A series of diphenylsilanediol modified epoxy resins and novel curing agents were synthesized. The modified epoxy resins were cured with regular curing agent diethylenetriamine (DETA); the curing agents were applied to cure unmodified diglycidyl ether of bisphenol A epoxy resin (DGEBA). The heat resistance, mechanical property, and toughness of all the curing products were investigated. The results showed that the application of modified resin and newly synthesized curing agents leads to curing products with lower thermal decomposition rate and only slightly decreased glass transition temperature (Tg), as well as improved tensile modulus and tensile strength. In particular, products cured with newly synthesized curing agents showed higher corresponding temperature to the maximum thermal decomposition rate, comparing with products of DGEBA cured by DETA. Scanning electron microscopy micro images proved that a ductile fracture happened on the cross sections of curing products obtained from modified epoxy resins and newly synthesized curing agents, indicating an effective toughening effect of silicon–oxygen bond. 相似文献
N,N,N′,N′-tetraglycidyl-4,4′-diaminodiphenylalkane epoxy resins with alkyl substituents on the methylene carbon were synthesized and characterized. The thermal and dynamic mechanical properties of these resins when cured with diaminodiphenylsulfone were compared with those of the cured unsubstituted epoxy resin. Although the resins have similar structures, the cured resin from the unsubstituted epoxy has the higher polymer decomposition temperature and glass transition temperature. The substituted epoxy resins have higher dynamic Young's moduli and loss moduli. 相似文献
Two novel epoxy resins; namely, R1 and R2 were synthesized and characterized. These two resins were isomers and both contained naphthalene units and two symmetric flexible aliphatic ester chains terminated by epoxy groups. To investigate the influence of different structural isomers on the performance of these epoxy resins, they were both cured with various curing agents which results in the choosing of 4,4′-diaminodiphenylmethane (DDM) as the optimized curing agent. The curing technical temperature was obtained from extrapolated plots of T–β curve at different heating rates. The kinetic parameters, the activation energy (Ea) and the reaction order (n) were deduced by Kissnger’s isoconversional method and Crane equation. The moisture absorption and mechanical and thermal properties of the cured epoxy resins were investigated. Experimental results indicated that the R1/DDM and R2/DDM epoxy resins displayed improved mechanical performance without significant decrease in their important inherent properties, e.g., temperature of glass transition (Tg), moisture absorption and thermal properties when compared with the corresponding commercial biphenyl-type epoxy resins. The average inter-segment distances in R1/DDM and R2/DDM systems were 4.46 and 4.88 Å, respectively, which were measured by wide-angle X-ray diffraction. The result showed R1/DDM (1,5-di-substituted) was strongly hindered in comparison with R2/DDM (2,7-di-substituted) and Ea and Tg values of the R1/DDM were slightly higher than those of R2/DDM. Furthermore, mechanical properties and moisture absorption of the R1/DDM were lower than those of R2/DDM. Nevertheless, the position of the substituent only weakly affected the thermal properties and the reaction order (n). 相似文献
Summary: The epoxy copolymers containing sulfone groups, diglycidyl ether of bisphenol‐A – Bisphenol‐S (DGEBA‐S) were synthesized by a hot‐melt method. The thermal properties of the epoxy systems initiated by two cationic latent catalysts, i.e., N‐benzylpyrazinium hexafluoroantimonate (BPH) and N‐benzylquinoxalinium hexafluoroantimonate (BQH), were investigated by using a dynamic DSC, DMA, and TGA. The mechanical properties were measured by single‐edge‐notched (SEN) beam fracture toughness tests. As a result, the thermal stability and mechanical interfacial properties of the DGEBA‐S/catalyst system were found to be higher than those of the DGEBA/catalyst. This was probably due to the fact that the introduction of sulfone groups with a polar nature to the main chain of the epoxy resins led to an improvement of thermal stability and toughness of the cured epoxy copolymers.
Conversion of the epoxy/catalyst systems as a function of curing temperature. 相似文献
Novel epoxy resin modifiers, DOPO–TMDS and DOPO–DMDP were synthesized by addition reaction of divinylsiloxane with 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide
(DOPO). Halogen-free flame retardant epoxy resins were obtained through modification of o-cresol novolac epoxy resin cured by phenol novolac resin using DOPO–TMDS and DOPO–DMDP which were characterized by 1H NMR, 13C NMR, 31P NMR and FT-IR measurements. Effects of the phosphorus-containing siloxanes on thermal stabilities, mechanical properties
and flame retardant properties of the epoxy resins were investigated. The cured epoxy resins exhibited better mechanical properties
and greatly improved flame retardant properties due to the presence of phosphorus-containing siloxanes. The cured epoxy resins
with phosphorus loading of 2.0 wt% showed LOI values of 32–33 and achieved UL94V-0 ratings. 相似文献
o-Cresol novolac-type epoxy resins having hydroxymethyl group were synthesized. These epoxy resins were cured with a mixture of 4,4′-diaminodiphenylmethane and m-phenylenediamine (molar ratio, 6:4) as a hardener. Effects of molecular weight distribution of epoxy resins on curing behavior were studied. Curing behavior of epoxy resins with hardener were examined by differential scanning calorimetery (DSC), and cure reaction parameters were obtained. Viscoelastic properties of the cured epoxy resins were studied by dynamic mechanical analyzer. It was found that the lower the average molecular weight of the epoxy resin, that is, the higher the concentration of hydroxymethyl group, the shorter the onset time of exothermal reaction, the higher the rate constant (k), and the lower the activation energy (Ea) were. It was also found that glass transition temperature (Tg) of fully cured epoxy resins was higher than those of fully cured general novolac-type epoxy resins. 相似文献
A new curing agent based on palmitoleic acid methyl ester modified amine (PAMEA) for epoxy resin was synthesized and characterized. Diglycidyl ether of bisphenol A (DGEBA) epoxy resins cured with different content of PAMEA along with diethylenetriamine (DETA) were prepared. The mechanical properties, dynamic mechanical properties, thermal properties, and morphology were investigated. The results indicated that the PAMEA curing agent can improve the impact strength of the cured epoxy resins considerably in comparison with the DETA curing agent, while the modulus and strength of the cured resin can also be improved slightly. When the PAMEA/epoxy resin weight ratio is 30/100, the comprehensive mechanical properties of the cured epoxy resin are optimal; at the same time, the crosslinking density and glass transition temperature of the cured epoxy resin are maximal. 相似文献