有机锡类PVC热稳定剂及其协同作用的探讨

以有机锡为主体,加入金属皂、亚磷酸酯作为热稳定剂，对PVC塑料的热稳定效果进行了研究，发现有机锡与硬脂酸钡起到较好的协同作用，与硬脂酸镉、亚磷酸酯则无协同作用。     

环氧大豆油对软PVC性能影响的研究

研究了环氧大豆油对软聚氯乙烯(PVC)性能的影响。实验表明,铅盐和有机锡的热稳定性较好,单独使用硬脂酸钙、硬脂酸锌、环氧大豆油或不足量的有机锡热稳定剂时,PVC样品很快变色。环氧大豆油与硬脂酸钙、硬脂酸锌、有机锡热稳定剂并用时,环氧大豆油具有很好的协同效应;但环氧大豆油和硬脂酸钙、硬脂酸锌不能简单替代有机锡稳定剂。热重分析证明了不同热稳定剂的效果。作为辅助增塑剂,环氧大豆油用量应低于5份。     

复合钙/锌热稳定剂中的辅助热稳定剂

正辅助热稳定剂是一种特殊的热稳定剂,其特点是单独使用时热稳定作用甚微,但与金属皂类或有机锡类稳定剂并用时会产生协同作用,有效提高金属皂类或有机锡类稳定剂的使用效率,常见的钙/锌复合热稳定剂用的辅助热稳定剂有多元醇类、亚磷酸酯类、环氧类化合物、β-二酮化合物以及水滑石、沸石等。本文总结并论述了常见辅助稳定剂在聚氯乙烯(PVC)加工体系中对钙/锌稳定剂作用与影响。1钙/锌复合热稳定剂     

硬质PVC用钙锌复合热稳定剂的研究

运用刚果红试纸法和热烘箱老化实验法，对硬质PVC（聚氯乙烯）用钙锌复合稳定剂的主要组分如硬脂酸钙、硬脂酸锌、多元醇、环氧大豆油、亚磷酸酯以及稳定性助剂等进行了考察，得到了各组分及各组分用量之间协同作用的关系，同时还得到了硬质PVC用钙锌复合热稳定剂的实用配方。     

Ca/Zn复合型PVC热稳定剂的性能研究

研究确定了几种稳定剂间的协同作用和较佳复配结果。研究结果表明:(1)Ca/Zn与环氧大豆油、亚磷酸酯、β-二酮均有较好的协同作用,优化的Ca/Zn稳定剂配方为:Ca/Zn总量2.0份、环氧大豆油5份、13-二酮0.4份、亚磷酸酯0.5份;Ca/Zn、13-二酮、ESO与有机锡有很好的协同效应。     

有机锡和金属皂类热稳定剂并用对软质PVC脱HCl反应的影响

采用刚果红法研究了有机锡和金属皂类热稳定剂的并用对软质PVC脱HCl反应的影响。在实验过程中,硬脂酸钡(BaSt2)、硬脂酸钙(CaSt2)、硬脂酸锌(ZnSt2)分别单独、两两和三者混合后与双丁基硫醇锡并用。重点讨论了金属皂用量对软质PVC刚果红初始变色时间和完全变色时间以及初始变色温度的影响。实验结果表明,单独使用时,BaSt2与有机锡的并用效果最好,能产生明显的协同效应;在两两混合与有机锡并用的过程中,BaSt2/CaSt2的并用效果最好,它们与有机锡也能产生较明显的协同作用;而在3种金属皂与有机锡并用后,软质PVC的脱HCl过程不但没有被抑制,反而被加速。     

钙/锌盐复合热稳定剂对CPE高温脱氯化氢的影响

采用刚果红试验法研究钙/锌盐复合热稳定剂对氯化聚乙烯(CPE)脱氯化氢热降解性的影响.结果表明.硬脂酸钙/硬脂酸锌复合热稳定剂与辅助稳定剂环氧大豆油和亚磷酸酯配合使用后具有比普通钙/锌盐更好的稳定效果;当硬脂酸钙/硬脂酸锌并用比为5 : 1,用量为5份,环氧大豆油和亚磷酸酯用量分别为5和1份时,CPE的热稳定性最好.     

氰尿酸镧的协同作用及其复合稳定剂的研究

以氰尿酸、硝酸镧、氢氧化钠为原料合成了氰尿酸镧,通过刚果红试纸法研究了氰尿酸镧与硬脂酸钙、硬脂酸锌、季戊四醇、β-二酮对PVC热稳定性的协同作用;以协同作用为依据,合成了3组复合稳定剂,并且研究了这3组稳定剂的热稳定性、变色性。结果表明:氰尿酸镧与硬脂酸钙、硬脂酸锌、季戊四醇之间有明显的协同作用,但与β-二酮协同作用不明显;复合稳定剂a在热稳定性试验中比另外两组效果好,而复合稳定剂c在变色性方面比另外两组效果都好。     

稀土盐对聚氯乙烯热稳定作用的研究

研究了各种稀土稳定剂的合成工艺、配方及其对ＰＶＣ热稳定性能、加工性能的影响，并用红外光谱法对其作用机理进行了初步探讨。结果表明：单一的水杨酸混合稀土盐对ＰＶＣ有较好的热稳定作用；硬脂酸混合稀土同有机锡、环氧大豆油三者之间有协同效应，其动态热稳定时间及加工性能均优于水杨酸混合稀土稳定剂，可以用硬脂酸混合稀土部分代替价格昂贵的有机锡，具有实际应用价值     

世界热稳定剂现状、发展趋势和新产品动态

目前世界每年塑料热稳定剂的生产和消费量达30万t以上,仅次于增塑剂,我国每年的生产和消费量也在3万t以上。热稳定剂主要包括:铅盐类、有机锡类、金属皂类、复合热稳定剂、亚磷酸酯类、一元醇及多元醇类、环氧类和含氮化合物类,其中前四类占热稳定剂用量的     

国外热稳定剂发展现状

PVC产量的增加刺激着热稳定剂消费量的增长,目前,全球热稳定剂的消费量约为30万t/a。不同国家和地区在热稳定剂品种构成上依然有较大差异,如美国以有机锡类和复合钡/镉皂类为主,日本和西欧还仍然以铝盐类产品为主。     

三月桂酸单丁基锡对PVC热稳定性的影响

用刚果红试纸测试含有三月桂酸单丁基锡和二月桂酸二丁基锡的PVC的静态热稳定性和脱HCl温度。研究发现:采用三月桂酸单丁基锡,PVC的初期热稳定性优于二月桂酸二丁基锡,而长期热稳定性略差于二月桂酸二丁基锡;采用三月桂酸单丁基锡,PVC的脱HCl温度与含有二月桂酸二丁基锡的大致一样。用Brabender流变仪测试含有三月桂酸单丁基锡和二月桂酸二丁基锡的PVC的润滑性和动态热稳定性,根据流变仪扭矩的大小进行分析可知,三月桂酸单丁基锡的润滑性低于二月桂酸二丁基锡;采用三月桂酸单丁基锡后,PVC的动态热稳定性劣于二月桂酸二丁基锡。     

有机锡热稳定剂的毒性及其控制与防护

综述了有机锡热稳定剂的毒性;分析了有机锡热稳定剂的毒性及其毒性控制原理;并简述了有机锡热稳定剂的应用防护以及因不当使用而中毒所要采取的有利措施;旨在确保人们能正确认识有机锡热稳定剂的毒性以及防护,为有机锡热稳定剂的安全生产与应用提供理论依据。     

月桂酸甲基锡的应用研究

用刚果红试纸及流变仪分别测试了加入月桂酸甲基锡的PVC树脂的动、静态热稳定性和加工性能。实验表明,与硫醇甲基锡相比,加入月桂酸甲基锡的PVC树脂的初期和长期稳定性稍差,润滑性和透明性较好。在每10份月桂酸甲基锡中加入1．5份硬脂酸锌后,可使PVC制品的初期色相和润滑性得到改善。月桂酸甲基锡与硫醇甲基锡复配可以改善各项性能,其比例为1：1时,可以得到与纯硫醇甲基锡相似的热稳定性,润滑性和加工性上升,成本下降。     

Biodegradable polyester layered silicate nanocomposites based on poly(ϵ‐caprolactone)

Nanocomposites based on biodegradable poly(?‐caprolactone) (PCL) and layered silicates (montmorillonite, MMT) were prepared either by melt interaction with PCL or by in situ ring‐opening polymerization of ?‐caprolactone as promoted by the so‐called coordination‐insertion mechanism. Both non‐modified clays (Na⁺ ‐MMT) and silicates modified by various alkylammonium cations were studied. Mechanical and thermal properties were examined by tensile testing and thermogravimetric analysis. Even at a filler content as low as 3 wt% of inorganic layered silicate, the PCL‐layered silicate nanocomposites exhibited improved mechanical properties (higher Young's modulus) and increased thermal stability as well as enhanced flame retardant characteristics as a result of a charring effect. It was shown that the formation of PCL‐based nanocomposites depended not only on the nature of the ammonium cation and related functionality but also on the selected synthetic route, melt intercalation vs. in situ intercalative polymerization. Interestingly enough, when the intercalative polymerization of ?‐caprolactone was carried out in the presence of MMT organo‐modified with ammonium cations bearing hydroxyl functions, nanocomposites with much improved mechanical properties were recovered. Those hybrid polyester layered silicate nanocomposites were characterized by a covalent bonding between the polyester chains and the clay organo‐surface as a result of the polymerization mechanism, which was actually initiated from the surface hydroxyl functions adequately activated by selected tin (II) or tin (IV) catalysts.     

Heterobimetallorganische 1,2‐(N,N‐Dimethylaminomethyl)ferrocenyl‐Derivate des vier‐ und zweiwertigen Zinns: Synthesen,Charakteristika und Kristallstrukturen

SnCl₄ reacts with [1,2‐(N,N‐dimethylaminomethyl) ferrocenyl]lithium (FcNLi) under formation of the organo tin compounds of the four valued tin (FcN)_n SnCl _4‐n [n = 1( 1 ), 2( 2 ), 3( 3 ), 4( 4 )]. The heterobimetallic chelate complex bis[1,2‐(N,N‐dimethylaminomethyl)ferrocenyl]tin(II) (FcN)₂ Sn ( 5 ) is formed at the reaction of SnCl₂ with two equivalents of FcNLi. The heterobimetallic tin compounds 1 — 5 were characterized by ¹H NMR‐, ¹³C‐NMR and mass spectroscopy, single crystal x‐ray analyses ( 1,3,4,5 ), ⁵⁷ Fe‐Moessbauer spectroscopy ( 1, 3, 4, 5 ), respectively cyclic voltammetry.     

锡及其合金镀层的氧化腐蚀与防护

测试了锡及其合金镀层经电接触润滑保护剂涂覆后的耐湿热性、耐高温老化性及可焊性,分析了锡及其合金镀层的腐蚀防护原理.试验结果表明,涂覆电接触润滑剂可提高锡及其合金镀层的耐湿热性、耐高温老化性及可焊性,效果满足国家标准要求.     

有机粘土吸附处理水中苯酚的性能及应用

分别用溴化十六烷基三甲铵（ＣＴＭＡＢ）、氯化十六烷基吡啶（ＣＰＣ）和氯化十四烷基吡啶（ＴＰＣ）改性膨润土、沸石和硅藻土；探讨了制备有机粘土的适宜条件；研究了粘土类型、表面活性制种类及其浓度对有机粘土吸附处理水中苯酚性能的影响。结果表明，有机粘土吸附处理苯酚的性能较钉适应的的土好得多。通过Ｘ－衍射分析等手段探讨了有机粘土的结构及其吸附处理。     

NaBH_4还原法制备纳米锡的研究

以SnCl4为原料,NaBH4作还原剂,采用液相还原法,分别在水溶液及聚乙二醇-水溶液中制备了纳米锡,并用XRD、FESEM及DSC对制备物进行了分析。结果表明,所制备的纳米锡为β-锡,四方晶系,粒度小于100 nm,聚乙二醇溶液中得到纳米锡的粒度比水溶液中小。锡粉纳米化后,熔点和熔化热较普通锡粉显著减小,并随着纳米颗粒的增大,熔点增加,熔化热增大。     

PVC热稳定剂酯基锡的研究现状与展望

介绍了PVC用酯基锡热稳定剂的类别、结构与性能及国内外生产情况,阐述了其合成方法,并指出了酯基锡热稳定剂的发展动向。