)的高氯酸为测定介质,建立了火焰原子吸收光谱法(FAAS)测定铜磁铁矿中0.1%~2%铜的方法。干扰试验表明,铜磁铁矿中杂质元素在最大量存在的条件下不干扰铜的测定。在选定的实验条件下,铜校准曲线的相关系数为0.999 1,方法检出限为0.017μg/mL。将实验方法应用于5个铜磁铁矿样品中铜的测定,测得结果与电感耦合等离子体原子发射光谱法(ICPAES)基本一致,相对标准偏差(RSD,n=11)在1.2%~3.7%之间,加标回收率在96%~104%之间。分别在7家实验室采用实验方法进行测定,结果显示,实验方法的再现性限(R)在0.020%~0.118%之间。     

德昌红柱石矿化学物相分析方法的研究

结合德昌红柱石矿的组成特征, 研究了红柱石矿的化学物相分析方法。试样在常温下经氢氟酸和王水的混合酸(V(氢氟酸)∶V(王水)=1∶1)浸取14 h, 然后过滤溶液, 洗涤并灰化沉淀物, 以重量法测定红柱石矿物含量。由于红柱石在溶解过程中会有一定量的损失, 使红柱石回收率偏低, 但可以用实验求得的人工模拟红柱石样的溶失校正系数对测定结果进行校正而解决。用实验方法测定德昌矿区红柱石样品中红柱石含量, 其测定结果与滴定法的测定结果基本一致, 相对标准偏差(n=25)为1.9%。     

氢化物发生-电感耦合等离子体原子发射光谱法测定尾矿渣固体废物水浸出液中痕量铅

建立了一种简单、灵敏度高的测定尾矿渣固体废物水浸出液中痕量铅的方法。样品经用水振荡浸取和硝酸处理后,在4%(体积分数)盐酸介质中,用10 g/L的硼氢化钠-氢氧化钠-铁氰化钾作为还原剂,将自行设计的一种新型氢化物发生器与电感耦合等离子体原子发射光谱仪(ICP-AES)联用测定了浸出液中痕量铅。方法通过在还原剂中加入一种自制的铅稳定剂,解决了测量体系不稳定的问题。方法检出限为1.0 μg/L,样品的加标回收率为90.5%~106.5%,相对标准偏差(RSD)小于6%。样品测量过程快速、简单,无记忆效应的影响,适合尾矿渣固体废物水浸出液中痕量铅的测定。