半纤维素预提取对玉米秆浆纤维性质的影响

利用稀碱液对玉米秆半纤维素进行预抽提,考察了半纤维素预提取对玉米秆蒸煮和漂白性质的影响,并比较了蒸煮后纸浆纤维表面超微结构的不同.相比未经预提取的对照实验,预先提取半纤维素能使未漂浆和漂白浆的白度提高5%～10%ISO,未漂浆卡伯值降低43.9%,未漂浆所抄纸张的撕裂指数提高了72.3%,而抗张指数和耐破指数分别下降6.5%和7.6%.应用原子力显微镜(AFM)分析纸浆纤维的表面发现,玉米秆经预提取半纤维素之后再蒸煮,所得纸浆表面沉积的有半纤维素和木素特征的物质消失,大量的纤维素微细纤维暴露出来,使纸浆的卡伯值降低、纸页撕裂指数增大.     

桦木常规硫酸盐浆与RDH硫酸盐浆的对比研究

通过对桦木常规硫酸盐浆与RDH硫酸盐浆的蒸煮条件及纸浆得率和特性的比较,得出如下结论：RDH硫酸盐法蒸煮可在低H-因子条件下,制备低卡伯值的纸浆,但得率较低。桦木RDH硫酸盐浆的抗张指数、耐破指数和耐折度均低于常规硫酸盐浆,但撕裂指数高于常规硫酸盐浆。无论是未漂还是漂白RDH硫酸盐浆均比常规未漂和漂白硫酸浆难于打浆。     

桉木RDH硫酸盐浆和常规硫酸盐浆的ECF和TCF漂白

对桉木RDH硫酸盐浆和常规硫酸盐浆的ECF和TCF漂白进行了研究,并与有元素氯漂白进行了对比.主要研究了用H2O2代替一段ClO2段以减少ClO2用量;采用H2O2强化碱抽提段(Ep)以实现短程序漂白;强化H2O2漂白(添加助剂的H2O2漂白)用以代替氧漂.结果表明,采用DEpP、Q(A+P1)P2和CEPH短程序漂白,均可将桉木RDH硫酸盐浆和常规硫酸盐浆漂至85%(ISO)以上的白度.两种漂白浆相比,RDH漂白浆具有相对较高的撕裂强度和较低的抗张强度.但两种漂白浆的强度均较高,抗张指数和撕裂指数均分别达到73N     

酶预处理对麦草NaOH-AQ制浆性能的影响

利用木聚糖酶、漆酶和纤维素酶在蒸煮前对麦草进行预处理,可降低化学浆的卡伯值,提高未漂浆的白度。和对照浆相比,酶预处理的化学浆尤其是木聚糖酶和漆酶化学浆具有更高的裂断长和撕裂指数。酶法化学浆具有良好的可漂性。漆酶和木聚糖酶的协同作用使纸浆的卡伯值进一步下降,并具有更高的强度性能。     

杨木硫酸盐浆HP漂白的研究

对杨木硫酸盐浆HP漂白进行了研究。实验结果表明,使用HP两段漂白,当用氯量为4%时,漂浆白度达到65.35%ISO,白度增值为32.84%ISO,再用3%的H2O2进行漂白,纸浆的白度可达到76.42%ISO,pc值为0.78,抗张指数为21.9N·m/g,撕裂指数为4.8mN·m2/g。     

高白度马尾松机械浆漂白工艺

马尾松是用于生产高得率浆的一种常用原料,但其机械浆漂白困难,纸浆白度较低,限制了在高档纸种中的使用。研究改进的马尾松CTMP浆的QP1P2Y漂白工艺,探讨了DTPA用量、H2O2用量及一二段分配比、连二亚硫酸钠用量对漂后纸浆白度的影响。研究发现,Q段DTPA最佳用量为0.4%,P1段H2O2用量2%,P2段H2O2用量4%,Y段Na2S2O4用量2.5%,漂后纸浆白度达到了78.1%ISO,并且纸浆的抗张指数和撕裂指数相比于未漂浆都有所提高,抗张指数为15.6N·m·g-1,撕裂指数为6.74mN·m2·g-1,能够满足配抄文化用纸的要求。     

热水和木聚糖酶预处理制备麦草碱法化机浆的研究

对热水和木聚糖酶预处理的麦草碱法化学机械制浆过程中热水和木聚糖酶预处理的效果进行了研究.结果表明,在适宜条件下,采用热水和木聚糖酶预处理原料可以有效改善麦草碱法化机浆的抗张指数和撕裂度、降低碱的消耗,虽然成浆的白度稍有降低,但可漂性增加,漂白浆白度增加.热水预处理适宜的温度是90℃,酶预处理段较佳的木聚糖酶用量和处理时间分别为15 IU/g和120min.     

马尾松KP浆生产纸袋纸打浆工艺研究

以未漂马尾松硫酸盐浆生产纸袋纸,研究了纸袋纸高浓打浆(HCR)和低浓打浆(LCR)工艺,并对其纸浆和手抄片的性质进行了对比分析.研究结果表明,马尾松硫酸盐浆制纸袋纸其打浆工艺以高浓打浆为宜;其中,HCR更有利于保持纤维长度,而且撕裂指数、伸长率也明显高于LCR,虽然抗张指数、耐破指数低于LCR,但在改善纸袋纸抗张能量吸...     

麦草烧碱法制浆应用表面活性剂的效果

介绍了2种非离子表面活性剂（ELA-7和PEG1500）在麦草烧碱法制浆中的作用。实验结果表明,这2种表面活性剂都能提高纸浆得率,降低筛渣率;在卡伯值基本相同的情况下纸浆得率提高,主要是因为表面活性剂作为共溶剂,提高了脱木素的选择性;蒸煮液中加入ELA-7对纸张性能没有显著影响;加入PEG1500对纸张性能影响较大,降低了抗张指数和耐破指数,提高了撕裂指数,这或许是表面活性剂分解造成的;2种表面活性剂都可提高未漂浆和漂白浆的白度。     

麦草的生物-化学制浆

报导了用两种菌Ceriporiopsis subvermispora(C.S.)和Phlebia suberialis(P.S.)分别预处理麦草对碱-蒽醌(AQ)蒸煮得到麦草浆、纸性质的影响。结果表明:菌预处理麦草能提高脱木素和碳水化合物的降解作用,P.S.比C.S.预处理更能提高纸浆的白度、降低卡伯值和黏度。菌预处理浆在所有磨浆度情况下可提高纸页的松密度、白度和撕裂指数,而降低抗张和破裂指数,C.S.比P.S.预处理浆对提高纸页松密度和降低抗张、破裂指数更加明显。还研究了阳离子聚乙烯醇(CPVA)用作干强添加剂改性纤维能够弥补菌预处理对纸页强度的损失。C.S.比P.S.预处理的碱-AQ麦草浆更易吸附CPVA,从而提高纸页强度。应用CPVA对菌预处理未磨浆工磨浆的纤维,在相同抗张强度情况下,都能达到降低纸页定量的目的。     

硫酸盐法蒸煮脱木素历程的近红外光谱表征法

利用近红外光谱法对木材硫酸盐法蒸煮过程脱木素历程进行了研究。结果表明,利用红外光谱能较好地表征木材的三段脱木素历程。这为下一步近红外光谱在线测量仪的开发奠定了理论基础。     

漆酶和漆酶/介体处理对未漂硫酸盐浆白度和色度的影响

探讨了不同的漆酶/介体处理对未漂硫酸盐浆白度和色度的影响,着重研究了单独漆酶和以丁香酸甲酯(MS)为介体的漆酶/介体体系对白度和色度的影响。结果表明:不同的漆酶/介体体系,均未改善纸浆的白度。单独漆酶处理可导致纸浆白度和L*值稍有降低,a*值稍有增加,b*值下降。漆酶/MS处理造成纸浆白度和L*值下降更为明显,a*值大幅上升,b*值下降。纸页的白度随漆酶用量的增加稍有下降;不同的处理温度对纸浆白度和色度影响不大;增加介体MS用量导致纸页的白度和L*值进一步下降,a*值明显增加,b*值变化不大。     

基于SIMCA模型的纸浆种类近红外光谱鉴别

研究了近红外光谱分析与SIMCA模式识别技术相结合鉴别纸浆种类的方法。收集了桉木浆、麦草浆(漂白与未漂白)、棉浆、湿地松浆等4种纸浆共90个样品,抄成不同定量纸样并采集其近红外光谱,其中部分桉木浆添加化学助剂。选择60个样品作为训练集建立SIMCA类模型,剩余30个样品用于模型检验。研究结果表明,建立的模型能完全正确识别各类纸浆,且不受抄纸定量和添加化学助剂因素的影响,为快速无损鉴别纸浆种类提供了一种准确可靠的方法。     

Carbamoylethyl Wheat Flour as a Wet- and Dry-Strength Agent for Paper

Unbleached kraft paper exhibiting a ten- to fifteenfold increase in wet-tensile strength accompanied by substantial increases in burst, dry-tensile strength and folding endurance was obtained from the use of hypochlorite-treated carbamoylethyl wheat flour as a wet-end additive. Results with bleached kraft pulps were less spectacular but still good. Such variables as pH of the carbamoylethyl wheat flour (CEWF) paste before hypochlorite treatment, pulp type and freeness, drying and curing temperature of the treated paper and the amount of CEWF influence strength properties of paper. A pH of 2 was optimum for treatment of aqueous CEWF pastes with hypochlorite. Unbleached kraft pulp having a Canadian Standard freeness (CSf) of about 500 ml produced paper exhibiting the best overall strength properties. Maximum wet- and dry-tensile strength was imparted to unbleached kraft handsheets dried at 105°C for 15 min. Strength properties increased as level of addition increased from 0.25 to 5%. Addition of CEWF at a 2% level to unbleached kraft furnishes gave handsheets exhibiting wet- and dry-tensile strength as high as 3340 and 10,510m, respectively, as compared with corresponding values of 240 and 6980 m for the control. Hypochlorite-treated CEWF was comparable to carbamoylethyl starch in imparting wet-strength properties to unbleached kraft paper.     

国内常用加拿大长纤维木浆的技术分析

详细论述了国内常用的原产加拿大漂白长纤维硫酸盐木浆(NBSK)和本色硫酸盐木浆(UKP)的制浆树种、纤维形态特征、技术指标,并对相同游离度、不同种类的长纤维木浆成纸物理性能指标进行分析对比.     

近红外光谱法快速测定桉木硫酸盐浆卡伯值和水分

利用近红外光谱快速测定桉木硫酸盐浆的卡伯值和水分。经过内部、外部以及重现性检验,结果表明通过红外方法建立起来的纸浆卡伯值和水分预测模型具有良好的测量准确度及重现性,与传统的实验室化学检测方相比具有快速、准确和环保的优点。     

马尾松纸浆性能在家系间的遗传差异

对１３ 年生２０ 个马尾松自由授粉家系１００ 株树木进行硫酸盐法制浆试验, 研究未漂硫酸盐木浆品质和物理性能在家系间的遗传差异。除耐破指数外, 观察到其他成浆性能在家系间都存在着巨大的遗传差异, 受较强的遗传控制。性状相关分析发现, 木材密度和热水抽出物含量似是预测成浆性能较可靠的间接选择指标。基于单株纸浆产量、吨干浆材耗量和成浆物理性能的综合考虑, 可评选出８ 个纸浆材优良家系。     

Estimation of physical and mechanical properties of agro-based particleboards by near infrared spectroscopy

Partial least square regression (PLS-R) calibrations based on near infrared (NIR) spectroscopic data were developed in order to predict mechanical and physical properties of agro-based particleboards. The panels were manufactured using Eucalyptus and Pinus wood particles and sugar cane bagasse. The following panel properties were evaluated according to standard methods: modulus of elasticity (MOE), modulus of rupture (MOR), internal bonding (IB) strength, water absorption (WA24H), and thickness swelling (TS24H) after 24 hours of immersion. NIR spectra information was measured on samples cut from each particleboard and correlated with their physical and mechanical properties by PLS-R to build predictive NIR models. The NIR models for IB, WA24H and TS24H presented satisfactory coefficient of determination (0.73; 0.72 and 0.75, respectively.) The key role of resins (adhesives), cellulose, and lignin for NIRS calibrations of mechanical and physical properties of the particleboards is shown. These models can be useful to quickly verify such properties in unknown agro-based particleboards.     

漆酶对不同漂段纸浆催化氧化木素的效果研究

以未漂硫酸盐桉木浆(Sp浆)、氧脱木素桉木浆(O浆)、H_2O_2漂白桉木浆(P浆)作为不同漂段原料,探讨漆酶-谷氨酸体系对不同漂段纸浆的催化效果。结果表明,漆酶催化总体上可使纸浆的卡伯值增大,纸浆的白度随之下降;漆酶协同谷氨酸可催化氧化纤维表面木素与相邻纤维上的木素发生自由基偶合反应,同时使纤维表面的微细纤维暴露出来,两者共同作用使相邻纤维形成更好的结合力,使纸浆的强度性能大幅度提升;谷氨酸可通过漆酶催化氧化作用连接到木素上,增加纤维原料中的羧基含量,Sp浆、O浆、P浆羧基含量分别较未处理纸浆提高20%、50%、43%。