氧气闭环控制系统辅助反应磁控溅射沉积γ-Al_2O_3薄膜

采用双极脉冲反应磁控溅射方法在衬底温度300℃的条件下制备了结晶态γ相Al2O3薄膜。借用speedflo闭环控制系统,整个沉积过程持续稳定进行且沉积速率高达16 nm/min。XRD结果揭示,不同工作点下制备的薄膜均为单一相的γ-Al2O3。薄膜的硬度值受靶表面沉积状态影响很大,在反应模式状态下沉积的薄膜具有良好的硬度,而在靶表面中毒状态下沉积的薄膜硬度值很低。本文对硬度的变化原因做了详细的探讨。     

ECR结合磁控溅射——制备DLC薄膜的新方法

介绍了新型的结合电子回旋共振(ECR)微波等离子体气相沉积与磁控溅射镀膜特点的ECR-650型镀膜系统,并利用该系统通过溅射石墨靶和金属钛靶在不锈钢基底上制备了具有Ti/TiNx/TiNxCy中间层结构的C薄膜。由于镀膜工艺问题,得到的薄膜主要由石墨构成。研究了制备时不同的气压和氩气分压对薄膜表面形貌、硬度等的影响。     

钽喷丝头表面覆加金刚石膜的研究

为改善钽喷丝头的品质,提高其硬度和耐碱腐蚀能力,利用热丝CVD制备不同粒径的金刚石薄膜,并通过对钽衬底的碳化处理,成功使之沉积于纯钽啧丝头表面,对纯钽喷丝头进行表面强化.通过场发射扫描电镜观察,大粒径金刚石薄膜有少量孔隙,小粒径金刚石薄膜细腻致密.硬度测试结果表明,金刚石薄膜钽喷丝头表面硬度达HV1 000以上,远高于纯钽及其它工艺处理后的钽喷丝头.可纺性试验结果表明,其性能都达到或超过传统喷丝头,完全可以取代成本高昂的铂金喷丝头.     

不同介质下CrN_X薄膜的摩擦学特性研究

采用电弧离子镀技术在45#钢衬底表面沉积了CrNX薄膜.用显微硬度计测试了薄膜的硬度,用X射线衍射仪分析了薄膜的相结构,用球-盘式摩擦磨损试验机评价了在不同介质条件下(干摩擦、水润滑、油润滑)CrNX薄膜的摩擦学性能,用表面轮廓仪测试了磨痕处的磨痕轮廓,用扫描电镜(SEM)观察了薄膜磨痕形貌.结果表明,相对于干摩擦,水润滑和油润滑条件下,CrNX薄膜的摩擦因数和磨痕深度都有明显降低的趋势.干摩擦条件下薄膜主要表现为磨粒磨损;水润滑条件下,主要表现为腐蚀磨损;油润滑条件下由于油膜在两摩擦表面的吸附,薄膜几乎无磨损.     

衬底对溶胶-凝胶法制备ZnO压电薄膜的影响

采用溶胶-凝胶法分别在晶态衬底Si/SiO2/Ti/Pt和无定形态衬底Si/SiO2上制备了ZnO压电薄膜.以X射线衍射仪和原子力显微镜研究了薄膜的002择优取向度和表面形貌.结果表明,采用溶胶-凝胶法在Si/SiO2/Ti/Pt和Si/SiO2衬底上都能制备出具有较好择优取向,表面粗糙度低的ZnO薄膜,而且由于Pt和ZnO的晶格失配度较小,在Si/SiO2/Ti/Pt衬底上生长的ZnO薄膜形成002择优取向的退火温度低于在Si/SiO2衬底上生长的薄膜形成002择优取向的退火温度.     

磁控溅射法制备用作铜互连阻挡层的钛-铝薄膜

采用射频磁控溅射法在Si(100)基片上首先沉积了厚度40 nm的非晶钛-铝薄膜,然后在其上又原位生长了厚度100 nm的铜薄膜,制备了铜膜/钛-铝膜/硅试样;对试样分别在400～800℃内进行真空退火处理,用原子力显微镜、X射线衍射仪、四探针测试仪对试样的表面形貌、结晶状态及方块电阻进行了分析.结果表明:当退火温度低于750℃时,试样表面平整,表面粗糙度和方块电阻均较小且基本不随退火温度的升高而改变,此时,非晶钛-铝薄膜能够起到阻挡铜向硅中扩散的作用;当退火温度在800℃时,试样的表面粗糙度和方块电阻急剧增大,此时,非晶钛-铝薄膜已经不能起到阻挡层的作用.     

沉积温度对脉冲真空弧源沉积类金刚石薄膜性能的影响

利用脉冲真空弧源沉积技术在Cr17Ni14Cu4不锈钢和Si(100)基体上制备了类金刚石(DLC)薄膜,研究了基体沉积温度对DLC薄膜的性能和结构的影响。研究表明,随着沉积温度由100 ℃提高到400 ℃,DLC薄膜中sp3 键质量分数减少,sp2键质量分数增多,薄膜复合硬度逐渐降低。当DLC薄膜沉积温度达到400 ℃时,薄膜中C原子主要以sp2键形式存在,与沉积温度为100 ℃时制备的DLC薄膜相比,薄膜复合硬度降低50%。DLC薄膜具有优异的耐磨性,摩擦因数低,随着沉积温度由100 ℃提高到400 ℃,Cr17Ni14Cu4不锈钢表面沉积的DLC薄膜耐磨性降低。沉积温度为100 ℃时,Cr17Ni14Cu4不锈钢表面沉积的DLC薄膜后,耐磨性大幅度提高。DLC薄膜与不锈钢基体结合牢固。     

纳米结构碳基薄膜的制备及性能研究

利用单极脉冲等离子体增强化学气相沉积技术在单晶硅衬底上沉积含氢碳薄膜,用高分辨透射电子显微镜和激光拉曼光谱仪研究薄膜的微观结构,用X射线光电子能谱分析薄膜的化学键状态,并用纳米压痕仪测定薄膜的硬度和弹性模量,在CSM往复式摩擦磨损试验机上考察薄膜的摩擦学性能。结果表明:在单极脉冲等离子体增强化学气相沉积系统上成功制备出在非晶基体上镶嵌弯曲类富勒烯纳米结构的含氢碳薄膜,其独特的类富勒烯纳米结构赋予薄膜良好的力学性能,其弹性恢复系数和硬度分别高达86%和26.37 GPa;与非晶结构薄膜相比,制备的纳米结构含氢碳薄膜在室温环境下摩擦学性能更为优异,在机械摩擦表面具有广阔的应用前景。     

CVD金刚石涂层拉丝模温度场数值分析

衬底温度是热丝化学气相沉积(HFCVD)制备金刚石薄膜的重要参数之一,在拉丝模表面沉积CVD金刚石涂层时,均匀的衬底温度场显得尤为重要.对HFCVD系统中制备CVD金刚石涂层时拉丝模衬底温度场进行数值分析,得到了拉丝模温度场的分布和热丝参数对衬底温度场的影响规律,为CVD金刚石涂层拉丝模的制备提供重要指导.     

分子沉积膜的纳米压痕试验

制备了金衬底表面上的分子沉积膜，用原子力显微镜观测了其表面形貌；用纳米压痕仪研究其纳米力学特性。结果表明，沉积一层膜后衬底表面的弹性模量、硬度都减小，而且弹性变形增加，塑性变形减小，从而证明膜改善了金衬底的力学特性。     

叶切面最大厚度数值计算与应用

以叶切面最大厚度的数值计算方法为基础,探讨叶切面最大厚度计算的计算机实现,介绍叶切面厚度数值计算法的应用实例.     

Natural frequencies of vibration of a class of solids composed of layers of isotropic materials

In a recent paper, the Ritz method with simple algebraic polynomials as trial functions was used to obtain an eigenvalue equation for the free vibration of a class of homogeneous solids with cavities. The method presented is here extended to the study of a class of non-homogeneous solids, in which each solid is composed of a number of isotropic layers with different material properties. The Cartesian coordinate system is used to describe the geometry of the solid which is modelled by means of a segment bounded by the yz, zx and xy orthogonal coordinate planes and by two curved surfaces which are defined by fairly general polynomial expressions in the coordinates x, y and z. The surface representing the interface between two material layers in the solid is also described by a polynomial expression in the coordinates x, y and z. In order to demonstrate the accuracy of the approach, natural frequencies are given for both a two- and three-layered spherical shell and for a homogeneous hollow cylinder, as computed using the present approach, and are compared with those obtained using an exact solution. Results are then given for a number of two- and three-layered cylinders and, to demonstrate the versatility of the approach, natural frequencies are given for a five-layered cantilevered beam with a central circular hole as well as for a number of composite solids of more general shape.     

盘丝极心偏对三爪自定心卡盘找标精度影响的分析

三爪自定心卡盘作为机床的主要附件,已有一百多年的发展历史,尽管目前随着数控技术的不断发展,越来越多地需求高速动力卡盘,但三爪自定心卡盘目前仍有一定的市场。 要保证卡盘可靠地夹紧工件,必须使其有可靠的夹持精度;要保持卡盘的精度,必须要严格控制各零部件公差及误差,如盘丝的极心偏。 　　极心偏是形成圆的渐开线的基圆圆心 (极心 )与盘丝内孔中心不同心所造成的偏差值。它对卡盘精度的影响分两种情况,一是卡爪夹持弧采用配磨,二是卡爪夹持弧采用单磨。本文主要探讨配磨时的影响。 　　卡爪夹持弧采用配磨,即每台卡盘整体…     

双丝杠驱动机构同步分析

介绍了双丝杠驱动机构工作原理,论述了双丝杠运动产生不同步的原因以及如何判定与解决同步问题。     

圆柱面素线的直线度公差带解析

详细分析了圆柱面素线的直线度公差带在新旧标准中定义和解释的区别，并从对圆柱面素线实际要素检测的角度，提出了推行新标准的实际意义。     

膨胀套导向机构的设计

通过分析膨胀套在实际使用产生滑移受阻现象、卡死现象原因的实质,并在分析产生问题原因的基础上提出了改进措施即：增加导向机构。     

广州地铁APM列车制动机理分析

根据广州市珠江新城旅客自动运输系统(APM)列车的运行特点,介绍APM列车制动系统的制动方式及其特点,分析APM列车动态制动和摩擦制动的工作机理及其区别和联系,阐明APM列车制动系统的电控制过程和气控制过程,从而为APM列车制动系统的维护和管理提供一定的依据.     

磨粉机快辊轴承座加工工艺设计

设计了磨粉机快辊轴承座的加工工艺和具体的工装夹具.利用卧式加工中心加工磨粉机快辊轴承座,辅以能够高效快速夹紧的夹具,既可以保证加工精度,又能够提高加工效率.     

活塞销孔加工工艺的改进

我公司于８０年代末引进Aspera公司年产８０万台冰箱（冷柜）压缩机生产线及软件技术，在压缩机加工中，活塞销孔（如图１所示）的加工是难点之一。用镗床加工，质量一直难以达到要求，废品率很高。后来我们将Aspera公司的加工工艺即精镗后滚光改为精镗后用金刚石铰刀粗、精铰孔，由此解决了这个技术难题。（１）原意大利Aspera公司工艺简述其工艺流程为：钻６．５通孔→扩孔至７＋０．１→粗镗７．４７３＋０．０３６、圆柱度０．０１→精镗至７．９３５＋０．００６、圆柱度０．００２→滚光７．９３８＋０．００６、圆柱度０…     

我校工业设计教育改革初探

针对目前市场对工业设计人才的需求,本文论述了我校在工业设计教育方面的改革措施,着重介绍了我校工业设计教育在软件和硬件方面所进行的一系列的改革。