Current crowding effect on copper dual damascene via bottom failure for ULSI applications

Reliability of interconnect via is increasing an important issue in submicron technology. Electromigration experiments are performed on line/via structures in two level Cu dual damascene interconnection system and it is found that wide line/via fails earlier than the narrow line/via. Atomic flux divergence based finite element analyses is performed and stress-migration is found to be important in the failure rate behavior observed. Semi-classical width dependence Black's equation together with the finite element analysis revealed that the difference in the time to failure is due to the much larger average current density along the interface between the line and via for the wide line/via structure, and good agreement is obtained between the simulation and experimental results.     

凝汽器铜管残碳膜腐蚀实例分析

对蒲山电厂凝汽器铜管的腐蚀泄漏原因进行了试验和腐蚀过程分析，找出了原始铜管存在的残碳膜和品体缺陷是腐蚀的诱发因素，采取了针对性的镀膜处理和一系列运行管理措施，达到了预期的效果。     

凝汽器空冷区铜管氨腐蚀过程分析与防护措施

由于氨的聚集与氧的存在，在凝汽器空冷区出现过冷度的情况下，铜管的氨腐蚀是不可避免的。文章分析、计算在机组正常水工况下，凝汽器空冷区凝结水中可能出现的氨浓度，并对氨腐蚀过程与影响因素进行探讨，提出防护建议。     

Application of INKORAM-75 copper corrosion inhibitor

Treatment of cooling water with INKORAM-75 copper corrosion inhibitor is applied for reducing corrosion processes in the copper-containing alloy of which turbine condensers are made. The results obtained from industrial trial of the INKORAM-75 inhibitor in the service cooling water system of the Novovoronezh NPP Units 3 and 4 are presented.     

现场椭圆偏振方法对铜电极腐蚀及缓蚀的研究

应用现场反射式椭圆偏振技术和循环伏安法研究氯离子以及苯并三氮唑对铜电极腐蚀性能的影响,探索铜电极的腐蚀及缓蚀机理,为铜材料在含有氯离子的腐蚀介质（如一次锌锰干电池）中的使用和保护提供依据。研究结果表明：电解液中氯离子的存在将明显加速铜电极的腐蚀,在电解液中添加苯并三氮唑能够抑制铜的腐蚀,即使电解液中没有氯离子存在,苯并三氮唑也能够阻止铜的氧化;与电化学研究方法比较,椭圆偏振测量技术对于检测表面层的微小变化有其独特的优点,在研究抑制铜腐蚀时能弥补电化学研究方法灵敏度不足的缺陷;文中还提出了苯并三氮唑和氯离子参与形成铜表面保护膜层的模型,并结合该模型对铜腐蚀性能和缓蚀机制进行了解释。     

凝汽器铜管缓蚀剂的使用

实验室试验和现场应用结果表明，少量使用缓蚀剂就可以对铜管有较好的缓蚀作用。分析认为现场应用中存在着缓蚀剂肖度过大或过小以及对缓蚀剂的评价方法不正确等问题。应根据拟使用的水质和钢管条件，通过试验，正确选择缓蚀剂和缓蚀剂使用浓度。     

300MW机组凝汽器铜管腐蚀分析及处理

用交流阻抗等电化学方法分析了新旧铜管的耐蚀性，通过试验、分析，认为偏高的水温．偏低的流速是铜管腐蚀的主要原因，加入一定量BTA能显著提高铜管耐蚀性。     

主冷却剂泵石墨瓦磨损原因分析

针对田湾核电机组主冷却剂泵(主泵)运行中出现的止推轴承石墨瓦块表面存在异常磨损的问题,根据水润滑轴承工作原理和磨损机理进行分析研究,发现磨损的主要原因是:1)主泵启、停过程摩擦副瓦块轴向载荷偏大;2)主泵内流体存在大量小气泡在高压作用下被压缩和凝结,使石墨瓦表面形成明显的空化腐蚀。因此,提出:1)长期投用电磁铁,可将主泵的轴向载荷由450kN降至约200kN(该方法正处于试验阶段);2)将主泵水箱封闭,采用盐水系统压力提高石墨瓦冷却回路静压力。该方案实施后主泵运行正常,未再发生因参数超标而导致的机组停机故障,有效解决了石墨瓦块表面磨损问题。     

低电导率体系中铜的腐蚀规律及缓蚀剂的应用

归纳和阐述了纯水中溶解氧、pH值、电导率、水温等对铜腐蚀的影响规律 ,介绍了目前几种缓蚀剂的应用情况 ,并对今后有机铜缓蚀剂的发展方向提出了建议     

连州发电厂1号凝汽器铜管点蚀原因分析

连州发电厂1号机组出现大量凝汽器铜管迅速腐蚀的现象。为查明腐蚀原因,对腐蚀产物和备品黄铜管内表面膜进行了成分分析和动态对比试验。从腐蚀产物的形貌和成分判断该腐蚀属于点蚀,通过备品黄铜管内表面膜成分分析和动态对比试验得出产生腐蚀的主要原因是铜管内存在残碳膜。最后对铜管点蚀的机理进行了探讨。     

环保型覆铜板连续化层压生产工艺

论文介绍了环保型覆铜板的无溶剂上胶、连续层压生产的新工艺     

利用杂铜直接生产纯铜产品的技术--FRHC法杂铜精炼工艺及应用

介绍一种利用杂铜直接生产纯铜产品的新技术 ,即 FRHC法杂铜精炼工艺及应用。这工艺采用废杂铜为原材料 ,经火法精炼 ,得到符合要求的液态钝铜 ,再拉制成铜杆或制成其他铜制品 ,可获较高经济效益和环保社会效益。     

The effect of heat flux on the rate of iron and copper corrosion product deposition in boilers

This publication is concerned with experimental data on the effect of heat flowrate (50–300 kW/m²) and iron concentration (10–40 µg/dm³) in water on the rate of corrosion-product deposition on a carbon steel surface under two (ammonia and metered-ammonia oxygenated) water-chemistry conditions.     

二层型聚酰亚胺薄膜挠性覆铜板的制备与分析

采用磁控溅射和电镀相结合的方法制备了PI/Cu挠性覆铜板并研究了不同电流密度对产品性能的影响.结果表明:电流密度越大则镀层的沉积速度越快,从而导致镀层的晶粒粗大,镀层电阻变小,附着力下降;采用该方法制备的PI/Cu挠性覆铜板镀层厚度及电阻都比较均匀.     

绥中电厂凝汽器铜管腐蚀泄漏原因分析和治理

国华绥中发电公司的主机凝汽器为俄配套生产的800KLIC-8型凝汽器,用海水开式循环冷却,换热铜管材质为含Ni30%的铜镍合金管.从2000年投产以来,经常发生泄漏,分析研究后确定了泄漏的主要是铜管的设计、生产和安装工艺问题,以及海水的强腐蚀性和固液两相流的冲刷腐蚀等原因.通过将近6年的努力治理,凝汽器铜管漏泄治理工作取得到了一定的成效,分析和治理泄漏的方法及经验有利于同行的借鉴.     

汽轮机铜沉积技术分析及解决方案

分析了汽轮机高压缸铜化合物沉积的原因。针对铜沉积过程提出了去除铜沉积物的方法和防范铜沉积的措施。     

基于蒙特卡罗的接地网故障诊断可测性分析

为了分析接地网故障诊断的可测性,提出了一种基于蒙特卡罗的评估方法.在合理范围内,随机设置接地网各条支路的电阻,采用迭代最小二乘法进行故障诊断,计算各条支路诊断结果的平均相对误差和相对标准差.直至达到期望的精度要求.相对标准差小于给定阈值的支路被判定为明晰支路,其余支路被判定为不确定支路.一个60条支路的接地网诊断结果验证了提出方法的可行性.同时该方法表明接地网故障诊断的可测性是可以预计的.可测性研究对于优化测试方案和科学利用诊断结果具有指导意义.     

锅炉低温再热器烟侧管壁腐蚀原因分析

通过对锅炉运行和停备用期间低温再热器管受热面烟侧表面腐蚀形貌、腐蚀特征、外壁腐蚀产物实验研究结果的分析，并结合其腐蚀的机理。判断锅炉低温再热器烟侧管壁出现大范围点腐蚀坑的原因，与停炉保护不当导致的氧腐蚀有关的结论。最后根据低温再热器表面腐蚀检查状况，提出保障其长期安全运行的措施。     

铜导线连续退火过程冷却规律的研究

该文讨论了电线电缆生产中导线连续退火装置冷却过程的工作原理,从理论上导出了冷却过程所遵循的规律。讨论了影响导线冷却的诸因素,并给出了一些实验结果。     

提高设计完善度的要素分析与过程控制

本文阐述了设计完善度的概念和内涵,通过对影响设计质量的要素进行分析,提出课题并进行过程控制.