Transport results from untwinned YBCO: Washboard frequency of the vortex lattice,and the quasiparticle mean free path

The washboard frequency of the moving vortex lattice in untwinned YBa₂ Cu₃ O_6.93 may be observed through mode-locking to an externally applied ac current of frequency _ext. The interference between and _ext results in jumps in the dc current-voltage characteristics when and _ext are harmonically related¹. The interference effect disappears in the vortex liquid state. The Hall conductivity _xy below T_c in YBCO contains contributions² from a positive quasiparticle (qp) term (H) and a negative vortex term (1/H). The qp term is surprisingly large well below T_c and implies a large gap anisotropy and a long qp mean free path (mfp). The thermal Hall effect³ _xy is closely related to the qp _xy; _xy is produced by asymmetric scattering of qp by pinned vortices. The qp mfp at H = 0, extracted from _xy and extended to low T by _xy, increases remarkably from 90 Å at T_c to more than 0.5m at 22 K.     

Continuous,martensitic nature of the transition ß→γ Li3PO4

The transformation Li₃PO₄ shows characteristics of both continuous and martensitic transformations. Below 340° C, no detectable transformation occurs; between 340 and 410° C, the transformation goes only partially to completion; above 410° C the transformation rapidly goes to completion. At any temperature in the range 340 to 410° C, transformation proceeds rapidly in the initial stages to attain a certain degree of transformation. With prolonged isothermal heating or grinding of the samples, further transformation does not occur. The reverse transformation could not be effected under normal, dry conditions.     

Creep of ceramics

This review analyses a wide range of experimental data on the creep of ceramic materials and reveals many similarities with the creep of metals. It is demonstrated that there are two important differences in the creep behaviour of ceramics: (1) there is an enhanced role of diffusion creep, and (2) in the power-law regime, ceramics divide into two categories with stress exponents of 5 and 3, respectively. It is concluded that the behaviour with an exponent of 5 represents fully ductile behaviour as in f cc metals, whereas the behaviour with an exponent of 3 is due to dislocation climb from Bardeen-Herring sources under conditions where there is either a lack of five independent slip systems or, if five independent slip systems are available, a lack of interpenetration of these systems.     

Correlation between Superconducting Gap and Pseudogap in High-T c Cuprates

We studied the low-temperature energy gap 2 ₀ on Bi ₂ Sr ₂ CaCu ₂ o ₈₊ (Bi2212) and La _2–x Sr _x CuCO ₄ (La214) systematically over a wide range of doping level p using STS, break junction tunneling spectroscopy, Raman scattering and low-T electronic specific heat data. We have also studied the electronic specific heat of La214 in the normal state at T > T _c , and confirmed that pseudogap behavior appears at around T*, below which the in-plane resistivity and magnetic susceptibility tend to be slightly suppressed. Similar suppression appears in and of Bi2212 below the onset temperature of pseudogap T*. It is pointed out in the present study that 2 ₀ is closely related to T* in both Bi2212 and La214 systems; T* 2 ₀ /4.3k _B . It is also pointed out that 2 ₀ is in almost linear proportion to k _B T _max ( T*), where T _max is the temperature exhibiting a broad peak in –T curves and k _B T _max can be considered to give a measure of the effective antiferromagnetic exchange energy J _eff. The factors in 2 ₀ k _B T _max J _eff are 1 for La214 and 2 for Bi2212, respectively. We also report that in both Bi22l2 and La214 systems T _c roughly scales with p ₀ except in highly doped samples, where T _c 2 ₀ .     

Chemical Control of Underdoped and Overdoped States in Y(Ba2 ? ySry)Cu3O6 + δ

The chemical control of underdoped and overdoped states in the Y(Ba_{2 – y} Sr _y )Cu₃O_{6 +} (0.1 and 0.9) compounds has been observed by high-resolution O K-edge X-ray-absorption near-edge-structure spectra. The chemical substitution of Sr for Ba in the fully-oxygenated Y(Ba_2–y Sr _y )Cu₃O_{6 +} (0.9) compounds gives rise to high hole concentrations within both the CuO₂ planes and the out-of-plane sites, leading to the overdoped state and the decrease in the superconducting transition temperature from 92 K for y=0 to 84 K for y=0.8. In contrast, an increase in the Sr content in the oxygen-deficient Y(Ba_{2 – y} Sr _y )Cu₃O_{6 +} (0.1) compounds did not indicate superconductivity. The oxygen-deficient compounds exhibit the underdoped state due to the low hole concentration.     

Investigation of the excitonic insulator phase in bismuth-antimony alloys

Pressure-induced metal-semiconductor transitions in bismuth-antimony alloys in a strong magnetic field (up to 70 kOe) at helium temperatures have been investigated. It is found that for values of the overlap-gap |G|1 meV the alloy forms an excitonic insulator (EI) in magnetic fields above a certain threshold (30–40 kOe). It is inferred that the EI energy gap increases with the magnetic field. The maximum gap observed in fields of 70 kOe turns out to be ₀₀7.5 K. An analysis of the results shows that transitions to the EI phase are observed from both the semimetal and the semiconducting states. The critical transition temperatureT _c is related to the EI gap by the expressionT _c0.7. Arguments are advanced in support of the fact that the formation of the EI phase involves the pairing of electrons at theL point with holes at theT point.     

Single-Mode As–S Glass Fibers

Single-mode As–S glass fibers with a core diameter from 3 to 20 m and a clad diameter of 125 m are prepared by the double-crucible method. The cutoff wavelength of the fibers is 0.9–6 m. The lowest transmission losses in the fibers at 2.2–2.3 m are 100 dB/km, and their mean bending strength is 800–1000 MPa.     

Vortex imaging in superconducting films by scanning hall probe microscopy

We have used a low noise Scanning Hall Probe Microscope (SHPM) to study vortex structures in superconducting films. The microscope has high magnetic field (2.9×10^–8T/Hz at 77K) and spatial resolution, 0.85m. Magnetic field profiles of single vortices in High T_c YBa₂Cu₃O_7– thin films have been successfully measured and the microscopic penetration depth of the superconductor has been extracted as a function of temperature. Flux penetration into the superconductor has been imaged in real time (8s/frame).     

Metal-Insulator Transition and Cu K-Edge XANES Studies for Pr1.85Ce0.15CuO4+δ High-Tc Superconductors

Metal-insulator transition near oxygen content parameter –0.018 was observed for electron-doped Pr_1.85Ce_0.15CuO₄₊ (–0.0030.03) cuprates. Cu K-edge X-ray absorption near-edge structure (XANES) studies with nearly identical threshold edge energy E₀ of 8980.8 eV indicate a Cu formal valence smaller than 2 for all samples, which is consistent with the estimated Cu valence of 1.84 for 20.5 K superconductor Pr_1.85Ce_0.15CuO_3.997 and 1.91 for Pr_1.85Ce_0.15CuO_4.03 insulator. The XANES spectrum reflects the Cu 3d ⁿ character where low energy peak A ₁ reflects the 3d ¹⁰ configuration of Cu(I) oxidation state and A ₂ peak reflects the 3d¹⁰ ( for a oxygen ligand hole) configuration for Cu(II) oxidation state. The variation of energy separation E(A ₂–A ₁) is consistent with the observed metal-insulator transition, increases sharply from 2.42 eV for Pr_1.85Ce_0.15CuO_4.018 insulator to 2.74 eV for 15 K underdoped superconductor Pr_1.85Ce_0.15CuO_4.015.     

Theory of periodically driven,current-carrying,superconducting filaments. I. Spatially homogeneous states

Starting from the nonequilibrium theory of dirty superconductors in the Ginzburg-Landau regime, spatially homogeneous states with an applied currentI=I ₀+I ₁ cos (t) are considered. Expressions for the linear response (I₁ small) valid up to high frequencies (k _BT_c) are derived and evaluated analytically for the experimentally important case of smallI ₀ and ₀(T). Then the nonlinear response is treated for frequencies with _E1. Interesting new behavior is found for frequencies ₀ 1, where ₀ is essentially the GL relaxation time.     

Microstructure and mechanical properties of rapidly quenched L20 and L20+L12 alloys in Ni-Al-Fe and Ni-Al-Co systems

Ductile L2₀-type wires and+L1₂-type duplex wires with high strengths and large elongation in the Ni-Al-Fe and Ni-Al-Co ternary systems have been manufactured directly from the liquid state by an in-rotating-water spinning method. The wire diameter was in the range 80 to 180m and the average grain size was 2 to 4m for the wires and 0.2 to 1.0m for the+ wires. _y, _f and _p of the wires were found to be about 360 to 760 MPa, 560 to 960 MPa, and 0.2 to 5.5%, respectively, for the Ni-Al-Fe system, those of the+ wires were about 395 to 660 MPa, 670 to 1285 MPa, and 3.5 to 17%, respectively, for the Ni-Al-Fe system, and about 260 to 365 MPa, 600 to 870 MPa, and 4.0 to 7.0%, respectively, for the Ni-Al-Co system. Cold-drawing caused a significant increase in _y and _f and the values attained were about 1850 and 2500 MPa, respectively, for Ni-20Al-30Fe and Ni-25Al-30Co wires drawn to about 90% reduction in area. The high strengths, large elongation and good cold-workability of the melt-quenched and+ compound wires have been inferred to be due to the structural change into a low-degree ordered state containing a high density of phase boundaries, suppression of grain-boundary segregation and refinement of grain size.     

Non fermi liquid ground states in strongly correlated f-electron materials

Experimental efforts to characterize and develop an understanding of non Fermi liquid (NFL) behavior at low temperature in f-electron materials are reviewed for three f-electron systems: M_1–xU_xPd₃ (M = Sc, Y), U_1–xTh_xPd₂Al₃, and UCu_5–xPd_x. The emerging systematics of NFL behavior in f-electron systems, based on the present sample of nearly ten f-electron systems, is updated. Many of the f-electron systems exhibit the following temperature dependences of the electrical resistivity p, specific heat C, and magnetic susceptibility for T T₀, where T_o is a characteristic temperature: P(T) 1 –aT/T ₀, where a < 0 or > 0, C(T)/T (-1/T _o) In (T/bT ₀), and (T) 1 –c(T/T_o)^1/2. In several of the f-electron systems, the characteristic temperature T_o can be identified with the Kondo temperature T_k.     

Prolonged laser ablation effects of YBCO ceramic targets during thin film deposition: Influence of processing parameters

Cumulative laser irradiation during high-Tc superconducting thin film pulsed laser deposition (PLD) may have a detrimental effect on film characteristics. Initial decrease of deposition rate and gradual shift of the center of the deposited material spot towards the incoming laser beam were registered on cold glass substrates. Their absorbance was used for evaluation of the film thickness distribution over the substrate area. At the initial stage, two components of the spot could be distinguished along its short axis: central (cosⁿ , n1) and peripherial (cos ), while with cumulative irradiation the thickness followed an overall cos^m (m相似文献   

Sr2YRu1?uCuuO6: Evidence for SrO-Layer Superconductivity

Sr₂YRuO₆ doped on its Ru site by Cu superconducts at the below 45 K, although its Ru and Cu are magnetically ordered at 23 K and 86 K, respectively. The SrO layers superconduct. Ba₂GdRuO₆, when doped with Cu, does not superconduct, because L = 0 Gd is not crystal-field split, and so induces Cooper pair-breaking.     

A note on the similarity solutions for free convection on a vertical plate

Summary The similarity solutions for free convection on a vertical plate when the (non-dimensional) plate temperature is x and when the (non-dimensional) surface heat flux is –x are considered. Solutions valid for 1 and 1 are obtained. Further, for the first problem it is shown that there is a value ₀, dependent on the Prandtl number, such that solutions of the similarity equations are possible only for >₀, and for the second problem that solutions are possible only for >–1 (for all Prandtl numbers). In both cases the solutions becomes singular as ₀ and as –1, and the natures of these singularities are discussed.     

The frictional behaviour of LiF single crystals

A study has been made of the influence of initial surface roughness, renewable and non-renewable surface contaminants, and irradiation hardening on the coefficient of friction for one LiF single crystal (A) sliding on another (B) in {100}_A<010>_A{100}_B 010_B orientation at 295 K. The normal load was 1 N, the nominal contact pressure 0.1 MPa, the sliding velocity 0.2 to 0.6 mm sec^–1, and the amplitude of the (reciprocate) motion a few millimetres. Any influence of non-renewable contaminants persisted only for cumulative relative displacements 0.1 m, and that of micrometre-scale initial surface roughness only for a few metres. At steady state in the presence of renewable contaminants the coefficient of friction varied only from a high of 0.45 in ultra-high vacuum ( 7.5 × 10^–8 Pa) and dry nitrogen-rich air ( 10⁵ Pa, relative humidity 15%) to a low of 0.38 in moist nitrogen-rich air ( 10⁵ Pa, relative humidity 50%). Irradiation hardening had no effect on the coefficient of friction at steady state. The worn surfaces created by steady-state sliding always exhibited a grooved topography partly obscured by more-or-less adherent layers of variously consolidated equiaxed debris particles 100 nm in size. Owing to the action of image forces, these particles contained no dislocations. It is suggested that the coefficient of friction was determined at steady state by the stress needed to shear these tiny particles past one another as near-rigid bodies.     

Sol-gel prepared Ni-alumina composite materials

The sol-gel method has been utilized for the preparation of dense, homogeneous ceramic-metal composites with up to 50% Ni in Al₂O₂. Examination by SEM and TEM shows that the materials consist of micrometre-size Al₂O₃ with metallic Ni in isolated regions from 50 m down to nanometre size. The density ranges from 97% (10% Ni) to 74% (50% Ni) of the theoretical number. The hardness decreases from 18 GPa for pure alumina to 10 GPa for alumina containing 50% Ni. The fracture toughness increases significantly from K _1c=3–4 MPa m^1/2 to K _1c=8.5 MPa m^1/2. The elastic and shear moduli decrease from E=400 GPa and G=160 GPa for pure alumina to E=320 GPa and G=135 GPa when containing 50% Ni. The electrical resistivity is 10⁶m with 10 to 40% Ni but decreases drastically at 50% Ni content.     

Coherent Brillouin Spectroscopy in Solid Parahydrogen

We applied coherent Brillouin spectroscopy to solid parahydrogen, and measured the Brillouin spectra of longitudinal acoustic modes at 5.6K. It was found that the linewidth of these spectra is 1.5MHz. From the observed Brillouin shift and the crystal orientation, the elastic stiffness was determined as C ₁₁=0.355±0.016GPa and C ₃₃=0.432±0.022GPa.     

Measurements of temperature conductivity by the method of radial temperature waves in a cylinder

Summary The analysis of errors, confirmed experimentally, shows that, for measurements under optimum conditions, the absolute value of temperature conductivity can be easily obtained by the radial temperature wave method with an accuracy of 3% over a very wide temperature range. These optimum conditions consist in providing that Pd_r9 and that the ratio of the diameter to the length of the sample 13. The experiment is not complicated and can be made completely automatic. This method can be recommended for badly conducting materials which can be easily machined (for instance, plastics).     

Microstructure-property studies in friction-stir welded, Thixomolded magnesium alloy AM60

Thixomolded magnesium alloy AM60 plates joined by friction-stir welding were observed to be as strong or stronger than the unwelded base material. The thixotropic microstructures of the as-molded plates consisted of either 3% or 18% primary solid fraction of -Mg globules (45 m average size) in a eutectic mixture consisting of -Mg grains (10 m) surrounded by Mg₁₇Al₁₂ intermetallic grains in the -Mg grain boundaries (having an average size of 1–2 m). This complex, composite microstructure became a homogeneous (Mg + 6% Al)), recrystallized, equiaxed grain (10–15 m) microstructure in the weld zone.