以ABS废机壳料(F-ABS)为研究对象,讨论增韧剂对F-ABS的力学性能、尺寸稳定性、维卡软化点(VST)和热变形温度(HDT)的影响,结果发现:高胶粉可以很好增韧F-ABS,随着高胶粉的加入,复合材料的缺口冲击强度和尺寸稳定性升高,拉伸强度、弯曲强度、弯曲模量、HDT和VST降低,当在F-ABS中加入8%的高胶粉时,复合材料的缺口冲击强度、断裂伸长率、拉伸强度、弯曲强度、弯曲模量、HDT、VST、水平和垂直模后收缩率分别为9.8 k J·m^-2、22.8%、34.9 MPa、51.3 MPa、1 976.1 MPa、74.8℃、92.4℃、0.49%和0.45%;在FABS中同时添加2%的SBS和6%的高胶粉,复合材料的缺口冲击强度和断裂伸长率分别为10.9 k J·m^-223.2%,相对单独添加8%高胶粉的分别提高11.22%和1.8%,尺寸稳定性、HDT和VST变化不大。     

增韧剂对废聚苯乙烯的力学性能、HDT、VST及尺寸稳定性的影响

研究了苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)和高胶粉对废电视机后壳料聚苯乙烯(F-PS)的力学性能、尺寸稳定性、热变形温度(HDT)和维卡软化点温度(VST)的影响,结果表明:SBS和高胶粉在F-PS中有协同增韧作用,在F-PS中复配加入w=6%的SBS和w=2%的高胶粉时,材料的缺口冲击强度从4.5 kJ/m^(2)提高到7.6 kJ/m^(2),增加量为3.1 kJ/m^(2),比单独添加w=8%的SBS的缺口冲击强度(6.9 kJ/m^(2))高0.7 kJ/m^(2),伸长率从28.6%提高到36.7%,增加量为8.1个百分点;高胶粉和SBS都可提高F-PS的尺寸稳定性,但会使F-PS的HDT和VST降低。     

有机蛭石/竹炭/PS废塑料的制备及表征

先对蛭石(VMT)进行改性,得到有机蛭石(O-VMT),并用FTIR和XRD对其进行表征。再通过熔融挤出制备PS废机壳(J-PS)系列复合材料,对复合材料的力学性能和尺寸稳定性进行分析,结果发现,J-PS能够填满竹炭(BC)的内部孔隙;加入O-VMT后,复合材料的物理性能与添加VMT相比更佳;加入BC或O-VMT后,J-PS的尺寸稳定性提升,当加入4%的O-VMT时,J-PS的弯曲模量提高了8.3%,缺口冲击强度下降了28.2%;当加入4%的BC时,J-PS的弯曲模量提高了4.9%,缺口冲击强度下降了11.5%;在O-VMT/J-PS-4中加入4%的BC,复合材料的拉伸强度、弯曲强度和模量分别提高了12.9%、9%和12.7%,伸长率和缺口冲击强度分别下降了17.8%和19.6%,垂直和水平方向的模后收缩率分别降低至41.7%和36.5%。     

云母对聚乳酸热性能的影响

利用转矩流变仪将聚乳酸(PLA)与云母(Mica)熔融共混,制得复合材料(PLA/Mica)。利用热失重仪(TGA)和维卡软化温度仪(VST)仪测试热分解温度和热变形温度,来表征PLA热性能随云母含量变化而变化的情况。结果表明,添加云母后,PLA热稳定性降低,热分解温度随着云母含量的增加而降低;同时,添加云母后PLA耐热变形温度增加,其中云母含量5%的复合材料的维卡软化温度为72.5℃,与纯PLA的64.5℃相比,提高了8℃;在铝酸酯偶联剂DL411、硅烷偶联剂KH-550、KH-560、KH-570四种偶联剂中,偶联剂KH-550表面处理后云母和PLA共混制得的复合材料具有相对较好的热稳定性和热变形温度。     

PP/纳米竹炭粉复合材料的制备与性能研究

通过熔融共混和注塑成型方法制备出不同纳米竹炭粉(NBC)含量的聚丙烯/NBC(PP/NBC)纳米复合材料,并对该复合体系的熔体流变行为和材料的力学性能进行了详细研究。结果表明:PP/NBC共混熔体具有明显的假塑性和剪切变稀的特征,在一个较宽的NBC用量和剪切速率范围内均具有较好的加工性能;随着NBC用量的增加,PP/NBC复合材料的表观黏度和非牛顿指数均逐渐降低,其拉伸强度呈先增加后降低的趋势,而断裂伸长率则逐渐降低。     

超细硅灰石改性聚丙烯的研究

超细硅灰石经铝酸酯偶联剂表面偶联处理,与聚丙烯熔融共混制备改性聚丙烯.研究超细硅灰石的加入及铝酸酯偶联剂处理对聚丙烯性能的影响.结果表明,超细硅灰石的加入可以提高聚丙烯的拉伸强度、冲击强度、维卡软化温度和硬度.超细硅灰石经过铝酸酯偶联剂表面处理后,聚丙烯性能进一步提高.表面处理超细硅灰石改性聚丙烯的拉伸强度在超细硅灰石...     

云母与成核剂复配改性PP

采用云母和成核剂填充改性聚丙烯(PP),研究了复合材料的力学性能、结晶性能及耐热性能。结果表明:云母可有效提高PP的弯曲强度及模量、悬臂梁缺口冲击强度和耐热性能;少量成核剂NA11和表面活性剂硬脂酸钙可使PP/云母复合材料的拉伸强度、弯曲强度、弯曲模量及悬臂梁缺口冲击强度较纯PP分别提高10.4%,32.9%,92.6%,9.2%,热变形温度由纯PP的105℃提高到135℃;云母及NA11对PP具有异相成核作用,复合材料的结晶温度明显提高,晶粒细化、致密。     

蛭石的有机化及其对PCTG性能的影响

采用苄基三苯基氯化磷对蛭石(VMT)进行有机改性,制备有机蛭石(O-VMT),以二甲酸乙二醇酯-1,4-环己烷二甲醇酯(PCTG)为基体材料,通过熔融挤出制备PCTG/O-VMT复合材料,分析O-VMT添加量对PCTG性能的影响。结果表明：与VMT相比,O-VMT对PCTG性能的提高效果更好。随着O-VMT添加量的增加,PCTG/O-VMT的弯曲模量、热变形温度(HDT)、维卡软化点温度(VST)、热分解温度和尺寸稳定性逐渐提升,拉伸强度和弯曲强度先增大后减少。当O-VMT的添加量为4.0%,PCTG/O-VMT-4.0的拉伸强度、弯曲强度和弯曲模量分别为48.2、70.6和2 264 MPa,相比PCTG分别提高6.9%、7.8%和22.4%。相比PCTG,PCTG/O-VMT-7.0在水平和垂直方向的模后收缩率分别降低54.4%和56.8%,HDT和VST分别上升11.7%和9.6%,700℃残炭率、起始分解温度(T_5%)和最大分解温度(T_max)分别提高7.25%、28℃和21.20℃。     

PVC／环氧树脂E51合金性能的研究

采用模压法制备了PVC/环氧树脂E51合金,研究了环氧树脂E51用量对合金力学性能及维卡软化温度的影响.结果表明:当环氧树脂E51用量为1～5份时,随着环氧树脂E51用量的增加,试样的缺口冲击强度、拉伸强度、断裂伸长率、维卡软化温度先增加后减小.当环氧树脂E51用量为3份时,试样的缺口冲击强度、拉伸强度、维卡软化温度出现最大值;当环氧树脂E51用量为4份时,试样的断裂伸长率出现最大值;当环氧树脂E51用量为5份时,试样的缺口冲击强度、拉伸强度、维卡软化温度虽有所降低,但仍比原始PVC试样(指未添加环氧树脂E51的试样)高,而试样的断裂伸长率则骤降,比原始PVC试样还低.在试验条件下,环氧树脂E51的最佳用量为3份.试样冲击断面SEM照片的分析结果与缺口冲击强度的测试结果相符.     

利用废旧PE/PP制备木塑复合材料的研究

利用生活垃圾中分选出的废旧塑料进行复配挤出制成聚乙烯、聚丙烯塑料合金颗粒,通过接枝和偶联两种增容方法,与木纤维废物共混、热压制备新型增强塑木复合材料,并用生活垃圾中的废玻璃、废织物、废纸和废磁砖做增强填料。结果表明,加入KH570硅烷偶联剂的木塑复合材料在织物短纤维的增强作用下,力学性能指标最好,并利用热重分析和扫描电镜分别对不同木塑比例的复合材料的物相和微观形貌等特性进行了分析,由此提出了一种生活垃圾资源化利用的途径。     

镁矿废渣的表面改性研究及应用

研究了镁矿废渣的改性和在聚丙烯中的应用,包括偶联荆种类、废渣粒径、改性方法对复合材料力学性能的影响。结果表明：KH-570的改性效果最好;1000目的填充效果优于325目,湿法改性后与PP的柏容性好于干法改性;当粉料填充到聚丙烯的质量分数为40％时,其力学损失小,且氧指数达29．8％。     

Study on the Far Infrared Ray Emission Property and Adsorption Performance of Bamboo Charcoal/Polyvinyl Alcohol Fiber

In this study, bamboo charcoal materials were blended into polyvinyl alcohol (PVA) solution in various proportions to prepare bamboo charcoal/PVA fibers. A series of estimation was executed to discuss the performance of above fibers such as far infrared ray emission, heat preservation, deodorization of ammonia gas, and the adsorption of methylene blue. The spectrum of far infrared ray of bamboo charcoal/PVA fiber revealed that the average emission rate between 8–14 μm wavelengths increased with the increase in the bamboo charcoal content. From the heat preservation test, it is obvious that the surface temperature of bamboo charcoal/PVA fiber also increased with the increase in the bamboo charcoal content. This increase in content in the fiber specimen achieved a superior adsorption performance for ammonia gas and methylene blue.     

不同温度条件下废弃牛奶盒/聚乙烯复合材料性能的研究

研究了温度对于废弃牛奶盒/聚乙烯复合材料性能的影响。结果表明:(1)废弃牛奶盒/聚乙烯复合材料在52、85、-29、-40℃四种典型的温度环境中处理15 d后,各个方向的尺寸变化率符合热胀冷缩的规律,且各个方向的尺寸变化率呈现出典型的各项异性特征,其中厚度方向的尺寸变化率最大;(2)材料在52、85℃下处理一个月后,弹性模量和弯曲强度都降低了很多,且随着温度的升高,降低的幅度也有所增加,85℃下材料几乎丧失了弯曲强度;在-29、-40℃下处理一个月后,弹性模量和弯曲强度都呈现出了增大的趋势,且随着温度的降低,增大的幅度也在变大;(3)材料经历不同的温度段的冻融循环后,弹性模量和弯曲强度降低的幅度随着温度差的增加而增加;随着循环次数的增加而增加;与经历单纯的高温或者低温的材料的弹性模量和弯曲强度保留率进行对比,冻融循环对材料的弯曲性能影响更大。     

Effect of Waste Tire Dust (WTD) Size on the Mechanical and Morphological Properties of Polypropylene/Waste Tire Dust (PP/WTD) Blends

Waste tire dust (WTD) of mechanically reclaimed scrap tires was blended with polypropylene (PP) in five different compositions to prepare PP/WTD blends. Three series of blends with three different sizes of WTD (250–500 µm, 500–710 µm, and 710 µm–1 mm) were prepared in a Haake Rheomix Polydrive R 600/610 at a temperature of 180°C and a rotor speed of 50 rpm for 9 min. The results show that at the same blending composition, the PP/WTD blends with fine WTD size require higher equilibrium torque and exhibit higher values of tensile strength, Young's modulus, and elongation at break (E_b) than that of blends with coarser WTD size. The swelling index of the PP/WTD blends reveals that the blends with fine WTD size have better swelling resistance in both oil and toluene than all blends with coarser WTD. Scanning electron microscope (SEM) observation indicates that the PP/WTD blends with the finest WTD size exhibit better PP/WTD adhesion than blends with coarse WTD sizes.     

微发泡PP/竹塑复合材料发泡行为及性能研究

采用注塑成型方法,在二次开模条件下制备微发泡聚丙烯(PP)/竹粉复合材料,分析了不同含量的竹粉对微发泡PP复合材料力学性能和发泡行为的影响。结果表明:随着竹粉用量的增加,泡孔平均直径逐渐减小,泡孔密度逐渐增加。竹粉用量为30%时,泡孔直径最小,为23.4μm,泡孔密度达到10.4×106个/cm3,具有理想的发泡效果。竹粉用量在20%时,发泡材料的冲击强度和纯PP基本相同,在性能不降低情况下,节约了原材料成本。     

Mg(OH)_2表面处理对阻燃PP性能的影响

分别采用硬脂酸和硅烷偶联剂对阻燃剂Mg(OH)2进行表面处理,研究了Mg(OH)2的表面处理方法对聚丙烯(PP)复合材料熔体流动性能和阻燃性能的影响。结果表明,经表面处理的Mg(OH)2与PP组成的复合材料的加工性能得到明显改善,对材料的阻燃性能没有明显影响。相同条件下,硅烷偶联剂比硬脂酸的改性效果更好,酸化水解条件对硅烷偶联剂的改性效果没有影响。     

改性PP的研究与应用

用马来酸酐(MAH)对聚丙烯(PP)进行接枝改性,制得改性PP膜。系统研究了反应温度、反应时间、引发剂(过氧化二苯甲酰)和单体(MAH)等对PP膜接枝率的影响。结果表明:改性后的PP膜性能得到提高。     

废塑料气力输送数值模拟的初步研究

采用Fluent软件对废塑料气力输送进行了数值模拟分析。模拟结果揭示了废塑料气力输送过程中废塑料颗粒速度、气体速度和颗粒体积分率沿管长的变化规律以及管径的改变对废塑料颗粒体积分率的分布和固气比的影响。以期为进一步优化废塑料气力输送参数提供理论依据。     

保温层对废热锅炉温度及温差应力影响的有限元分析

对壳体外部设有保温层及未设保温层的两台废热锅炉用ANSYS进行了数值模拟,分析了该废热锅炉的温度场分布情况,计算出由温度梯度产生的温差热应力。并将两台废热锅炉的温度和温差热应力情况进行对比,得出保温层可以降低外壁面温度和温差热应力的结论。