高密度聚乙烯／蒙脱土纳米复合材料的制备与性能研究

采用马来酸酐接枝乙烯醋酸乙烯酯（EVA-g-MAH）和马来酸酐接枝低密度聚乙烯（PE-LD-g-MAH）为相容剂，制备了高密度聚乙烯傣脱土（PE-HD／MMT）纳米复合材料。用X射线衍射和扫描电镜对有机蒙脱土和PE-HD／MMT复合材料的结构进行了表征，研究了蒙脱土和相容剂含量对制备的纳米复合材料力学性能及热性能的影响。结果表明，相容剂的加入有利于插层。MMT在复合材料中呈纳米级分散。其层间距可由2．10nm增大至3．85nm。MMT含量为3％（质量分数，下同）、EVA-g-MAH含量为15％时，复合材料的综合力学性能最好，冲击强度和拉伸强度分别较PE-HD提高43．7％和5.8％。     

回收高密度聚乙烯结构与性能的研究

采用傅里叶变换红外光谱仪、差示扫描量热仪和热重分析仪分析了市售回收高密度聚乙烯（PE-HD）的结构特点,并对其熔体流动性和力学性能进行了研究。结果表明,在回收再利用过程中,PE-HD的结构发生了明显的变化,产生了羰基,其老化程度越大,产生的杂峰越多。回收PE-HD的熔融流动性较差,力学性能也有不同程度的下降。根据拉伸强度的大小,回收PE-HD可分为一级料、二级料和三级料。     

Structure and Properties of Vibrating Extruded High-Density Polyethylene Sheet

Summary The effect of vibration frequency and vibration amplitude on the microstructure and mechanical properties of high-density polyethylene (HDPE) sheets, obtained through electromagnetic dynamic plasticating extruder, were studied systematically. The mechanical properties, characterized by tensile and impact strengths, have been tested along the flowing and transverse directions (MD&TD). The mechanical tests show that the tensile strength and impact toughness, especially in TD, were much improved under the reciprocating axial vibration. Differential scanning calorimetry (DSC), scanning electron microcopy (SEM) and wide angle X-ray diffraction (WAXD) were executed to analyze the microstructure of the samples. The results indicate that the vibration extrudate has higher crystallinity, perfect crystallite, and strong inter-spherulite ties, which account for enhancement of the mechanical properties of sheets, compared to conventional static extrusion.     

相容剂对有机蒙脱土改性聚乙烯塑料性能的影响

利用相容剂对有机蒙脱土改性聚乙烯塑料进行改性研究,结果表明,加入相容剂后聚乙烯与有机蒙脱土的界面相容性得到改善,颗粒引起的应力集中和产生缺陷的几率大大降低,改性聚乙烯塑料的拉伸强度和断裂伸长率均有不同程度的提高。综合改性聚乙烯塑料的物理性能,相容剂用量在5份左右最佳。     

线性双峰聚乙烯／低密度聚乙烯共混物的流变行为与力学性能

研究了线性双峰聚乙烯（LBPE）与低密度聚乙烯（LDPE）共混物溶体的流变行为，讨论了共混物的组成，剪切应力和剪切速率以及温度对熔体流变行为，熔体粘度的影响，测定了不同配比熔体的非牛顿指数（n)，熔体流动速率（MFR）及力学性能，为双峰聚乙烯的加工和使用提供了理论依据。     

同质异构交联法对再生聚乙烯的改性研究

通过硅烷交联法制备了交联聚乙烯（PE）,并将其加入到水选废旧塑料薄膜再生PE颗粒中进行改性研究。通过扫描电子显微镜（SEM）对再生料冲击样条的断口进行观察,研究了交联料用量对再生PE的力学性能和加工流动性的影响;用差示扫描量热法（DSC）和X射线衍射法(XRD)研究了当交联料添加量为15份时,再生料结晶性能与交联度的关系。结果表明,添加了交联料的再生料的聚集态结构发生了变化,形成了“同质异构分散结构”,该结构会使再生料的拉伸强度和冲击强度大幅提升,而断裂伸长率和熔体流动速率则有一定程度的下降;当交联料的添加量为15份时,材料具有最佳的综合性能,且当添加量为15份、交联度为33.5 %时,再生料的结晶性能最好。     

PE蜡和硬脂酸钙对PVC的树脂润滑作用——OPE蜡的影响与机理

通过转矩流变仪测定塑化时间(tf),并比较塑化时间延长效应[Δtf=tf(PVC+润滑剂)-tf(PVC)],研究了高密度氧化聚乙烯蜡A-C 316A对聚乙烯蜡A-C 617A和硬脂酸钙(CaSt2)作为PVC润滑剂润滑性能的影响。结果表明,A-C 617A单独使用及其与CaSt2并用时,PVC树脂的外润滑性能均由于A-C 316A的添加而下降,而A-C 617A-CaSt2并用体系的性能下降,这是A-C 617A性能下降和协同效应没有叠加的结果,因此,其幅度比A-C 617A单独使用时更大。由此可以推测,A-C 316A的效应并不能归因于内润滑作用,其实际机理应该是由于独特的结构、性质,其既难溶于PVC又难溶于A-C 617A,但是却可以吸附A-C 617A和吸收CaSt2,而吸附A-C 617A则可以导致其有效用量减少,吸收CaSt2,破坏了A-C 617A-CaSt2的协同作用。     

CPE-g-PEG在CPE/P(AA-AM)吸水膨胀弹性体中的增容作用

选择自制的吸水树脂丙烯酸/丙烯酰胺共聚物(P(AA-AM))与氯化聚乙烯(CPE)为共混原料,以CPE-g-PEG两亲性接枝共聚物为增容剂,机械共混制备了增容型吸水膨胀弹性体(WSE).对共混物的亚微形态、吸水膨胀特性以及力学性能进行了研究.TEM结果表明简单共混时,CPE/P(AA-AM)共混物试样的相容性差.添加CPE-g-PEG后CPE与P(AA-AM)相间有一定程度的连接.接枝物的加入,改善了共混试样的重复使用情况,降低了其质量损失率,提高了WSE的稳定性,改善了试样的力学性能,接枝物加入量为6份时,拉伸强度最大.     

阳-非复合离子型氧化聚乙烯蜡乳液的制备

阳-非复合离子型氧化聚乙烯蜡乳液广泛应用于皮革涂饰、造纸、印染等领域,该文用三乙醇胺对氧化聚乙烯蜡进行酯化改性,再用相转变法和复合乳化体系对酯化改性的氧化聚乙烯蜡进行乳化,并对乳液性能进行检测分析。实验结果表明,三乙醇胺对氧化聚乙烯蜡进行酯化改性后,可明显提高氧化聚乙烯蜡的可乳化性和乳液的稳定性。乳化剂的种类、用量、乳化温度以及剪切搅拌速度等乳化因素对乳液性能有较大影响。乳化实验优化的条件为:乳化剂OS-15用量为氧化聚乙烯蜡质量的15%,乳化剂1631用量为氧化聚乙烯蜡质量的5%;乳化温度为90～95℃;连续剪切分散40～60min。     

回收聚乙烯再生料补强增韧改性研究

利用现代化分析手段，从研究回收聚乙烯再生料（Ｒ－ＰＥ）分子结构变化入手，进一步验证了“特效炭黑”对再生料具有 强增韧与抗老化双重功效，交研制了“炭黑再生聚乙烯地膜”，其物理力学性能达到原生料地膜的国标水平（ＧＢ１３７３５－９２），耐老化性能大幅度提高。     

聚乙烯原料对高密度聚乙烯土工膜性能的影响

本实验采用吹塑成型工艺,以不同牌号的聚乙烯(PE)树脂为原料生产2 mm厚度双光面高密度聚乙烯(HDPE)土工膜,研究PE原料对HDPE土工膜性能的影响。结果表明:中密度聚乙烯(MDPE)土工膜综合性能优异,主要是由其特有的分子结构(如分子量分布双峰性、α烯烃长支链)所决定的;不同PE原料氧化诱导时间不同,可通过调节含抗氧剂色母料(或抗氧剂)的含量,使HDPE土工膜氧化诱导时间达到要求;HDPE土工膜在焊接时应根据PE材质的不同而选择不同的焊接条件。     

空心玻璃微珠增韧高密度聚乙烯

采用悬臂梁缺口冲击、DSC、SEM 等方法研究了空心玻璃微珠(HGB)用量、粒径大小、偶联剂处理和基体韧性等因素对高密度聚乙烯(PE-HD)/HGB 复合材料冲击强度和热性能的影响。结果表明:复合材料的冲击强度首先随 HGB 含量的增加而增大,当 HGB 用量超过一定值后,冲击强度又随 HGB 含量的增加而减小。HGB 的粒径越小,增韧效果越好,当粒径较大时,增韧作用不明显。偶联剂可以明显改善 HGB 在基体中的分散,进而达到较好的增韧效果。对于 PE-HD/HGB 复合材料,要求基体的最低冲击强度为5.2 kJ/m~2。     

Mechanical,Thermal and Morphological Characterization of High-Density Polyethylene and Vermiculate Composites

High-density polyethylene composites containing 7, 10, 15 and 20% w/w vermiculite (VMT) were prepared by extrusion in a twin-screw extruder at various shear rates. The thermal and mechanical properties and morphological characteristics of the composites were evaluated and compared with pure high-density polyethylene. The blend morphologies were determined by scanning electron microscopy (SEM). The thermal properties of the composites were investigated by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). The TGA results reveal that the use of VMT particles to fill polyethylene increased the thermal stability of the composite. The results obtained indicate that a shear speed of 400 rpm and vermiculite content of 7% showed the best properties of impact resistance. These observations were confirmed by morphology analysis.     

Solid State Rheological Properties of Ultra‐High Molecular Weight Polyethylene Foams

The rheological properties of ultra‐high‐molecular‐weight polyethylene (UHMWPE) foams were studied using solid state rheometry. Frequency and temperature sweeps were performed in the linear viscoelastic regime. For comparison purposes, low‐density polyethylene (LDPE) and high density polyethylene (HDPE) foams were also studied. For the range of densities under consideration (200‐700 kg/m³), several models for prediction of elastic moduli were compared. It was found that none of the models succeeded in representing completely the mechanical behavior of foams. Further refinements must be made in order to take into account parameters relating the morphology of the foam to its mechanical properties.     

石墨和短纤维填充聚乙烯抗静电材料的研究

采用鳞片石墨FG和短纤维CF对高密度聚乙烯HDPE进行抗静电及增强改性研究。测试及分析了HDPE混合体系的电学性能和拉伸性能。得出结论:添加一定量的石墨能明显提高材料的抗静电性能,通过加入纤维可以改善体系的强度,同时短纤维有助于降低材料的体积电阻率。     

PE滴灌带耐老化性能研究

将线性低密度聚乙烯(PE–LLD)/高密度聚乙烯(PE–HD)/低密度聚乙烯(PE–LD)的滴灌带试样经过自然暴露老化,并对老化前后试样进行力学性能、流变性能及红外光谱测试分析以研究滴灌带的耐老化性能。结果表明:户外暴晒60 d后,纯PE(0#)试样的拉伸强度保持率和断裂伸长率保持率分别为81%和15.6%,已失去使用价值;而户外暴晒120 d后,1~#,2~#,3~#,4~#试样断裂伸长率保持率分别为61.9%,75.1%,82.3%,87.8%。毛细管流变10 min时,户外暴晒120 d试样扭矩保持率顺序为4~#3~#2~#1~#0~#试样;户外暴晒120 d后,试样红外谱图在1 757 cm~(-1)处生成的羰基峰从0~#~4~#依次向低波数移动,并且变得越来越弱。基于此,同时加抗氧剂、光稳定剂和炭黑复配使用的4~#试样耐老化性能最佳。     

高密度聚乙烯振动注射试样的结构与性能

为了研究高密度聚乙烯振动注射试样的晶体结构与性能．研制并采用压力振动装置进行振动注射实验一通过振动，高密度聚乙烯由常规注射试样的典型球晶结构转变为明显取向的片晶结构，在不同的振动条件下，片晶的尺寸和取向度都不同。振动试样的拉伸强度随振动频率和振动压力的提高而提高，最大增幅为41.0％。断裂伸长率随振动压力的增高而下降，随振动频率的增高开始时下降，然后开始回升。     

敌火龙阻燃聚乙烯的研究

采用膨胀型阻燃剂敌火龙(Deflam)对聚乙烯(PE)进行填充改性,制备了阻燃PE复合材料,研究Deflani添加量对PE复合材料的力学性能、热稳定性能和阻燃性能的影响.结果表明:随阻燃剂的增加,阻燃PE复合材料的力学性能明显下降,但阻燃等级、极限氧指数均有显著提高,并且有利于提高PE材料的总体热稳定性.热重(TG)曲...     

茂金属加合物催化剂及其聚乙烯的研究开发

在简述国外聚乙烯技术开发动态的基础上,报道了中国石油化工总公司石油化工科学研究院近年来在研究开发茂金属基聚乙烯树脂（ｍＰＥ）方面的进展,包括气相流化模试聚合和中试（２００ｔ／ａ）聚合实验３．２ｍ＾３淤浆法间歇式中试（３００ｔ／ａ）聚合实验及所得ｍＰＥ的结构和部分物理机械性能的表征等。     

Composites of Low-Density Polyethylene and Castor Presscake

Composites of low density polyethylene were prepared by melt mixing in a co-rotating twin screw extruder. Castor presscake, a biodiesel process co-product, was used as filler for the polyethylene composites. Different concentrations of this filler were added to the polymer matrix. Melt flow index and. mechanical properties were measured by following standardized tests. The results showed that the addition of the filler to the polymer matrix provoked an increase on the values of Young Modulus and on the flexural properties. However, the impact strength and the tensile stress values tended to decrease with the increasing of the filler concentration.