微合金化对Al-Cu-Mg合金时效行为的影响

以微合金化元素对Al-Cu-Mg合金常规时效析出相的影响为出发点,分析了Ag,Si,Ge,Cd等元素对合金时效行为的影响.结果表明具有:完全改变常规析出相结构,形成新析出相;部分改变常规析出相结构,提高析出相的强化效果;促进析出相析出3种作用.分析了采用微合金化方法提高Al-Cu-Mg合金热强性所存在的问题,并对发展趋势进行了展望.     

电脉冲处理HSi59-2.5 硅黄铜热处理后的相组成

采用固溶时效热处理对电脉冲处理后的HSi59-2.5硅黄铜进行了软化处理,分析了电脉冲处理硅黄铜中β相与γ相的转变特点,探究了这种变化与基体硬度及合金切削性能的关系。结果表明,在相同固溶处理条件下,电脉冲处理使硅黄铜中γ相数量减少,β/γ溶解度曲线随合金元素Zn含量变化更趋平缓,导致Cu-Zn相图中β相区向右扩大。随固溶温度降低,电脉冲处理硅黄铜组织中的γ相增加,且分布均匀;随着时效温度的降低,γ相析出数量逐渐减小。电脉冲处理硅黄铜热处理后的显微硬度均较未处理的有明显降低。     

Pd-Ag-Sn-In-Zn合金时效特性

研究了不同时效工艺对Pd-Ag-Sn-In-Zn合金的力学性能、电学性能及显微组织和相结构的影响.结果表明:固溶-冷变形后合金的时效过程由过饱和固溶体的析出和基体的再结晶两个过程控制;合金高强度主要来源于加工硬化和第二相的析出强化,合金的电阻率变化主要受时效过程中再结晶和析出过程的综合影响.     

Ag对Al-Cu-Mg合金Ω相析出行为的影响

用硬度测试、差热分析(DSC)以及透射电镜(TEM)研究Al-Cu-Mg-(Ag)合金时效过程中组织和性能的演变;根据不同升温速率的DSC曲线,采用Kissinger法计算Ω相和θ'相的激活能,探讨Ag对Al-Cu-Mg合金Ω相和θ'相析出行为的影响.结果表明:Al-Cu-Mg合金经185℃时效后,时效硬化曲线呈双阶段硬化特征,生成少量Ω相;添加Ag后,合金的时效硬化能力显著提高,经170、185和200℃时效时,对应的峰值时效时间分别为10、5和2h,峰值硬度随着时效温度的升高而下降;Ag能促进Ω相析出,使θ'相的激活能提高,从而抑制θ'相的析出.     

电脉冲孕育处理对Al-Cu-Mn合金时效过程的影响

考察了不同电脉冲孕育处理参数对Al-Cu-Mn合金时效过程的影响,结果表明:电脉冲孕育处理加速了Al-5%Cu-0.8%Mn合金时效进程,缩短了时效时间,使合金最大显微硬度较未处理试样提高了13%～17%;但不同的电脉冲参数影响时效过程的程度不同,一定范围内,500V电压,30s处理时间,频率为3Hz的电脉冲参数在740℃处理时,合金时效后的显微硬度最高.     

Mg和RE对Cu—Fe—P合金组织性能的影响

对框架材料类Cu-Fe-P合金进行了成分优化和微合金化实验,通过实验分析了添加镁和RE对Cu-Fe-P合金组织的影响以及对合金形变时效的性能的影响情况.结果表明:由于减小了合金中的P含量,而添加了一定量的镁,使得铸态组织为α-Cu基体和沿基体内分布的网状亚结构组成.在网状结构中网边相对粗大,轮廓清晰.网边上的沉淀相是镁与磷的金属间化合物.对合金进行固溶处理后,网状第二相基本消失,但晶粒长大晶界变细.固溶后的组织为粗大的过饱和固溶体和基体上少量的热稳定相组成.经形变时效后合金会从固溶体中析出新相Mg3P2和弥散质点,合金中镁含量越多析出的第二相越多,从而影响了合金时效性能.     

固溶温度对2A97合金组织与性能的影响

研究了固溶温度对一种新型Al-Cu-Li系合金(2A97铝合金)组织性能的影响。在460～540℃,合金经不同温度固溶处理,水淬后进行相同的时效(165℃×48h)处理。分析了在不同温度固溶处理的淬火态和时效态合金的显微组织、时效态合金的断口形貌。结果表明:在520℃固溶处理能够使合金充分固溶,时效后有较细小均匀分布的析出相和较多的析出量,时效强化效果最好。     

时效前的预变形对喷射成形2195铝锂合金组织与性能的影响

研究了时效前的预拉伸变形量对喷射成形2195铝锂合金时效析出行为及力学性能的影响规律.结果表明:2195合金经固溶处理后直接时效,组织以 δ′(Al3Li)相+少量T1(Al2CuLi)相为主,晶界处分布着大量断续分布的颗粒析出相组织(富AlCu相及AlCuFe相).时效前的预拉伸变形在合金基体中引入的大量位错成为T1...     

热处理对Mg-8Gd-2.5Nd-0.5Zr合金组织和力学性能的影响

通过OM、XRD、TEM、SEM和电子拉力试验机等,研究了固溶和时效处理对Mg-8Gd-2.5Nd-0.5Zr(质量分数,%)合金显微组织和力学性能的影响。结果表明:合金铸态组织由α-Mg基体和含Mg5Gd相、Mg12Nd相的粗大枝晶组成,经过热处理后,合金中方块状颗粒相明显增多,且分布在晶界处;固溶时效态合金析出的纳米尺寸方块相可有效强化合金。时效态合金中β'析出相形态类似多个纺锤形相连接而成,相互之间的夹角呈120°,且具有周期结构。铸态、固溶态和时效态合金在不同状态下的室温拉伸强度分别为:189.3、201.4和251.1MPa。     

Mg和Er对Cu-Fe-P合金组织性能的影响

对框架材料类Cu-Fe-P合金进行了成份优化和微合金化,分析了Mg和Er、形变时效对Cu-Fe-P合金组织性能的影响.结果表明减小合金中的P含量,并添加一定量镁,可以细化合金铸态组织,铸态下合金晶界上分布有长条状析出相.对合金进行固熔处理后,晶界上的条状相基本消失,固溶到基体中,固溶后的组织为过饱和固溶体和少量的残留相组成.形变时效后Mg3P2相从固溶体中析出,并形成弥散质点;合金中析出相与镁含量成正比,这种析出相对合金的性能有影响.     

高温合金C130电火花沉积工艺

通过控制3H-ES型电火花金属表面强化修复机的电压、频率、功率以及保护气体的流量等工艺参数,采用Ni35阳极材料对C130高温合金进行了电火花沉积修复,并对沉积层进行了金相分析、显微硬度测试.结果表明,电火花沉积层与C130基体有很好的冶金结合,沉积层的显微硬度与基体相比提高了100%.同时沉积层内部也存在着组织不均匀的缺陷,这主要是焊接速度控制得不够均匀以及作用在阳极棒上的作用力不稳定造成的.

Abstract：

Through controlling voltage, frequency, power and gas flow of the 3H-ES electric spark harding machine, Ni35 was used to deposit on C130. After deposition, microstructure and mi-crohardness were studied. The result indicates that the sedimentary deposit joins with the substrate firmly, the microhardness of the sedimentary deposit is 100% of substrate. The structure of the sedimentary deposit is non-uniform because of the speed and the force is instability.     

Electron fractionalization

A largely qualitative, and rather idiosyncratic discussion of electron fractionalization in condensed matter physics is presented, including some historical reflections and some speculations concerning future application of these ideas. Particular attention is paid to systems which exhibit spin–charge separation, i.e. the electron can decay into separate excitations which carry the electron spin and the electron charge; the soliton model of polyacetylene is treated as a paradigmatic example. This paper is based on a talk given at a symposium honoring A.J. Heeger, A.C. MacDiarmid, and H. Sirikawa, the winners of the year 2000 Nobel Prize in Chemistry.     

Electron tunneling measurements on TSeF-TCNQ and TTF-TCNQ

Using a point contact geometry we realized tunnel junctions between single crystals of TTF-TCNQ, TSeF-TCNQ and an oxidized aluminum plate; we studied the dynamic conductance of these junctions as a function of temperature between 4.2 K and room temperature.Above the transition temperature T_c, i.e., in the metallic regime, dI/dV(V) is remarkably well fitted by a parabolic function, in agreement with theoretical considerations. Below the critical temperature, both with TTF-TCNQ and TSeF-TCNQ we observed a flattering of the dI/dV curves, and thus a clear deviation from the parabola.From the low-temperature results, a more sophisticated fit of the curves enabkes an upper limit value of the Peierls gap in these compounds to be calculated which is in good agreement with known values.     

铝酸钡盐电子发射材料的研究

采用液相共沉淀法和机械混合法成功制备了阴极用(nBaO:nCaO: nAl2O3=6:1:2)铝酸盐,并研究了烧结温度对612铝酸盐的影响,同时探讨其烧结机制以及烧结过程中物相之间存在的化学反应。采用扫描电镜、能谱仪、X射线衍射仪和激光粒度分析仪对铝酸盐形貌、粒度分布以及物相变化进行了研究。结果表明：采用液相共沉淀法成功制备出亚微米粒径的准球形前驱粉末,D (n, 50)值仅为815 nm。前驱粉末经过高温烧结(1500 ℃b)后,得到了晶化程度高,主晶相为Ba5CaAl4O12的612铝酸盐,浸渍钡钨阴极后,1100 ℃b下的发射电流密度达15.56 A/cm-2,蒸发速率仅为14.5 nm/h     

自旋(磁)电子技术

自 198 8年巨磁电阻 (ＧＭＲ)发现以来 ,磁电子传导引起人们极大关注。由此产生了称为自旋 (磁 )电子学的新研究领域。目前处于发展时期 ,在世界范围内研究十分活跃 ,由此可能会出现崭新的装置。迄今与自旋电子学相关的主要物理现象、材料及研究现状如下表所列 :材料、技术现状     

镁合金表面电子束熔覆铝涂层

为提高镁合金表面耐蚀性,采用火焰喷涂与高能电子束重熔技术在AZ91D镁合金表面制备了A1涂层.分析了涂层的微观组织结构和各区域的元素分布情况,测试了涂层硬度与耐蚀性.结果表明,在电子束重熔过程中,Al-Mg元素在涂层与基体间产生了明显的扩散,呈现交错的界面结合特征.涂层主要由熔覆区、合金化区和热影响区三部分组成,其中合金化层为典型的树枝晶结构.由于涂层中形成大量金属间化合物如Mg2Al3、Mg17Al12,使硬度由基体的70～80 HV0.05提高到220 HV0.05.这些相的存在也显著的提高了AZ91D镁合金表面的耐蚀性.     

镍基高温合金K403电火花沉积工艺

高Al、Ti型镍基高温合金具有良好的热稳定性、热强度和高温组织稳定性,广泛地应用于航空发动机叶片、燃气轮机热端部件等高端精密领域。由于这些热端部件造价昂贵且极易损坏,对该种零件进行维修与再制造成为降低该类部件运行成本的重要方法。由于Al、Ti含量会增大高温合金的焊接裂纹发生率,传统的熔焊技术很难应用到该类部件的维修当中,利用微弧电火花沉积技术对高Al、Ti型镍基高温合金K403进行了沉积试验,获得无裂纹堆焊层,为高Al、Ti高温合金的再制造工程增加了新的工艺方法。