茶叶废料在脲醛树脂中的应用研究

将不同颗粒度的茶叶废料粉添加到脲醛树脂胶中,研究了茶叶废料的颗粒度、加入量等对脲醛树脂胶黏剂的游离甲醛含量、黏接胶合板的甲醛释放量及胶合强度的影响。实验结果表明,茶叶废料作为填料添加到脲醛树脂胶黏剂中,能够降低其游离甲醛含量以及其黏接胶合板的甲醛释放量;茶叶废料颗粒度越小,与脲醛树脂混合性越好,消除甲醛效果越显著;茶叶废料的适量加入不会降低胶合板胶合强度。     

尤戎(Uron)树脂及其用法对脲醛树脂性能的影响

以不同工艺制备了三种含尤戎结构的脲醛树脂(Uron树脂),通过其与普通脲醛树脂的混合制得多种混合脲醛树脂。研究了Uron树脂及其使用方法对降低脲醛树脂胶粘剂游离甲醛含量及胶接胶合板甲醛释放量的作用与效果。结果表明:1)三种不同摩尔比的Uron树脂对脲醛树脂游离甲醛含量及胶接胶合板甲醛释放量都有明显的降低作用,游离甲醛含量最多可降低43％,甲醛释放量最多可降低61％;2)Uron树脂的添加量在10％-20％时对胶合强度的提高有利,强度最大可提高29％;3)低摩尔比Uron树脂对脲醛树脂的改性效果优于高摩尔比Uron树脂。     

有机硅乳液改性脲醛树脂胶粘剂的研究

采用对比实验,考查有机硅乳液加入时间、加入量等因素对脲醛树脂的改性效果,将制成的改性脲醛树脂胶粘荆压制三层杨木胶合板,检测胶合板的甲醛释放量和胶合强度等指标。试验结果表明,改性效果最佳的nP／nU为1.2,当有机硅的加入量为树脂总量的5％,加入方式为树脂合成后期加入,对于提高树脂胶合强度、降低游离甲醛及甲醛释放量效果最佳。     

AR—M—AR粉对脲醛树脂增强效果研究

利用AR－M－AR粉对脲醛树脂（UF树脂）进行增强和降低游离甲醛释放量研究结果表明，由羟甲基化三聚氰胺和烷基间苯二酚制成的线型AR－M－AN粉能显著提高UF树脂胶合板的胶接强度，特别是胶合耐水性，并能明显地减少UF树脂胶合板的游离甲醛释放量。但是，对于在强酸性条件下合成的部分UF树脂添加AR－M－AR粉后胶接强度下降。     

低nF/nM三聚氰胺-甲醛低聚物对脲醛树脂性能的影响

采用自制的可溶性三聚氰胺-甲醛低聚物作为脲醛树脂的添加剂,通过DSC及压制胶合板等方法评价该低聚物对脲醛树脂的固化特性、游离甲醛释放量和胶合强度的影响.结果表明,对于nF/nU为1.1的脲醛树脂UF1.随着三聚氰胺-甲醛低聚物加入量的增加,树脂固化活化能和胶合板的甲醛释放量都呈现先降低后增加的趋势,而胶合强度变化趋势不...     

淀粉降低UF树脂中游离甲醛及胶合板中甲醛释放量的研究

介绍了自制改性淀粉对脲醛树脂改性的方法,探讨了不同添加时间段与不同添加量对改性淀粉最低游离甲醛、甲醛释放量及胶合板胶合强度的影响。结果表明,加入改性淀粉可明显降低甲醛释放量及游离甲醛含量,同时胶合强度也得到一定的提高。     

不同固化剂下低摩尔比脲醛树脂热行为及胶接胶合板性能

通过对3种固化剂下5种低摩尔比脲醛树脂进行热分析和胶合板制造实验,研究了摩尔比、游离甲醛含量、固化剂种类等对低摩尔比脲醛树脂胶粘剂固化反应起始温度、峰顶温度、终止温度和胶合板胶合强度及其甲醛释放量的影响。实验结果表明:1)与传统的氯化铵固化剂相比,过硫酸铵催化的脲醛树脂的热分析曲线的起始温度和峰顶温度都很低,显示出良好的固化促进作用;2)以过硫酸盐作固化剂时,低摩尔比脲醛树脂固化过程中起始温度和峰顶温度受摩尔比的影响较小;3)摩尔比为1．0的脲醛树脂胶接胶合板的胶合强度也能够满足GB／T 9846．3-2004Ⅱ类胶合板的要求;4)用过硫酸盐作固化剂制备的胶合板的甲醛释放量较低。     

硫代硫酸钠/三聚氰胺改性脲醛树脂制备工艺研究

以硫代硫酸钠和M(三聚氰胺)作为复合改性剂,F(甲醛)和U(尿素)作为主要原料,采用弱酸-弱碱-弱酸-弱碱法合成了改性UF(脲醛树脂),并着重探讨了不同因素对UF中的游离F含量、胶合板的胶接强度及F释放量的影响。研究结果表明:合成改性UF的最佳工艺条件是反应温度为85℃,n(F)∶n(U)=1.10∶1,起始pH为5.0,M第2批加入,硫代硫酸钠第4批加入且加入量为U总质量的2%,U分批加入比例为55%、20%、15%和10%;此时UF中的游离F含量(降至0.11%)符合GB/T 14732—2006标准中的指标要求,胶合板的胶接强度(为1.05 MPa)满足国家标准中II类胶合板的指标要求、F释放量(为1.26 mg/L)达到普通胶合板通用技术条件中的E1级指标且耐水性也明显提高。     

氧化淀粉改性脲醛树脂胶粘剂的合成工艺研究

以氧化淀粉作为改性剂,采用正交试验法探讨了最终n(甲醛或F)∶n(尿素或U)、淀粉氧化时间、氧化淀粉加入量和交联时间等对氧化淀粉改性UF(脲醛树脂)胶粘剂的游离甲醛含量和胶接强度的影响。研究结果表明:当最终n(F)∶n(U)=1.2∶1、淀粉氧化时间为3 h、氧化淀粉加入量为10%(相对于甲醛和尿素总质量而言)和交联时间为60 min时,氧化淀粉改性UF胶粘剂的游离甲醛含量低于0.09%、胶接强度为1.48 MPa且耐水性明显提高;此时,相应胶合板的甲醛释放量(0.04 mg/L)满足GB/T 9846.3—2004标准中E0级指标要求。     

苯酚/聚乙烯醇改性脲醛树脂胶粘剂的制备及性能研究

以苯酚和聚乙烯醇(PVA)作为改性剂,采用正交试验法探讨了最终n(甲醛)∶n(尿素)、苯酚含量以及PVA含量对脲醛树脂(UF)的游离甲醛含量和胶接强度的影响。研究结果表明:当最终n(甲醛)∶n(尿素)=1.2∶1、w(苯酚)=20%和w(PVA)=1.0%(均相对于尿素总质量而言)时,苯酚/PVA改性UF的游离甲醛含量、胶接强度等均能满足GB/T 14732—2006标准中Ⅱ类胶合板的要求,并且相应胶合板的甲醛释放量(为1.70 mg/L)远低于GB/T 9846.3—2004标准中E2级指标要求。     

Melamine‐bridged alkyl resorcinol modified urea–formaldehyde resin for bonding hardwood plywood

A powdery product was obtained by the reaction of methylolated melamine with alkyl resorcinols to form melamine‐bridged alkyl resorcinols (MARs). The effects of the addition of this powder on the bonding strength and formaldehyde emission of urea–formaldehyde (UF) resins were investigated. Three types of UF resins with a formaldehyde/urea molar ratio of 1.3 synthesized by condensation at pH 1.0 (UF‐1.0), pH 4.5 (UF‐4.5), and pH 5.0 (UF‐5.0) were fabricated. The addition of MAR to UF‐4.5 and UF‐5.0 for bonding hardwood plywood enhanced the bonding strength and reduced formaldehyde emission. For UF‐1.0, the addition of MAR adversely affected the bonding strength. However, the UF‐1.0 resin yielded the lowest formaldehyde emission of all of the UF resins in the study. The effects of the MAR addition were related to the molecular structures of the UF resins. UF‐1.0 contained a large amount of free urea, a considerable number of urons, and a highly methylene‐linked, ring‐structured higher molecular weight fraction and had a smaller number of methylol groups. Therefore, the addition of MAR was considered to cause a shortage of the methylol groups, which in turn, led to incomplete resin curing. In contrast to UF‐1.0, UF‐5.0 contained a smaller amount of free urea and a linearly structured higher molecular weight fraction and had a larger number of methylol groups. In this case, MAR was considered to effectively react with the methylol groups to develop a three‐dimensional crosslinked polymer network to enhance the bonding strength and suppress the generation of free formaldehyde to reduce formaldehyde emission. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

弱酸性条件合成脲醛树脂工艺的探讨

探讨了在弱酸性条件下合成低甲醛释放量的脲醛树脂工艺的可能性。同时,对不同pH值条件下合成脲醛树脂的工艺及其性能进行了研究,并采用傅立叶红外光谱和化学方法对脲醛树脂的官能团进行了分析,同时定性分析了不同pH值条件下合成树脂的热学性能。研究表明在弱酸性条件下合成脲醛树脂的树脂性能和其胶合板的力学性能达到国家标准并且其胶合板甲醛释放量达到GB／T17657—1999中的E,级标准。弱酸性条件下合成脲醛树脂的工艺不仅能降低生产成本,还能生产性能优异的脲醛树脂胶黏剂。     

改性脲醛树脂的合成及性能

采用传统方法合成了脲醛树脂,得出甲醛与尿素的最佳摩尔比为2。采用不同改性剂合成了改性脲醛树脂,得出：随三聚氰胺、聚乙烯醇复合改性剂用量的增加,树脂的游离甲醛含量、固化时间呈逐渐下降趋势,当复合改性剂用量为8%时树脂性能最佳,压缩强度为9.0 MPa;苯酚改性剂的最佳用量为10%,材料的压缩强度为14.2 MPa;糠醛改性剂的最佳用量为15%,材料的压缩强度为19.5 MPa;综合比较,三聚氰胺、聚乙烯醇复合改性剂可以明显降低游离甲醛的含量和固化时间,但材料的压缩强度增加不大,而采用糠醛改性剂制得改性脲醛树脂的压缩强度较大。     

Influence of Ammonium Pentaborate (APB) on the Performance of Urea Formaldehyde (UF) Adhesives for Plywood

Ammonium pentaborate (APB) was used to modify urea formaldehyde (UF) resins, in which the formaldehyde to urea molar ratio was set at 1.80, 1.50, 1.25, and 1.05. Some specific properties, including gel time, free formaldehyde content in UF, bond strength, and formaldehyde emission levels from plywood were evaluated. The result showed that APB increased the gel time length, but also decreased free formaldehyde content and emission levels, which was reduced mostly by 79.0% and 81.4%, respectively. The result of bond strength indicated that APB was proper to modify high F/U molar ratio of UF resin regardless of the loading level, but a recommended loading level should be considered to relevantly lower the F/U molar ratio of UF. The suggested loading level of APB to UF is 8.0% to 6.0%, 6.0%, and 4.0% to UF resin with F/U molar ratio of 1.8, 1.5, and 1.25 separately.     

脲醛树脂胶黏剂低毒化改性剂研究进展

低毒化改性剂是指为了降低脲醛树脂及其制品毒性而在胶黏剂合成过程的不同阶段加入或在胶黏剂使用前加入的各种添加剂。从脲醛树脂胶黏剂游离甲醛的界定及其人造板甲醛释放机理、低毒化改性剂的国内外研究现状、低毒化改性剂的作用机理与选用原则等几个方面,综述了近几年来脲醛树脂胶黏剂低毒化改性剂的研究进展;并介绍了几种比较常用的单一类和复合类低毒化改性剂的降醛机理、作用效果及其使用方法,最后对低毒化改性剂的未来研究做了展望。     

玉米淀粉的氧化工艺对改性低毒脲醛树脂性能的影响

为了进一步降低胶合板中的游离甲醛释放量和提高其胶接强度,采用湿法自制的氧化玉米淀粉对胶合板用低毒脲醛树脂(UF)胶粘剂进行改性。通过改变氧化体系的酸碱性、氧化时间以及氧化淀粉用量,优选出制备改性UF胶粘剂的较佳工艺条件。结果表明:在碱性条件下将玉米淀粉氧化40 min,然后将其作为UF胶粘剂的改性剂,当w(氧化淀粉)=15%(相对于尿素质量而言)时,改性UF胶粘剂的综合性能较好。     

气膜法低醛化脲醛树脂合成及木材胶合性能

采用中间加入起泡剂鼓泡,进行气液传质交换的方法,合成环保型脲醛胶,游离甲醛降到0．05％以下,胶合板胶合强度达0．7MPa以上,并且对板材生产工艺可操作性强,其制品甲醛释放量都达到1．5mg,／L(干燥器法)以下,符合GB18580-2001E1标准要求。红外(IR)光谱进一步证实,气膜法可提高脲醛树脂、尿素中-NH2的加成反应率以及树脂固化的交联度,降低游离甲醛。