混合氨-碱沉淀剂制备Ni(OH)_2/还原氧化石墨烯复合材料及其电化学性能

利用简单易行的化学沉淀-回流法制备了Ni(OH)_2/还原氧化石墨烯(RGO)复合材料,研究了不同混合氨-碱沉淀剂对复合材料电化学性能的影响。采用XRD、拉曼光谱(Raman)和SEM表征Ni(OH)_2/RGO复合材料的微观结构和形貌。当以NH_3·H_2O-NaOH作为沉淀剂时,Ni(OH)_2/RGO复合材料中β-Ni(OH)_2纳米片均匀分散在石墨烯片层之间,形成相互插层结构。利用循环伏安(CV)、恒电流充放电(GCD)和电化学交流阻抗(EIS)测试了复合电极材料的电化学性能。研究结果表明:放电倍率为0.2C时,Ni(OH)_2/RGO复合电极材料的放电比容量达到344.8mAh/g,比β-Ni(OH)2的放电比容量高出约29%;5C时放电比容量为274.5mAh/g,经过50个循环,容量保持率为98.8%,呈现出良好的倍率性能和循环性能。     

Mn掺杂Ni(OH)2的合成及电化学性能研究

本工作采用缓冲溶液法制备Mn掺杂Ni(OH)₂(Ni_1-xMn_x(OH)₂, x=0.1, 0.2, 0.3, 0.4), X射线衍射测试表明样品主要是β相, 有少量Mn₃O₄杂相; 循环伏安测试表明, x=0.2的材料还原峰积分面积最大、还原分支的峰电流最高; 恒流充放电测试表明, 在100 mA/g电流密度下, Ni_0.8Mn_0.2(OH)₂放电比容量最高, 其第20次循环放电比容量为271.8 mAh/g, 同等条件测试的商用β-Ni(OH)₂放电比容量为253.6 mAh/g; 在300、500 mA/g电流密度下, Ni_0.8Mn_0.2(OH)₂放电比容量仍保持最高, 分别为294.7、291.5 mAh/g, 而且Mn掺杂Ni(OH)₂的循环稳定性也优于商用β-Ni(OH)₂。Mn掺杂可改善镍电极的循环稳定性、降低镍电极成本, 具有广阔的应用前景。     

还原剂对Ni(OH)_2/还原氧化石墨烯复合材料结构及电化学性能的影响

为研究还原剂对Ni(OH)_2/还原氧化石墨烯(RGO)复合材料结构及电化学性能的影响,首先以氧化石墨烯(GO)和硝酸镍作前驱体,采用水热法制备了Ni(OH)_2/RGO复合材料;然后,利用XRD、SEM和Raman光谱仪表征了复合材料的结构和形貌,并采用循环伏安法、恒流充放电曲线和电化学阻抗谱研究了复合材料的电化学性能。结果表明:以(NH2)2CSO2作还原剂时,制备的β-Ni(OH)_2/RGO复合材料为RGO纳米片与Ni(OH)_2纳米片相互插层的结构;在电解液(6mol/L KOH溶液)中,0.2C放电倍率时β-Ni(OH)_2/RGO复合材料的比容量高达341.0mAh/g,10.0C放电倍率为时复合材料的比容量为242.2mAh/g,仍能保持β-Ni(OH)_2理论比容量的83.8%。所得结论表明制备的Ni(OH)_2/RGO复合材料显现出良好的电化学性能。     

Ni(OH)_2/RGO复合材料的化学沉淀-回流法制备和放电性能

以氧化石墨(GO)和NiSO_4·6H_2O为前驱体,氨水为沉淀剂,用化学沉淀-回流法制备Ni(OH)_2/还原氧化石墨烯(RGO)复合材料,用XRD、SEM表征材料的结构和表面微观形貌,用循环伏安(CV)、恒电流充放电和电化学阻抗(EIS)测试电极材料的电化学性能,研究了GO:Ni(OH)_2质量比和氨水浓度对复合材料结构、形貌和电化学性能的影响。结果表明:所制备的β-Ni(OH)_2/RGO复合材料为Ni(OH)_2纳米片与RGO片相互插层的结构,当氨水的浓度为3 mol/L,GO:Ni(OH)_2=1:8(质量比)时复合电极材料在0.2C的放电比容量高达334.9 mAh/g,5C的放电比容量为260.2 mAh/g,保持在β-Ni(OH)_2理论比容量的90%,表现出良好的倍率性能和循环性能。     

水热温度对Ni(OH)_2/RGO复合材料结构及其电化学性能影响

以氧化石墨(GO)和硝酸镍为原料,采用水热法制备氢氧化镍/还原氧化石墨烯(Ni(OH)_2/RGO)复合材料,通过FT-IR光谱、X射线衍射仪和扫描电镜表征了材料的形貌和结构,并采用循环伏安法、恒流充放电和交流阻抗谱测试了复合材料的电化学性能。结果表明,当水热温度为100℃时,制备了具有α相与β相互嵌型的α/β-Ni(OH)_2/RGO复合材料。在电解液为6 mol/L的KOH溶液中,放电倍率0.2C时复合材料比容量高达388.6mAh/g,放电倍率为10C时,复合材料比容量为266.1mAh/g,比容量保持率为68.5%,显现出良好的电化学性能。     

Co9S8/CNTs/C复合物的制备及其储锂性能研究

以Co(NO)₃·6H₂O为钴源，(NH₄)₂S₂O₈为聚合引发剂和硫源，通过原位聚合和煅烧两步法制备Co₉S₈/C复合材料，同时，为了进一步提高其电化学性能，在原位聚合过程中掺杂碳纳米管(CNTs),得到Co₉S₈/CNTs/C复合材料，并研究CNTs掺杂对Co₉S₈/CNTs/C复合材料电化学性能的影响。结果表明：复合物中CNTs的作用主要在于提高复合材料的电子和离子传导特性，使所制备的复合材料表现出更高的比容量。当CNTs掺杂量为0.2g时所制备Co₉S₈/CNTs/C-0.2复合物在0.1A/g、0.2A/g、0.3A/g、0.5A/g、1.0A/g和2.0A/g时比容量分别为1117mAh/g、985mAh/g、916mAh/g、846mAh/g、793mAh/g和710m...     

石墨烯掺杂的纳米金属复合材料的制备及其电化学性能研究

选择改进的Hummers法制备了氧化石墨烯(GO),将GO进行高温热还原处理，形成还原氧化石墨烯(RGO),再以油酸作为表面活性剂，通过球磨法与金属氧化物正极材料LiFePO₄通过复合生成了LiFePO₄/RGO正极材料。采用XRD、TEM和电化学性能测试等手段对复合材料进行了表征。结果表明，RGO的掺杂没有影响LiFePO₄材料的晶体结构，没有产生新的产物，当RGO的掺杂量为6%(质量分数)时，复合材料中RGO和LiFePO₄分散较为均匀，形貌结构较好。随着RGO掺杂量的增加，复合材料的首次充放电比容量均先增大后减小，当RGO的掺杂量为6%(质量分数)时，复合材料的首次放电、充电比容量均达到最大值，分别为137.5和139.5 mAh/g。在0.2 C的倍率下循环30次后，6%(质量分数) RGO掺杂的复合材料的放电比容量的保持率最高可达86.1%,电荷转移电阻最小为512.70Ω,电化学性能最佳。因此可知，RGO的最佳掺杂量为6%(质量分数)。     

微波法合成Ni(OH)_2/RGO复合材料及其电化学性能研究

利用改进的Hummers法制备氧化石墨烯(GO),以GO为碳源、Ni(NO_3)_2为镍源、尿素为沉淀剂,采用微波二甲基亚砜溶剂法一步成功合成α-Ni(OH)_2/还原氧化石墨烯(α-Ni(OH)_2/RGO)复合电极材料,研究了不同微波功率、不同GO与Ni(OH)_2质量比对复合材料性能的影响。采用X射线衍射和扫描电镜测试其结构、表面微观形貌;利用恒电流充放电技术对其电化学性能进行研究。结果表明:α-Ni(OH)_2在石墨烯片层上形核长大,当微波功率为600W,GO∶Ni(OH)_2=1∶6(质量比)时,0.2C放电比容量可以达到326.7mAh/g,从0.2C到5C,放电比容量仅下降了15.6%,显示了高的容量保持率和循环稳定性。     

高温还原GO制备LiFePO_4/石墨烯复合正极材料及表征

通过对氧化石墨烯(GO)进行微观调控处理得到少层GO。采用喷雾干燥再高温改性的方法制备LiFePO_4/石墨烯锂离子电池复合正极材料;GO还原后即可得到石墨烯,其优良的导电性可以提高LiFePO_4的电子传输能力。通过X射线衍射(XRD)、红外光谱(FTIR)、扫描电镜(SEM)、透射电镜(TEM)和电化学测试技术等方法对复合材料的结构、形貌及电化学性能进行表征。石墨烯的复合使材料颗粒间构建空间三维导电网络,提高了电解质/电极材料界面的电荷转移速率,改善了LiFePO_4的电化学性能。电化学测试结果表明,在0.1C时LiFePO_4的放电比容量为155mAh/g,LiFePO_4/石墨烯复合材料的放电比容量为164mAh/g;1C和2C倍率时,LiFePO_4/石墨烯复合材料的放电比容量分别为140,119mAh/g。     

CNTs添加对MmMn0.4Co0.7Al0.3Ni3.4贮氢合金负极性能的影响

对商用MmMn_0.4Co_0.7Al_0.3Ni_3.4贮氢合金中添加多壁碳纳米管(CNTs)、Ni的电化学性能进行了研究.结果表明,CNTs的加入可以提高电极的放电容量和初始活化性能,合金中添加CNTs、CNTs+Ni的电极完全活化只需11个循环,其最大放电容量分别为255、271mAh/g.而添加Ni的电极则需24个循环才达到最大容量(245mAh/g);合金中添加CNTs、CNTs+Ni的电极具有更高的放电平台和更好的高倍率放电性能(HRD),在1000mAh/g放电电流下,添加CNTs、CNTs+Ni、Ni以及未添加电极的HRD值依次为80.5%、83.9%、66.9%和62.4%,线性极化和电化学阻抗测试表明,CNTs的加入可有效减少欧姆电阻、提高电极表面的电荷迁移速率,更有利于在大电流下进行放电.     

A two-step approach to synthesis of Co(OH)2/γ-NiOOH/reduced graphene oxide nanocomposite for high performance supercapacitors

A two-step approach was reported to fabricate cobaltous?hydroxide/γ-nickel?oxide?hydroxide/reduced graphene oxide (Co(OH)₂/γ-NiOOH/RGO) nanocomposites on nickel foam by combining the reduction of graphene oxide with the help of reflux condensation and the subsequent hydrothermal of Co(OH)₂ on RGO. The microstructural, surface morphology and electrochemical properties of the Co(OH)₂/γ-NiOOH/RGO nanocomposite were investigated. The results showed that the surface of the first-step fabricated γ-NiOOH/RGO nanocomposites was uniformly coated by Co(OH)₂ nanoflakes with lateral size of tens of nm and thickness of several nm. Co(OH)₂/γ-NiOOH/RGO nanocomposite demonstrated a high specific capacitance (745 mF/cm² at 0.5 mA/cm²) and a cycling stability of 69.8% after 1000 cycles at 30 mV/cm². γ-NiOOH/RGO//Co(OH)₂/γ-NiOOH/RGO asymmetric supercapacitor was assembled, and maximum gravimetric energy density of 57.3 W?h/kg and power density of 66.1 kW/kg were achieved. The synergistic effect between the highly conductive graphene and the nanoflake Co(OH)₂ structure was responsible for the high electrochemical performance of the hybrid electrode. It is expected that this research could offer a simple method to prepare graphene-based electrode materials.     

FeOOH-Ni(OH)2复合材料的制备及其电催化析氧性能

以碳纤维布（CFC）为基底,通过两步法(恒电流电沉积法、溶剂热法)成功制备了FeOOH-Ni(OH)₂复合材料。与FeOOH和Ni(OH)₂相比,该FeOOH-Ni(OH)₂复合材料作为电催化剂时,电催化析氧反应(OER)活性显著提高。在1 mol/L KOH电解质溶液中,达到10 mA·cm?2电流密度时所需要的过电位仅为270 mV,Tafel斜率为78 mV/dec,电化学阻抗谱进一步揭示了电解过程中良好的动力学特性。FeOOH-Ni(OH)₂复合材料在碱性介质中具有优异的稳定性,其在高电流密度下(50 mA·cm?2)的过电势经过连续24 h的测试之后几乎没有发生明显变化。FeOOH和Ni(OH)₂之间的强电子相互作用和协同效应有效提高了电导性,促进了电荷转移;此外,这种核壳结构有效增强了电催化活性面积,进而增强了其电催化析氧性能。      

FeS2/RGO纳米复合材料的制备及热电池放电性能

以氯化亚铁、硫代硫酸钠和氧化石墨烯(GO)为原料, 采用水热法制备FeS₂/还原氧化石墨烯(RGO)纳米复合材料, 并采用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、激光粒度分布仪和差热分析仪(DTA)等对FeS₂/RGO复合材料进行了表征。结果表明, 在水热反应过程中加入GO可以防止FeS₂颗粒的团聚, 使FeS₂形成疏松的球状颗粒。采用LiCl-KCl电解质, 在450℃以100mA/cm²电流密度放电时, 截止1.5 V时, FeS₂/RGO比容量为314.9 mAh/g, 较FeS₂高65.6 mAh/g; 采用LiF-LiCl-LiBr电解质, 在500℃以100 mA/cm²电流密度放电, 截止1.5 V时, FeS₂/RGO放电比容量为302.3 mAh/g, 较FeS₂高29.8 mAh/g。与FeS₂相比, 加入石墨烯提高了正极材料的导电性, 单体电池在放电过程中极化电阻相对较小, 使得FeS₂/RGO复合材料表现出较高的放电比容量。     

用于超级电容器的还原氧化石墨烯/NixMn1-x/2O2复合材料的电化学性能

MnO₂为有前景的超级电容器正极材料,具有较高的理论比电容及良好的循环稳定性,但电子电导性不佳限制了其应用。采用一步水热法制备了还原氧化石墨烯（RGO）/Ni_xMn_1-x/2O₂复合材料。通过XRD、SEM、TEM、FTIR、电化学分析等手段对制备的RGO/Ni_xMn_1-x/2O₂物相组成、微观形貌和电化学性能进行了表征和分析。电化学测试结果表明：Ni元素的引入提高了MnO₂的电容性能,以水热法制备的MnO₂的比电容为66 F/g （扫描速度10 mV/s）,而Ni元素掺杂量x=0.02时,Ni_0.02Mn_0.99O₂比电容为111 F/g;材料中引入RGO后,RGO/Ni_xMn_1-x/2O₂复合材料电容性能进一步提高,加入2wt%的RGO时,RGO/Ni_0.02Mn_0.99O₂的比电容为136 F/g。RGO的引入提高了活性材料的电子迁移速率,Ni元素的掺杂造成了MnO₂晶格中存在适量的点缺陷,提高了其导电性。以RGO/Ni_xMn_1-x/2O₂为正极的超级电容器可同时具备双电层电容器和赝电容器的优点,以Ni掺杂MnO₂和RGO的负载协同提高了该复合材料电化学性能。     

四氧化三钴/碳纳米管薄膜的水热合成及其储锂性能

以5-磺基水杨酸和戊二酸为螯合和氧化试剂,在水热条件下将硫酸钴氧化成纳米级Co₃O₄。以碳纳米管薄膜为载体将Co₃O₄颗粒紧密地附着在碳纳米管上使其填充入碳纳米管薄膜的空隙生成Co₃O₄/碳纳米管复合材料薄膜(Co₃O₄@CNTs),并研究其储锂性能。电化学测试结果表明,Co₃O₄@CNTs薄膜具有较高的放电比容量和优异的倍率性能,在0.2C倍率下初始放电比容量高达1712.5 mAh·g^-1,100圈循环后放电比容量为1128.9 mAh·g^-1的;在1C倍率下100圈循环后放电比容量仍然保持527.8 mAh·g^-1。Co₃O₄@CNTs薄膜优异的性能源于Co₃O₄与CNTs的协同作用。高分散性的Co₃O₄增大了活性材料与电解液之间的接触面积,CNTs有助于形成良好的导电网络提高电子电导率,进而提高了Co₃O₄负极材料的循环性能和倍率性能。     

钠离子电池TiO_2/还原氧化石墨烯负极材料的制备及储钠性能

由于钠离子半径比锂离子半径大70%,使得钠离子在石墨电极材料中脱嵌较困难,需要对石墨负极材料进行改性。以天然石墨为原料,采用Hummers法制备氧化石墨烯;在此基础上以钛酸丁酯为原料,采用溶胶-凝胶法制备了TiO_2前驱体/氧化石墨烯(TiO_2/GO)复合材料,通过热处理获得锐钛矿型TiO_2/还原氧化石墨烯(TiO_2/RGO)复合材料。电化学测试结果表明:TiO_2含量为15wt%的TiO_2/RGO复合材料在电流密度为20mA·g~(-1)下的首次放电比容量为74.08mAh·g~(-1),随着循环次数的增加,放电比容量逐渐增大,循环50次后达109.10mAh·g~(-1);充放电效率也呈现出逐渐增大的趋势,循环50次后达65.59%。而纯还原氧化石墨烯首次放电比容量为41.43mAh·g~(-1),循环50次后仅为20.47mAh·g~(-1)。     

A facile preparation of graphene/reduced graphene oxide/Ni(OH)2 two dimension nanocomposites for high performance supercapacitors

A Ni(OH)₂ composite with good electrochemical performances was prepared by a facile method. Ni(OH)₂ was homogeneously grown on the hydrophilic graphene/graphene oxide (G/GO) nanosheets, which can be prepared in large scale in my lab. Then G/GO/Ni(OH)₂ was reduced by L-Ascorbic acid to obtain G/RGO/Ni(OH)₂. Caused by the synergy effects among the components, the G/RGO/Ni(OH)₂ electrode showed good electrochemical properties. The G/RGO/Ni(OH)₂ electrode possessed a specific capacitance as high as 1510 F g⁻¹ at 2 A g⁻¹ and even 890 F g⁻¹ at 40 A g⁻¹. An asymmetric supercapacitor device consisting of G/RGO/Ni(OH)₂ and reduced graphene oxide (RGO) was installed and displayed a high energy density of 44.9 W h kg⁻¹ at the power energy density of 400.1 W kg⁻¹. It was verified that the G/GO nanosheets are ideal supporting material in supercapacitor.