AZ91D镁合金低温快速化学镀Ni-P工艺的研究

采用化学镀方法,在AZ91D镁合金上沉积Ni-P镀层,研究了添加剂对镀层的影响.结果表明:未加添加剂时,沉积速度慢;加入添加剂后,镀层的沉积速度增加,65℃时只需30min就可获得无气孔或裂纹、具有“菜花状”结构的均匀完整的Ni-P镀层.XRD测试结果表明,沉积的Ni-P镀层为非晶态.镀层的耐蚀性实验结果表明,化学镀Ni-P镀层后,AZ91D镁合金的耐蚀性优于基体.     

AZ91D 镁合金表面 Ni-P / Ni-Sn-P 双镀层的制备与性能研究

目的提高AZ91D镁合金的耐腐蚀性能,扩大其应用范围。方法先在AZ91D镁合金表面化学镀Ni-P镀层,再化学镀Ni-Sn-P镀层,形成Ni-P/Ni-Sn-P双镀层。研究Ni-P/Ni-Sn-P双镀层的表面形貌和耐腐蚀性能,并与Ni-P单镀层进行对比。结果 Ni-P/Ni-Sn-P双镀层表面分布更均匀平整,缺陷较少,孔隙率较低,具有无定形结构。二次Ni-Sn-P镀层的腐蚀电位约为-0.77 V,略低于一次化学镀Ni-P层(约-0.68 V),两镀层间的电位差使得其构成了微腐蚀电偶,Ni-P层作为阴极,Ni-Sn-P层作为阳极,阳极优先被腐蚀。结论 Ni-P/Ni-Sn-P双镀层的Ni-Sn-P外层能为Ni-P内层提供阴极保护,较好地横向分散腐蚀电流,从而增强AZ91D镁合金基底的耐腐蚀性能。     

络合剂对AZ31D镁合金化学镀Ni-P合金的影响

以AZ31D镁合金为研究材料,研究了化学镀Ni-P工艺配方中络合剂对镀层的沉积速度、镀层表面形貌与结构、镀层成分及其各种性能的影响,获得了最佳工艺参数.结果表明,可以实现在AZ31D镁合金上直接化学镀Ni-P合金,并且其镀层表面光亮、均匀致密,镀层的显微硬度比AZ31D镁合金基体有明显的提高,镀层与基底的结合力良好.     

镁合金表面化学镀 Ni-P 和 Ni-P-SiC 的对比

目的提高镁合金的耐磨性、耐蚀性,扩大其应用领域。方法采用"磷酸+钼酸铵酸洗→HF活化"的方法进行前处理,直接在AZ91D镁合金表面化学镀Ni-P合金镀层和Ni-P-SiC复合镀层。对两种镀层的表面和截面形貌、成分、结构、硬度、耐蚀性及耐磨性进行了系统比较。结果在Ni-P合金镀层中引入SiC粉末后,镀层的胞状颗粒细化,硬度提高至643HV,但其腐蚀电流密度有所增大。结论与Ni-P合金镀层相比,Ni-P-SiC复合镀层的耐蚀性有所下降,但耐磨性能大大提高。     

模拟海洋环境中Ni-Co合金镀层对AZ91D镁合金的腐蚀防护研究

目的提高AZ91D镁合金的腐蚀防护性能。方法采用化学镀前处理在AZ91D镁合金表面制备一种保护性的Ni-Co合金镀层。分别采用环境扫描电镜(ESEM)、X射线衍射(XRD)和能量散射谱(EDS)分析合金镀层的表面形貌、微结构特点和化学成分。采用动电位极化(PC)和电化学阻抗谱(EIS),分析测试在模拟海洋环境(中性3.5%Na Cl溶液)中Ni-Co合金镀层对AZ91D镁合金的腐蚀防护性能。结果镁合金表面化学镀Ni-P镀层均匀覆盖,晶粒生长较致密,表面呈菜花状形貌,Ni-P镀层中P质量分数约为5.6%。Ni-Co合金镀层表面均匀且呈金字塔状形貌,形成了面心固溶体(FCC),镀层中Co质量分数约为31%。Ni-P镀层和Ni-Co合金镀层的厚度分别约为11μm和19μm。在模拟海洋(中性3.5%Na Cl溶液)环境中,镁合金裸基体、化学镀前处理Ni-P镀层、Ni-Co合金镀层的腐蚀电位分别为-1485、-372、-284 m V,其腐蚀电流密度分别是3.4×10-5、1.8×10-6、2.9×10~(-7) A/cm2,所拟合的电荷转移电阻分别为4.72×103、1.70×104、2.06×106?/cm2。结论化学镀前处理Ni-P镀层可为镁合金提供较好的腐蚀防护,Ni-Co合金镀层能够为镁合金提供更显著的腐蚀防护。     

AZ91D镁合金Ni-P／CeO2化学复合镀层的耐蚀性

在AZ91D化学镀镍的镀液中添加CeO2微粒,以获得Ni-P/CeO2化学复合镀层.试验结果表明,镀层与基体的结合力良好;镀后的镁合金在3.5%NaCl溶液和5%醋酸溶液中浸泡,耐蚀能力大为提高;封孔后的试样在短时间内基本不被腐蚀.     

沉积时间对AZ91D合金表面Ni-P-SiC复合镀层性能的影响

目的提高镁合金的耐蚀性和耐磨性。方法以AZ91D镁合金为基体,采用SiC颗粒质量浓度为3 g/L的Ni-P化学镀溶液,在其表面沉积不同时间,制备Ni-P-SiC复合镀层。通过扫描电子显微镜(SEM)、显微硬度测试、粗糙度仪、电化学腐蚀和磨损等试验来分析和评价Ni-P-SiC复合镀层的厚度、表面粗糙度、显微硬度、耐腐蚀性能和耐磨性能。结果 Ni-P-SiC复合镀层的厚度和表面粗糙度随沉积时间增加而增加,沉积时间为150 min时,镀层厚度可达53μm,表面粗糙度为2.5μm。沉积时间为120 min时,镀层的显微硬度最高,为641HV,此时复合镀层的耐蚀性和耐磨性最好,自腐蚀电位高达-0.73 V,腐蚀电流密度为0.78μA/cm~2,磨损体积最小,为1.04×10~(-3)mm~3。与AZ91D镁合金基体相比,沉积复合镀层后的样品更耐蚀,说明复合镀层有效改善了镁合金基体的耐蚀性。结论沉积时间对Ni-P-SiC复合镀层的性能有一定影响,在沉积时间为120 min时获得的复合镀层具有较好的耐蚀性和耐磨性。     

AZ91D镁合金的均一化前处理与化学镀Ni-P

采用新型环保的均一化前处理工艺在AZ91D镁合金表面制备了化学镀Ni-P镀层。研究了前处理过程中AZ91D基体微观形貌、镀层沉积过程、成分和相结构。研究结果表明：基体表面的β相在前处理过程中被选择性去除,表面组织得到均一化,从而获得均匀致密的浸Zn层。Ni-P颗粒均匀形核生长,并最终形成致密的镀层。镀层具有优良的耐腐蚀性能。     

AZ91HP镁合金电沉积Ni-SiO_2纳米复合镀层的显微结构与耐磨性(英文)

以AZ91HP镁合金为研究对象,以纳米氧化硅为第二相粒子,通过纳米复合电沉积法制备AZ91HP镁合金Ni-SiO2纳米复合镀层。利用扫描电镜观察纳米复合镀层的显微形貌与微观结构,利用显微硬度计测定纳米复合镀层显微硬度,利用M200摩擦磨损试验机测试纳米复合镀层的耐磨性能。结果表明:在AZ91HP镁合金表面获得了结晶均匀、结构致密的Ni-SiO2纳米复合镀层;纳米复合镀层剖面形貌显示纳米复合镀层与镁合金基体结合良好;镀液中纳米颗粒含量为10g/L时,AZ91HP镁合金表面电沉积Ni-SiO2纳米复合镀层的显微硬度最高,最高达HV367;摩擦磨损试验表明纳米复合镀层与镀镍层、镁合金基体相比,耐磨性明显提高,这是由于纳米颗粒的细晶强化和弥散强化所致;纳米复合镀层的磨损机制主要是磨粒磨损,镁合金基体磨损机制为粘着磨损,镀镍层磨损机制为剥层磨损。     

热处理温度对AZ91D合金表面Ni-P-SiC复合镀层性能的影响

目的提高镁合金表面Ni-P-SiC复合镀层的耐腐蚀性能和耐磨性能。方法采用加入SiC微粒的Ni-P化学镀溶液,在AZ91D镁合金表面制备Ni-P-SiC复合镀层,并在不同温度下进行热处理,通过X射线衍射(XRD)、显微硬度测试、电化学腐蚀测试和摩擦磨损实验等方法分析和评价镀层的组织构成、显微硬度、耐腐蚀性能和耐磨性能。结果 Ni-P-SiC复合镀层经320℃热处理后,组织结构由非晶向晶体转变,并伴随有Ni3P相的析出。此温度下热处理的Ni-P-SiC复合镀层:显微硬度最高,可达1120HV,为未热处理时显微硬度(620HV)的1.81倍;自腐蚀电位为–0.697 V,较未热处理样品的(–0.727 V)有所提高;腐蚀电流密度基本最小,为0.984μA/cm~(–2);磨损体积最小,为0.324×10~(–3) mm~3。340℃热处理的复合镀层则磨损体积最大,为1.43×10~(–3) mm~3。结论在AZ91D镁合金表面制备的Ni-P-SiC复合镀层经过320℃热处理保温1 h后,复合镀层的硬度、耐腐蚀性能和耐磨性能均有所提高。     

纳米金刚石的加入对镁合金Ni-P镀层组织和性能的影响

目的提高镁合金化学镀层的力学性能。方法选择出一组优良镁合金化学镀Ni-P工艺参数,在Ni-P镀液中加入不同的纳米金刚石浓度。通过观察所得镀层的微观组织形貌,对比镀层形貌组织;通过对复合镀层进行热处理,分析镀层组织结构的变化;通过测定金刚石加入前后镀层的摩擦系数,检测了复合镀层的耐磨损性能;通过查看镀层腐蚀斑点数目,检测复合镀层的耐腐蚀性能。结果随着纳米金刚石浓度的增加,复合镀层的形貌越好,当纳米金刚石加入量达到6 g/L时,所得复合镀层的微观形貌均匀、致密。热处理使镀层结构由非晶态变为结晶态,显微硬度明显提高。金刚石的加入致使镀层的摩擦系数降低且稳定,相比化学镀Ni-P镀层,加入金刚石后的复合镀层的腐蚀斑点数较少。结论纳米金刚石的加入大大提高了镀层的力学性能。     

Corrosion and wear properties of electroless Ni-P plating layer on AZ91D magnesium alloy

A direct electroless Ni-P plating treatment was applied to AZ91D magnesium alloy for improving its corrosion resistance and wear resistance. Corrosion resistance of the Ni-P coatings was evaluated by potentiodynamic polarization and immersing experiments in 3.5% NaCl solution. The wear resistance of the coatings was investigated by the wear track and the mass change after ball-on-disk experiment. The results show that corrosion resistance and wear resistance of the AZ91D alloy are greatly improved after direct electroless Ni-P plating. No discoloration is noticed until 4 d of immersion in 3.5% NaC1 solution. Potentiodynamic polarization experiments show that the free corrosion potential of magnesium alloy is shifted from -1 500 mV to -250 mV and passivation occurs at 1 350 mV after direct electroless plating. The friction coefficients and wear rates of Ni-P coating and Ni-P coating after tempering are 0.10-0.351, 9.038×10^-3 mm^3/m and 0.13-0.177, 3.056×10^-4 mm^3/m, respectively, at a load of 1.5 N with dry sliding. Although minor hurt on corrosion resistance was caused, significant improvement of wear resistance was obtained after tempering treatment of the coating.     

A novel dual nickel coating on AZ91D magnesium alloy

Magnesium alloys covered with metal coating display excellent corrosion resistance,wear resistance,conductivity and electromagnetic shielding properties.The electroless plating Ni-P as bottom layer following the electroplating nickel as surface layer on AZ91D magnesium alloy was investigated.The coating surface morphology was observed with SEM and the structure was analyzed with XRD.Electrochemical tests and salt spray tests were carried out to study the corrosion resistance.The experimental results indi...     

锡酸盐转化前处理对镁合金化学镀镍镀层的影响

目的利用锡酸盐转化膜中间层避免化学镀镍镀层与金属基体的直接接触,降低其产生原电池腐蚀的趋势,提高镁合金化学镀镍层的耐蚀性及稳定性。方法采用锡酸盐化学转化膜技术在AZ31镁合金表面制备锡酸盐转化膜层,然后通过直接化学镀镍技术在该膜层上沉积Ni-P镀层。利用SEM、EDS、浸泡析氢、电化学测试等手段,研究了复合镀层的显微结构、相组成、耐蚀性。结果锡酸盐转化膜由细小均匀的球形颗粒堆积而成,颗粒之间存在空隙,为直接化学镀镍时镍磷的初始沉积提供了可能。化学转化膜表面沉积的化学镀镍层均匀致密,形成典型的胞状结构。基体-化学转化膜-化学镀Ni-P合金层三者之间的结合良好,保证了复合镀层优良的耐蚀性能。结论化学镀Ni-P层能够在不经过钯活化处理的条件下直接在锡酸盐转化膜上沉积,锡酸盐转化膜中间层避免了Ni-P阴极性镀层与阳极性镁基体的直接接触,降低了Ni-P镀层局部缺陷对整体防护效果的影响,提高了镀层的耐蚀性及耐久性。     

镁合金表面Ni+C涂层的耐腐蚀与耐磨性能研究

目的提高镁合金表面的耐腐蚀和耐磨损性能。方法采用非平衡磁控溅射离子镀技术与化学镀技术相结合,在GW83镁合金表面制备Ni+C复合膜层。通过扫描电子显微镜和拉曼光谱分析了薄膜的形貌、成分和结构。利用电化学和浸泡后ICP-AES测试,评价了该复合碳膜涂层的耐腐蚀性能。同时采用摩擦磨损试验获得Ni+C复合膜层的磨损寿命。结果 Ni+C复合膜层致密均匀,表面孔隙率极低,表面碳层为典型的类石墨膜并且含有大量的无序结构。相对于GW83镁合金来说,Ni+C复合膜层的存在导致在3.5%Na Cl溶液中的腐蚀电位正移了301 m V,腐蚀电流密度从186μA/cm2降低至11μA/cm2。浸渍后ICP-AES试验显示,Ni+C涂覆的镁合金GW83的金属离子释放量更低。摩擦磨损试验表明,Ni+C涂层的磨损寿命为7000 s,与镁合金基体相比,Ni+C复合涂层极大地提高了其磨损寿命。结论在该Ni+C复合膜层中,表面碳层较致密,与Ni层结合良好,显著提高了基体的耐腐蚀性能。此外由于存在较厚的Ni中间层,对膜层起到了较大的支撑作用,Ni+C复合膜层从而延长了基体镁合金的磨损寿命。     

ZrO2 加入量对Zr-8Al合金化学复合镀性能的影响

对Zr-8Al合金进行了化学复合镀Ni-P-ZrO_2处理,并研究了不同ZrO_2粒子加入量制备的复合镀层的显微结构、显微硬度、耐磨性和抗蚀性。结果表明,与单纯化学镀Ni-P镀层相比,Ni-P-ZrO_2复合镀层的显微硬度值显著提高,ZrO_2的添加量为4 g/L获得复合镀层显微硬度最高,耐磨性好;在3.5%(质量分数)NaCl溶液中耐蚀性虽有所下降,但腐蚀后镀层完整,仍具有较好的抗蚀性。Zr-8Al合金表面采用4 g/L ZrO_2粒子制备的Ni-P-ZrO_2复合镀层兼具很好的耐磨性和较好的耐蚀性,适用于既要耐磨又要抗蚀的空间活动构件。     

A new method for electroless Ni-P plating on AZ31 magnesium alloy

Coating Ni-P films on AZ31 magnesium alloys via electroless plating and organic coatings (organsilicon heat-resisting varnish), was studied. An organic coating was proposed as the interlayer between Ni-P coating and AZ31magnesium alloy substrate, to replace the traditional chromium oxide plus HF pretreatment. The Ni-P deposited on the interlayer was also characterized by its structure, morphology and corrosion-resistance. The interlayer on the substrate not only reduces the corrosion of magnesium during Ni-P plating process, but also reduces the potential difference between the matrix and the second phase. The result of the cross-cut test indicates the adhesion between the substrate and the interlayer is good enough. A Ni-P film with fine and dense structure was obtained on the AZ31 magnesium alloy. The electrochemical measurements show that the sample with Ni-P film exhibits lower corrosion current density and more positive corrosion potential than the substrate. Furthermore, the Ni-P coating on the AZ31 magnesium alloy exhibits high corrosion resistance in the rapid corrosion test illustrated in this paper. The method proposed in this work is environmentally friendly: no fluoride or hexacalent chromium compounds are used. In addition, it provides a new concept for plating the metals, which are considered difficult to plate due to high reactivity.     

镁合金化学镀中预处理氟化镁膜的特征与作用

对镁合金的表面前处理工艺进行研究,探讨氟化镁在化学镀层中的存在形式及作用。结果表明：酸浸使镁合金表面形成一层氧化物膜;活化过程生成的氟化镁不具备反应活性,对镁合金基体有保护作用,使之免于受镀液的过度腐蚀;对化学镀层断口进行SEM元素分布分析显示氟化镁层集中存在于镁合金基体与Ni-P镀层之间;但过度活化会导致化学镀层孔隙率升高,以3.5%NaCl溶液为介质的动电位极化测试表明,过度活化会导致化学镀层耐蚀性下降。