加剂柴油凝点及冷滤点反弹回升的研究

加入低温流动性能改进剂生产的低凝柴油，在储存和使用过程中存在凝点、冷滤点反弹回升现象，因此对辽河原油的常压柴油、加氢裂化柴油进行了加剂研究。在低温储存条件下，实际加剂柴油的凝点、冷滤点反弹回升幅度比常规测试的反弹幅度大，在0℃下放置6小时直接测定的加剂常压柴油的凝点回升幅度已经达到或超过在室温下放置35天的回升幅度。研究发现，加入低温流动性能改进剂能减缓蜡晶生长速度，但不能从根本上阻断蜡晶的生长。加剂柴油长时间处于低温时，柴油中的蜡晶逐渐长大，当蜡晶长大到某一定临界稳定尺寸时，会形成较大三维网状骨架，低温流动性能改进剂就失去降凝作用。     

清防蜡剂对潍北高蜡高凝原油的降凝机理探讨

针对胜利油田潍北86-斜2区块原油含蜡量高,凝点高的特点,通过对用实验室合成的丙烯酸二十二酯/马兰酸酐/醋酸乙烯酯三元共聚物复配出效果较好的油基清防蜡剂配方,当药剂加量1 000 mg/L时,其防蜡率可达41.46%,溶蜡速率为0.082 9 g·min-1,48℃降粘率为71.80%,凝点降低幅度为7℃。并用该配方对处理前后的石蜡进行红外特征吸收峰、X射线衍射峰以及蜡晶微观形态变化的研究,结果表明,石蜡经药剂处理后红外吸收峰面积比值均增大,X射线衍射峰的强度减弱。在冷却过程中,通过偏光显微镜发现加剂后原油中的蜡晶由片状、针状等形状不规则的单体形成准球状的絮凝体。并且发现在高于析蜡温度时,降凝剂首先析出并起晶核作用使小蜡晶增多;在蜡晶增长阶段,吸附-共晶机理在起主要作用。     

化学防蜡、降凝、降粘复合工艺在胜利高凝高粘油田的应用

胜利油田太平、英雄滩、邵家等油田原油属于高含蜡、高胶质、高沥青质原油,原油粘度大、凝点高。针对该油田原油特性研制了FJN-6防蜡降凝剂,优选了SJN-1降粘剂。介绍了FJN-6防蜡降凝剂及SJN-1降粘剂的配方设计、性能指标,简要分析了防蜡、降凝、降粘机理。经室内试验表明：FJN-6防蜡降凝剂可以降低原油凝点11℃,防蜡率达72.3%。SJN-1型降粘剂降粘率达98%以上。现场采用在井筒中实施防蜡、降凝工艺,在输油中实施化学降粘工艺的复合工艺,很好地解决了该油田原油开采及输送的难题。     

加剂模拟高蜡原油热性能的研究

用自由基溶液聚合法合成了丙烯酸十八酯/马来酸酐/苯乙烯共聚物,用正十六胺胺解共聚物中的酸酐基团,得到共聚物的不完全长链酰胺化产物,即为原油降凝剂PMB.以4种不同熔点的切片石蜡混合物在0号柴油中的溶液为模拟含蜡原油,以2℃/min的速率降温至约-50℃后升温测试,得到空白和加剂油的DSC曲线.含蜡25%的空白油,蜡晶型转变和蜡晶熔化溶解峰合并形成低宽峰,相变能29.28 J/g,加剂(200μg/g)油的两峰分离,后一峰很尖,出峰温度上移,熔程变长,相变能148.5 J/g,表明PMB参与共晶,且与蜡有良好的匹配性.含蜡30%的空白油的两峰明显分离.加剂量增大时(200～600μg/g),起始峰温移向低温方向,放热量(相变能)有所减小,原油降凝幅度增大,对于含蜡25%的模拟含蜡原油(凝点35℃),凝点降低幅度由6.5℃增至17.5℃,与加剂温度20℃时相比,加剂温度为50℃时的平均降凝幅度平均增加2.5℃.     

蜡晶形态结构对原油降凝的影响

 采用偏光显微镜观察了不同条件下蜡晶的形态变化，对蜡结晶过程中的结构、分布状态和生长规律进行了深入的研究，采用气相色谱分析了用52#、62#、80#蜡配制的模拟油中蜡的碳数分布，考察了凝点与蜡含量之间的变化规律，以及沥青质、胶质和大分子降凝剂(PPD)对模拟油降凝、降粘的影响，为改善原油流动性提供理论依据。实验结果表明，蜡晶的微观形态结构、蜡在油中的溶解性能以及降凝剂的降凝作用与模拟油中蜡的碳数分布密切相关，只有当降凝剂分子结构与油中蜡的结构匹配时，才能达到理想的降凝效果。通过实验确定了模拟油降凝时的临界蜡含量为40%（质量分数），大于该临界值后，凝点随着蜡含量的变化幅度将大大降低。     

热处理对添加防蜡剂长庆原油流动性及蜡沉积特性的影响研究

基于流变性测试和蜡沉积实验研究了热处理温度对添加EVA/PAMSQ复合防蜡剂的长庆原油的流动性和蜡沉积特性的影响。研究发现加剂原油依然具有热处理效果,50℃热处理条件下加剂原油的流动性改进效果较差,随着热处理温度升高至60、70和80℃,加剂原油的流动特性(如凝点、黏度、小振幅振荡剪切特性)显著改善。80℃热处理条件下,加剂原油的凝点已低于0℃,表明热处理与EVA/PAMSQ复合防蜡剂具有良好的协同效果。同时,随着热处理温度的升高,加剂原油的蜡沉积速率逐渐降低,但蜡沉积物的含蜡量逐渐升高,这可能不利于蜡沉积物的剥离。蜡沉积物呈现出非均质结构,表层蜡沉积物为凝油状,底层蜡沉积物具有比表层蜡沉积物更高的析蜡点和屈服强度。     

阴离子聚合物St-OMA的合成和应用

采用阴离子聚合法合成苯乙烯（Styrene）-甲基丙烯酸十八酯（Octadecyl methyl acrylate）的二元共聚物St-OMA,评价了不同聚合条件下的聚合物对苏丹原油的降凝效果。通过偏光显微镜和图片处理软件对加剂前后原油中的蜡晶形态和分布进行微观分析,原油中蜡晶由大量片状、针状形态改变为颗粒状,蜡晶尺寸较小,蜡晶间也密实,分散得更细更匀称。这表明降凝剂的加入确实改变了原油中蜡的结晶形态,使析出的蜡晶尺寸变小变密,从而改善了原油的流动性,降低了原油的凝点。     

肇州201区块油基清防蜡剂的研究

针对大庆肇州201区块原油含蜡量高,凝点高,易结蜡的特点,研制出了效果较好的油基清防蜡剂,确定了最佳配方,并且考察了防蜡剂加量对防蜡率和降凝效果的影响。结果表明,对A油样,1^#防蜡剂加量为1．0％时,其防蜡率可达88．6％,凝点可降低7℃;对B油样,4^#防蜡剂具有较好的防蜡降凝效果。     

阿赛线首站原油流动性改进研究

针对阿赛线原油输油温度高、蜡堵现象严重等生产技术问题,评价与分析阿赛线原油对常用降凝剂EVA的感受性,为降低输油温度、保障输油安全奠定理论基础。以阿赛线首站原油为研究对象,采用原油凝点、流变学测试方法,评价典型国产降凝剂对阿赛线原油的降凝降粘效果,对比分析阿赛线原油加剂前后的蜡晶形态,探讨其低温流动改进的主要影响因素。结果表明,阿赛线原油在70 mg/kg的EVA作用下,凝点、反常点和低温表观粘度均有显著降低,但加剂温度及高速剪切对EVA的作用效果影响较大,当加剂温度低于60℃时,加剂作用效果明显变差;加剂原油在析蜡高峰期受到高速剪切时,其低温表观粘度随剪切作用增强而增大;长时间低速剪切对原油加剂效果影响不大。     

潍北高凝点原油降凝降黏剂的研制

实验室自制的三元共聚物AMV-22与EVA复配,添加SLA-107作助剂,制备适用于胜利油田潍北区块高凝点原油的降凝剂AMVES。实验考察了该降凝剂对原油的降凝降黏效果。DSC热分析结果表明,AMVES加量为1000 mg/L时,可使原油凝点从48℃降低到37℃,析蜡点降低2℃。流变性曲线表明原油的剪切稀释作用随温度升高显著增强,当剪切速率大于100 s^-1后黏度基本不变,降凝剂可以大幅降低启动原油的屈服应力。偏光显微镜图显示原油温度越低,蜡晶网状结构越致密,交联度强,黏度大,流动性差;加AMVES之后原油中蜡晶变为团簇状颗粒,原油的流动性增强。由此可见降凝剂AMVES作用于蜡晶使其三维网状结构破坏,从而有效降低原油凝点和黏度。     

Improved Safety and Loadability of Coated DBX-1

Several additives such as polyvinylpyrrolidone (PVP), polyvinyl butyral (PVB), and ethyl cellulose (Ethocel^TM) were selected to improve the flowability and safe pressing of copper(I) 5-nitrotetrazolate (DBX-1), a green replacement for lead azide currently under development. These properties are important for pressing the material into small-volume detonators, especially during manufacturing when saving cost, while maximizing efficiency and safety, is critical. Sensitivity tests such as ball drop impact, Bundesanstalt fur Materialprufung (BAM) friction, and electrostatic discharge (ESD) along with compatibility testing and performance testing in M55 stab detonators were conducted. For comparison, all testing was done on both uncoated DBX-1 (control sample) and DBX-1 coated with various additives. DBX-1 coated with PVP and PVB showed better flowability compared to the Ethocel additive. Moreover, a considerable safety improvement during pressing was observed with all coated DBX-1 samples compared to the uncoated control batch; whereas uncoated DBX-1 typically detonates when pressed to 35–40 kpsi, the coated DBX-1 could be pressed to greater than 70 kpsi with no adverse effect. More studies will need to be completed to find a suitable solvent for the safe long-term storage of DBX-1.     

原油流动改进剂在冀东油田的研制与应用

通过大量的调研和试验,研究开发出了适用于冀东油田地区的JDK系列原油流动改进剂.JDK系列原油流动改进剂是根据冀东油田油品性质,由亲水性表面活性剂和针对性较强的破乳剂复配而成.该药剂加入系统后,可改善原油的性质,提高原油流动能力,降低系统掺水温度,从而减少集输系统的热力损耗.同时该产品在脱水设备中还具备辅助的破乳作用,例如在柳赞地区实现了流动改进剂对破乳剂的成功替换,其它地区破乳剂用量也大幅度减少,相应的脱水指标却有所提高,达到了一剂多效的目的.     

EVA加剂量对含沥青质蜡油流变性的改善效果

通过流变实验、差示扫描量热分析以及显微观察,探究了乙烯-醋酸乙烯酯共聚物(EV A)质量分数对含沥青质蜡油流变性改善效果的影响,并揭示了EVA与沥青质协同降凝降黏机理.结果表明,单独添加EVA或沥青质可在一定程度上改善纯蜡油的低温流变性,且随着EV A质量分数的增大,蜡油的凝点不断降低,低温流变性逐渐变好,在EVA质量...     

液体胍胶非水悬浮液的制备与水合性能

采用羟丙基胍胶、聚乙二醇及悬浮剂等制备了液体胍胶非水悬浮液,分别考察了液体胍胶非水悬浮液的表观黏度、悬浮率及水合速率,进一步探讨了该液体胍胶体系快速水合起黏的影响因素。流变及静置沉降实验结果表明,季铵盐改性的有机黏土适合作为液体胍胶的悬浮剂,液体胍胶的黏度随悬浮剂加量的增加而轻微增加,且其悬浮率随该悬浮剂加量的增加而急剧增大。悬浮剂加量为5%的液体胍胶在340 s-1下的表观黏度为650m Pa·s左右,在1 d内基本不沉降,在2 d内的悬浮率能够保持在98%以上。粉液比(胍胶与聚乙二醇的质量比)在1∶5~1∶2之间时,其对应的液体胍胶于340 s-1下的表观黏度值在200~700 m Pa·s之间,具备较好的流动性,便于连续混配设备泵送。水合起黏实验结果表明,与在中性环境下相比,弱酸性环境下采用该液体胍胶配制的压裂液基液具有更快的水合起黏速率,而碱性环境下该压裂液基液基本不起黏。配液用水pH值为5时,基液黏度在3~5 min内即达到最佳基液黏度的85%~90%。配液时采用高剪切循环速率会加快液体胍胶的起黏速率。     

丁苯胶乳水泥浆体系消泡剂优选与评价研究

由于国产丁苯胶乳中含有大量的表面活性剂,在拌合过程中易导致气泡在水泥浆中形成并稳定存在,从而起泡严重,对水泥石密度和抗压强度产生较大的影响。本文对不同消泡剂的表面张力、胶乳稳定性以及不同温度下水泥浆流动性、密度进行了实验测试和讨论,并对添加复配消泡剂前后丁苯胶乳所形成水泥石的抗压强度和微观结构进行了分析。结果表明:丁苯胶乳浓度相对于消泡剂的种类对水泥浆体系影响较小,并且胶乳水泥浆高温下起泡比常温下严重;消泡剂异辛醇和二甲基硅油均具有较低的表面张力、不破坏胶乳稳定性以及对流动性影响较小,且在90℃下具有较好的消泡效果,加量为0.3%时的效果最佳;加入复配消泡剂(二甲基硅油和异辛醇质量比为1:1.5)后的丁苯胶乳(加量为水泥质量的10%)所形成的水泥石抗压强度得到明显提高,气泡、孔量明显降低,结构更加致密。图10表5参14     

应用流动能力指数评价砂砾岩储层有效性

有效性是储层评价的重要内容,是岩性、物性、储层厚度及孔隙结构等诸多因素的综合反映。对于砂砾岩储层,由于其碎屑颗粒变化范围较大,非均质性较强,给储层有效性评价带来了较大的困难,直接影响了储量评价的客观性。在流动孔隙度理论分析的基础上,通过不同探测深度范围内流动孔隙度特征的对比分析,提出了一种利用流动能力指数评价储层有效性的新方法,将该方法与孔隙度谱分析程序联合应用于储层有效性评价中,建立了研究区砂砾岩储层分类标准,为后续开发生产提供了重要的决策依据。     

C.I.颜料红57:1应用性能改进的研究

通过选择适当的工艺条件及采用松香、表面活性剂和有机胺衍生物对颜料进行表面处理，改善C．I．颜料红57：1的色光、流动性、透明性等应用性能，使其适于不同的使用需求。     

热处理温度对长庆原油蜡沉积特性的影响

通过Couette蜡沉积装置及DSC热分析探究了热处理温度对长庆原油蜡沉积特性的影响,发现随着热处理温度的升高,长庆原油蜡沉积速率减缓,蜡沉积层老化速率加快;经50 ℃和60 ℃热处理的长庆原油,蜡沉积层出现了分层现象,其表层为流动性较强的凝油状蜡沉积层,底层为结构较为致密的类固态蜡沉积层;经70 ℃热处理的长庆原油,蜡沉积层极薄且致密,无分层现象,其表面无凝油状蜡沉积层。采用沥青质分散程度分析、DSC热分析及蜡晶形貌显微观察探究了其影响机理,发现随着热处理温度的升高,长庆原油沥青质分散程度增大,从而使其析蜡点降低,蜡晶团聚性增强,原油低温流动性得以改善,进而对其蜡沉积特性产生了显著影响。     

H89-2原油流动性改进剂的研究

应用流动性改进剂(化学添加剂)可改善原油的低温流动性能.本文以烯烃、脂肪酸烯基酯和烯基酰胺或烯基磺酸盐为主要原料,在含有自由基引发剂的溶液中,在温度55～85℃,压力5～9MPa,聚合3～8h合成了能降低原油凝点的流动性改进剂H89-2(三元共聚物).综合评定了H89-2改善青海原油低温流动性能的效果,在原油中加入15×10^-5H89-2,可使凝点从31.5℃降至12℃;表观粘度(20℃)从5158.9mPa·s降至79.2mPa·s;屈服值从73.6Pa降至0Pa.探讨了H89-2的降凝作用机理.因为H89-2既含有适度的烷烃碳链,又含有两种极性不同的极性基因,所以对原油的适应性较强.