背景地下水作用下铀在砂岩铀矿微界面上的扩散模式研究

上游背景地下水流入酸法地浸采铀退役采区地下水中时产生了稀释和冲洗作用。为探究背景地下水作用下酸法地浸退役采区地下水中铀在水岩微界面上的扩散模式和控制机理,开展了静态稀释实验和动态冲洗实验。静态稀释实验结果显示,背景地下水与污染地下水比例为50∶1时,1 440 min内铀浓度降到背景值60 μg/L以下;初期阶段（0~20 min）,反应速率主要受膜扩散控制;中期阶段（20~150 min）,反应速率受膜扩散和颗粒内扩散共同控制;后期阶段（150~600 min）,反应速率主要受颗粒内扩散控制。动态冲洗实验结果表明,用25个孔隙体积的背景地下水,10 d内铀浓度降至50 μg/L;初期阶段（0~4 d）,反应速率主要受膜扩散控制;中期阶段（4~7 d）,反应速率同时受膜扩散与颗粒内扩散控制;后期阶段（7~10 d）,反应速率主要受颗粒内扩散控制。这些研究结果揭示了上游背景地下水流入酸法地浸采铀退役采区地下水中后铀的扩散和迁移规律,为酸法地浸采铀退役采区地下水自然净化的可行性评估提供了理论依据。     

新疆某砂岩铀矿碱法地浸加压溶解氧浸出试验

较为详细地介绍了砂岩铀矿碱法地浸加压溶解氧浸出的试验结果。结果表明，砂岩铀矿实施低碱耗溶解氧地浸技术是有町能的。在O2分压980kPa(溶解O2质量浓度约300mg／L)条件下，溶浸剂中NaHCO3质量浓度5g／L，平均流速0．34m/d．浸出16d．总液同体积质量比达4．08L／kg，铀浸出率为86％；溶浸剂中NaHCO3质量浓度1g／L，平均流速0．13m／d，浸出96d，总液周体积质量比达9．42L／kg，铀浸出率为76％。     

酸法地浸采铀退役采区地下水二步修复法研究

酸法地浸采铀退役采区地下水具有酸性强、铀及SO42-浓度超标的特性,其修复是亟待研究解决的问题。本文以西北某地浸采铀退役采区地下水为研究对象,先采用CaO中和法去除其中的铀;再采用厌氧脱硫脱硫弧菌微生物膜反应器去除SO42-,并探究碳源与进水流速对去除中和处理后的地下水中的SO42-的影响。试验结果表明：每升地下水经0.167 g CaO中和处理后,pH值由3.0升至7.0左右,铀浓度从最初的0.4 mg/L降至0.04 mg/L,达到了排放标准,SO42-浓度从1349.2 mg/L降至840.3 mg/L;中和处理后的地下水经脱硫脱硫弧菌微生物膜反应器处理,当进水流速为1.0 mL/min、碳源为葡萄糖时,SO42-浓度从840.3 mg/L降至256 mg/L,也达到了排放标准。本项研究表明,先采用CaO中和法去除铀、再采用厌氧脱硫脱硫弧菌微生物膜反应器去除SO42-的二步修复法在酸法地浸采铀退役采区地下水处理中具有潜在应用前景。     

硝酸盐还原菌群的富集及其去除酸法地浸矿山地下水中硝酸盐的研究

为去除酸法地浸矿山地下水中的硝酸盐,采用富集反应体系从不同地区岩石样品中富集得到了硝酸盐还原菌群,研究了其对酸法地浸矿山地下水中硝酸盐的还原作用.结果表明,共富集得到了３组有硝酸盐还原能力的菌群,但只有从西北某退役铀矿山岩心样中富集的菌群能适应酸性铀污染地下水环境,并表现出较好的硝酸盐还原能力,该菌群能在１０d内将酸法地浸矿山地下水中的硝酸盐浓度从１００mg/L降至１mg/L,地下水的pH 由３．０提高至５．０左右,其优势菌为 Tumebacillus,占比达到３１．６２％.     

我国首次探明鄂尔多斯盆地地下水总量

2006年12月12日，中国地质调查局召开新闻发布会，国土资源部党组成员、中国地质调查局局长孟宪来到会并介绍了情况。我国科学家首次探明了鄂尔多斯盆地区域地下水补给资源总量为105亿m^3／年，可采资源量为58亿m^3／年，目前开采量为11亿m^3／年．开采潜力为47亿m^3／年，为鄂尔多斯能源基地规划与建设提供了水资源基础数据。     

脉冲电解制备纯铜的工艺条件

在小型电解槽中。研究脉冲电解法精炼铜的最佳工艺条件。脉冲电解参数为：平均电流密度500A／m^2，脉冲宽度6．0ms，脉冲间隔12．0ms。结果表明。最佳电解工艺条件：电解温度30℃；硫酸浓度140～180g／L；极间距5～6cm；氯离子添加量3．0mg／L；硫脲添加量0．5mg／L；骨胶添加量0．75mg／L；有害杂质允许含量(g／L)，As^3 ≤0．1,Sb^3 ≤0．05,Bi^3 ≤0．05。     

地下溶浸防渗漏技术试验研究

在溶浸采矿试验采场采用注浆防渗和导流孔导流相结合的技术方案。经实践证明这种方法是一种切实可行的方法。目前，国内外还没有在地下溶浸采矿的矿场中使用此项技术的先例。采场经防渗处理后，矿块底板的渗透系数由原来的0.156-0.358m/d降为0.0261m/d。根据现场2000年5月17日－2000年7月15日的实际生产纪录，喷淋量11116.8m^3，实际收液量10247.5m^3，集液率达到92.18%，渗透率为14％，完全达到了攻关指标溶液的渗漏率应不高于15％的要求，防渗成本1.42元／t矿，经济效益显著。     

四方金矿富氧浸出的试验研究

介绍了四方金矿依据现场的实际情况进行富氧浸出工艺的试验研究工作。当氰化钠浓度控制在0．026％-0．028％时,与常规浸出相比可节省浸吸时间8．8h,缩短25％;若把氰化钠耗量降低50％,氰化钠浓度控制在0．013％-0．014％时,浸吸35．2h仍可保证尾渣0．10g／t,尾液0．020g／m^3的指标。     

用于酸法地浸采铀地下水修复的混合SRB驯化试验研究

采集尾矿坝厌氧污泥,通过微生物培养富集,获得混合SRB菌种。对富集菌种进行梯度驯化,使之能够适应酸法地浸采铀地下水环境。经驯化后,混合SRB耐受温度可低到20℃、pH可低到4、硫酸根质量浓度可高达4g/L、铀质量浓度可高达5mg/L,该研究为SRB应用于酸法采铀地下水的修复提供了必要的基础。     

我国地浸采铀地下水修复若干问题的思考

地浸采铀是我国天然铀生产的主要工艺，生产过程中向含矿含水层中注入了一定量的化学试剂，矿床终采后的残余溶液不可避免会对地下水造成污染，存在严重环境隐患，因此，地浸终采后开展地下水修复十分必要。针对地浸采铀地下水修复存在的若干问题，总结了我国地浸采铀矿山终采区地下水源项特征，对比了酸法地浸和中性地浸地下水污染物的种类和水平，调研了国外地浸矿山地下水修复目标值，提出了我国地浸采铀地下水修复目标值的确定方法，探讨了地浸采铀地下水修复主流工艺的优缺点及应用情况，总结了国外地浸矿山地下水修复周期，讨论了地浸采铀地下水修复的时机。基于地浸采铀地下水修复涉及的问题提出了见解，指出了未来的研究方向，旨在为我国地浸地下水修复技术研究和政策制定提供参考。     

Current situation and future trend of China rare earth luminescent material industry

<正>Rare earth luminescent material is one of the most important application sectors of rare earths.China enjoys the exceptional advantage to develop rare earth luminescent material for its abundant rare earth resources.After several decades'endeavor,China's rare earth luminescent material industry,headed by rare earth phosphor for lamp and LED and high efficient rare earth energy-saving light source,has been gradually developed into a scale industry.China has become a major production base of rare earth phosphor for lamps and rare earth     

China rare earth market review

正June 1~10,2014Rare earth market remained weak.Quoted price of rare earth products was similar to that in May.There was no sign of recovery in downstream market.The market of NdFeB magnetic materials and phosphor was depressed.Catalyst,polishing powder and ceramic industries remained inactive.Demand from downstream industry was soft.Consumers purchased on their needs.Suppliers had strong intention to sell.Prices of rare earth products     

Annual Report analysis of Chinese rare earth-related listed companies in 2013

<正>Chinese rare earth-related listed companies have published their 2013 annual reports.It can be understood from their reports that production and operation activities of Chinese rare earth-related companies were still heavily affected by macro economy and industrial policies.They basically followed the steps of national economy.In 2013,world economy recovered slowly but the economy     

Market opportunities and challenges for rare earth polishing powder

正1.Status of rare earth polishing powder Rare earth polishing powder with high content of cerium oxide began to replace iron oxide for glass polishing and became one of the key materials in glass polishing process since 1940.Compared with traditional iron oxide,rare earth polishing powder has many advantages,such as fast polishing rate,high polishing quality and long service life.It can achieve good surface quality and improve operation conditions.For example,in lens polishing,the polishing work that cerium     

Baotou Research Institute of Rare Earths developed a new RE alloy preparation technology

正Pyrometallurgy Laboratory of Baotou Research Institute of Rare Earths had independently developed a new preparation technology of rare earth alloy for NdFeB.The alloy can remarkably enhance the coercivity of NdFeB magnet but also evidently reduce the production cost of the magnet.The new master alloy was prepared in the kA pilot-scale electrolytic cell by the independent technology.The rare earth master alloy can be used as the raw material for NdFeB.Compared     

Market and recycling of NiMH battery

<正>Market status and future trend of NiMH battery1.Global market of small NiMH battery Global market size of small NiMH batteries declined year on year since 2011.The trend will continue to 2018,at the rate of 5%to 10%annually.Demand for small NiMH batteries will be stable gradually.Many electrical apparatuses are powered by the built-in lithium battery today,which is the main reason for the shrunk market of small NiMH batteries.But,for some products,small NiMH     

China rare earth market review

正September 1-10,2014 Affected by the National Day holiday,rare earth transaction was stagnant and the market showed a weak steady state.As there was no good news for downstream market,some products with flat demand would likely rally slightly for some time to     

2014 second batch of rare earth quota released

正~~     

矿用防爆轴流对旋主要通风机叶片ANSYS模态分析及应用

高效节能矿用防爆对旋主要通风机的叶片是主要通风机运行的关键部件,叶片在运行时不断受到气流的作用力,从而使叶片产生振动,当叶片振动的频率与叶片的固有频率接近时,容易产生共振从而导致叶片的断裂。一旦叶片断裂时,对主要通风机的安全运行产生致命的影响,从而导致矿山、化工等企业发生重大事故,将会产生不可估量的损失。基于有限元分析软件ANSYS,对高效节能矿用防爆轴流对旋主要通风机叶片进行模态分析及产生对应的六阶模态频率,对主要通风机叶片的运行频率、固有频率及产生的共振问题进行了原理分析,并且解决了叶片频率共振的问题,从而为主要通风机叶片结构设计提供理论依据,并对主要通风机叶片的安全运行提供保障。     

2013 NdFeB export analysis

<正>China totally exported nearly 24,000 tonsof NdFeB products during 201 3,including 18,825 tons of permanent magnet,valued USD 1.34 billion at an average price of 71.4 USD/kg;3,277 tons of NdFeB magnetic powder,valued USD 1 01 million at an average price of 30.9 USD/kg;1,334 tons of strip casting ribbon,with total export value of USD 74million at an average price of 55.3 USD/kg;and 586