前处理对不锈钢表面化学镀Ni-P镀层结合力影响的研究

为了在不锈钢表面获得结合力合格的化学镀Ni-P镀层,研究了化学活化、化学活化 闪镀镍、阳极活化 闪镀镍3种前处理工艺对不锈钢上化学镀Ni-P层结合力的影响.采用淬冷法和划痕试验2种镀层结合力测试方法,对化学镀Ni-P层与不锈钢基体之间的结合力进行了评价.结果表明,采用化学活化 闪镀镍和阳极活化 闪镀镍的前处理工艺,Ni-P镀层与不锈钢基体之间的结合强度合格,而采用化学活化前处理的试样,Ni-P镀层与不锈钢基体之间结合强度不合格,原因在于经化学活化后,在不锈钢表面形成了一层黑灰色的腐蚀产物.在168 h的NaCl溶液中腐蚀失重试验表明,不锈钢失重1.2 mg,而化学镀Ni-P镀层未发现失重,说明化学镀Ni-P镀层耐腐蚀失重性能较不锈钢为好.     

钢芯铝绞线钢芯表面植酸活化对化学镀Ni-P层耐蚀性的效用

为了提高钢芯铝绞线钢芯的耐蚀性,采用植酸对其活化再化学镀覆Ni-P合金,研究了植酸活化处理对钢芯钢表面Ni-P镀层耐蚀性的影响。采用SEM和EDS对Ni-P镀层腐蚀前后的形貌和成分进行了分析,在1mol/L H_2SO_4+3%NaCl混合溶液中测定了其极化曲线,比较了其腐蚀速率;利用超声波振荡法研究了植酸活化前后Ni-P镀层与基体的结合力。结果表明:钢芯表面经植酸活化后Ni-P镀层的胞状凸起细小,结构更加均匀、致密,与基体有较好的结合力;植酸活化后,Ni-P镀层的腐蚀电位变大,腐蚀电流减小,腐蚀9 h时Ni-P镀层表面几乎无变化。     

AZ91D镁合金化学镀Ni-P/Ni-W-P双层镀层研究

为了提高镁合金的耐磨耐蚀性,研究了一种镁合金直接化学镀Ni-P/Ni-W-P双层镀层的方法.采用扫描电镜(SEM)和X-射线衍分析射仪(XRD)分析了镀层的微观结构.对镀层进行了极化曲线分析,并进行了盐酸腐蚀试验和结合力试验.结果表明,该复合镀层组织致密无孔,具有较高的显微硬度和高耐蚀性.镀层硬度可达622HKV,试样在10%的HCl溶液中可保持近3h不腐蚀基体,对镁合金起到很好的保护作用.     

镁合金表面Ni-P-纳米SiC复合化学镀层的耐腐蚀性能

为了提高AZ91D镁合金的应用性能,将纳米SiC引入Ni-P镀液,采用化学镀的方法制备了Ni-P-纳米SiC复合镀层,研究了Ni-P-纳米SiC镀层的孔隙率、盐雾性能以及阳极极化曲线,并与Ni-P化学镀层的耐蚀性进行了对比.结果表明:Ni-P-纳米SiC镀层均匀、致密,纳米SiC在镀层表面呈弥散分布;当纳米SiC浓度为4 g/L时,复合镀层的孔隙率最小,为1个/cm,耐蚀时间(90 h)明显长于Ni-P镀层(60 h),腐蚀电位为-0.58 V,略高于Ni-P镀层(-0.59 V).     

晶须增强AZ91D镁基复合材料化学镀镍工艺优选及镀层性能

晶须增强AZ91D镁基复合材料的耐蚀性不佳,为了提高其耐蚀性,采用普通化学镀镍技术对其进行化学镀镍,初步筛选了4种工艺,然后根据Ni-P镀层的形貌和镀液性能确定了适用于晶须增强AZ91D镁基复合材料表面化学镀镍的较佳工艺.采用扫描电镜(SEM)观察了镀层的表面形貌;采用电化学方法(电位-时间曲线,动电位极化曲线,交流阻抗)研究了镀层的耐蚀性;用锉刀试验测试了镀层与基体的结合力.结果表明:普通镁合金化学镀镍技术适用于晶须增强AZ91D镁基复合材料;较佳镀镍工艺为20 g/L 2NiCO3·3Ni(OH)2·4H2O,10 g/L NH4HF2,20 g/L NaH2PO2·H2O,pH值为6.5,温度为65℃,时间为2h;该工艺制备的化学Ni-P镀层表面无明显缺陷,致密性较好,自腐蚀电位较基体升高0.41 V,耐蚀性有所提高,与基体结合良好.     

Ni-Cu-P化学镀层的腐蚀行为

为了进一步提高Ni-P镀层的耐蚀性能,在Ni-P化学镀液中加入硫酸铜制备了Ni-Cu-P三元合金化学镀层,测试了镀层的沉积速度,采用扫描电镜(SEM)观察了镀层的表面形貌,测试了镀层在5.0%H2SO4,5.0%NaOH及3.5%NaCl溶液中的动电位极化曲线,并与Ni-P化学镀层进行了比较。结果表明:Ni-Cu-P镀层表面的胞状物比Ni-P镀层的更加细小,镀层致密性更好;Ni-Cu-P镀层在3种介质中均表现出更好的耐均匀腐蚀性和抗点蚀性能,主要是因为Ni-Cu-P镀层的非晶态结构减少了镀层缺陷数量,从而减少了腐蚀发生的敏感位置和腐蚀微电池的数量,同时更加细小的晶粒也使Ni-Cu-P镀层比Ni-P镀层更容易钝化和维持钝态,另外Ni-Cu-P镀层更为致密也减少了腐蚀介质渗入基体的通道。     

淡水泥浆钻杆化学镀Ni-P层的防护性能

G105钢油田钻杆在淡水泥浆中腐蚀严重,为此,对其进行化学镀高磷Ni-P层处理.用附带能谱仪的扫描电镜观察了镀层形貌、分析了镀层成分,用测厚仪测试了镀层厚度;通过动态模拟腐蚀装置考察了流速对G105钢及Ni-P镀层腐蚀速率的影响,比较了油田现用的有机涂层和Ni-P镀层的耐高温腐蚀性能和耐磨蚀性能.结果表明:Ni-P镀层表面呈胞状,磷含量为13.23％,属高磷耐蚀镀层;流速对Ni-P镀层腐蚀速率影响较小,Ni-P镀层耐蚀性明显优于G105钢;有机涂层经10 h强化磨蚀就发生损伤,Ni-P镀层50 h基本没有变化;低流速下,有机涂层高温腐蚀10 h而鼓泡,Ni-P镀层则没有变化.     

回转体表面喷射电沉积Ni-P-ZrO2复合镀层耐腐蚀性能研究

为延长回转体零件的使用寿命,提高其耐腐蚀性能,本文利用喷射电沉积技术在45钢外圆表面制备Ni-P合金镀层和Ni-P-ZrO₂复合镀层,采用扫描电镜、腐蚀失重法和电化学测试分析等测试手段对Ni-P-ZrO₂复合镀层、Ni-P合金镀层和45钢基体在50 g/L NaCl溶液中的表面形貌和耐腐蚀性能进行研究,并探究腐蚀机理。研究表明:Ni-P-ZrO₂镀层相对Ni-P镀层表面致密度更高,缺陷较少;浸泡相同时间, Ni-P-ZrO₂镀层的失重量最小,腐蚀速率最小;电化学测试实验中,Ni-P-ZrO₂复合镀层的腐蚀电流最低(43.2×10^-5 A/cm²),共沉积ZrO₂颗粒后,Ni-P-ZrO₂复合镀层容抗弧半径更大,极化电阻值R_p增大为Ni-P合金的3倍,双层电容值C_d由4.743 8 μF/cm²降低为3.887 2 μF/cm²。在相同条件下腐蚀后,Ni-P-ZrO₂复合镀层的表面较为完好,腐蚀产物较少;Ni-P合金次之,有较多黑色腐蚀产物;45钢表面形貌最差。综上,采用喷射电沉积在回转体表面制备的Ni-P-ZrO₂复合镀层相对Ni-P合金镀层和45钢基体表现出更优良的耐腐蚀性能。     

两种镍盐体系中镁合金表面化学镀Ni-P层的结构性能

研究了在AZ31B镁合金表面以硫酸镍和碱式碳酸镍为主盐镀液体系化学镀Ni-P.通过扫描电镜(SEM)、能谱分析(EDX)、X射线衍射(XRD)及动电位极化曲线分析,探讨了2种不同镀层的组织形貌、物相成分及耐蚀性.结果表明:两种不同镍盐体系均能得到致密、均匀、无缺陷的Ni-P镀层;磷的含量相近,质量分数分别为6.67%,6.60%,属于中磷镀层;镀层的腐蚀电位分别为-0.24,-0.37 V(vs SCE).比较两种镀层发现,以硫酸镍为主盐体系得到的镀层晶胞更细小,均匀、致密;镀层腐蚀电位正移了0.1 V,钝化区间更为明显,耐蚀性能更为优异.     

Ni-P功能梯度层及均质Ni-P化学镀层的磨损性能

目前,Ni-P化学镀层内应力大,结合强度低,耐磨性差,功能单一,不能满足工业应用要求.为此,采用化学镀技术在45钢表面制备了Ni-P功能梯度镀层,并与3种不同磷含量的均质Ni-P镀层对比,研究了镀层硬度、结合力、耐磨性等特征,分析了成分与结构的梯度变化对Ni-P镀层耐磨性能的影响.结果表明:Ni-P梯度镀层的硬度高于中磷和高磷镀层,略低于低磷镀层,400℃热处理1 h后其硬度达到最大值;镀层与基体结合紧密;在相同条件下试验,Ni-P梯度镀层的耐磨性均优于均质Ni-P镀层,热处理后其耐磨性比均质Ni-P镀层提高1～2倍;与单层Ni-P镀层相比,梯度镀层在整个磨损过程中摩擦系数变化平稳,波动范围较小,镀层内部成分和结构的梯度化进一步提高了镀层与基体的结合力和耐磨性能.     

镁合金磷化处理对化学镀镍层性能的影响

为了有利于环保,采用磷化工艺对AZ31B镁合金进行化学镀镍前处理.采用直观法、扫描电子显微镜和阴极极化曲线法对磷化膜及其化学镀镍层进行了分析.结果表明:AZ31B镁合金表面经磷化处理后得到了良好的化学镀镍层;AZ31B镁合金化学镀镍层的耐蚀性随磷化时间的延长先增加后减小,当磷化时间为75 s时,化学镀镍层的腐蚀电势比直...     

镁合金化学镀镍的研究现状与展望

镁合金用途广泛,但耐蚀性能差,通过化学镀镍可以改善其耐蚀性能.从改善镀层与基体的结合力、提高镀层耐蚀性和化学镀液组成及作用等角度出发,对近年来镁合金化学镀镍的研究状况进行了综述,并提出了今后发展的几点建议.     

烧结NdFeB永磁体化学镀镍前的酸洗工艺研究

对NdFeB永磁体化学镀镍前的不同酸洗处理工艺进行了试验,并对不同酸洗工艺获得的镀层结合力和耐蚀性进行了测定比较.结果表明,经硝酸与氢氟酸混合酸液酸洗后的试样具有较平整的表面,在此表面上得到的镀层经高压锅及锉刀试验证明具有良好的结合力,浸泡试验检测表明其具优良有的耐蚀性.     

A study of corrosion performance of electroless Ni–P and Ni–W–P coatings on AZ91D magnesium alloy

The autocatalytic nature of the electroless nickel‐based alloy coating process will inevitably produce H₂ bubbles which may be left in electroless nickel‐based alloy coating. If the H₂ cannot be removed and left in the coating, it can lead to its poor corrosion resistance due to hydrogen cracks. So, the post treatment is an essential step for electroless deposition process. In this paper, electroless Ni–P and Ni–W–P coatings with chromium‐free pretreatment and dehydrogenation post treatment have been successfully prepared on AZ91D magnesium alloy, and the corrosion behaviors of the two kind coating samples in NaCl solution, HCl solution, and H₂SO₄ solution have been investigated. Both the polarization test and immersion tests show that the electroless Ni–W–P coating has better corrosion resistance than that of electroless Ni–P coating.     

Preparation and Performance of Electroless Nickel on AZ91D Magnesium Alloy

The corrosion of magnesium alloy in different plating solutions was researched. The results demonstrated that corrosive condition of the alloy immersed in nickel chloride solution and nickel sulfate solution is serious and in nickel acetate solution and nickel nitrate solution is less. Magnesium alloy was handled with four acid pickling formulas and two activation formulas and the effects of different pickling formulas and activation formulas were researched through comparative experiment. The experimental results indicated that after handed with pickling formula about 500 mL L^?1 H₃PO₄ (85%), 110 mL L^?1 HNO₃ (68%), room temperature for 30 s and activation formula about 375 mL L^?1 HF (40%), room temperature for 10 min, magnesium alloy could realize electroless nickel plating directly and the performance of the prepared plating was much better. The properties of the nickel-plating coating were researched by electrochemical workstation, scanning electron microscope, and X-ray diffraction. The results demonstrated that this Ni–P coating was very uniform and meticulous; the structure of Ni–P coating was amorphous; and comparing with magnesium alloy, the corrosion potential of this plating increased about 799 V and the corrosion current density declined obviously. The nickel-plating coating effectively improved the anticorrosion performance of magnesium alloy.     

硅基体表面无钯活化化学镀镍工艺

硅材化学镀镍的活化是为了获取金属原子沉积中心,但现有的活化工艺存在种种不足。金纳米粒子具有小尺寸效应、表面与界面效应,呈现出良好的催化活性。采用金纳米粒子对硅基体进行活化后化学镀镍,并采用浸泡腐蚀试验,SEM及EDS测试将其与传统的钯活化法对比,研究了活化后的沉积速度及镀层形貌、结构、耐腐蚀性能,结果表明：金纳米粒子活...     

Electroless Ni‐P coating on Cu substrate with strike nickel activation and its corrosion resistance

Electroless Ni‐P coating was successfully deposited on Cu substrate by strike nickel activation process. The specific pretreatment steps were discussed. The surface and cross‐section morphologies, phosphorus content, adhesive force, and corrosion resistance were characterized for electroless Ni‐P coating. Scanning electron microscopy shows the compact surface. Energy dispersed X‐ray shows the 11.4% phosphorus content. Adhesive test shows the qualified adhesion of electroless Ni‐P coating to substrate. Porosity test shows pores free of the coating, and immersion test in 10% HCl solution indicates the better corrosion resistance of electroless Ni‐P coating in protecting Cu substrate from the corrosion of Cl ions. Thus, strike nickel activation pretreatment is suitable for electroless Ni‐P coating on Cu substrate.     

一种提高钛合金化学镀镍层结合力的方法

为了提高钛合金与化学镀镍层的结合力,以微弧氧化、HCl和HF活化对钛合金作前处理后再进行化学镀镍并在300°C下进行热处理,研究了镀镍层与基体的结合力及其硬度。结果表明：钛合金化学镀镍前进行微弧氧化可以显著提高镀镍层的结合力,镀层经热处理后结合力得到进一步提高,临界载荷为35．30N,硬度达1186．9HV。     

Ni-Cu-P化学镀层的制备及其耐烟气冷凝液的腐蚀性能

为了解决冷凝式燃气利用设备的腐蚀问题,采用化学镀工艺在紫铜基体上沉积Ni-Cu-P层.利用扫描电镜(SEM)、电子能谱(EDX)、电子探针(EPMA)分析镀层的形貌和成分,利用极化曲线和交流阻抗谱考察了紫铜基材及其Ni-Cu-P镀层在15℃和60℃煤气烟气冷凝液中的耐腐蚀性能.结果表明:Ni-Cu-P化学镀层表面均匀平...     

化学镀镍对碳纤维增强聚酰亚胺表面WC/Co涂层抗热震性能的影响

在航空发动机涡轮叶片用碳纤维增强聚酰亚胺(C/PMR15)复合材料表面喷涂WC/Co涂层可以提高其抗氧化耐冲刷性能,采用整体热震法能够评定涂层与基体的结合力.研究了在C/PMR15基体上化学镀镍作为粘结底层对WC/Co喷涂层抗热震性能的影响,并与喷涂PMR15粉末作为过渡层的方法进行了比较.结果表明,在PMR15过渡层上不能得到完整的后续涂层,在化学镀镍粘结底层上可得到连续致密的镍基合金层和WC/Co涂层,镀镍层大幅度提高了基体抗氧化能力,缓和了WC/Co涂层和基体界面位置的热应力,涂层抗热震性提高.