Effect of pH values on photocatalytic properties of Bi<Subscript>2</Subscript>WO<Subscript>6</Subscript> synthesized by hydrothermal method

Highly crystalline orthorhombic Bi₂WO₆ powders were hydrothermally synthesized from aqueous solutions of Na₂WO₄ · 2H₂O and Bi (NO₃)₃ · 5H₂O over a wide range of pH. The effect of pH on morphologies, sizes and properties of the Bi₂WO₆ crystals was investigated. The band gaps of the as-prepared Bi₂WO₆ were determined from the onset of the absorption edge of UV-vis diffuse reflectance spectra. The methyl orange photodegradation was employed as a probe reaction to test the photocatalytic activity of the as-prepared samples under visible light irradiation. The photocatalytic activities of methyl orange degradation under visible light irradiation are strongly dependent on the pH used in the synthesis. The highest efficiency is observed at pH=7. Funded by the PCSIRT, the National Natural Science Foundation of China (Nos. 50532030 and 50625206) and the Zhejiang Provincial Natural Science Foundation of China (No. Z4080021)     

Effect of ZnO-B<Subscript>2</Subscript>O<Subscript>3</Subscript> glass addition on the microwave dielectric properties of BaO-Nd<Subscript>2</Subscript>O<Subscript>3</Subscript>-TiO<Subscript>2</Subscript>-Bi<Subscript>2</Subscript>O<Subscript>3</Subscript> system

The effect of ZnO-B₂O₃(ZB) glass addition on the sintering behavior, microstructures and microwave dielectric properties of BaO-Nd₂O₃-TiO₂-Bi₂O₃ (BNTB) system was investigated with the aid of X-ray diffraction, scanning electron microscopy and capacitance meter. It is found that the ZB glass addition, acting as a sintering aid, can effectively lower the sintering temperature of BNTB system to 850 °C. The dielectric constant of BNTB-ZB ceramics increases with the increase of soaking time and the value of dielectric loss decreased with increasing soak time. The optical dielectric properties at 1 GHz of ɛ=74, tan δ=4×10⁻⁴, and TCC=25 ppm/°c were obtained for the BNTB system doped with 25 wt% ZB glass sintered at 850 °C for 2 h, representing that the BNTB-ZB ceramics could be promising for multilayer low temperature co-fired ceramics applications.     

Density function theory study of electronic,optical and thermodynamic properties of CaN<Subscript>2</Subscript>, SrN<Subscript>2</Subscript> and BaN<Subscript>2</Subscript>

We put forward a first-principles density-functional theory about the impact of pressure on the structural and elastic properties of bulk CaN₂, SrN₂ and BaN₂. The ground state properties of three alkaline earth diazenides were obtained, and these were in good agreement with previous experimental and theoretical data. By using the quasi-harmonic Debye model, the thermodynamic properties including the debye temperature Θ _D, thermal expansion coefficient α, and grüneisen parameter γ are successfully obtained in the temperature range from 0 to 100 K and pressure range from 0 to 100 GPa, respectively. The optical properties including dielectric function ε(?), absorption coefficient α(?), reflectivity coefficient R(?), and refractive index n(?) are also calculated and analyzed.     

Effect of aluminum addition on microstructure and properties of SiO<Subscript>2</Subscript>-B<Subscript>2</Subscript>O<Subscript>3</Subscript>-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-CaO vitrified bond

Influence of aluminum addition on the structures and properties of SiO₂-B₂O₃-Al₂O₃-CaO vitrified bond at low sintering temperature and high strength was discussed. FTIR and XRD analyses were used to characterize the structures of the basic vitrified bond with different contents of aluminum. The bending strength and the thermal expansion coefficients were also tested. Meanwhile, the microstructures of composite specimens at sintering temperature of 660 °C were observed by scanning electron microscope (SEM). The experimental results showed that the properties of vitrified bond with 1wt% aluminum were improved significantly, where the bending strength, Rockwell hardness, and thermal expansion coefficient of the vitrified bond reached 132 MPa, 63 HRB, and 6.73×10^-6 °C^-1, respectively.     

Preparation and optical properties of Er<Superscript>3+</Superscript>: Na<Subscript>2</Subscript>O-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-SiO<Subscript>2</Subscript> transparent glass-ceramics

Na₂O-Al₂O₃-SiO₂ glass-ceramics doped with Er³⁺ ions were synthesized by the conventional melt quenching technique at a low melting temperature. The samples were characterized by differential scanning calorimetry (DSC), X-ray diffraction (XRD), scanning electron microscopy (SEM), UV-vis-NIR scanning spectrophotometry, and fluorescence spectrometry. The results show that the main crystalline phase of glass-ceramics is nepheline.The best heat-treatment process is at 520 °C for 2 h. Because the up-conversion luminescence and near infrared luminescence properties of glass doped with Eu³⁺ are studied in detail.     

Synthesis of Rod-like Ternary Carbide LaNiC2 by a Solvothermal Route

LaNiC2 was synthesized by a solvothermal route in a stainless steel autoclave at 600℃. In this process, nickel chloride, lanthanum chloride and toluene were used as raw materials, and metallic Na and Li alloy were used as reductant. The products were characterized with an X-ray diffractometer （XRD） and a scanning electron microscope （SEM）. The LaNiC2 products consisted of a great deal of micro-rods. The micro-rods had diameters ranging from hundreds of nanometers to several micrometers and lengths ranging from several micrometers to tens of micrometers.     

Effect of La doping on microstructure and ferroelectric properties of Bi<Subscript>4</Subscript>Ti<Subscript>3</Subscript>O<Subscript>12</Subscript> thin films prepared by sol-gel method

The Bi4Ti3Oi2 and Bi3.25La0.75Ti3O12 thin films were prepared on the Pt/Ti/SiO2/Si substrate using the sol-gel method. The effect of La doping on the microstructure and ferroelectric properties of Bi4Ti3O12 films were investigated. Both the Bi4Ti3O12 and Bi3.25La0.75Ti3O12 thin films exhibited typical bismuth layered perovskite structure. The 2Pr （remanent polarization） value of Bi3.25La0.75Ti3O12 thin films is 18.6 μC/cm^2, which is much larger than that of Bi4Ti3O12 thin films. And the Bi3.2eLa0.75Ti3O12 films show fatigue-free behavior, while the Bi4Ti3O12 thin films exhibit the fatigue problem. The mechanism of improvement of La doping was discussed.     

Effect of Ga<Subscript>2</Subscript>O<Subscript>3</Subscript> on structure and properties of calcium aluminate glasses

The effect of Ga₂O₃ on the structure and properties of calcium aluminate glasses fabricated by vacuum melting process was investigated by Raman spectrum, differential scanning calorimeter (DSC), and infrared spectrum methods. The results show that calcium aluminate glass network only consists of [AlO₄] tetrahedral units. With the gradual addition of Ga₂O₃, the quantity of [GaO₄] tetrahedral units increases. Substitution of Ga₂O₃ for Al₂O₃ results in a decrease in T _g T _x, and T _p, and an increase in the thermal stable index ΔT. Similarly, the absorption band around 3.0 μm obviously reduces and the transparency in 4.0-6.0 μm rapidly increases with increasing Ga₂O₃ content. However, the chemical stability of calcium aluminate glasses decreases if Ga₂O₃ is introduced due to the increasing of [GaO₄] units in the glass network.     

Optical and magnetic properties of Fe<Subscript>2</Subscript>O<Subscript>3</Subscript>/SiO<Subscript>2</Subscript> nano-composite films

Fe₂O₃/SiO₂ nano-composite films were prepared by sol-gel technique combining heat treatment in the range of 100–900 °C. The particle size was observed by FE-SEM. Optical properties of the films were investigated by UV-visible spectra. Structural and magnetic characteristics were investigated through FT-IR and VSM. The transparency of the Fe₂O₃/SiO₂ nano-composite films decreased with the content of the Fe₂O₃. Water and organic solvent in the films were evaporated with heat treatment, so the transparency of the films was enhanced under high temperature. It is also found that the saturation magnetization (M _s) of the films increases with the temperature. As the content of the Fe₂O₃ increases, when the content of the Fe₂O₃ is around 30wt%, the M _s of the films has a maximum value.     

Effect of the silicon powder content on the properties of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-SiC-Me composites

By means of transient plastic phase process, the Al₂O₃-SiC-Me composites were produced throungh adding metal aluminium and silicon-powder to Al₂O₃-SiC materials. Under the condition of the same content of silicon and aluminium mixed-powder, the effect of silicon powder addition on properties of Al₂O₃-SiC-Me composites was studied by means of XRD and EPMA analyses in the temperature range of 300°–1600°C. The results indicated that the content of metal phase in the sample at 1600°C increases with increasing silicon powder content. At the same time, when the temperature is lower than 1100°C, the strength of samples gradually increases with increasing temperature. However when the temperature is higher than 1100°C, the strength of samples gradually decreases with increasing temperature, and this change is very small. The results also indicated that at the same sintering temperature, the sample with 6% silicon powder has the maximum strength. Supported by the Chen Yunbo Academician Fund (Grant No. 2007CY021)     

Effect of diatomite additive on the mechanical and dielectric properties of porous SiO<Subscript>2</Subscript>-Si<Subscript>3</Subscript>N<Subscript>4</Subscript> composite ceramics

Porous SiO₂-Si₃N₄ composite ceramics with high porosity and excellent mechanical properties were fabricated by pressureless-sintering at relatively low temperature of 1 500 °C using diatomite as pore forming agent. The effects of diatomite on flexural strength, fracture toughness, shrinkage, porosity and phase transformation of the porous ceramics were investigated in detail. Compared with that of the ceramic without adding diatomite, the porosity of the ceramic with 10% diatomite is increased by about 27.4%, the flexural strength and fracture toughness reaches 78.04 MPa and 1.25 MPa·m^1/2, respectively. As the porosity increases, the dielectric constant of porous SiO₂-Si₃N₄ ceramic decreases obviously from 3.65 to 2.95.     

Microstructure and mechanical properties of TiB<Subscript>2</Subscript>-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> composites

Effects of Al2O3 and Ni as the additives on the sinterability, microstructure and mechanical properties were systematic studied. The experimental results show that only a relative density about 96.2% of hot-pressing TiB2-30%Al2O3 can be attained due to the plate-like TiB2 particle and its random orientation and excessive Al2O3 grain growth. When sintering temperature is higher than 1 700 ℃, TiB2 grain growth can be found, which obvious improves flexural strength of TiB2 matrix but decreases toughness. It seems that mechanical properties of TiB2-Al2O3 composites are mainly depended on relative density besides grain growth. otherwise, they will be determined by relative density and TiB2 matrix strength together. Anyway, Al2O3 addition can weaken the grain boundary and thus improve the toughness of the materials. A flexural strength of 529 MPa, Vickers hardness of 24.8 GPa and indentation toughness of 4.56 MPa·m1/2 can be achieved inTiB2-30vol% Al2O3.     

Glass formation and optical band gap studies on Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>-B<Subscript>2</Subscript>O<Subscript>3</Subscript>-BaO ternary system

The glass forming region of Bi₂O₃-B₂O₃-BaO ternary system was investigated. A serial of glass samples with high Bi₂O₃ content in Bi₂O₃-B₂O₃-BaO system were prepared by using conventional melting and quenching meld, and the refractive indexes and absorption spectra of samples were measured. It is found that the refractive index of samples as well as the UV absorption increase with the increase of BaO content. According to the Tauc law, optical band gap E _opg which is assumed to be the effective energy band gap E _g is calculated and decreases with the increasing BaO content, and the ratio of E _g/E _opg is 1.3.     

Effect of Al<Subscript>2</Subscript>O<Subscript>3</Subscript> content on residual stress and properties of CAS glass-ceramics

The structure and properties of the glass-ceramics were tested with X-ray diffraction testing instrument,correlative software,and other modern testing means.Then the effect of Al2O3 content on internal stresses in CaO-Al2O3-SiO2 glass-ceramics was studied deeply.In order to study the relationship of Al2O3 to the residual stress of CaO-Al2O3-SiO2 glass-ceramics,X-ray diffraction ＂sin2ψ＂ was used.The means utilized the x radial incidence produced from cathode radial tube,and took the space between crystals as measurement of strain.When the stresses produced,the space between crystals changed and the diffraction peak moved during Bragg diffraction.The magnitude of movement is related to the stresses.The experimental results show the residual stress is considerably high and Al2O3 can influence the mechanical properties of this material hugely.     

Dielectric properties of Bi<Subscript>4</Subscript>Ti<Subscript>3</Subscript>O<Subscript>12</Subscript> ceramics by impedance spectroscopic method

Various lead-free ceramics have been investigated in search for new high-temperature dielectrics. In particular, Bi₄Ti₃O₁₂ is a type of ferroelectric ceramics, which is supposed to replace leadcontaining ceramics for its outstanding dielectric properties in the near future. Ferroelectric ceramics of Bi₄Ti₃O₁₂ made by conventional mixed oxide route have been studied by impedance spectroscopy in a wide range of temperature. X-ray diffraction patterns show that Bi₄Ti₃O₁₂ ceramics are a single-phase of ferroelectric Bi-layered perovskite structure whether it is calcined at 800 °C or after sintering production. This study focused on the effect of the grain size on the electric properties of BIT ceramics. The BIT ceramics with different grain sizes were prepared at different sintering temperatures. Grain becomes coarser with the sintering temperature increasing by 50 °C, relative permittivity and dielectric loss also change a lot. When sintered at 1 100 °C, r values peak can reach 205.40 at a frequency of 100 kHz, the minimum dielectric losses of four different frequencies make no difference, all close to 0.027. The values of E _a range from 0.52 to 0.68 eV. The dielectric properties of the sample sintered at 1 100 °C are relatively better than those of the other samples by analyzing the relationship of the grain, the internal stresses, the homogeneity and the dielectric properties. SEM can better explain the results of the dielectric spectrum at different sintering temperatures. The results show that Bi₄Ti₃O₁₂ ceramics are a kind of dielectrics. Thus, Bi₄Ti₃O₁₂ can be used in high-temperature capacitors and microwave ceramics.     

Effect of temperature on polishing and flatting time of float-formed Li<Subscript>2</Subscript>O-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-SiO<Subscript>2</Subscript> glass

Li₂O-Al₂O₃-SiO₂ glass prepared from traditional melting and cooling process was investigated. The surface characteristic of LAS glass was studied by simulating tin bath with different temperature and time, and the effect of surface tension/viscosity ratio on flatting time was analyzed. The results demonstrated that LAS glass can polish effectively when polishing at 1 300 for 8 °C min, and the optimum flatting and polishing temperature was 1 250–1 300 °C.     

Synthesis of Ti3SiC2/TiB2 Composite by In-situ Hot Pressing （HP） Method

Ti3SiC2/TiB2 composite was successfully obtained by hot pressing Ti/TiC/Si/B4C power mixtures.Volume fraction of TiB2 in Ti3SiC2/TiB2 composite can not exceed 10%.Incorporation of excessive TiB2 will affect the reactions process.TiC and Ti5Si3 were two important intermediate phases during the whole reactions.The microstructure characteristics of the Ti3SiC2/TiB2 composites were analyzed using scanning electron microscopy （SEM） and transmission electron microscopy （TEM）.The experimental results show that the grains of Ti3SiC2/TiB2 composite are structured in a layered form,and the formation of TiB2 particles as reinforcements with elongated or equiaxed shape distributes in Ti3SiC2 matrix.     

Eleetronie Structures and Bonding Properties of Ti2AlC and Ti3AlC2

The relation among electronic structure, chemical bond and property of Ti2AlC, Ti3AlC2 and doping Si into Ti2AlC was studied by density function and the discrete variation （DFT-DVM） method. After adding Si into Ti2AlC, the interaction between Si and Ti is weaker than that between Al and Ti, and the strengths of ionic and covalent bonds decrease both. The ionic and covalent bonds in Ti3AlC2, especially in Ti-Al, are stronger than those in Ti2AlC. Therefore, in synthesis of Ti2AlC, the addition of Si enhances the Ti3AlC2 content instead of Ti2AlC. The density of state （DOS） shows that there is mixed conductor characteristic in Ti2AlC and Ti3AlC2. The DOS of Ti3AlC2 is much like that of Ti2AlC. Ti2SiAl1-xC has more obvious tendency to form a semiconductor than Ti2AlC, which is seen from the obvious difference of partial DOS between Si and Al 3/7.     

Ferroelectric properties of Bi<Subscript>4</Subscript>Zr<Subscript>0.5</Subscript>Ti<Subscript>2.5</Subscript>O<Subscript>12</Subscript> thin films prepared on LaNiO<Subscript>3</Subscript> bottom electrode by sol-gel method

The Bi4Zr0.5Ti2.5O12 (BZT) thin films were fabricated on the LaNiO3 bottom electrode using sol-gel method. The structure and morphology of the films were characterized using X-ray diffraction, AFM and SEM. The results show that the films have a perovskite phase and dense microstructure. The 2Pr and 2Vc of the Pt/BZT/LaNiO3 capacitor are 28.2 μC/cm2 and 14.7 V respectively at an applied voltage of 25 V. After the switching of 1×1010 cycles, the Pr value decreases to 87% of its pre-fatigue values. The dielectric constant (ε) and the dissipation factor (tanδ) of the BZT thin films are about 204 and 0.029 at 1 kHz, respectively. The films show good insulating behavior according to the test of leakage current. The clockwise C-V hysteresis curve observed shows that the Pt/BZT/LaNiO3 structure has a memory effect because of the BZT film's ferroelectric polarization.     

Effect of pre-heating temperature on structural and optical properties of sol-gel derived Zn<Subscript>0.8</Subscript>Cd<Subscript>0.2</Subscript>O thin films

Zn_0.8Cd_0.2O thin films prepared using the spin-coating method were investigated. X-ray diffraction, scanning electron microscopy, and UV-Vis spectrophotometry were employed to illustrate the effects of the pre-heating temperature on the crystalline structure, surface morphology and transmission spectra of Zn_0.8Cd_0.2O thin films. When the thin films were pre-heated at 150 °C, polycrystalline ZnO thin films were obtained. When the thin films were pre-heated at temperatures of 200 °C or higher, preferential growth of ZnO nanocrystals along the c-axis was observed. Transmission spectra showed that thin films with high transmission in the visible light range were prepared and effective bandgap energies of these thin films decreased from 3.19 eV to 3.08 eV when the pre-heating temperature increased from 150 °C to 300 °C.